Influência da espessura nas propriedades anticrustantes de filmes finos de TiO2 depositados em aço inoxidável AISI 316L

Detalhes bibliográficos
Autor(a) principal: Dedeco, Igor Kasper
Data de Publicação: 2020
Tipo de documento: Dissertação
Idioma: por
Título da fonte: Repositório Institucional da UFSC
Texto Completo: https://repositorio.ufsc.br/handle/123456789/220032
Resumo: Dissertação (mestrado) - Universidade Federal de Santa Catarina, Campus Joinville, Programa de Pós-Graduação em Engenharia e Ciências Mecânicas, Joinville, 2020.
id UFSC_a5264b30454180c8a48f05a8012502dc
oai_identifier_str oai:repositorio.ufsc.br:123456789/220032
network_acronym_str UFSC
network_name_str Repositório Institucional da UFSC
repository_id_str 2373
spelling Universidade Federal de Santa CatarinaDedeco, Igor KasperSoethe, Viviane LilianDelatorre, Rafael Gallina2021-02-11T22:18:17Z2021-02-11T22:18:17Z2020370192https://repositorio.ufsc.br/handle/123456789/220032Dissertação (mestrado) - Universidade Federal de Santa Catarina, Campus Joinville, Programa de Pós-Graduação em Engenharia e Ciências Mecânicas, Joinville, 2020.Um dos grandes desafios da indústria marítima relaciona-se ao controle dos processos de bioincrustação em superfícies submersas em ambiente aquático por longos períodos. Neste sentido, verifica-se um grande esforço para o desenvolvimento de agentes antincrustantes com impactos ambientais aceitáveis a fim de substituir o biocida tributilestanho, amplamente utilizado até 2008 para grandes embarcações. Neste sentido, no presente trabalho verificou-se o potencial de aplicação de filmes finos de TiO2 em diferentes espessuras como agente antincrustante. Desta forma, filmes com diferentes espessuras de TiO2 foram depositados sobre aço inoxidável AISI 316L pela técnica de magnetron sputtering e, então, caracterizados pelas técnicas de perfilometria, espectroscopia Raman, difração de raios-X e avaliação do ângulos de contato antes e depois da irradiação por UV-A e UV-C. A caracterização da propriedade antincrustantes dos filmes foi realizada por meio de experimento de campo, onde superfícies com e sem revestimento foram submersas por 110 dias com acompanhamento fotográfico e quantitativo do desenvolvimento da bioincrustação marinha no Rio Cubatão com auxílio do software PhotoQuad. Os filmes avaliados consistiam em revestimentos de espessuras de 3,5 nm até 172,5 nm de TiO2, sendo que o filme mais fino apresentou característica amorfa e os mais espessos apresentaram estrutura cristalina composta por rutile e anatase. No que diz respeito à molhabilidade, todas as espessuras apresentaram hidrofilicidade fotoinduzida para ambos os comprimentos de onda. Por outro lado, o revestimento com espessura de 172,5 nm se destacou por apresentar transição mais rápida para hidrofilicidade e ângulo de contato de até 16 graus para UV-A. Acerca da bioincrustação, foi possível verificar um atraso no início do processo de incrustação da superfície, independentemente da espessura do filme. Também se verificou a redução da área total média incrustada por Balanus Amphitrite em superfícies com revestimento de TiO2 em relação às amostras sem revestimento de até 36%. No estudo identificou-se as diatomáceas Amphora coffeaeformis, Terpsinoë musica e Cocconeis fluviatilis como espécies microincrustantes das superfícies submersas com auxílio da técnica de MEV. No presente estudo verificou-se que filmes com espessuras muito finas, da ordem de 3,5nm até os mais espessos apresentaram ação antincrustante e retardamento do início do processo de bioincrustação.Abstract: One of the great challenges of the maritime industry is related to the control of biofouling processes on surfaces submerged in the aquatic environment for long periods of time. In this sense, there is a great effort to develop antifouling agents with acceptable environmental impacts in order to replace the tributyltin biocide, widely used until 2008 for large vessels. Thus, in the present work it was verified the potential of applying thin films of TiO2 in different thicknesses as an antifouling agent. Therefore, films with different thicknesses of TiO2 were deposited on AISI 316L stainless steel by the technique of magnetron sputtering and, then, characterized by the techniques of profilometry, Raman spectroscopy, X-ray diffraction and evaluation of the contact angles before and after irradiation by UV-A and UV-C. The characterization of the antifouling properties of the films was carried out through a field experiment, where surfaces with and without coating were submerged for 110 days with photographic and quantitative monitoring of the development of marine biofouling in the Cubatão River with the aid of the PhotoQuad software. The evaluated films consisted of coatings of thickness from 3.5 nm to 172.5 nm of TiO2, with the thinnest film presenting an amorphous characteristic and the thickest films presenting a crystalline structure composed of rutile and anatase. Regarding the wettability, all thicknesses showed photoinduced hydrophilicity for both wavelengths. On the other hand, the 172.5 nm thick coating stood out for presenting a faster transition to hydrophilicity and a contact angle of up to 16 degrees for UV-A. Regarding biofouling, it was possible to verify a delay in the beginning of the fouling process of the surface, regardless of the thickness of the film. There was also a reduction in the mean total area fouled by Balanus Amphitrite on surfaces with TiO2 coating compared to samples without coating by up to 36%. In the study, the diatoms Amphora coffeaeformis, Terpsinoë musica and Cocconeis fluviatilis were identified as microfoulers species of the submerged surfaces with the aid of the SEM technique. In the present study it was found that films with very thin thicknesses, in the order of 3.5nm to the thickest ones, presented anti-fouling and delayed action in the beginning of the biofouling process.91 p.| il., gráfs.porEngenharia mecânicaDióxido de titânioFilmes finosInfluência da espessura nas propriedades anticrustantes de filmes finos de TiO2 depositados em aço inoxidável AISI 316Linfo:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/masterThesisreponame:Repositório Institucional da UFSCinstname:Universidade Federal de Santa Catarina (UFSC)instacron:UFSCinfo:eu-repo/semantics/openAccessORIGINALPPCM0064-D.pdfPPCM0064-D.pdfapplication/pdf6293853https://repositorio.ufsc.br/bitstream/123456789/220032/1/PPCM0064-D.pdf9d654d2a92d91cf329bb0e8a1dca0b58MD51123456789/2200322021-02-11 19:18:18.197oai:repositorio.ufsc.br:123456789/220032Repositório de PublicaçõesPUBhttp://150.162.242.35/oai/requestopendoar:23732021-02-11T22:18:18Repositório Institucional da UFSC - Universidade Federal de Santa Catarina (UFSC)false
dc.title.none.fl_str_mv Influência da espessura nas propriedades anticrustantes de filmes finos de TiO2 depositados em aço inoxidável AISI 316L
title Influência da espessura nas propriedades anticrustantes de filmes finos de TiO2 depositados em aço inoxidável AISI 316L
spellingShingle Influência da espessura nas propriedades anticrustantes de filmes finos de TiO2 depositados em aço inoxidável AISI 316L
Dedeco, Igor Kasper
Engenharia mecânica
Dióxido de titânio
Filmes finos
title_short Influência da espessura nas propriedades anticrustantes de filmes finos de TiO2 depositados em aço inoxidável AISI 316L
title_full Influência da espessura nas propriedades anticrustantes de filmes finos de TiO2 depositados em aço inoxidável AISI 316L
title_fullStr Influência da espessura nas propriedades anticrustantes de filmes finos de TiO2 depositados em aço inoxidável AISI 316L
title_full_unstemmed Influência da espessura nas propriedades anticrustantes de filmes finos de TiO2 depositados em aço inoxidável AISI 316L
title_sort Influência da espessura nas propriedades anticrustantes de filmes finos de TiO2 depositados em aço inoxidável AISI 316L
author Dedeco, Igor Kasper
author_facet Dedeco, Igor Kasper
author_role author
dc.contributor.none.fl_str_mv Universidade Federal de Santa Catarina
dc.contributor.author.fl_str_mv Dedeco, Igor Kasper
dc.contributor.advisor1.fl_str_mv Soethe, Viviane Lilian
dc.contributor.advisor-co1.fl_str_mv Delatorre, Rafael Gallina
contributor_str_mv Soethe, Viviane Lilian
Delatorre, Rafael Gallina
dc.subject.classification.none.fl_str_mv Engenharia mecânica
Dióxido de titânio
Filmes finos
topic Engenharia mecânica
Dióxido de titânio
Filmes finos
description Dissertação (mestrado) - Universidade Federal de Santa Catarina, Campus Joinville, Programa de Pós-Graduação em Engenharia e Ciências Mecânicas, Joinville, 2020.
publishDate 2020
dc.date.issued.fl_str_mv 2020
dc.date.accessioned.fl_str_mv 2021-02-11T22:18:17Z
dc.date.available.fl_str_mv 2021-02-11T22:18:17Z
dc.type.status.fl_str_mv info:eu-repo/semantics/publishedVersion
dc.type.driver.fl_str_mv info:eu-repo/semantics/masterThesis
format masterThesis
status_str publishedVersion
dc.identifier.uri.fl_str_mv https://repositorio.ufsc.br/handle/123456789/220032
dc.identifier.other.none.fl_str_mv 370192
identifier_str_mv 370192
url https://repositorio.ufsc.br/handle/123456789/220032
dc.language.iso.fl_str_mv por
language por
dc.rights.driver.fl_str_mv info:eu-repo/semantics/openAccess
eu_rights_str_mv openAccess
dc.format.none.fl_str_mv 91 p.| il., gráfs.
dc.source.none.fl_str_mv reponame:Repositório Institucional da UFSC
instname:Universidade Federal de Santa Catarina (UFSC)
instacron:UFSC
instname_str Universidade Federal de Santa Catarina (UFSC)
instacron_str UFSC
institution UFSC
reponame_str Repositório Institucional da UFSC
collection Repositório Institucional da UFSC
bitstream.url.fl_str_mv https://repositorio.ufsc.br/bitstream/123456789/220032/1/PPCM0064-D.pdf
bitstream.checksum.fl_str_mv 9d654d2a92d91cf329bb0e8a1dca0b58
bitstream.checksumAlgorithm.fl_str_mv MD5
repository.name.fl_str_mv Repositório Institucional da UFSC - Universidade Federal de Santa Catarina (UFSC)
repository.mail.fl_str_mv
_version_ 1766805103356936192

Registros relacionados