Avaliação nos estados fresco e endurecido de concretos autodensáveis de alto desempenho com aditivos redutor e compensador de retração

Detalhes bibliográficos
Autor(a) principal: Pilar, Ronaldo
Data de Publicação: 2017
Tipo de documento: Tese
Idioma: por
Título da fonte: Repositório Institucional da UFSC
Texto Completo: https://repositorio.ufsc.br/handle/123456789/185533
Resumo: Tese (doutorado) - Universidade Federal de Santa Catarina, Centro Tecnológico, Programa de Pós-Graduação em Engenharia Civil, Florianópolis, 2017
id UFSC_c97338ff399667a21a51178a75388fbd
oai_identifier_str oai:repositorio.ufsc.br:123456789/185533
network_acronym_str UFSC
network_name_str Repositório Institucional da UFSC
repository_id_str 2373
spelling Avaliação nos estados fresco e endurecido de concretos autodensáveis de alto desempenho com aditivos redutor e compensador de retraçãoEngenharia civilConcreto de alto desempenhoConcreto autoadensávelReologiaTese (doutorado) - Universidade Federal de Santa Catarina, Centro Tecnológico, Programa de Pós-Graduação em Engenharia Civil, Florianópolis, 2017O concreto de autoadensável de alto desempenho (CAAAD) é tipo de concreto que tem sido desenvolvido para apresentar elevada fluidez e estabilidade e, ao mesmo tempo, elevada resistência mecânica e durabilidade. Entretanto, em decorrência de grandes quantidades de cimento Portland, aditivo superplastificante e adições minerais, junto com uma baixa relação água/aglomerante empregada, essas misturas se tornam vulneráveis aos fenômenos autógenos de retração. Com o objetivo de mitigar os efeitos da retração autógena, este trabalho estudou composições de CAAAD com os aditivos redutor de retração nos teores 0,5; 1,0 e 1,5% e compensador de retração para os teores de 5, 10 e 15% em composições com relações água/aglomerante de 0,25 e 0,32. No estado fresco foi avaliado o comportamento reológico das misturas, por meio de um reômetro de concreto, para os intervalos de 10, 25, 40, 60 e 90 minutos. Os ensaios de espalhamento, funil V, anel J e segregação também foram realizados. No estado endurecido, foram avaliadas as propriedades mecânicas, retração autógena livre e restringida pelo anel de restrição. Em pastas, foram realizados ensaios de calorimetria de condução isotérmica e ensaios reológicos, para os mesmos teores de aditivos mitigadores de retração empregados nos concretos. De posse dos resultados, pôde-se observar que todos os concretos com os aditivos redutor e compensador de retração puderam ser classificados como CAA aos 10 minutos, com valores de espalhamento variando entre 650 e 710 mm. As misturas com aditivo compensador de retração apresentaram os maiores consumos de aditivo superplastificante e as maiores perdas de fluidez, ao contrário das misturas com aditivo redutor de retração que apresentaram as menores reduções. Pôde-se perceber que todas as composições com aditivos mitigadores de retração geraram os menores valores de retrações autógena livres até os 7 dias de hidratação e não apresentaram fissuras no ensaio retração autógena restringida para o mesmo período. As composições com aditivos compensadores (10 e 15%) e relação água/aglomerante 0,32 apresentaram expansão aos 7 dias de hidratação. As propriedades mecânicas não foram comprometidas pelo uso dos aditivos redutor e compensador de retração, exceto para a composições com 15% de aditivo compensador de retração.Abstract: High performance self-compacting concrete (HPSCC) is a type of concrete that has been developed to exhibit high flowability and mix stability and, at the same time, high strength and durability. However higher amounts of Portland cement, superplasticizer, and mineral admixtures, together with low water/binder ratios are used to produce these concretes. Thus, these mixtures became susceptible the autogenous shrinkage. Shrinkage-reducing admixture (SRA) and compensating admixture (SCA) were used in high performance self-compacting concrete (HPSCC) to mitigate autogenous shrinkage. The mixtures were designed with a water/binder ratio of 0.25 and 0.32. Three different dosages of SRA (0.5%, 1.0%, and 1.5%) and SCA (5%, 10%, and 15%) were used. In the fresh state, the rheological behavior of each concrete was obtained at 10, 25, 40, 60 and 90 min after mixing begins. The slump flow diameter, J-ring diameter and V-funnel flow time tests were conducted simultaneously. In the hard state, mechanical properties, autogenous shrinkage and shrinkage-restrained ring were evaluated. Conduction calorimetry and rheological tests were carried out on pastes with the same contents of shrinkage-reducing and shrinkage-compensating admixture used in concretes. Based on the results, it was observed that concretes with the shrinkage-reducing and shrinkage-compensating admixture could be classified as SCC (10 minutes after the start of the mixture) with slump flow between 650 and 710 mm. The mixtures with shrinkage-compensating admixture required the highest superplasticizer content and had the highest losses of fluidity, in contrast to the mixtures with shrinkage-reducing admixture that showed the highest workability retention. All compositions with shrinkage mitigation admixtures presented the lowest autogenous shrinkage values up to 7 days of hydration and they did not show cracks in the restrained shrinkage study for the same period. The mixtures with shrinkage-compensating admixture (10 and 15%) and water/binder ratio 0.32 showed expansion at 7 days of hydration. The use of shrinkage-reducing admixture and shrinkage-compensating admixture were not effect on mechanical properties of concretes, except for compositions with 15% shrinkage-compensating admixture.Repette, Wellington LonguiniUniversidade Federal de Santa CatarinaPilar, Ronaldo2018-04-13T19:33:18Z2018-04-13T19:33:18Z2017info:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/doctoralThesis215 p.| il., gráfs., tabs.application/pdf350631https://repositorio.ufsc.br/handle/123456789/185533porreponame:Repositório Institucional da UFSCinstname:Universidade Federal de Santa Catarina (UFSC)instacron:UFSCinfo:eu-repo/semantics/openAccess2018-04-13T19:33:19Zoai:repositorio.ufsc.br:123456789/185533Repositório InstitucionalPUBhttp://150.162.242.35/oai/requestopendoar:23732018-04-13T19:33:19Repositório Institucional da UFSC - Universidade Federal de Santa Catarina (UFSC)false
dc.title.none.fl_str_mv Avaliação nos estados fresco e endurecido de concretos autodensáveis de alto desempenho com aditivos redutor e compensador de retração
title Avaliação nos estados fresco e endurecido de concretos autodensáveis de alto desempenho com aditivos redutor e compensador de retração
spellingShingle Avaliação nos estados fresco e endurecido de concretos autodensáveis de alto desempenho com aditivos redutor e compensador de retração
Pilar, Ronaldo
Engenharia civil
Concreto de alto desempenho
Concreto autoadensável
Reologia
title_short Avaliação nos estados fresco e endurecido de concretos autodensáveis de alto desempenho com aditivos redutor e compensador de retração
title_full Avaliação nos estados fresco e endurecido de concretos autodensáveis de alto desempenho com aditivos redutor e compensador de retração
title_fullStr Avaliação nos estados fresco e endurecido de concretos autodensáveis de alto desempenho com aditivos redutor e compensador de retração
title_full_unstemmed Avaliação nos estados fresco e endurecido de concretos autodensáveis de alto desempenho com aditivos redutor e compensador de retração
title_sort Avaliação nos estados fresco e endurecido de concretos autodensáveis de alto desempenho com aditivos redutor e compensador de retração
author Pilar, Ronaldo
author_facet Pilar, Ronaldo
author_role author
dc.contributor.none.fl_str_mv Repette, Wellington Longuini
Universidade Federal de Santa Catarina
dc.contributor.author.fl_str_mv Pilar, Ronaldo
dc.subject.por.fl_str_mv Engenharia civil
Concreto de alto desempenho
Concreto autoadensável
Reologia
topic Engenharia civil
Concreto de alto desempenho
Concreto autoadensável
Reologia
description Tese (doutorado) - Universidade Federal de Santa Catarina, Centro Tecnológico, Programa de Pós-Graduação em Engenharia Civil, Florianópolis, 2017
publishDate 2017
dc.date.none.fl_str_mv 2017
2018-04-13T19:33:18Z
2018-04-13T19:33:18Z
dc.type.status.fl_str_mv info:eu-repo/semantics/publishedVersion
dc.type.driver.fl_str_mv info:eu-repo/semantics/doctoralThesis
format doctoralThesis
status_str publishedVersion
dc.identifier.uri.fl_str_mv 350631
https://repositorio.ufsc.br/handle/123456789/185533
identifier_str_mv 350631
url https://repositorio.ufsc.br/handle/123456789/185533
dc.language.iso.fl_str_mv por
language por
dc.rights.driver.fl_str_mv info:eu-repo/semantics/openAccess
eu_rights_str_mv openAccess
dc.format.none.fl_str_mv 215 p.| il., gráfs., tabs.
application/pdf
dc.source.none.fl_str_mv reponame:Repositório Institucional da UFSC
instname:Universidade Federal de Santa Catarina (UFSC)
instacron:UFSC
instname_str Universidade Federal de Santa Catarina (UFSC)
instacron_str UFSC
institution UFSC
reponame_str Repositório Institucional da UFSC
collection Repositório Institucional da UFSC
repository.name.fl_str_mv Repositório Institucional da UFSC - Universidade Federal de Santa Catarina (UFSC)
repository.mail.fl_str_mv
_version_ 1808652215415472128

Registros relacionados