Análise experimental do uso de resíduo do bagaço de cevada para a fabricação de compósitos poliméricos de resina poliéster

Detalhes bibliográficos
Autor(a) principal: Corrêa, Gabriel Luiz
Data de Publicação: 2023
Tipo de documento: Trabalho de conclusão de curso
Idioma: por
Título da fonte: Repositório Institucional da UFSC
Texto Completo: https://repositorio.ufsc.br/handle/123456789/253078
Resumo: TCC (graduação) - Universidade Federal de Santa Catarina. Centro Tecnológico, de Ciências Exatas e Educação. Engenharia de Materiais.
id UFSC_82bbcb90df17e6f654d9a3ef8096bf5b
oai_identifier_str oai:repositorio.ufsc.br:123456789/253078
network_acronym_str UFSC
network_name_str Repositório Institucional da UFSC
repository_id_str 2373
spelling Análise experimental do uso de resíduo do bagaço de cevada para a fabricação de compósitos poliméricos de resina poliésterResíduo cervejeiroModificação superficialResina poliésterCompósitos poliméricosTCC (graduação) - Universidade Federal de Santa Catarina. Centro Tecnológico, de Ciências Exatas e Educação. Engenharia de Materiais.A crescente preocupação global quanto à preservação do meio ambiente, geração de resíduos e utilização de materiais oriundos de fontes não renováveis impulsionam pesquisas em diversos setores cujo principal objetivo é desenvolver novas tecnologias e recursos que atendam aos requisitos ambientais desejados. Dessa forma, o objetivo deste trabalho é avaliar a morfologia e propriedades físico-químicas do bagaço de cevada, resíduo do processo cervejeiro, e a influência da sua utilização em diferentes frações volumétricas nas propriedades de compósitos poliméricos fabricados com matriz de poliéster. Inicialmente, o resíduo foi modificado através de soluções aquosas de hidróxido de sódio de concentrações 1%, 3%, 5% e 10% durante 1 hora. O resíduo tratado foi caracterizado através das técnicas de determinação de densidade por picnometria, análise de perda de massa, microscopia eletrônica de varredura com detector de energia dispersiva (MEV-EDS), espectroscopia no infravermelho por transformada de Fourier (FTIR) e análise termogravimétrica (TGA). Observou-se que o resíduo possui morfologia e composição químicas semelhantes às fibras vegetais e que o tratamento alcalino retira componentes da superfície, modificando a estrutura do resíduo. Os resíduos tratados com diferentes condições foram utilizados para a fabricação de compósitos poliméricos com frações volumétricas de 35% vol. de resíduo, através de moldagem por compressão. Os compósitos foram caracterizados através de ensaios de tração, FTIR, TGA e MEV. Com base nos resultados observou-se que compósitos com resíduos tratados com concentração de 5% de NaOH, resultaram em melhores propriedades no ensaio de tração. Assim, posteriormente, na segunda parte foram fabricados compósitos com frações volumétricas de 10% vol. e 20% vol. de resíduo nos estados sem tratamento e com o tratamento alcalino correspondente a melhor condição observada, 5% de NaOH. Observou-se que os resultados dos ensaios de tração dos compósitos se mantêm praticamente constantes de acordo com cada tipo de resíduo utilizado na fabricação, indicando que não há efeito sobre o reforço mecânico. Esse resultado é comprovado pelos ensaios de FTIR e MEV, que não apresentam sinais de interação entre o resíduo de cevada e a matriz de poliéster.The growing global concern regarding environmental preservation, waste generation and use of materials from non-renewable sources drives research in various sectors whose main objective is to develop new technologies and resources that meet the desired environmental requirements. Therefore, the objective of this work is to evaluate the morphology and physicalchemical properties of barley bagasse, a brewing process residue, and the influence of its use in different volumetric fractions on the properties of polyester matrix polymer composites. Initially, barley bagasse was modified by aqueous sodium hydroxide solutions with concentrations of 1%, 3%, 5% and 10% for 1 hour. The residue samples were characterized through density determination tests by solid pycnometry, mass loss analysis, scanning electron microscopy with energy dispersive detector (SEM-EDS), Fourier transform infrared spectroscopy (FTIR) and thermogravimetric analysis (TGA). It was observed that barley bagasse has a morphology and chemical composition similar to vegetable fibers and that the alkaline treatment removes components from the surface, modifying the structure of the bagasse. The waste treated with different conditions was used to manufacture polymer composites with volume fractions of 35% vol. of residue, through room temperature compression molding. The composites were characterized through tensile tests, FTIR, TGA and SEM. Based on the results, it was observed that compounds with residues treated with a concentration of 5% NaOH resulted in better properties in the tensile test. Thus, subsequently, compounds with volumetric fractions of 10% vol. and 20% vol. of residue in the untreated states and with the alkaline treatment corresponding to the best observed condition, 5% NaOH, were manufactured. It was observed that the results of the tensile tests of the composites remained practically constant according to each type of bagasse used in manufacturing when comparing different volumetric fractions, showing that there is no positive mechanical reinforcement effect. This result is confirmed by FTIR and SEM tests, which show no signs of interaction between barley exposure and the polyester matrix.Blumenau, SCMerlini, ClaudiaUniversidade Federal de Santa Catarina.Corrêa, Gabriel Luiz2023-12-13T17:04:14Z2023-12-13T17:04:14Z2023-11-30info:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/bachelorThesis77 f.application/pdfhttps://repositorio.ufsc.br/handle/123456789/253078Open Access.info:eu-repo/semantics/openAccessporreponame:Repositório Institucional da UFSCinstname:Universidade Federal de Santa Catarina (UFSC)instacron:UFSC2023-12-13T17:04:14Zoai:repositorio.ufsc.br:123456789/253078Repositório InstitucionalPUBhttp://150.162.242.35/oai/requestopendoar:23732023-12-13T17:04:14Repositório Institucional da UFSC - Universidade Federal de Santa Catarina (UFSC)false
dc.title.none.fl_str_mv Análise experimental do uso de resíduo do bagaço de cevada para a fabricação de compósitos poliméricos de resina poliéster
title Análise experimental do uso de resíduo do bagaço de cevada para a fabricação de compósitos poliméricos de resina poliéster
spellingShingle Análise experimental do uso de resíduo do bagaço de cevada para a fabricação de compósitos poliméricos de resina poliéster
Corrêa, Gabriel Luiz
Resíduo cervejeiro
Modificação superficial
Resina poliéster
Compósitos poliméricos
title_short Análise experimental do uso de resíduo do bagaço de cevada para a fabricação de compósitos poliméricos de resina poliéster
title_full Análise experimental do uso de resíduo do bagaço de cevada para a fabricação de compósitos poliméricos de resina poliéster
title_fullStr Análise experimental do uso de resíduo do bagaço de cevada para a fabricação de compósitos poliméricos de resina poliéster
title_full_unstemmed Análise experimental do uso de resíduo do bagaço de cevada para a fabricação de compósitos poliméricos de resina poliéster
title_sort Análise experimental do uso de resíduo do bagaço de cevada para a fabricação de compósitos poliméricos de resina poliéster
author Corrêa, Gabriel Luiz
author_facet Corrêa, Gabriel Luiz
author_role author
dc.contributor.none.fl_str_mv Merlini, Claudia
Universidade Federal de Santa Catarina.
dc.contributor.author.fl_str_mv Corrêa, Gabriel Luiz
dc.subject.por.fl_str_mv Resíduo cervejeiro
Modificação superficial
Resina poliéster
Compósitos poliméricos
topic Resíduo cervejeiro
Modificação superficial
Resina poliéster
Compósitos poliméricos
description TCC (graduação) - Universidade Federal de Santa Catarina. Centro Tecnológico, de Ciências Exatas e Educação. Engenharia de Materiais.
publishDate 2023
dc.date.none.fl_str_mv 2023-12-13T17:04:14Z
2023-12-13T17:04:14Z
2023-11-30
dc.type.status.fl_str_mv info:eu-repo/semantics/publishedVersion
dc.type.driver.fl_str_mv info:eu-repo/semantics/bachelorThesis
format bachelorThesis
status_str publishedVersion
dc.identifier.uri.fl_str_mv https://repositorio.ufsc.br/handle/123456789/253078
url https://repositorio.ufsc.br/handle/123456789/253078
dc.language.iso.fl_str_mv por
language por
dc.rights.driver.fl_str_mv Open Access.
info:eu-repo/semantics/openAccess
rights_invalid_str_mv Open Access.
eu_rights_str_mv openAccess
dc.format.none.fl_str_mv 77 f.
application/pdf
dc.publisher.none.fl_str_mv Blumenau, SC
publisher.none.fl_str_mv Blumenau, SC
dc.source.none.fl_str_mv reponame:Repositório Institucional da UFSC
instname:Universidade Federal de Santa Catarina (UFSC)
instacron:UFSC
instname_str Universidade Federal de Santa Catarina (UFSC)
instacron_str UFSC
institution UFSC
reponame_str Repositório Institucional da UFSC
collection Repositório Institucional da UFSC
repository.name.fl_str_mv Repositório Institucional da UFSC - Universidade Federal de Santa Catarina (UFSC)
repository.mail.fl_str_mv
_version_ 1808652034481586176

Registros relacionados