Recobrimento de partículas ferromagnéticas com óxidos isolantes via mistura de pós a seco

Detalhes bibliográficos
Autor(a) principal: Daros, Maisa Topanotti
Data de Publicação: 2016
Tipo de documento: Dissertação
Idioma: por
Título da fonte: Repositório Institucional da UFSC
Texto Completo: https://repositorio.ufsc.br/handle/123456789/194082
Resumo: Dissertação (mestrado) - Universidade Federal de Santa Catarina, Centro Tecnológico, Programa de Pós-Graduação em Ciência e Engenharia de Materiais, Florianópolis, 2016.
id UFSC_aeca90715e4d72e8c439ae065d6d2158
oai_identifier_str oai:repositorio.ufsc.br:123456789/194082
network_acronym_str UFSC
network_name_str Repositório Institucional da UFSC
repository_id_str 2373
spelling Universidade Federal de Santa CatarinaDaros, Maisa TopanottiRodrigues Neto, João BatistaKlein, Aloisio Nelmo2019-03-25T16:53:51Z2019-03-25T16:53:51Z2016353261https://repositorio.ufsc.br/handle/123456789/194082Dissertação (mestrado) - Universidade Federal de Santa Catarina, Centro Tecnológico, Programa de Pós-Graduação em Ciência e Engenharia de Materiais, Florianópolis, 2016.Este trabalho avaliou a viabilidade da formação de filmes isolantes a base de óxidos cerâmicos sobre a superfície de partículas ferromagnéticas via mistura de pós a seco, a fim de obter materiais compósitos magnéticos macios. Primeiramente, as partículas de ferro puro passaram por um tratamento de esferoidização, que propicia a diminuição da rugosidade superficial, gerando partículas mais esféricas que auxiliam a formação de filmes contínuos. Sequencialmente, óxidos isolantes são incorporados a mistura, promovendo o recobrimento das partículas ferromagnéticas. Os materiais óxidos utilizados como recobrimento foram NiO2, MnO2, Fe2O3, e uma ferrite soft de manganês. Composições contendo 7% em volume destes óxidos foram estudadas, e suas formações, estabilidades e propriedades foram caracterizadas através de microscopia eletrônica de varredura, microscopia ótica, análises térmicas, densidade e propriedades mecânicas, propriedades elétricas e magnéticas. Pode-se verificar que as composições contendo Fe2O3 são menos estáveis termicamente, e composições contendo MnO2 puro possibilitam a produção de filmes mais contínuos. A influência da temperatura sobre a integridade da camada e sobre as propriedades elétricas e magnéticas foi analisada. Variou-se a temperatura de tratamento térmico em 880, 700 e 500°C, observando-se que, quanto menor a temperatura, menor a degradação da camada isolante e melhores são os resultados de resistividade elétrica e perdas magnéticas dos compósitos desenvolvidos. Para as composições contendo 7% de MnO2 observou-se valores de resisitividade próximos a 25 µ?.m para todas as temperaturas analizadas, no entanto, para composições contendo 7% de Fe2O3 o valor de resistividade variou de 0,3 a 77 µ?.m para as temperaturas de 880 e 500°C, respectivamente. A magnetização inicial, a permeabilidade e as perdas magnéticas dos materiais produzidos foram avaliadas, e a fim de se obter melhores resultados magnéticos um pó de ferro puro com tamanho de partículas maior foi utilizado juntamente com menores percentuais de óxidos isolantes. Todo este estudo utilizou um material comercial como referência, o Somaloy 3P 700 da empresa Höganäs, e verificou-se que para a indução de 800mT, as perdas totais para o Somaloy são de 4,07 W/kg, enquanto para a amostra contendo 4% de MnO2 são de 6,17 W/kg, sendo este o melhor resultado magnético obtido neste trabalho.Abstract : This study evaluated the feasibility of forming ceramic oxides based insulating films on the surface of ferromagnetic particles via dry powder mixture, to obtain soft magnetic composites. First, pure iron particles passed through a spheroidization treatment, which promotes the reduction of surface roughness, generating more spherical particles which promotes the formation of continuous films. Sequentially, insulating oxides are incorporated into the mixture, promoting coating over ferromagnetic particles. The oxides used as coating materials were NiO2, MnO2, Fe2O3 pure and mixed stoichiometrically one with another, and a soft ferrite of manganese. Compositions containing 7% vol. of these oxides were studied, and their formations, stabilities and properties were characterized by scanning electron microscopy, optical microscopy, thermal analysis, density and mechanical properties, electrical and magnetic properties. It can be seen that the compositions containing Fe2O3 are less thermally stable, and compositions containing pure MnO2 and Mn ferrite enable the production of more continuous films. The influence of temperature on the integrity of the layer and on the electrical and magnetic properties was examined by varying the heat treatment temperature (880, 700 and 500°C), observing that a lower temperature, provides a lower degradation of the insulating layer and a better result of electrical resistivity and magnetic losses of the developed composites. For compositions containing 7% of MnO2 was observed resistivity values near 25 µO.m for all temperatures, however, for the compositions containing 7% Fe2O3 the resistivity varied from 0.3 to 77 µO.m for the temperatures of 880 and 500°C respectively. The initial magnetization, permeability and magnetic losses of the produced materials were evaluated, in order to obtain better results magnetic pure iron powder with greater particle size was used with lower percentages of insulating oxides. All this study used a commercial material as a reference, Somaloy 3P 700 from Höganäs company, and it was found that for the induction of 800mT, induction that is usually employed in domestic electric engines, the total losses for Somaloy is 4, 07 W/kg, while for the sample containing 4% of MnO2 are 6.17 W/kg, which is the best magnetic result obtained in this work.104 p.| il., gráfs., tabs.porEngenharia de materiaisMetalurgia do póMateriais compostosMateriais isolantesRecobrimento de partículas ferromagnéticas com óxidos isolantes via mistura de pós a secoinfo:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/masterThesisreponame:Repositório Institucional da UFSCinstname:Universidade Federal de Santa Catarina (UFSC)instacron:UFSCinfo:eu-repo/semantics/openAccessORIGINALPCEM0460-D.pdfPCEM0460-D.pdfapplication/pdf3506721https://repositorio.ufsc.br/bitstream/123456789/194082/-1/PCEM0460-D.pdff5ad0438bcd17722719d67c3c5fa7c03MD5-1123456789/1940822019-03-25 13:53:52.489oai:repositorio.ufsc.br:123456789/194082Repositório de PublicaçõesPUBhttp://150.162.242.35/oai/requestopendoar:23732019-03-25T16:53:52Repositório Institucional da UFSC - Universidade Federal de Santa Catarina (UFSC)false
dc.title.none.fl_str_mv Recobrimento de partículas ferromagnéticas com óxidos isolantes via mistura de pós a seco
title Recobrimento de partículas ferromagnéticas com óxidos isolantes via mistura de pós a seco
spellingShingle Recobrimento de partículas ferromagnéticas com óxidos isolantes via mistura de pós a seco
Daros, Maisa Topanotti
Engenharia de materiais
Metalurgia do pó
Materiais compostos
Materiais isolantes
title_short Recobrimento de partículas ferromagnéticas com óxidos isolantes via mistura de pós a seco
title_full Recobrimento de partículas ferromagnéticas com óxidos isolantes via mistura de pós a seco
title_fullStr Recobrimento de partículas ferromagnéticas com óxidos isolantes via mistura de pós a seco
title_full_unstemmed Recobrimento de partículas ferromagnéticas com óxidos isolantes via mistura de pós a seco
title_sort Recobrimento de partículas ferromagnéticas com óxidos isolantes via mistura de pós a seco
author Daros, Maisa Topanotti
author_facet Daros, Maisa Topanotti
author_role author
dc.contributor.none.fl_str_mv Universidade Federal de Santa Catarina
dc.contributor.author.fl_str_mv Daros, Maisa Topanotti
dc.contributor.advisor1.fl_str_mv Rodrigues Neto, João Batista
dc.contributor.advisor-co1.fl_str_mv Klein, Aloisio Nelmo
contributor_str_mv Rodrigues Neto, João Batista
Klein, Aloisio Nelmo
dc.subject.classification.none.fl_str_mv Engenharia de materiais
Metalurgia do pó
Materiais compostos
Materiais isolantes
topic Engenharia de materiais
Metalurgia do pó
Materiais compostos
Materiais isolantes
description Dissertação (mestrado) - Universidade Federal de Santa Catarina, Centro Tecnológico, Programa de Pós-Graduação em Ciência e Engenharia de Materiais, Florianópolis, 2016.
publishDate 2016
dc.date.issued.fl_str_mv 2016
dc.date.accessioned.fl_str_mv 2019-03-25T16:53:51Z
dc.date.available.fl_str_mv 2019-03-25T16:53:51Z
dc.type.status.fl_str_mv info:eu-repo/semantics/publishedVersion
dc.type.driver.fl_str_mv info:eu-repo/semantics/masterThesis
format masterThesis
status_str publishedVersion
dc.identifier.uri.fl_str_mv https://repositorio.ufsc.br/handle/123456789/194082
dc.identifier.other.none.fl_str_mv 353261
identifier_str_mv 353261
url https://repositorio.ufsc.br/handle/123456789/194082
dc.language.iso.fl_str_mv por
language por
dc.rights.driver.fl_str_mv info:eu-repo/semantics/openAccess
eu_rights_str_mv openAccess
dc.format.none.fl_str_mv 104 p.| il., gráfs., tabs.
dc.source.none.fl_str_mv reponame:Repositório Institucional da UFSC
instname:Universidade Federal de Santa Catarina (UFSC)
instacron:UFSC
instname_str Universidade Federal de Santa Catarina (UFSC)
instacron_str UFSC
institution UFSC
reponame_str Repositório Institucional da UFSC
collection Repositório Institucional da UFSC
bitstream.url.fl_str_mv https://repositorio.ufsc.br/bitstream/123456789/194082/-1/PCEM0460-D.pdf
bitstream.checksum.fl_str_mv f5ad0438bcd17722719d67c3c5fa7c03
bitstream.checksumAlgorithm.fl_str_mv MD5
repository.name.fl_str_mv Repositório Institucional da UFSC - Universidade Federal de Santa Catarina (UFSC)
repository.mail.fl_str_mv
_version_ 1766805435640184832

Registros relacionados