Estudo do comportamento de ondas ultrassônicas no monitoramento do concreto em idades iniciais

Detalhes bibliográficos
Autor(a) principal: Bressan, Hella Fernanda Giehl
Data de Publicação: 2019
Tipo de documento: Dissertação
Idioma: por
Título da fonte: Repositório Institucional da UFSC
Texto Completo: https://repositorio.ufsc.br/handle/123456789/211574
Resumo: Dissertação (mestrado) - Universidade Federal de Santa Catarina, Centro Tecnológico, Programa de Pós-Graduação em Engenharia Civil, Florianópolis, 2019.
id UFSC_a7b55b48b9a7d270fd28434d95bead5c
oai_identifier_str oai:repositorio.ufsc.br:123456789/211574
network_acronym_str UFSC
network_name_str Repositório Institucional da UFSC
repository_id_str 2373
spelling Estudo do comportamento de ondas ultrassônicas no monitoramento do concreto em idades iniciaisEngenharia civilConcretoOndas ultrassonicasDissertação (mestrado) - Universidade Federal de Santa Catarina, Centro Tecnológico, Programa de Pós-Graduação em Engenharia Civil, Florianópolis, 2019.A técnica de ultrassom é amplamente utilizada na avaliação indireta de propriedades mecânicas do concreto endurecido e na detecção de possíveis não homogeneidades internas. Este método também mostra potencial de aplicação no monitoramento dos processos de hidratação do cimento e do desenvolvimento das propriedades mecânicas do material. Mudanças físicas na estrutura interna do material resultam em alterações na propagação de ondas ultrassônicas e, além da velocidade de pulso, outros parâmetros ultrassônicos podem ser determinados a partir do formato de onda, podendo ser mais sensíveis a alterações internas do que a análise convencional (via velocidade de pulso). O programa experimental desta pesquisa foi definido tendo por objetivo analisar o desenvolvimento de parâmetros associados à propagação da onda de ultrassom no monitoramento de concretos em suas primeiras horas. Para isso, a partir do monitoramento ultrassônico de seis diferentes misturas de concreto, foram obtidos os parâmetros: velocidade de pulso ultrassônico, amplitude máxima, velocidade de grupo, energia total, janelas de tempo referentes à 25%, 50%, 75% e 90% da energia total, pico de frequência e frequência central. Além disso, foi realizado o ensaio de resistência à penetração nas misturas analisadas, de acordo com a NBR NM 9 (2003), a fim de que fossem obtidos os tempos de início e fim de pega e possibilitando a correlação ensaios. Com base nos resultados obtidos, percebeu-se que todos os parâmetros propostos se mostraram afetados pelo desenvolvimento da microestrutura do concreto. Da correlação entre os parâmetros ultrassônicos e os tempos de início e fim de pega, não foi possível obter padrões de comportamento ou intervalos dos parâmetros no domínio do tempo que pudessem ser utilizados como indicativos da ocorrência da pega do material. Por outro lado, os parâmetros analisados no domínio da frequência, pico de frequência e frequência central, permitiram estabelecer um intervalo de ocorrência do início de pega para o pico de frequência de 8,4 a 10 kHz, com desvio padrão relativo (DPR) de 7%, e 9,1 a 12,1 kHz (DPR=3%) para a frequência central, com atraso na identificação do início de pega da mistura a/c 0,50 de 12 minutos em comparação com o ensaio de resistência à penetração, para ambos os parâmetros. Além disso, com exceção da mistura a/c 0,55, através da frequência central, mostrou-se possível obter um resultado médio de 44,4±6,2 kHz (DPR=14%) no final de pega indicado pelo desenvolvimento da resistência à penetração.Abstract: The ultrasound technique is widely used to indirectly evaluate the mechanical properties of hardened concrete and to detect possible internal non-homogeneities. This method also shows potential application in the monitoring of cement hydration processes and the development of mechanical properties of the material. Physical changes in the material's internal structure result in changes in the ultrasonic waves propagation and, besides ultrasonic pulse velocity, other ultrasonic parameters can be determined from the waveform and may be more sensitive to internal changes than conventional analysis (with pulse velocity). The experimental program of this research was defined aiming to analyze the development of parameters associated with the propagation of the ultrasound wave in the monitoring of concretes in its early hours. For this, from the ultrasonic monitoring of six different concrete mixtures, the following parameters were obtained: ultrasonic pulse velocity, maximum amplitude, group velocity, total energy, time windows of 25%, 50%, 75% and 90% of total energy, peak frequency and center frequency. In addition, the penetration resistance test was performed in the mixtures analyzed, according to NBR NM 9 (2003), in order to obtain the initial and final setting times and allowing the correlation between tests. Based on the results, it was noticed that all the proposed parameters were affected by the development of the concrete microstructure. From the correlation between the ultrasonic parameters and the setting times, it was not possible to obtain behavioral patterns or ranges in time domain parameters that could be used as indicative of the occurrence of the setting of the material. On the other hand, the parameters analyzed in the frequency domain, frequency peak and center frequency, it was possible to establish a interval for initial setting of 8.4 to 10 kHz for frequency peak, with relative standard deviation (RSD) of 7%, and 9.1 to 12.1 kHz (RSD = 13%) for the center frequency, with delay of 12 minutes in identifying the initial setting time of w/c 0.50 mixture, compared to the penetration resistance test for both parameters. In addition, except for w/c 0.55 mixture, using the center frequency, it was possible to obtain an average result of 44.4 ± 6.2 kHz (RSD=14%) in the final setting indicated by the penetration resistance test.Pinto, Roberto Caldas de AndradeUniversidade Federal de Santa CatarinaBressan, Hella Fernanda Giehl2020-08-20T05:47:46Z2020-08-20T05:47:46Z2019info:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/masterThesis148 p.| il., gráfs.application/pdf369093https://repositorio.ufsc.br/handle/123456789/211574porreponame:Repositório Institucional da UFSCinstname:Universidade Federal de Santa Catarina (UFSC)instacron:UFSCinfo:eu-repo/semantics/openAccess2020-08-20T05:47:47Zoai:repositorio.ufsc.br:123456789/211574Repositório InstitucionalPUBhttp://150.162.242.35/oai/requestopendoar:23732020-08-20T05:47:47Repositório Institucional da UFSC - Universidade Federal de Santa Catarina (UFSC)false
dc.title.none.fl_str_mv Estudo do comportamento de ondas ultrassônicas no monitoramento do concreto em idades iniciais
title Estudo do comportamento de ondas ultrassônicas no monitoramento do concreto em idades iniciais
spellingShingle Estudo do comportamento de ondas ultrassônicas no monitoramento do concreto em idades iniciais
Bressan, Hella Fernanda Giehl
Engenharia civil
Concreto
Ondas ultrassonicas
title_short Estudo do comportamento de ondas ultrassônicas no monitoramento do concreto em idades iniciais
title_full Estudo do comportamento de ondas ultrassônicas no monitoramento do concreto em idades iniciais
title_fullStr Estudo do comportamento de ondas ultrassônicas no monitoramento do concreto em idades iniciais
title_full_unstemmed Estudo do comportamento de ondas ultrassônicas no monitoramento do concreto em idades iniciais
title_sort Estudo do comportamento de ondas ultrassônicas no monitoramento do concreto em idades iniciais
author Bressan, Hella Fernanda Giehl
author_facet Bressan, Hella Fernanda Giehl
author_role author
dc.contributor.none.fl_str_mv Pinto, Roberto Caldas de Andrade
Universidade Federal de Santa Catarina
dc.contributor.author.fl_str_mv Bressan, Hella Fernanda Giehl
dc.subject.por.fl_str_mv Engenharia civil
Concreto
Ondas ultrassonicas
topic Engenharia civil
Concreto
Ondas ultrassonicas
description Dissertação (mestrado) - Universidade Federal de Santa Catarina, Centro Tecnológico, Programa de Pós-Graduação em Engenharia Civil, Florianópolis, 2019.
publishDate 2019
dc.date.none.fl_str_mv 2019
2020-08-20T05:47:46Z
2020-08-20T05:47:46Z
dc.type.status.fl_str_mv info:eu-repo/semantics/publishedVersion
dc.type.driver.fl_str_mv info:eu-repo/semantics/masterThesis
format masterThesis
status_str publishedVersion
dc.identifier.uri.fl_str_mv 369093
https://repositorio.ufsc.br/handle/123456789/211574
identifier_str_mv 369093
url https://repositorio.ufsc.br/handle/123456789/211574
dc.language.iso.fl_str_mv por
language por
dc.rights.driver.fl_str_mv info:eu-repo/semantics/openAccess
eu_rights_str_mv openAccess
dc.format.none.fl_str_mv 148 p.| il., gráfs.
application/pdf
dc.source.none.fl_str_mv reponame:Repositório Institucional da UFSC
instname:Universidade Federal de Santa Catarina (UFSC)
instacron:UFSC
instname_str Universidade Federal de Santa Catarina (UFSC)
instacron_str UFSC
institution UFSC
reponame_str Repositório Institucional da UFSC
collection Repositório Institucional da UFSC
repository.name.fl_str_mv Repositório Institucional da UFSC - Universidade Federal de Santa Catarina (UFSC)
repository.mail.fl_str_mv
_version_ 1808651915899174912

Registros relacionados