Formulação de produtos cerâmicos a partir de resíduos minerais usando o diagrama de fases do sistema SiO2-Al2O3-K2O

Detalhes bibliográficos
Autor(a) principal: Junkes, Janaína Accordi
Data de Publicação: 2012
Tipo de documento: Tese
Idioma: por
Título da fonte: Repositório Institucional da UFSC
Texto Completo: http://repositorio.ufsc.br/xmlui/handle/123456789/95142
Resumo: Tese (doutorado) - Universidade Federal de Santa Catarina, Centro Tecnológico, Programa de Pós-Graduação em Ciência e Engenharia de Materiais, Florianópolis, 2011
id UFSC_a85a73f7f9cbae9a032d01eb3ffe4b80
oai_identifier_str oai:repositorio.ufsc.br:123456789/95142
network_acronym_str UFSC
network_name_str Repositório Institucional da UFSC
repository_id_str 2373
spelling Formulação de produtos cerâmicos a partir de resíduos minerais usando o diagrama de fases do sistema SiO2-Al2O3-K2OCiencia dos materiaisResiduosCerâmicaIndústriaDiagramas de faseRevestimento cerâmicoTese (doutorado) - Universidade Federal de Santa Catarina, Centro Tecnológico, Programa de Pós-Graduação em Ciência e Engenharia de Materiais, Florianópolis, 2011Nos trabalhos científicos dos últimos anos as questões ligadas à preservação ambiental têm adquirido grande relevância e um dos grandes desafios a serem alcançados é a reciclagem de materiais descartados pelos diferentes setores produtivos. Devido às agressões causadas ao meio ambiente, pelo desenvolvimento tecnológico através do descarte de resíduos, buscou-se, neste estudo avaliar a possibilidade de utilizar apenas resíduos industriais como matérias-primas alternativas na fabricação de revestimentos cerâmicos. Diferentes resíduos industriais classificados como não perigosos foram selecionados: lamas de processos de britagem de gnaisse, lamas do processo de corte e polimento do varvito, lodos do processo de clarificação/purificação de água potável e uma argila também classificada como resíduo. Todos os resíduos, na forma como foram gerados, foram secos e desagregados em moinhos de bolhas, sendo caracterizados por fluorescência de raios X, difratometria de raios X, análise térmica diferencial e gravimétrica, dilatometria ótica e distribuição de tamanho de partículas. A aplicabilidade destes resíduos na confecção de cerâmicas rústicas para revestimento foi guiada pelo diagrama de fases do sistema SiO2-K2OAl2O3 e quatro formulações foram estabelecidas. Para os testes iniciais, estas formulações foram homogeneizadas e prensadas na forma de Resumo pastilhas e sinterizadas a 900, 950, 1000, 1050, 1100 e 1150ºC. A plasticidade das formulações foi avaliada pelo método de Casagrande, e a técnica de extrusão foi utilizada como processo de conformação. As amostras extrudadas foram sinterizadas a 1100 e 1150ºC com 40 min de patamar e caracterizadas por difratometria de raios X, análise térmica diferencial e gravimétrica, dilatometria ótica, retração linear, absorção de água e resistência mecânica a flexão. As fases cristalinas identificadas foram associadas às condições de queima (temperatura, tempo, atmosfera), bem como às características intrínsecas das matériasprimas, como composição química, distribuição de tamanho de partícula e homogeneidade. Os resíduos provaram ser uma boa fonte de matériasprimas alternativas e suas formulações correspondentes se mostraram viáveis para a fabricação de revestimentos cerâmicos.In recent years scientific issues related to environmental preservation have acquired great importance and a major challenge to be achieved is the recycling of materials discarded by the different productive sectors. Due to the damage caused to the environment by technological development through the disposal of waste, this study sought to evaluate the possibility of using only industrial waste as alternative raw materials in the manufacture of ceramic tiles. Different industrial wastes classified as non-hazardous were selected: sludge from the crushing process of gneiss, sludge from the cutting and polishing process of varvite, sludge from the process of filtration/clarification of potable water and a clay also classified as waste. All wastes were dried and disaggregated in ball mills, and characterized by X-ray fluorescence, X-ray diffraction, differential thermal and gravimetric analysis, optical dilatometry and particle size distribution. The applicability of these wastes in the rustic ceramic tiles manufacture was guided by the phase diagram of the system SiO2-K2O-Al2O3, and four formulations were established. For initial testing, these formulations were mixed and pressed into pellets, and sintered at 900, 950, 1000, 1050, 1100 and 1150ºC. The formulations plasticity was evaluated by the Casagrande method, and the extrusion technique was used for the shaping process. The extruded samples were fired at 1100 and 1150ºC Abstract for 40 min and characterized by X-ray diffraction, differential thermal and gravimetric analysis, optical dilatometry, linear shrinkage, water absorption and flexural strength. The identified crystalline phases were associated with the sintering conditions (temperature, time, atmosphere) as well the intrinsic characteristics of raw materials such as chemical composition, particle size and homogeneity. The waste proved to be a good alternative raw material and corresponding formulations were shown to be viable for the manufacture of ceramic tiles.Hotza, DachamirSegadães, Ana M.Universidade Federal de Santa CatarinaJunkes, Janaína Accordi2012-10-25T21:10:51Z2012-10-25T21:10:51Z2012-10-25T21:10:51Zinfo:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/doctoralThesis[165] p.| il., grafs., tabs.application/pdf288061http://repositorio.ufsc.br/xmlui/handle/123456789/95142porreponame:Repositório Institucional da UFSCinstname:Universidade Federal de Santa Catarina (UFSC)instacron:UFSCinfo:eu-repo/semantics/openAccess2016-03-07T18:55:19Zoai:repositorio.ufsc.br:123456789/95142Repositório InstitucionalPUBhttp://150.162.242.35/oai/requestopendoar:23732016-03-07T18:55:19Repositório Institucional da UFSC - Universidade Federal de Santa Catarina (UFSC)false
dc.title.none.fl_str_mv Formulação de produtos cerâmicos a partir de resíduos minerais usando o diagrama de fases do sistema SiO2-Al2O3-K2O
title Formulação de produtos cerâmicos a partir de resíduos minerais usando o diagrama de fases do sistema SiO2-Al2O3-K2O
spellingShingle Formulação de produtos cerâmicos a partir de resíduos minerais usando o diagrama de fases do sistema SiO2-Al2O3-K2O
Junkes, Janaína Accordi
Ciencia dos materiais
Residuos
Cerâmica
Indústria
Diagramas de fase
Revestimento cerâmico
title_short Formulação de produtos cerâmicos a partir de resíduos minerais usando o diagrama de fases do sistema SiO2-Al2O3-K2O
title_full Formulação de produtos cerâmicos a partir de resíduos minerais usando o diagrama de fases do sistema SiO2-Al2O3-K2O
title_fullStr Formulação de produtos cerâmicos a partir de resíduos minerais usando o diagrama de fases do sistema SiO2-Al2O3-K2O
title_full_unstemmed Formulação de produtos cerâmicos a partir de resíduos minerais usando o diagrama de fases do sistema SiO2-Al2O3-K2O
title_sort Formulação de produtos cerâmicos a partir de resíduos minerais usando o diagrama de fases do sistema SiO2-Al2O3-K2O
author Junkes, Janaína Accordi
author_facet Junkes, Janaína Accordi
author_role author
dc.contributor.none.fl_str_mv Hotza, Dachamir
Segadães, Ana M.
Universidade Federal de Santa Catarina
dc.contributor.author.fl_str_mv Junkes, Janaína Accordi
dc.subject.por.fl_str_mv Ciencia dos materiais
Residuos
Cerâmica
Indústria
Diagramas de fase
Revestimento cerâmico
topic Ciencia dos materiais
Residuos
Cerâmica
Indústria
Diagramas de fase
Revestimento cerâmico
description Tese (doutorado) - Universidade Federal de Santa Catarina, Centro Tecnológico, Programa de Pós-Graduação em Ciência e Engenharia de Materiais, Florianópolis, 2011
publishDate 2012
dc.date.none.fl_str_mv 2012-10-25T21:10:51Z
2012-10-25T21:10:51Z
2012-10-25T21:10:51Z
dc.type.status.fl_str_mv info:eu-repo/semantics/publishedVersion
dc.type.driver.fl_str_mv info:eu-repo/semantics/doctoralThesis
format doctoralThesis
status_str publishedVersion
dc.identifier.uri.fl_str_mv 288061
http://repositorio.ufsc.br/xmlui/handle/123456789/95142
identifier_str_mv 288061
url http://repositorio.ufsc.br/xmlui/handle/123456789/95142
dc.language.iso.fl_str_mv por
language por
dc.rights.driver.fl_str_mv info:eu-repo/semantics/openAccess
eu_rights_str_mv openAccess
dc.format.none.fl_str_mv [165] p.| il., grafs., tabs.
application/pdf
dc.source.none.fl_str_mv reponame:Repositório Institucional da UFSC
instname:Universidade Federal de Santa Catarina (UFSC)
instacron:UFSC
instname_str Universidade Federal de Santa Catarina (UFSC)
instacron_str UFSC
institution UFSC
reponame_str Repositório Institucional da UFSC
collection Repositório Institucional da UFSC
repository.name.fl_str_mv Repositório Institucional da UFSC - Universidade Federal de Santa Catarina (UFSC)
repository.mail.fl_str_mv
_version_ 1808652014810300416

Registros relacionados