Influência do pH na liberação de íons metálicos em pastas cimentícias contendo finos com potencial adsortivo

Detalhes bibliográficos
Autor(a) principal: Françozo, Mariana de Oliveira
Data de Publicação: 2019
Tipo de documento: Dissertação
Idioma: por
Título da fonte: Repositório Institucional da UFSC
Texto Completo: https://repositorio.ufsc.br/handle/123456789/215327
Resumo: Dissertação (mestrado) - Universidade Federal de Santa Catarina, Centro Tecnológico, Programa de Pós-Graduação em Engenharia Civil, Florianópolis, 2019.
id UFSC_99c892d64f37482013cfd004854be682
oai_identifier_str oai:repositorio.ufsc.br:123456789/215327
network_acronym_str UFSC
network_name_str Repositório Institucional da UFSC
repository_id_str 2373
spelling Influência do pH na liberação de íons metálicos em pastas cimentícias contendo finos com potencial adsortivoEngenharia civilÍons metálicosAdsorçãoCimentoDissertação (mestrado) - Universidade Federal de Santa Catarina, Centro Tecnológico, Programa de Pós-Graduação em Engenharia Civil, Florianópolis, 2019.Tendo em vista o crescente interesse na incorporação de resíduos ou sub-produtos industriais em matriz cimentícia, atenção especial deve ser dada à liberação de íons metálicos para o meio ambiente devido aos seus potenciais riscos de contaminação. Alguns autores verificaram que cinzas com potencial adsortivo podem melhorar a fixação dos metais na matriz cimentícia e que a avaliação da influência do pH na liberação desses metais se mostra um método mais completo para análise de possíveis cenários em que o material cimentício é exposto. Esta pesquisa buscou avaliar de que forma a substituição do Cimento Portland por Cinza Pesada (CZP) ou Cinza de Casca de Arroz (CCA) pode influenciar na lixiviação dos íons metálicos Zn2+ e Cr6+ e a possível relação com a capacidade de adsorção dessas cinzas. Para isso foram produzidas pastas cimentícias com 20 e 40% de substituição do Cimento Portland (CP-V ARI) por CZP ou CCA com uma relação água/ligante de 0,35 e contaminadas sinteticamente com os sais cromato de sódio (Na2CrO4) e nitrato de zinco (Zn(NO3)2) na concentração de 0,013 mol/Kg, equivalente a 676 e 850 mg/Kg, respectivamente. Foram estudadas as propriedades adsortivas das cinzas, como potencial zeta e capacidade de adsorção através das isotermas de adsorção. A mobilidade dos íons metálicos das pasta cimentícias em idade de 28 dias foi avaliada por meio do teste de influência do pH (Método 1313 EPA) em uma faixa de pH de 2 a 13. A Capacidade de Neutralização Ácida (ANC) da matriz cimentícia também foi analisada juntamente com as informações da análise termogravimétrica (TG/DTG). Verificou-se que a CCA e CZP possuem maior capacidade de adsorção para o metal zinco, com capacidade máxima de adsorção (qmax) 2,31 mg/g e 0,49 mg/g, respectivamente, sendo que a CZP possui maior afinidade com o metal, segundo o modelo de Langmuir. O metal zinco teve maior liberação em pH menor que 6, sendo que as amostras com 20% de CCA e CZP foram mais eficazes, retendo cerca de 75% do metal quando analisada a disponibilidade em pH menor que 3. O metal cromo foi liberado em menores concentrações quando comparado ao metal zinco, apresentando uma retenção na faixa de 86 a 91%. Não foi possível identificar uma relação sistemática entre a capacidade de adsorção das cinzas e lixiviação do metais da matriz cimentícia, visto que tanto a CCA quanto a CZP apresentaram baixos valores de quantidade adsorvida (mg/g), principalmente para o metal Cromo, sendo que este teve maior percentual retido na amostra cimentícia.Abstract: Given the growing interest in the incorporation of industrial waste or by-products in cementitious matrix, special attention should be given to the release of metal ions into the environment due to their potential contamination risks. Some authors have found that ashes with adsorptive potential can improve the fixation of metals in the cementitious matrix and that the evaluation of the pH influence on the release of these metals is a more complete method for analyzing possible scenarios in which the cementitious material is exposed. Thus, this research aimed to evaluate how the substitution of Portland cement by Bottom Ash (CZP) or Rice Husk Ash (CCA) can influence the leaching of Zn2+ and Cr6+ metal ions and its possible relationship with the adsorption capacity of these ashes. For this, were produced cementitious pastes with 20 and 40% substitution of Portland cement (CP-V ARI) with CZP or CCA with a water/binder ratio of 0,35 and spiked with sodium chromate (Na2CrO4) and nitrate of zinc (Zn(NO3)2) at a concentration of 0,013 mol/Kg. The adsorbent properties of ashes, as zeta potential and adsorption capacity were studied and the mobility of metal ions from the cementitious matrix was evaluated by pH dependence test (Method 1313 EPA) in a pH range from 2 to 13. The Acid Neutralization Capacity (ANC) of the cementitious matrix was also analyzed with information from the thermogravimetric analysis (TG/DTG). It was found that CCA and CZP have higher adsorption capacity for zinc metal, with qmax 2,31 mg/g and 0,49 mg/g, respectively, and CZP has higher affinity with the metal, according to the Langmuir model. Zinc metal had higher release at pH lower than 6, and samples with 20% CCA and CZP were more effective, retaining about 75% of the metal when analyzing availability at pH lower than 3. Chromium metal was released at lower concentrations when compared to zinc metal, with a retention in the range of 86 to 91%. It was not possible to identify a systematic relationship between ash adsorption capacity and metal leaching in the cementitious matrix, as both CCA and CZP presented low qmax values, especially for Chromium metal, which had a higher percentage retained in the cementitious pastes samples.Rocha, Janaíde CavalcanteUniversidade Federal de Santa CatarinaFrançozo, Mariana de Oliveira2020-10-21T21:15:29Z2020-10-21T21:15:29Z2019info:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/masterThesis141 p.| il., gráfs.application/pdf369443https://repositorio.ufsc.br/handle/123456789/215327porreponame:Repositório Institucional da UFSCinstname:Universidade Federal de Santa Catarina (UFSC)instacron:UFSCinfo:eu-repo/semantics/openAccess2020-10-21T21:15:29Zoai:repositorio.ufsc.br:123456789/215327Repositório InstitucionalPUBhttp://150.162.242.35/oai/requestopendoar:23732020-10-21T21:15:29Repositório Institucional da UFSC - Universidade Federal de Santa Catarina (UFSC)false
dc.title.none.fl_str_mv Influência do pH na liberação de íons metálicos em pastas cimentícias contendo finos com potencial adsortivo
title Influência do pH na liberação de íons metálicos em pastas cimentícias contendo finos com potencial adsortivo
spellingShingle Influência do pH na liberação de íons metálicos em pastas cimentícias contendo finos com potencial adsortivo
Françozo, Mariana de Oliveira
Engenharia civil
Íons metálicos
Adsorção
Cimento
title_short Influência do pH na liberação de íons metálicos em pastas cimentícias contendo finos com potencial adsortivo
title_full Influência do pH na liberação de íons metálicos em pastas cimentícias contendo finos com potencial adsortivo
title_fullStr Influência do pH na liberação de íons metálicos em pastas cimentícias contendo finos com potencial adsortivo
title_full_unstemmed Influência do pH na liberação de íons metálicos em pastas cimentícias contendo finos com potencial adsortivo
title_sort Influência do pH na liberação de íons metálicos em pastas cimentícias contendo finos com potencial adsortivo
author Françozo, Mariana de Oliveira
author_facet Françozo, Mariana de Oliveira
author_role author
dc.contributor.none.fl_str_mv Rocha, Janaíde Cavalcante
Universidade Federal de Santa Catarina
dc.contributor.author.fl_str_mv Françozo, Mariana de Oliveira
dc.subject.por.fl_str_mv Engenharia civil
Íons metálicos
Adsorção
Cimento
topic Engenharia civil
Íons metálicos
Adsorção
Cimento
description Dissertação (mestrado) - Universidade Federal de Santa Catarina, Centro Tecnológico, Programa de Pós-Graduação em Engenharia Civil, Florianópolis, 2019.
publishDate 2019
dc.date.none.fl_str_mv 2019
2020-10-21T21:15:29Z
2020-10-21T21:15:29Z
dc.type.status.fl_str_mv info:eu-repo/semantics/publishedVersion
dc.type.driver.fl_str_mv info:eu-repo/semantics/masterThesis
format masterThesis
status_str publishedVersion
dc.identifier.uri.fl_str_mv 369443
https://repositorio.ufsc.br/handle/123456789/215327
identifier_str_mv 369443
url https://repositorio.ufsc.br/handle/123456789/215327
dc.language.iso.fl_str_mv por
language por
dc.rights.driver.fl_str_mv info:eu-repo/semantics/openAccess
eu_rights_str_mv openAccess
dc.format.none.fl_str_mv 141 p.| il., gráfs.
application/pdf
dc.source.none.fl_str_mv reponame:Repositório Institucional da UFSC
instname:Universidade Federal de Santa Catarina (UFSC)
instacron:UFSC
instname_str Universidade Federal de Santa Catarina (UFSC)
instacron_str UFSC
institution UFSC
reponame_str Repositório Institucional da UFSC
collection Repositório Institucional da UFSC
repository.name.fl_str_mv Repositório Institucional da UFSC - Universidade Federal de Santa Catarina (UFSC)
repository.mail.fl_str_mv
_version_ 1808652103463206912

Registros relacionados