Avaliação do efeito da topografia de substratos macios no desempenho tribológico de revestimentos de DLC

Detalhes bibliográficos
Autor(a) principal: Soprano, Pedro Besen
Data de Publicação: 2016
Tipo de documento: Dissertação
Idioma: por
Título da fonte: Repositório Institucional da UFSC
Texto Completo: https://repositorio.ufsc.br/xmlui/handle/123456789/172339
Resumo: Dissertação (mestrado) - Universidade Federal de Santa Catarina, Centro Tecnológico, Programa de Pós-Graduação em Ciência e Engenharia de Materiais, Florianópolis, 2016.
id UFSC_738b83b91ae5593adb01ea8670f8a613
oai_identifier_str oai:repositorio.ufsc.br:123456789/172339
network_acronym_str UFSC
network_name_str Repositório Institucional da UFSC
repository_id_str 2373
spelling Universidade Federal de Santa CatarinaSoprano, Pedro BesenMello, José Daniel Biasoli deBinder, Cristiano2017-01-17T03:12:56Z2017-01-17T03:12:56Z2016343192https://repositorio.ufsc.br/xmlui/handle/123456789/172339Dissertação (mestrado) - Universidade Federal de Santa Catarina, Centro Tecnológico, Programa de Pós-Graduação em Ciência e Engenharia de Materiais, Florianópolis, 2016.Dentre os diversos tipos de lubrificantes sólidos, um grupo de materiais a base de carbono conhecidos como carbono tipo diamante, ou Diamond-like Carbon (DLC), tem se destacado nas últimas décadas por apresentar elevada resistência ao desgaste, além das propriedades autolu-brificantes. Em geral, estes filmes são aplicados sobre substratos de ele-vado suporte mecânico para garantir a integridade dos filmes durante os contatos tribológicos. Neste contexto, o Laboratório de Materiais da Uni-versidade Federal de Santa Catarina (LabMat/UFSC) desenvolveu o pro-cesso CH?® que permite a deposição de filmes de DLC sobre substratos de baixo suporte mecânico, devido a nitretação prévia da superfície. No presente trabalho avaliou-se a influência da topografia de substratos de aço SAE 1020 nitretados e revestidos com DLC pelo processo CH?® no desempenho tribológico. Para tanto, amostras foram preparadas em cinco condições de acabamento superficial, obtendo-se superfícies com rugosi-dade média quadrática entre 0,01 e 0,25 µm. As superfícies foram anali-sadas por microscopia eletrônica de varredura e interferometria óptica de luz branca, antes e após processo de nitretação e deposição de DLC. Ape-sar da diferença topográfica inicial, após o tratamento a plasma as condi-ções avaliadas puderam ser agrupadas em duas famílias com característi-cas topográficas semelhantes, nomeadas Rugosas e Lisas. A espessura dos filmes formados foi medida por metalografia, e não apresentou alte-ração com a variação da topografia do substrato. Da mesma maneira a dureza e módulo elástico, medidos via nano indentação, não apresentaram variação nas condições estudas. Além disto, a configuração das ligações químicas foi avaliada por espectroscopia Raman e os filmes formados se mostraram homogêneos. A adesividade das amostras foi avaliada por in-dentação Rockwell-C, entretanto os resultados foram inconclusivos. A avaliação do desempenho tribológico foi realizada através de testes de durabilidade com configuração de esfera sobre plano ao ar. Assim como observado na análise topográfica, as condições avaliadas também pude-ram ser classificadas em Rugosas e Lisas de acordo com os coeficientes de atrito e durabilidade observados. Coeficientes de atrito da ordem de 0,05 foram observados nas superfícies Lisas, cerca de 50% menor queviiiaqueles observados nas amostras Rugosas. Através de alterações no es-pectro Raman obtido nas pistas de desgaste foi possível evidenciar a for-mação de tribocamadas nas superfícies das superfícies Lisas, juntamente com as imagens de MEV e análises químicas por EDS, justificam a redu-ção no coeficiente de atrito. Em síntese, a topografia do substrato influên-cia significativamente na formação de tribocamadas e, consequente-mente, no desempenho tribológico de filmes de DLC.<br>Abstract : Among the various types of solid lubricants, one group of carbon based materials known as Diamond-like Carbon (DLC), have been under the spotlight in the last decades due to have high wear resistance in addi-tion to the self-lubricating properties. In general, these films are applied over substrate that hold high mechanical support and therefore to assure the integrity of the DLC films during tribological contacts. Within this context, the Materials Laboratory (LabMat) from UFSC has developed the CH?® process, which allows the deposition of DLC films over soft metallic substrates, once the surfaces are nitrided prior to the deposition. The present study evaluated the influence of the topography of SAE 1020 steel substrates, which were nitrided and coated with DLC through the CH?® process, on the tribological performance of the components. To do so, samples were prepared in five surface finishing conditions, yielding with root mean square roughnesses (Sq) ranging from 0.01 to 0.25 µm. The surfaces were assessed through Scanning Electron Microscopy and White Light Optical iInterferometry before and after the nitriding and DLC deposition processes. Despite the initial topographical distinction between the conditions, the plasma surface treatment lead to two groups of samples with similar topographic features, named Rough and Smooth. The film thickness, which was measured by Optical Microscopy of metal-lographically prepared samples, is independent of surface topography. Likewise, no variation was observed in the hardness and the modulus. Furthermore, the configuration of the chemical bonds was evaluated through by Raman spectroscopy and the formed films were considered homogeneous. The adhesion of the samples was evaluated by Rockwell-C indentation however, the results were inconclusive. The tribological performance was assessed by durability tests on ball-to-plane tribotester in ambient air. As observed in the topographic analysis, the evaluated conditions were classified Rough and Smooth, according the measured friction coefficient and durability. Friction coefficients as low as 0.05 were observed for tribological system of the Smooth surfaces, about 50% lower than those measured on the Rough conditions. Due to changes inxthe Raman spectrum obtained from the wear scars, it was possible to iden-tify the formation tribofilms on the Smooth surfaces. In addition to the Raman analysis, SEM and EDS results supports the comprehension of the reduction of the friction coefficient measured on the Smooth samples. In summary, the substrate topography significantly influences tribofilms formation and tribological performance of DLC films.67 p.| il., grafs., tabs.porEngenharia de materiaisFilmes finos de diamantesLubrificação e lubrificantesTribologiaAvaliação do efeito da topografia de substratos macios no desempenho tribológico de revestimentos de DLCinfo:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/masterThesisreponame:Repositório Institucional da UFSCinstname:Universidade Federal de Santa Catarina (UFSC)instacron:UFSCinfo:eu-repo/semantics/openAccessORIGINAL343192.pdfapplication/pdf2942271https://repositorio.ufsc.br/bitstream/123456789/172339/1/343192.pdfba0bd67769b2ca044a6a666e41c061c4MD51123456789/1723392017-01-17 01:12:56.601oai:repositorio.ufsc.br:123456789/172339Repositório de PublicaçõesPUBhttp://150.162.242.35/oai/requestopendoar:23732017-01-17T03:12:56Repositório Institucional da UFSC - Universidade Federal de Santa Catarina (UFSC)false
dc.title.pt_BR.fl_str_mv Avaliação do efeito da topografia de substratos macios no desempenho tribológico de revestimentos de DLC
title Avaliação do efeito da topografia de substratos macios no desempenho tribológico de revestimentos de DLC
spellingShingle Avaliação do efeito da topografia de substratos macios no desempenho tribológico de revestimentos de DLC
Soprano, Pedro Besen
Engenharia de materiais
Filmes finos de diamantes
Lubrificação e lubrificantes
Tribologia
title_short Avaliação do efeito da topografia de substratos macios no desempenho tribológico de revestimentos de DLC
title_full Avaliação do efeito da topografia de substratos macios no desempenho tribológico de revestimentos de DLC
title_fullStr Avaliação do efeito da topografia de substratos macios no desempenho tribológico de revestimentos de DLC
title_full_unstemmed Avaliação do efeito da topografia de substratos macios no desempenho tribológico de revestimentos de DLC
title_sort Avaliação do efeito da topografia de substratos macios no desempenho tribológico de revestimentos de DLC
author Soprano, Pedro Besen
author_facet Soprano, Pedro Besen
author_role author
dc.contributor.pt_BR.fl_str_mv Universidade Federal de Santa Catarina
dc.contributor.author.fl_str_mv Soprano, Pedro Besen
dc.contributor.advisor1.fl_str_mv Mello, José Daniel Biasoli de
dc.contributor.advisor-co1.fl_str_mv Binder, Cristiano
contributor_str_mv Mello, José Daniel Biasoli de
Binder, Cristiano
dc.subject.classification.pt_BR.fl_str_mv Engenharia de materiais
Filmes finos de diamantes
Lubrificação e lubrificantes
Tribologia
topic Engenharia de materiais
Filmes finos de diamantes
Lubrificação e lubrificantes
Tribologia
description Dissertação (mestrado) - Universidade Federal de Santa Catarina, Centro Tecnológico, Programa de Pós-Graduação em Ciência e Engenharia de Materiais, Florianópolis, 2016.
publishDate 2016
dc.date.issued.fl_str_mv 2016
dc.date.accessioned.fl_str_mv 2017-01-17T03:12:56Z
dc.date.available.fl_str_mv 2017-01-17T03:12:56Z
dc.type.status.fl_str_mv info:eu-repo/semantics/publishedVersion
dc.type.driver.fl_str_mv info:eu-repo/semantics/masterThesis
format masterThesis
status_str publishedVersion
dc.identifier.uri.fl_str_mv https://repositorio.ufsc.br/xmlui/handle/123456789/172339
dc.identifier.other.pt_BR.fl_str_mv 343192
identifier_str_mv 343192
url https://repositorio.ufsc.br/xmlui/handle/123456789/172339
dc.language.iso.fl_str_mv por
language por
dc.rights.driver.fl_str_mv info:eu-repo/semantics/openAccess
eu_rights_str_mv openAccess
dc.format.none.fl_str_mv 67 p.| il., grafs., tabs.
dc.source.none.fl_str_mv reponame:Repositório Institucional da UFSC
instname:Universidade Federal de Santa Catarina (UFSC)
instacron:UFSC
instname_str Universidade Federal de Santa Catarina (UFSC)
instacron_str UFSC
institution UFSC
reponame_str Repositório Institucional da UFSC
collection Repositório Institucional da UFSC
bitstream.url.fl_str_mv https://repositorio.ufsc.br/bitstream/123456789/172339/1/343192.pdf
bitstream.checksum.fl_str_mv ba0bd67769b2ca044a6a666e41c061c4
bitstream.checksumAlgorithm.fl_str_mv MD5
repository.name.fl_str_mv Repositório Institucional da UFSC - Universidade Federal de Santa Catarina (UFSC)
repository.mail.fl_str_mv
_version_ 1766804992185860096

Registros relacionados