Fabricação de membranas de poliuretano termoplástico (TPU) e aditivos condutores à base de polipirrol (PPy) a partir do processo de eletrofiação

Detalhes bibliográficos
Autor(a) principal: Silveira, Adriana
Data de Publicação: 2016
Tipo de documento: Dissertação
Idioma: por
Título da fonte: Repositório Institucional da UFSC
Texto Completo: https://repositorio.ufsc.br/xmlui/handle/123456789/174420
Resumo: Dissertação (mestrado) - Universidade Federal de Santa Catarina, Centro Tecnológico, Programa de Pós-Graduação em Engenharia Mecânica, Florianópolis, 2016.
id UFSC_d55920fc8deb42b2b2f3bdc78c0c1184
oai_identifier_str oai:repositorio.ufsc.br:123456789/174420
network_acronym_str UFSC
network_name_str Repositório Institucional da UFSC
repository_id_str 2373
spelling Fabricação de membranas de poliuretano termoplástico (TPU) e aditivos condutores à base de polipirrol (PPy) a partir do processo de eletrofiaçãoEngenharia mecânicaMembranas (Tecnologia)PoliuretanasMateriais nanoestruturadosPolipirrolTermoplásticosDissertação (mestrado) - Universidade Federal de Santa Catarina, Centro Tecnológico, Programa de Pós-Graduação em Engenharia Mecânica, Florianópolis, 2016.Neste trabalho foram fabricadas membranas de poliuretano termoplástico (TPU) com aditivos condutores à base de polipirrol (PPy) a partir do processo de eletrofiação. Membranas eletrofiadas constituídas de fibras de TPU com diâmetros médios de 445 nm foram fabricadas a partir dos seguintes parâmetros de processamento: vazão de 1 mL.h-1; tensão elétrica de 17 kV; distância entre a agulha e coletor de 25 cm; concentração de TPU na solução de 10 %m; temperatura de 23 ± 3 °C e umidade relativa do ar de 55 ± 5 %. Posteriormente, foi avaliada a influência da incorporação dos aditivos condutores nas propriedades das soluções e na morfologia das membranas eletrofiadas. A condutividade iônica e viscosidade da solução aumentaram com a adição de polipirrol dopado com ácido dodecil benzeno sulfônico (PPy.DBSA) e PPy.DBSA sintetizado na presença de montmorilonita (MMT-PPy.DBSA). Além disso, as membranas com aditivos condutores apresentaram menor distribuição de diâmetro das fibras quando comparadas às membranas de TPU. Por fim, foi correlacionada a estrutura e propriedades das membranas eletrofiadas, com a utilização de coletor fixo e rotativo. Foi observado que a incorporação de PPy.DBSA e MMT-PPy.DBSA nas fibras de TPU exerce influência no módulo de elasticidade das membranas. A orientação das fibras alterou o comportamento mecânico sob tração das membranas, as quais apresentaram maiores tensões a uma deformação de 100%, para fibras orientadas paralelamente à tensão aplicada. Notou-se também que o valor de condutividade elétrica AC das membranas contendo MMT-PPy.DBSA foi três ordens de grandeza maior do que as membranas de TPU e de TPU/PPy.DBSA. A partir dos resultados obtidos neste trabalho, conclui-se que a incorporação dos aditivos afeta significativamente as propriedades da solução, influenciando as variáveis do processo e as propriedades finais das membranas. A partir do ajuste dos parâmetros de processamento foi possível fabricar membranas eletrofiadas baseadas em PPy com baixa quantidade de defeitos e valores de condutividade elétrica AC de até 3x10-9 S.cm-1. As membranas desenvolvidas neste trabalho apresentam potencial para serem aplicadas em diferentes áreas tecnológicas, tais como scaffolds para crescimento celular e sensores, devido principalmente à sua microestrutura, propriedades mecânicas e elétricas.<br>Abstract : In this work thermoplastic polyurethane (TPU) membranes with conductive additives based on polypyrrole (PPy) were fabricated by the electrospinning process. Electrospun membranes composed by TPU fibers with average diameters of 445 nm were manufactured using the following processing parameters: feed rate of 1 mL.h-1; electric tension of 17 kV; distance between needle and collector of 25 cm; TPU concentration in solution of 10 wt%; temperature of 23 ± 3 °C and relative humidity of 55 ± 5 %. Next, the influence of the incorporation of conductive additives on the solutions properties and the electrospun membranes microstructure was evaluated. The ionic conductivity and the solution viscosity increased with the incorporation of polypyrrole doped with dodecyl benzene sulfonic acid (PPy.DBSA) and PPy.DBSA synthesized in the presence of montmorillonite (MMT-PPy.DBSA). Moreover, the membranes with conductive additives displayed a lower fiber diameter distribution when compared with the neat TPU membranes. Finally, membranes structure and properties where correlated, with the use of fixed plate and rotating drum collector. It was observed that the incorporation of PPy.DBSA and MMT-PPy.DBSA in the TPU fibers has influence on the membrane elastic modulus. The fiber orientation altered the membranes mechanical behavior under traction, which presented higher stress at a strain of 100%, for fiber oriented in parallel with the stress. It was also notice that the AC electrical conductivity value of the membrane containing MMT-PPy.DBSA was three order of magnitude higher than the value for the neat TPU and TPU/PPy.DBSA membranes. From the results obtained in this work, it was concluded that the additive incorporation affects significantly the solution properties, effecting the process variables and the membranes final properties. By adjusting the process parameters, it was possible to manufacture electrospun mats based on PPy with low amount of defects and AC electrical conductivity up to 3x10-9 S.cm-1. The membranes developed in this work have the potential to be applied in different technological areas, such as scaffolds for cellular growth and sensors, especially due to its microstructure, mechanical and electrical properties.Barra, Guilherme Mariz de OliveiraMerlini, ClaudiaUniversidade Federal de Santa CatarinaSilveira, Adriana2017-04-04T04:08:06Z2017-04-04T04:08:06Z2016info:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/masterThesis114 p.| il., grafs., tabs.application/pdf344645https://repositorio.ufsc.br/xmlui/handle/123456789/174420porreponame:Repositório Institucional da UFSCinstname:Universidade Federal de Santa Catarina (UFSC)instacron:UFSCinfo:eu-repo/semantics/openAccess2017-04-04T04:08:06Zoai:repositorio.ufsc.br:123456789/174420Repositório InstitucionalPUBhttp://150.162.242.35/oai/requestopendoar:23732017-04-04T04:08:06Repositório Institucional da UFSC - Universidade Federal de Santa Catarina (UFSC)false
dc.title.none.fl_str_mv Fabricação de membranas de poliuretano termoplástico (TPU) e aditivos condutores à base de polipirrol (PPy) a partir do processo de eletrofiação
title Fabricação de membranas de poliuretano termoplástico (TPU) e aditivos condutores à base de polipirrol (PPy) a partir do processo de eletrofiação
spellingShingle Fabricação de membranas de poliuretano termoplástico (TPU) e aditivos condutores à base de polipirrol (PPy) a partir do processo de eletrofiação
Silveira, Adriana
Engenharia mecânica
Membranas (Tecnologia)
Poliuretanas
Materiais nanoestruturados
Polipirrol
Termoplásticos
title_short Fabricação de membranas de poliuretano termoplástico (TPU) e aditivos condutores à base de polipirrol (PPy) a partir do processo de eletrofiação
title_full Fabricação de membranas de poliuretano termoplástico (TPU) e aditivos condutores à base de polipirrol (PPy) a partir do processo de eletrofiação
title_fullStr Fabricação de membranas de poliuretano termoplástico (TPU) e aditivos condutores à base de polipirrol (PPy) a partir do processo de eletrofiação
title_full_unstemmed Fabricação de membranas de poliuretano termoplástico (TPU) e aditivos condutores à base de polipirrol (PPy) a partir do processo de eletrofiação
title_sort Fabricação de membranas de poliuretano termoplástico (TPU) e aditivos condutores à base de polipirrol (PPy) a partir do processo de eletrofiação
author Silveira, Adriana
author_facet Silveira, Adriana
author_role author
dc.contributor.none.fl_str_mv Barra, Guilherme Mariz de Oliveira
Merlini, Claudia
Universidade Federal de Santa Catarina
dc.contributor.author.fl_str_mv Silveira, Adriana
dc.subject.por.fl_str_mv Engenharia mecânica
Membranas (Tecnologia)
Poliuretanas
Materiais nanoestruturados
Polipirrol
Termoplásticos
topic Engenharia mecânica
Membranas (Tecnologia)
Poliuretanas
Materiais nanoestruturados
Polipirrol
Termoplásticos
description Dissertação (mestrado) - Universidade Federal de Santa Catarina, Centro Tecnológico, Programa de Pós-Graduação em Engenharia Mecânica, Florianópolis, 2016.
publishDate 2016
dc.date.none.fl_str_mv 2016
2017-04-04T04:08:06Z
2017-04-04T04:08:06Z
dc.type.status.fl_str_mv info:eu-repo/semantics/publishedVersion
dc.type.driver.fl_str_mv info:eu-repo/semantics/masterThesis
format masterThesis
status_str publishedVersion
dc.identifier.uri.fl_str_mv 344645
https://repositorio.ufsc.br/xmlui/handle/123456789/174420
identifier_str_mv 344645
url https://repositorio.ufsc.br/xmlui/handle/123456789/174420
dc.language.iso.fl_str_mv por
language por
dc.rights.driver.fl_str_mv info:eu-repo/semantics/openAccess
eu_rights_str_mv openAccess
dc.format.none.fl_str_mv 114 p.| il., grafs., tabs.
application/pdf
dc.source.none.fl_str_mv reponame:Repositório Institucional da UFSC
instname:Universidade Federal de Santa Catarina (UFSC)
instacron:UFSC
instname_str Universidade Federal de Santa Catarina (UFSC)
instacron_str UFSC
institution UFSC
reponame_str Repositório Institucional da UFSC
collection Repositório Institucional da UFSC
repository.name.fl_str_mv Repositório Institucional da UFSC - Universidade Federal de Santa Catarina (UFSC)
repository.mail.fl_str_mv
_version_ 1808652084719910912

Registros relacionados