Desenvolvimento de pasta de geopolímeros a base de cinza volante e hidróxido de sódio

Detalhes bibliográficos
Autor(a) principal: Livi, Carolina Noda
Data de Publicação: 2013
Tipo de documento: Dissertação
Idioma: por
Título da fonte: Repositório Institucional da UFSC
Texto Completo: https://repositorio.ufsc.br/handle/123456789/106842
Resumo: Dissertação (mestrado) - Universidade Federal de Santa Catarina, Centro Tecnológico. Programa de Pós-graduação em Engenharia Civil, Florianópolis, 2013
id UFSC_c178a09657514f66d297cf9a4d4449da
oai_identifier_str oai:repositorio.ufsc.br:123456789/106842
network_acronym_str UFSC
network_name_str Repositório Institucional da UFSC
repository_id_str 2373
spelling Desenvolvimento de pasta de geopolímeros a base de cinza volante e hidróxido de sódioEngenharia civilPolimerosCinza volanteCimentoHidroxidosDissertação (mestrado) - Universidade Federal de Santa Catarina, Centro Tecnológico. Programa de Pós-graduação em Engenharia Civil, Florianópolis, 2013A geopolimerização é um processo de transformação de fontes ricas em óxidos de alumínio e silício em materiais ligantes com características similares às do cimento Portland hidratado. Sabe-se que é possível obter níveis satisfatórios de resistência mecânica dependendo da composição química dos materiais precursores, do proporcionamento dos materiais e das condições de cura. Neste contexto, esta Dissertação de Mestrado reporta um estudo experimental exploratório em pastas de geopolímeros a base de cinza volante ativada com solução de hidróxido de sódio. Variaram-se a concentração molar do ativador alcalino de base hidróxido de sódio (8, 12 e 16M), a relação mássica entre a solução ativadora e a cinza volante (em massa, 0,50; 0,55 e 0,60), e a temperatura de cura (45, 65 e 85 °C). Foram moldados corpos-de-prova prismáticos de 4cm x 4cm x 16cm, submetidos a ensaios de resistência à flexão e compressão nas idades de 1, 3, 7 e 28 dias. Com exceção das pastas curadas à temperatura de cura de a 45°C, as demais apresentaram maior ganho resistência na primeira idade, de modo que não se observou um aumento significativo aos 28 dias. Evidenciou-se, portanto, o potencial do emprego de geopolímeros em situações que exigem rápida liberação de elementos moldados. Além disso, para misturas constituídas de solução 8 M foi possível obter o mesmo nível de resistências mecânicas tanto para 65°C quanto 85°C, sendo que as propriedades foram favorecidas diminuindo-se a relação solução ativadora por cinza volante ou aumentando-se a concentração molar. A mistura com resistência mais elevada foi preparada com solução ativadora com molaridade de 16 M, relação solução ativadora por cinza volante igual a 0,55 e curada à temperatura de 85°C. Nesse caso, foram alcançadas resistência à flexão e compressão, respectivamente, de 3,60 MPa e 20,62 MPa, com 1 dia; e 4,20 MPa e 24,16 MPa, com 28 dias de idade. Com os resultados obtidos, confirmou-se o potencial do emprego do cimento geopolimérico como material de construção civil <br>Abstract: Geopolymerisation is a process for transforming sources rich in aluminum oxide and silicon oxide into binders with characteristics similar to hydrated Portland cement. It is possible to achieve satisfactory mechanical behavior considering the chemical composition of the raw materials, the definition of mixture parameters and curing conditions. In this context, this Master?s Thesis reports an experimental study on fly ash-based geopolymer. Factors were varied such as concentration of solution-based sodium hydroxide (8, 12 and 16M), ratio of activator solution-to-fly ash, (by mass, 0.50, 0.55, 0.60), beyond curing temperature (45, 65 and 85°C). Prismatic specimens (4cm x 4cm x 16cm) were molded and submitted to tensile and compressive strength tests, after 1, 3, 7 and 28 days. With the exception of pastes subjected to cure at 45°C, samples showed great resistance at 1 day so it was not observed development until 28 days. This highlights the potential of using geopolymers in situations requiring rapid release of moldings. Also, for mixtures with 8 M solution, it was observed that it was possible to achieve the same performance range for both 65°C and 85°C. Mechanical properties could be improved by decreasing the ratio activator solution-to-fly ash or increasing molarity, although changing molarity was more advantageous. The mixture with highest resistance was composed by 16M sodium hydroxide solution, ratio of activator solution-to-fly ash 0.55 and curing temperature of 85°C. This resulted on tensile strength of 3.60 MPa at 1 day and 4.20 MPa at 28 days. likewise, compressive strength obtained was 20.62 MPa at 1 day and 24.16 MPa at 28 days. With the obtained results, it was confirmed the potential of geopolymeric cement as a building material.Repette, Wellington LonguiniUniversidade Federal de Santa CatarinaLivi, Carolina Noda2013-12-05T22:32:02Z2013-12-05T22:32:02Z2013info:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/masterThesis193 p.| il., grafs., tabs.application/pdf319571https://repositorio.ufsc.br/handle/123456789/106842porreponame:Repositório Institucional da UFSCinstname:Universidade Federal de Santa Catarina (UFSC)instacron:UFSCinfo:eu-repo/semantics/openAccess2013-12-05T22:32:02Zoai:repositorio.ufsc.br:123456789/106842Repositório InstitucionalPUBhttp://150.162.242.35/oai/requestopendoar:23732013-12-05T22:32:02Repositório Institucional da UFSC - Universidade Federal de Santa Catarina (UFSC)false
dc.title.none.fl_str_mv Desenvolvimento de pasta de geopolímeros a base de cinza volante e hidróxido de sódio
title Desenvolvimento de pasta de geopolímeros a base de cinza volante e hidróxido de sódio
spellingShingle Desenvolvimento de pasta de geopolímeros a base de cinza volante e hidróxido de sódio
Livi, Carolina Noda
Engenharia civil
Polimeros
Cinza volante
Cimento
Hidroxidos
title_short Desenvolvimento de pasta de geopolímeros a base de cinza volante e hidróxido de sódio
title_full Desenvolvimento de pasta de geopolímeros a base de cinza volante e hidróxido de sódio
title_fullStr Desenvolvimento de pasta de geopolímeros a base de cinza volante e hidróxido de sódio
title_full_unstemmed Desenvolvimento de pasta de geopolímeros a base de cinza volante e hidróxido de sódio
title_sort Desenvolvimento de pasta de geopolímeros a base de cinza volante e hidróxido de sódio
author Livi, Carolina Noda
author_facet Livi, Carolina Noda
author_role author
dc.contributor.none.fl_str_mv Repette, Wellington Longuini
Universidade Federal de Santa Catarina
dc.contributor.author.fl_str_mv Livi, Carolina Noda
dc.subject.por.fl_str_mv Engenharia civil
Polimeros
Cinza volante
Cimento
Hidroxidos
topic Engenharia civil
Polimeros
Cinza volante
Cimento
Hidroxidos
description Dissertação (mestrado) - Universidade Federal de Santa Catarina, Centro Tecnológico. Programa de Pós-graduação em Engenharia Civil, Florianópolis, 2013
publishDate 2013
dc.date.none.fl_str_mv 2013-12-05T22:32:02Z
2013-12-05T22:32:02Z
2013
dc.type.status.fl_str_mv info:eu-repo/semantics/publishedVersion
dc.type.driver.fl_str_mv info:eu-repo/semantics/masterThesis
format masterThesis
status_str publishedVersion
dc.identifier.uri.fl_str_mv 319571
https://repositorio.ufsc.br/handle/123456789/106842
identifier_str_mv 319571
url https://repositorio.ufsc.br/handle/123456789/106842
dc.language.iso.fl_str_mv por
language por
dc.rights.driver.fl_str_mv info:eu-repo/semantics/openAccess
eu_rights_str_mv openAccess
dc.format.none.fl_str_mv 193 p.| il., grafs., tabs.
application/pdf
dc.source.none.fl_str_mv reponame:Repositório Institucional da UFSC
instname:Universidade Federal de Santa Catarina (UFSC)
instacron:UFSC
instname_str Universidade Federal de Santa Catarina (UFSC)
instacron_str UFSC
institution UFSC
reponame_str Repositório Institucional da UFSC
collection Repositório Institucional da UFSC
repository.name.fl_str_mv Repositório Institucional da UFSC - Universidade Federal de Santa Catarina (UFSC)
repository.mail.fl_str_mv
_version_ 1808652049110269952

Registros relacionados