Estudo da variação dimensional de porcelanato esmaltado de grande formato

Detalhes bibliográficos
Autor(a) principal: Pinter Junior, Jamilson
Data de Publicação: 2020
Tipo de documento: Dissertação
Idioma: por
Título da fonte: Repositório Institucional da UFSC
Texto Completo: https://repositorio.ufsc.br/handle/123456789/215817
Resumo: Dissertação (mestrado) - Universidade Federal de Santa Catarina, Centro Tecnológico, Programa de Pós-Graduação em Ciência e Engenharia de Materiais, Florianópolis, 2020.
id UFSC_90aa2f8eeec091845796e17a9457ad93
oai_identifier_str oai:repositorio.ufsc.br:123456789/215817
network_acronym_str UFSC
network_name_str Repositório Institucional da UFSC
repository_id_str 2373
spelling Universidade Federal de Santa CatarinaPinter Junior, JamilsonPereira, Fabiano RauppNoni Junior, Agenor de2020-10-21T21:22:17Z2020-10-21T21:22:17Z2020370469https://repositorio.ufsc.br/handle/123456789/215817Dissertação (mestrado) - Universidade Federal de Santa Catarina, Centro Tecnológico, Programa de Pós-Graduação em Ciência e Engenharia de Materiais, Florianópolis, 2020.Nos revestimentos cerâmicos de grandes formatos é comum o surgimento de um defeito denominado ?curvatura diferida?. Este defeito está relacionado com a variação dimensional desenvolvida na forma de empeno desde a saída do forno até períodos de meses de armazenamento. Esse fenômeno é relacionado a tensões residuais geradas no interior destas grandes peças cerâmicas que ocorrem devido a formação de fases liquidas durante a sinterização. O presente trabalho objetivou correlacionar a influência da interação das matérias-primas e os parâmetros do processo produtivo com a absorção de água e com a variação dimensional como meio de desenvolver uma alternativa de controle processual para minimização do fenômeno de ?curvatura diferida?. Com base neste objetivo, realizou-se a caracterização físico-química individual de todas as matérias-primas da formulação padrão selecionada para o desenvolvimento do estudo. As análises de variação dimensional desenvolvidas em laboratório foram realizadas a partir da investigação das caracterizações tecnológicas e dos parâmetros de controle processual aplicados aos revestimentos produzidos com a formulação padrão. Estas análises perduraram por 10 dias e foram realizadas em duas temperaturas distintas: 1191°C (temperatura de produção) e 1203 °C (temperatura de teste), estabelecendo um range de avaliação de 12 °C, para garantir a redução da absorção de água. Dentro dessa condição, verificou-se que nas temperaturas mais elevadas, as peças tendem a minimizar as variações dimensionais devido a maior formação de fase liquida. Avaliações realizadas em escala piloto revelaram que as peças de porcelanato tendem a estabilizar as tenções ao longo de 72 horas após tratamento térmico (queima), diminuindo significativamente a variação dimensional destes revestimentos de grande formato. Com base nos resultados coletados, conseguiu-se criar um método de correlação com base na absorção de água, que demonstra que o comportamento de curvatura tem sua amplitude e velocidade de estabilização alteradas juntamente com a alteração da absorção de água.Abstract: In large-format ceramic tiles, a defect called ?delayed curvature? is common. This defect is related to the dimensional variation developed in the form of warping from the exit of the oven to periods of months of storage. This phenomenon is related to residual stresses generated inside these large ceramic pieces that occur due to the formation of liquid phases during sintering. The present work aimed to correlate the influence of the interaction of raw materials and the parameters of the production process with the water absorption and with the dimensional variation as a means of developing an alternative of procedural control to minimize the phenomenon of \"delayed curvature\". Based on this objective, the individual physical-chemical characterization of all raw materials of the standard formulation selected for the development of the study was carried out. The dimensional variation analyzes developed in the laboratory were carried out from the investigation of technological characterizations and procedural control parameters applied to coatings produced with the standard formulation. These analyzes lasted for 10 days and were carried out at two different temperatures: 1191 °C (production temperature) and 1203 °C (test temperature), establishing an evaluation range of 12 °C, to guarantee the reduction of water absorption. Within this condition, it was found that at higher temperatures, parts tend to minimize dimensional variations due to greater liquid phase formation. Evaluations carried out on a pilot scale revealed that the porcelain tiles tend to stabilize the strains over 72 hours after heat treatment (firing), significantly reducing the dimensional variation of these large format coatings. Based on the results collected, it was possible to create a correlation method based on water absorption, which demonstrates that the curvature behavior has its amplitude and stabilization speed altered together with the alteration of water absorption.63 p.| il., gráfs.porEngenharia de materiaisRevestimento cerâmicoPorcelanatosEstudo da variação dimensional de porcelanato esmaltado de grande formatoinfo:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/masterThesisreponame:Repositório Institucional da UFSCinstname:Universidade Federal de Santa Catarina (UFSC)instacron:UFSCinfo:eu-repo/semantics/openAccessORIGINALPCEM0552-D.pdfPCEM0552-D.pdfapplication/pdf1528604https://repositorio.ufsc.br/bitstream/123456789/215817/-1/PCEM0552-D.pdf9cf49a78ea356c1a840d06bbfd617f70MD5-1123456789/2158172020-10-21 18:22:17.797oai:repositorio.ufsc.br:123456789/215817Repositório de PublicaçõesPUBhttp://150.162.242.35/oai/requestopendoar:23732020-10-21T21:22:17Repositório Institucional da UFSC - Universidade Federal de Santa Catarina (UFSC)false
dc.title.none.fl_str_mv Estudo da variação dimensional de porcelanato esmaltado de grande formato
title Estudo da variação dimensional de porcelanato esmaltado de grande formato
spellingShingle Estudo da variação dimensional de porcelanato esmaltado de grande formato
Pinter Junior, Jamilson
Engenharia de materiais
Revestimento cerâmico
Porcelanatos
title_short Estudo da variação dimensional de porcelanato esmaltado de grande formato
title_full Estudo da variação dimensional de porcelanato esmaltado de grande formato
title_fullStr Estudo da variação dimensional de porcelanato esmaltado de grande formato
title_full_unstemmed Estudo da variação dimensional de porcelanato esmaltado de grande formato
title_sort Estudo da variação dimensional de porcelanato esmaltado de grande formato
author Pinter Junior, Jamilson
author_facet Pinter Junior, Jamilson
author_role author
dc.contributor.none.fl_str_mv Universidade Federal de Santa Catarina
dc.contributor.author.fl_str_mv Pinter Junior, Jamilson
dc.contributor.advisor1.fl_str_mv Pereira, Fabiano Raupp
dc.contributor.advisor-co1.fl_str_mv Noni Junior, Agenor de
contributor_str_mv Pereira, Fabiano Raupp
Noni Junior, Agenor de
dc.subject.classification.none.fl_str_mv Engenharia de materiais
Revestimento cerâmico
Porcelanatos
topic Engenharia de materiais
Revestimento cerâmico
Porcelanatos
description Dissertação (mestrado) - Universidade Federal de Santa Catarina, Centro Tecnológico, Programa de Pós-Graduação em Ciência e Engenharia de Materiais, Florianópolis, 2020.
publishDate 2020
dc.date.accessioned.fl_str_mv 2020-10-21T21:22:17Z
dc.date.available.fl_str_mv 2020-10-21T21:22:17Z
dc.date.issued.fl_str_mv 2020
dc.type.status.fl_str_mv info:eu-repo/semantics/publishedVersion
dc.type.driver.fl_str_mv info:eu-repo/semantics/masterThesis
format masterThesis
status_str publishedVersion
dc.identifier.uri.fl_str_mv https://repositorio.ufsc.br/handle/123456789/215817
dc.identifier.other.none.fl_str_mv 370469
identifier_str_mv 370469
url https://repositorio.ufsc.br/handle/123456789/215817
dc.language.iso.fl_str_mv por
language por
dc.rights.driver.fl_str_mv info:eu-repo/semantics/openAccess
eu_rights_str_mv openAccess
dc.format.none.fl_str_mv 63 p.| il., gráfs.
dc.source.none.fl_str_mv reponame:Repositório Institucional da UFSC
instname:Universidade Federal de Santa Catarina (UFSC)
instacron:UFSC
instname_str Universidade Federal de Santa Catarina (UFSC)
instacron_str UFSC
institution UFSC
reponame_str Repositório Institucional da UFSC
collection Repositório Institucional da UFSC
bitstream.url.fl_str_mv https://repositorio.ufsc.br/bitstream/123456789/215817/-1/PCEM0552-D.pdf
bitstream.checksum.fl_str_mv 9cf49a78ea356c1a840d06bbfd617f70
bitstream.checksumAlgorithm.fl_str_mv MD5
repository.name.fl_str_mv Repositório Institucional da UFSC - Universidade Federal de Santa Catarina (UFSC)
repository.mail.fl_str_mv
_version_ 1766805163620696064

Registros relacionados