Resistência à fadiga de diferentes restaurações de resina composta e cerâmica CAD/CAM, simulando o complexo dentina / esmalte: um estudo in vitro

Detalhes bibliográficos
Autor(a) principal: Contreras Molina, Ivan
Data de Publicação: 2015
Tipo de documento: Tese
Idioma: por
Título da fonte: Repositório Institucional da UFSC
Texto Completo: https://repositorio.ufsc.br/xmlui/handle/123456789/160542
Resumo: Tese (doutorado) - Universidade Federal de Santa Catarina, Centro de Ciências da Saúde, Programa de Pós-Graduação em Odontologia, Florianópolis, 2015.
id UFSC_d3fd191e32c9f6215addc2484715f770
oai_identifier_str oai:repositorio.ufsc.br:123456789/160542
network_acronym_str UFSC
network_name_str Repositório Institucional da UFSC
repository_id_str 2373
spelling Resistência à fadiga de diferentes restaurações de resina composta e cerâmica CAD/CAM, simulando o complexo dentina / esmalte: um estudo in vitroOdontologiaResinas compostasResinas dentáriasImplantes dentáriosDente suporteTese (doutorado) - Universidade Federal de Santa Catarina, Centro de Ciências da Saúde, Programa de Pós-Graduação em Odontologia, Florianópolis, 2015.Este estudo avaliou a resistência à fadiga de um projeto histo-anatômico experimental, com uma restauração bilaminada sobre implante confeccionada em cerâmica e resina nano-híbrida, além do efeito da seleção desses materiais. O sistema Cerec 4 CAD/CAM (versão 4.3, Sirona Dental Systems GmbH, Bensheim, Alemanha) foi utilizado para o desenho digital de 60 restaurações sobre implantes, realizando dois diferentes desenhos (desenho 1: coroa monolítica; desenho 2: desenho experimental simulando o complexo dentina-esmalte), totabilizando 4 grupos experimentais (n=15). Trinta coroas monolíticas foram fabricadas, sendo 15 em dissilicato de lítio (Grupo CE - Emax; Ivoclar Vivadent, Liechtenstein) e 15 em resina nanohíbrida (Grupo CL - Lava Ultimate; 3M/ESPE, EUA). Além disso, 15 mesoestruturas foram fabricadas em dissilicato de lítio simulando a dentina (Emax; Ivoclar Vivadent, Liechtenstein) associadas à 15 facetas em resina nanohíbrida simulando o esmalte (Grupo CEL - Lava Ultimate; 3M/ESPE, EUA) e 15 mesoestruturas em resina nano-híbrida (Lava Ultimate; 3M/ESPE, EUA) associadas com 15 facetas em dissilicato de lítio (Grupo CLE (Emax; Ivoclar Vivadent, Liechtenstein). As restaurações foram cimentadas sobre pilares de titânio personalizados (Solid Metal Abutment CM Universal Post, diâmetro 3,3mm, altura 4,0mm e cinta 0,8mm; Neodent, Curitiba, Brasil) aparafusados aos implantes (Cone Morse, Titamax CMEx 3,5mm x 10mm; Neodent, Curitiba, Brasil). Para as cerâmicas, as superfícies internas das restaurações foram condicionadas com ácido hidrofluorídrico e silanizadas (Ultradent, EUA), e no caso das resinas nanohídridas, jateadas e silanizadas. O protocolo adesivo após o aparafusamento do pilar sobre o implante utilizou adesivo (Optibond FL Bottle 2; Kerr, EUA) e resina composta fotopolimerizável pré-aquecida (Filtek Z100; 3M-ESPE, EUA). Os espécimens foram submetidos ao teste de esforço, simulando um movimento mastigatório cíclico e isométrico (5Hz) com carga de 50N (5.000 ciclos), seguido dos ciclos de 150N, 200N, 250N, 300N, 350N, 400N e 450N até um máximo de 20.000 ciclos em cada fase. Cada espécime foi carregado até fraturar ou até um máximo de 160.000 ciclos.Para o grupo CL, as restaurações fraturaram sob carga média de 347,39N (após 98.361 ciclos) e para o grupo CLE, a carga média foi de 313.20N (após 83.105 ciclos), Neste grupo, nenhum dos espécimens resistiu a todos os ciclos de carga (160.000). Para os grupos CE, as fraturas ocorreram com carga média de 381.47N (após 119.115 ciclos) e para o grupo CEL, sob 415.20N (após 132.873 ciclos). Suas respectivas taxas de sobrevivência foram de 26% e 33%. Testes Post-hoc com os dados das etapas de carregamento demonstraram uma maior resistência à fadiga para o grupo CEL quando comparado com o grupo CLE (p = 0,003). Falhas na restauração não ocorreram; porém, falhas de adesão na conexão entre a base de titânio e a mesoestrutura foram observadas. Coroas monolíticas e mesoestruturas de dissilicato de lítio facetadas com resina nanohíbrida apresentaram taxas de sobrevida mais altas quando comparadas com restaurações de resina nanohíbridas totais e mesoestruturas.<br>Abstract : Evaluate the fatigue resistance and failure mode of novel-design implant restorations made of histo-anatomic bilaminar assemblies. 60 implant restorations were fabricated. Monolithic crowns were used as a control group (15 lithium disilicate; group CE, and 15 nano-filled composite resin; group CL) and compared to bi-laminar restorations: 15 dentin- shaped lithium disilicate mesostructures with a nanofilled composite resin veneer (group CEL) and 15 dentin-shaped nanofilled composite resin mesostructures with a lithium disilicate veneer (group CLE). All monolithic and bi-laminar restorations were assembled and bonded to a customized metal implant abutment. Cyclic isometric chewing (5Hz) was simulated, starting with 5,000 cycles at a load of 150N, followed by 20,000 cycles with increments of 50N. Samples were loaded until fracture or to a maximum of 160,000 cycles. The groups were compared using the life table survival analysis (Logrank test at p=.05, post-hoc tests at p=.008). Results: In group CL, restorations failed at an average load of 347.39N (98.361 cycles) and for CLE at an average load of 313.20N (83.105 cycles) and none of the specimens withstood all 160,000-load cycles. For groups CE, failures were at an average load of 381.47N (119.115 cycles) and for CEL at 415.20N (132.873 cycles), with survival rates of 26% and 33% respectively. Post hoc tests from load step data showed higher fatigue resistance of CEL compared to CLE (p=.003). Lithium disilicate monolithic crowns and mesostructures with nanofilled composite resin veneer presented higher survival rates when compared to nanofilled composite resin restorations.Volpato, Cláudia Ângela MazieroMagne, PascalUniversidade Federal de Santa CatarinaContreras Molina, Ivan2016-04-15T13:13:44Z2016-04-15T13:13:44Z2015info:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/doctoralThesis113 p.| il., grafs., tabs.application/pdf337937https://repositorio.ufsc.br/xmlui/handle/123456789/160542porreponame:Repositório Institucional da UFSCinstname:Universidade Federal de Santa Catarina (UFSC)instacron:UFSCinfo:eu-repo/semantics/openAccess2016-04-15T13:13:45Zoai:repositorio.ufsc.br:123456789/160542Repositório InstitucionalPUBhttp://150.162.242.35/oai/requestopendoar:23732016-04-15T13:13:45Repositório Institucional da UFSC - Universidade Federal de Santa Catarina (UFSC)false
dc.title.none.fl_str_mv Resistência à fadiga de diferentes restaurações de resina composta e cerâmica CAD/CAM, simulando o complexo dentina / esmalte: um estudo in vitro
title Resistência à fadiga de diferentes restaurações de resina composta e cerâmica CAD/CAM, simulando o complexo dentina / esmalte: um estudo in vitro
spellingShingle Resistência à fadiga de diferentes restaurações de resina composta e cerâmica CAD/CAM, simulando o complexo dentina / esmalte: um estudo in vitro
Contreras Molina, Ivan
Odontologia
Resinas compostas
Resinas dentárias
Implantes dentários
Dente suporte
title_short Resistência à fadiga de diferentes restaurações de resina composta e cerâmica CAD/CAM, simulando o complexo dentina / esmalte: um estudo in vitro
title_full Resistência à fadiga de diferentes restaurações de resina composta e cerâmica CAD/CAM, simulando o complexo dentina / esmalte: um estudo in vitro
title_fullStr Resistência à fadiga de diferentes restaurações de resina composta e cerâmica CAD/CAM, simulando o complexo dentina / esmalte: um estudo in vitro
title_full_unstemmed Resistência à fadiga de diferentes restaurações de resina composta e cerâmica CAD/CAM, simulando o complexo dentina / esmalte: um estudo in vitro
title_sort Resistência à fadiga de diferentes restaurações de resina composta e cerâmica CAD/CAM, simulando o complexo dentina / esmalte: um estudo in vitro
author Contreras Molina, Ivan
author_facet Contreras Molina, Ivan
author_role author
dc.contributor.none.fl_str_mv Volpato, Cláudia Ângela Maziero
Magne, Pascal
Universidade Federal de Santa Catarina
dc.contributor.author.fl_str_mv Contreras Molina, Ivan
dc.subject.por.fl_str_mv Odontologia
Resinas compostas
Resinas dentárias
Implantes dentários
Dente suporte
topic Odontologia
Resinas compostas
Resinas dentárias
Implantes dentários
Dente suporte
description Tese (doutorado) - Universidade Federal de Santa Catarina, Centro de Ciências da Saúde, Programa de Pós-Graduação em Odontologia, Florianópolis, 2015.
publishDate 2015
dc.date.none.fl_str_mv 2015
2016-04-15T13:13:44Z
2016-04-15T13:13:44Z
dc.type.status.fl_str_mv info:eu-repo/semantics/publishedVersion
dc.type.driver.fl_str_mv info:eu-repo/semantics/doctoralThesis
format doctoralThesis
status_str publishedVersion
dc.identifier.uri.fl_str_mv 337937
https://repositorio.ufsc.br/xmlui/handle/123456789/160542
identifier_str_mv 337937
url https://repositorio.ufsc.br/xmlui/handle/123456789/160542
dc.language.iso.fl_str_mv por
language por
dc.rights.driver.fl_str_mv info:eu-repo/semantics/openAccess
eu_rights_str_mv openAccess
dc.format.none.fl_str_mv 113 p.| il., grafs., tabs.
application/pdf
dc.source.none.fl_str_mv reponame:Repositório Institucional da UFSC
instname:Universidade Federal de Santa Catarina (UFSC)
instacron:UFSC
instname_str Universidade Federal de Santa Catarina (UFSC)
instacron_str UFSC
institution UFSC
reponame_str Repositório Institucional da UFSC
collection Repositório Institucional da UFSC
repository.name.fl_str_mv Repositório Institucional da UFSC - Universidade Federal de Santa Catarina (UFSC)
repository.mail.fl_str_mv
_version_ 1808652116819968000

Registros relacionados