Obtenção de granilhas por gelificação de suspensões cerâmicas

Detalhes bibliográficos
Autor(a) principal: Figueira, Fernando Cardoso
Data de Publicação: 2013
Tipo de documento: Dissertação
Idioma: por
Título da fonte: Repositório Institucional da UFSC
Texto Completo: https://repositorio.ufsc.br/handle/123456789/106998
Resumo: Dissertação (mestrado) - Universidade Federal de Santa Catarina, Programa de Pós-Graduação em Ciência e Engenharia de Materiais, Florianópolis, 2013.
id UFSC_8dc0881eb75fe9c53a2d2afea901221f
oai_identifier_str oai:repositorio.ufsc.br:123456789/106998
network_acronym_str UFSC
network_name_str Repositório Institucional da UFSC
repository_id_str 2373
spelling Universidade Federal de Santa CatarinaFigueira, Fernando CardosoHotza, DachamirBernardin, Adriano Michael2013-12-05T22:56:33Z2013-12-05T22:56:33Z2013319581https://repositorio.ufsc.br/handle/123456789/106998Dissertação (mestrado) - Universidade Federal de Santa Catarina, Programa de Pós-Graduação em Ciência e Engenharia de Materiais, Florianópolis, 2013.O alginato de sódio é um polissacarídeo encontrado tanto na matriz intercelular de algas marrons como em algumas espécies de bactérias. Devido a suas propriedades estabilizantes, gelificantes e espessantes, o alginato é amplamente usado industrialmente. Neste trabalho, o alginato de sódio é avaliado quanto à ação de promover a gelificação de uma suspensão cerâmica, gerando granilhas cerâmicas com forma de pequenos grânulos. As granilhas são matérias-primas amplamente utilizadas na indústria cerâmica de revestimento, pois conferem às placas de pavimento propriedades como resistência à abrasão, risco, e deslizamento, além de efeitos de textura. Inicialmente, foi desenvolvido um esmalte mate, sendo avaliado seu comportamento reológico e realizada sua caracterização físico-química. O alginato de sódio foi adicionado ao esmalte cerâmico durante a etapa de moagem e então pulverizado sobre uma solução de cloreto de cálcio com auxílio de uma pistola aerógrafa. As variáveis envolvidas no processo de obtenção das granilhas foram a fonte e a concentração de alginato de sódio e concentração de cloreto de cálcio, cada uma avaliada a dois níveis segundo um planejamento experimental estatístico. Os alginatos foram caracterizados quanto ao seu comportamento reológico, peso molecular e razão entre ácidos manurônicos e gulurônicos. As granilhas a verde foram avaliadas quanto a sua resistência mecânica à compressão, e a superfície dos grânulos foi analisada por microscopia eletrônica de varredura. As granilhas foram aplicadas sobre placas de pavimento e queimadas em forno a rolo. Os revestimentos cerâmicos foram avaliados quanto à resistência à abrasão superficial, resistência ao ataque químico e por microscopia óptica. Os resultados mostram que a resistência mecânica dos grânulos é afetada pela fonte e concentração de alginato de sódio e concentração de cloreto de cálcio. A morfologia, superfície e porosidade da superfície dos grânulos a verde não sofreram influência das variáveis envolvidas no processo de sua produção. As propriedades finais como resistência à abrasão superficial e resistência ao ataque químico das placas de revestimento cerâmico contendo as granilhas não apresentaram diferenças relacionadas às variáveis de processo. As imagens de microscopia óptica realizada nas placas de revestimento após o ensaio de abrasão mostram que existe uma relação entre a área e tamanho médio dos poros com a fonte de alginato de sódio empregada para obtenção das granilhas. <br>Abstract : Sodium alginate is a polysaccharide found both in the intercellular matrix of brown algae and in some species of bacteria. Due to its stabilizing, thickening and gelling properties, alginate is widely used industrially. In this work sodium alginate is evaluated regarding the action of promoting the gellification of a ceramic suspension generating ceramic grits with form of small granules. Grits are materials widely used in the ceramic tile industry because they give the tile properties such as resistance to abrasion, scratch and slippage, as well as texture effects.Initially, a ceramic matte glaze was developed, and its rheological behavior and physicochemical characterization were carried out. Sodium alginate was added to the ceramic glaze during the grinding step and then pulverized into a solution of calcium chloride with the aid of a spray. The variables involved in obtaining the grits were source and concentration of sodium alginate, and calcium chloride concentration. Each variable was evaluated at two levels in a design of experiments (DoE). Sodium alginates were characterized regarding rheological behavior, molecular weight and ratio of mannuronic and guluronic acid. The green grits were evaluated by compression strength and the surface of the beads was analyzed by scanning electron microscopy. The grits were applied on tiles and fired in roller oven. Ceramic tiles were evaluated for surface abrasion resistance, resistance to chemical attack and by optical microscopy. The results show that the mechanical strength of the granules is affected by the source and concentration of sodium alginate and calcium chloride concentration. The morphology, surface area and porosity of the surface of the green granules were not influenced by variables of production process. The final properties such as surface abrasion resistance and resistance to chemical attack of tiles containing the granilhas showed no differences related to process variables. Optical microscopy images carried out in tiles after abrasion test showed that there is a relationship between the average size and area of pores with a source of sodium alginate used to obtain the grits.78 p.| il., grafs., tabs.porCiencia dos materiaisEngenharia de materiaisCerâmica (Tecnologia)AlginatosObtenção de granilhas por gelificação de suspensões cerâmicasinfo:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/masterThesisreponame:Repositório Institucional da UFSCinstname:Universidade Federal de Santa Catarina (UFSC)instacron:UFSCinfo:eu-repo/semantics/openAccessORIGINAL319581.pdfapplication/pdf6119956https://repositorio.ufsc.br/bitstream/123456789/106998/1/319581.pdf9377e5c2ee1315b5c7699d80d0c26d5aMD51TEXT319581.pdf.txt319581.pdf.txtExtracted texttext/plain107562https://repositorio.ufsc.br/bitstream/123456789/106998/2/319581.pdf.txt30ffa54a43b80623fa28fb1a2bdb10f9MD52123456789/1069982016-03-07 15:55:21.617oai:repositorio.ufsc.br:123456789/106998Repositório de PublicaçõesPUBhttp://150.162.242.35/oai/requestopendoar:23732016-03-07T18:55:21Repositório Institucional da UFSC - Universidade Federal de Santa Catarina (UFSC)false
dc.title.en.fl_str_mv Obtenção de granilhas por gelificação de suspensões cerâmicas
title Obtenção de granilhas por gelificação de suspensões cerâmicas
spellingShingle Obtenção de granilhas por gelificação de suspensões cerâmicas
Figueira, Fernando Cardoso
Ciencia dos materiais
Engenharia de materiais
Cerâmica (Tecnologia)
Alginatos
title_short Obtenção de granilhas por gelificação de suspensões cerâmicas
title_full Obtenção de granilhas por gelificação de suspensões cerâmicas
title_fullStr Obtenção de granilhas por gelificação de suspensões cerâmicas
title_full_unstemmed Obtenção de granilhas por gelificação de suspensões cerâmicas
title_sort Obtenção de granilhas por gelificação de suspensões cerâmicas
author Figueira, Fernando Cardoso
author_facet Figueira, Fernando Cardoso
author_role author
dc.contributor.en.fl_str_mv Universidade Federal de Santa Catarina
dc.contributor.author.fl_str_mv Figueira, Fernando Cardoso
dc.contributor.advisor1.fl_str_mv Hotza, Dachamir
dc.contributor.advisor-co1.fl_str_mv Bernardin, Adriano Michael
contributor_str_mv Hotza, Dachamir
Bernardin, Adriano Michael
dc.subject.classification.en.fl_str_mv Ciencia dos materiais
Engenharia de materiais
Cerâmica (Tecnologia)
Alginatos
topic Ciencia dos materiais
Engenharia de materiais
Cerâmica (Tecnologia)
Alginatos
description Dissertação (mestrado) - Universidade Federal de Santa Catarina, Programa de Pós-Graduação em Ciência e Engenharia de Materiais, Florianópolis, 2013.
publishDate 2013
dc.date.accessioned.fl_str_mv 2013-12-05T22:56:33Z
dc.date.available.fl_str_mv 2013-12-05T22:56:33Z
dc.date.issued.fl_str_mv 2013
dc.type.status.fl_str_mv info:eu-repo/semantics/publishedVersion
dc.type.driver.fl_str_mv info:eu-repo/semantics/masterThesis
format masterThesis
status_str publishedVersion
dc.identifier.uri.fl_str_mv https://repositorio.ufsc.br/handle/123456789/106998
dc.identifier.other.en.fl_str_mv 319581
identifier_str_mv 319581
url https://repositorio.ufsc.br/handle/123456789/106998
dc.language.iso.fl_str_mv por
language por
dc.rights.driver.fl_str_mv info:eu-repo/semantics/openAccess
eu_rights_str_mv openAccess
dc.format.none.fl_str_mv 78 p.| il., grafs., tabs.
dc.source.none.fl_str_mv reponame:Repositório Institucional da UFSC
instname:Universidade Federal de Santa Catarina (UFSC)
instacron:UFSC
instname_str Universidade Federal de Santa Catarina (UFSC)
instacron_str UFSC
institution UFSC
reponame_str Repositório Institucional da UFSC
collection Repositório Institucional da UFSC
bitstream.url.fl_str_mv https://repositorio.ufsc.br/bitstream/123456789/106998/1/319581.pdf
https://repositorio.ufsc.br/bitstream/123456789/106998/2/319581.pdf.txt
bitstream.checksum.fl_str_mv 9377e5c2ee1315b5c7699d80d0c26d5a
30ffa54a43b80623fa28fb1a2bdb10f9
bitstream.checksumAlgorithm.fl_str_mv MD5
MD5
repository.name.fl_str_mv Repositório Institucional da UFSC - Universidade Federal de Santa Catarina (UFSC)
repository.mail.fl_str_mv
_version_ 1766804964039983104

Registros relacionados