Modification of commercial polymeric membranes via electrospraying for membrane distillation applications aiming to water recovery from textile wastewater

Detalhes bibliográficos
Autor(a) principal: Madalosso, Heloísa Bremm
Data de Publicação: 2021
Tipo de documento: Dissertação
Idioma: eng
Título da fonte: Repositório Institucional da UFSC
Texto Completo: https://repositorio.ufsc.br/handle/123456789/226987
Resumo: Dissertação (mestrado) - Universidade Federal de Santa Catarina, Centro Tecnológico, Programa de Pós-Graduação em Engenharia Química, Florianópolis, 2021.
id UFSC_a9bac5907fc734759e699e7a0dd4e048
oai_identifier_str oai:repositorio.ufsc.br:123456789/226987
network_acronym_str UFSC
network_name_str Repositório Institucional da UFSC
repository_id_str 2373
spelling Modification of commercial polymeric membranes via electrospraying for membrane distillation applications aiming to water recovery from textile wastewaterEngenharia químicaEfluentesIndústria têxtilResíduos industriaisDestilaçãoDissertação (mestrado) - Universidade Federal de Santa Catarina, Centro Tecnológico, Programa de Pós-Graduação em Engenharia Química, Florianópolis, 2021.A complexidade do efluente têxtil, relacionada a grande quantidade de solutos em sua composição, faz com que processos convencionais de tratamento não apresentem completa degradação e gerem um volume crítico de lama, além de baixa qualidade da água resultante. O processo de Destilação por Membranas (DM) apresenta-se como uma alternativa promissora para a recuperação e reinserção da água deste efluente no processo, visto que possibilita a utilização de calor residual do processo de tingimento, resultando em um permeado de alta qualidade. Entretanto, alguns desafios para a consolidação desta tecnologia persistem, relacionados a fenômenos do processo, como a incrustação e o molhamento. A baixa resistência ao molhamento das membranas comerciais faz com que a DM ainda não seja capaz de ser aplicada à totalidade de componentes dos efluentes têxteis, como algumas classes de corantes e aditivos utilizados, como surfactantes. Neste contexto, este trabalho visou a modificação de membranas comerciais de poliamida (PA) e polipropileno (PP) utilizando a técnica de electrospraying, com blendas poliméricas contendo PVDF, PDMS com ou sem agente de cura e nanopartículas de sílica, em solução de THF:DMF 1:1, com o intuito de aumentar a hidrofobicidade e a resistência ao molhamento. A influência da concentração de polímero, cura do polímero, tempo de exposição sob o spray e concentração de nanopartículas de sílica na hidrofobicidade das membranas foram avaliadas. Ângulos de contato de 167,13º e 144,07º foram obtidos para as membranas de PA e PP, respectivamente, e estas foram caracterizadas em termos de estrutura morfológica e química (FTIR, MEV, EDX), estudo térmico (DSC), espessura, porosidade, ângulo de contato com diferentes soluções e Potencial Zeta. O potencial de remoção das membranas modificadas foi avaliado em operações de Destilação por Membranas por Contato Direto (DCDM), durante 4 h, em condições operacionais fixas. A membrana modificada de PP com a solução de porcentagem mássica 2% PVDF e 6% Sylgard (PDMS curado) foi testada com quatro diferentes classes de corantes utilizados industrialmente (reativo, disperso, direto e ácido), e apresentou fluxos de 29,7, 44,85, 29,79 e 35,41 kg m-2 h-1, respectivamente, com redução máxima de 11,6% em relação ao fluxo da membrana de PP pura. As taxas de rejeição obtidas para a membrana modificada foram maiores que 95%, e maiores que as taxas de rejeição da membrana pura com as diferentes classes de corantes. A cura do polímero PDMS, combinada com a estrutura rugosa obtida através do electrospraying, diminuiu o potencial zeta da membrana modificada na faixa de pH das soluções testadas, contribuindo para uma maior resistência ao molhamento e maior potencial de remoção de corantes. A membrana modificada de PA com a solução de porcentagem mássica 2% PVDF, 10% PDMS e 20% de nanopartículas de sílica apresentou fluxos mais baixos devido sua estrutura densa. Foi testada com os componentes do banho de tingimento de algodão (corante preto reativo e surfactante), resultando em fluxo de 0,6 e 0,39 kg m-2 h-1, respectivamente, e em taxas de rejeição superiores ao da PA pura. Este aspecto foi observado principalmente com a solução de surfactante, onde o início do molhamento foi evidenciado na membrana de PA pura. A membrana modificada de PA apresentou uma propriedade anti-incrustante mediante à deposição de corante em sua superfície. A modificação de membranas comerciais visando a criação de estruturas mais hidrofóbicas viabilizou a operação DCMD com diferentes classes de corantes e soluções de baixa tensão superficial (surfactante), com maior resistência ao molhamento e maior potencial de remoção de corante, sem comprometer a estrutura química e morfológica das membranas. Neste trabalho, a modificação das membranas comprovou a potencialidade do processo DCMD para recuperação de água de soluções contendo solutos do efluente têxtil.Abstract: The conventional processes of textile wastewater treatment show a not-completely effluent degradation and generates high sludge-volume, due to the high complexity of this effluent, related to the great number of solutes in its composition. The process of Membrane Distillation (MD) consists of a promisor alternative to water recuperation from textile wastewater and its reinsertion in the process. It enables the utilization of waste heat from the dyeing process and results in a high-quality permeate. However, some challenges to the consolidation of this technique persist, related to the fouling and wetting phenomena. The low wetting resistance of the commercial membranes makes the DM process not applicable to the whole textile effluents compounds, such as some classes of dyes and additives employed in the process, i.e., surfactants. In this context, this work aimed at the membrane modification of polyamide (PA) and polypropylene (PP) membranes, using electrospraying technique through the incorporation of polymeric blends on the membrane surface, with PVDF, cured or not-cured PDMS, and silica nanoparticles (Si NPs) in THF: DMF (1:1) solutions. The main goal of modifications was the hydrophobicity improvement and achievement of anti-wetting property. The influence of polymer and Si NPs concentration, polymer curing, and time under the spray were evaluated. Water contact angles of 167.13º and 144.07º were obtained to PA and PP membranes, respectively. These membranes were characterized in chemical and morphological structures (FTIR, SEM, and EDX), thermal analysis (DSC), membrane thickness and porosity, contact angle against different solutions, and Zeta Potential. The removal potential of modified membranes was evaluated in a Direct Contact Membrane Distillation (DCMD) operation, during four hours, in a fixed operational condition. The modified PP membrane using 2% PVDF and 6% Sylgard (cured PDMS) was tested with four different industrial dye classes (Reactive, Disperse, Direct, and Acid) and presented permeate fluxes of 29.7, 44.85, 29.79 e 35.41 kg m-2 h-1, respectively. The flux was reduced at most 11.9% comparing to the pristine PP membrane. The rejection rates reached more than 95%, and they were higher than the rejection rates of pristine PP against the different classes of dyes. The polymer curing, combined with the high roughness and hydrophobic structure obtained through electrospraying, decreased the zeta potential of the modified membrane in the pH range of dye solutions, contributing to a high wetting resistance and high rejection rates without loses in membrane porosity. The PA modified membrane using 2% PVDF, 10% PDMS, and 20% Si NPs showed lower permeate fluxes due to its dense structure. It was tested with a cotton dyeing bath compounds (reactive black dye and surfactant), resulting in permeate fluxes of 0.6 and 0.39 kg m-2 h-1. Higher rejection rates than the pristine PA membrane were achieved, mainly dealing with the surfactant solution, where the PA membrane has been beginning wetted. The PA modified membrane achieved an antifouling property against the deposition of dye particles. The modification of commercial membranes aiming to create more hydrophobic structures enabled the DCMD operation with different dye classes and low surface tension solutions (detergent), with higher wetting resistance and higher removal potential, without compromising the chemical and morphological structure of the membranes. In this work, the membrane modification proved the DCMD process?s potentiality in water recuperation from solutions containing textile wastewater solutes.Marangoni, CintiaMachado, Ricardo Antonio FranciscoUniversidade Federal de Santa CatarinaMadalosso, Heloísa Bremm2021-08-23T14:05:57Z2021-08-23T14:05:57Z2021info:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/masterThesis165 p.| il., gráfs., tabs.application/pdf371729https://repositorio.ufsc.br/handle/123456789/226987engreponame:Repositório Institucional da UFSCinstname:Universidade Federal de Santa Catarina (UFSC)instacron:UFSCinfo:eu-repo/semantics/openAccess2021-08-23T14:05:58Zoai:repositorio.ufsc.br:123456789/226987Repositório InstitucionalPUBhttp://150.162.242.35/oai/requestopendoar:23732021-08-23T14:05:58Repositório Institucional da UFSC - Universidade Federal de Santa Catarina (UFSC)false
dc.title.none.fl_str_mv Modification of commercial polymeric membranes via electrospraying for membrane distillation applications aiming to water recovery from textile wastewater
title Modification of commercial polymeric membranes via electrospraying for membrane distillation applications aiming to water recovery from textile wastewater
spellingShingle Modification of commercial polymeric membranes via electrospraying for membrane distillation applications aiming to water recovery from textile wastewater
Madalosso, Heloísa Bremm
Engenharia química
Efluentes
Indústria têxtil
Resíduos industriais
Destilação
title_short Modification of commercial polymeric membranes via electrospraying for membrane distillation applications aiming to water recovery from textile wastewater
title_full Modification of commercial polymeric membranes via electrospraying for membrane distillation applications aiming to water recovery from textile wastewater
title_fullStr Modification of commercial polymeric membranes via electrospraying for membrane distillation applications aiming to water recovery from textile wastewater
title_full_unstemmed Modification of commercial polymeric membranes via electrospraying for membrane distillation applications aiming to water recovery from textile wastewater
title_sort Modification of commercial polymeric membranes via electrospraying for membrane distillation applications aiming to water recovery from textile wastewater
author Madalosso, Heloísa Bremm
author_facet Madalosso, Heloísa Bremm
author_role author
dc.contributor.none.fl_str_mv Marangoni, Cintia
Machado, Ricardo Antonio Francisco
Universidade Federal de Santa Catarina
dc.contributor.author.fl_str_mv Madalosso, Heloísa Bremm
dc.subject.por.fl_str_mv Engenharia química
Efluentes
Indústria têxtil
Resíduos industriais
Destilação
topic Engenharia química
Efluentes
Indústria têxtil
Resíduos industriais
Destilação
description Dissertação (mestrado) - Universidade Federal de Santa Catarina, Centro Tecnológico, Programa de Pós-Graduação em Engenharia Química, Florianópolis, 2021.
publishDate 2021
dc.date.none.fl_str_mv 2021-08-23T14:05:57Z
2021-08-23T14:05:57Z
2021
dc.type.status.fl_str_mv info:eu-repo/semantics/publishedVersion
dc.type.driver.fl_str_mv info:eu-repo/semantics/masterThesis
format masterThesis
status_str publishedVersion
dc.identifier.uri.fl_str_mv 371729
https://repositorio.ufsc.br/handle/123456789/226987
identifier_str_mv 371729
url https://repositorio.ufsc.br/handle/123456789/226987
dc.language.iso.fl_str_mv eng
language eng
dc.rights.driver.fl_str_mv info:eu-repo/semantics/openAccess
eu_rights_str_mv openAccess
dc.format.none.fl_str_mv 165 p.| il., gráfs., tabs.
application/pdf
dc.source.none.fl_str_mv reponame:Repositório Institucional da UFSC
instname:Universidade Federal de Santa Catarina (UFSC)
instacron:UFSC
instname_str Universidade Federal de Santa Catarina (UFSC)
instacron_str UFSC
institution UFSC
reponame_str Repositório Institucional da UFSC
collection Repositório Institucional da UFSC
repository.name.fl_str_mv Repositório Institucional da UFSC - Universidade Federal de Santa Catarina (UFSC)
repository.mail.fl_str_mv
_version_ 1808651888646684672

Registros relacionados