Avaliação de compósito magnético mole baseado em partículas ferromagnéticas recobertas com pentóxido de nióbio nanoparticulado e fases vítreas

Detalhes bibliográficos
Autor(a) principal: Silva, Bernardo Sena da
Data de Publicação: 2023
Tipo de documento: Dissertação
Idioma: por
Título da fonte: Repositório Institucional da UFSC
Texto Completo: https://repositorio.ufsc.br/handle/123456789/254014
Resumo: Dissertação (mestrado) - Universidade Federal de Santa Catarina, Centro Tecnológico, Programa de Pós-Graduação em Ciência e Engenharia de Materiais, Florianópolis, 2023.
id UFSC_e1d3b698f12f7709f40add8eee23eb6e
oai_identifier_str oai:repositorio.ufsc.br:123456789/254014
network_acronym_str UFSC
network_name_str Repositório Institucional da UFSC
repository_id_str 2373
spelling Avaliação de compósito magnético mole baseado em partículas ferromagnéticas recobertas com pentóxido de nióbio nanoparticulado e fases vítreasCiência dos materiaisEngenharia de materiaisPerdas magnéticasNanopartículasNióbioBoroÓxidosDissertação (mestrado) - Universidade Federal de Santa Catarina, Centro Tecnológico, Programa de Pós-Graduação em Ciência e Engenharia de Materiais, Florianópolis, 2023.A eficiência energética é um dos principais focos do desenvolvimento tecnológico mundial e, sendo assim, os materiais magnéticos ganham destaque, visto que novos desenvolvimentos nessa área buscam a otimização de dispositivos ligados à geração e à conversão de energia elétrica. Os compósitos magnéticos moles (Soft Magnetic Composites ? SMCs) são uma classe de materiais magnéticos cuja configuração visa à redução de perdas devido à alta resistividade elétrica introduzida pelo revestimento isolante de partículas ferromagnéticas em um compactado, permitindo a condução do fluxo magnético de maneira isotrópica em três dimensões e possibilitando a miniaturização de motores elétricos, designs inovadores e aplicações mais sofisticadas. Essas vantagens têm sido vinculadas ao aumento na frequência de trabalho destes motores. No entanto, esse aumento leva a uma maior perda energética por conta da aparição de correntes parasitas no núcleo magnético. Uma forma de mitigar esses efeitos se dá através do desenvolvimento de propriedades nos SMCs que tragam simultaneamente alta magnetização de saturação e elevada resistividade elétrica. Tais propriedades são dependentes das características da partícula ferromagnética e do revestimento isolante. Portanto, tendo tudo isto em vista, o objetivo deste trabalho é avaliar um SMC contendo como primeira camada nanopartículas de óxido de nióbio (Nb2O5) e como segunda camada uma fase vítrea. Estas nanopartículas óxidas foram obtidas através de uma suspensão estável de Nb2O5 recebida de uma empresa parceira e caracterizadas por meio de análises de distribuição de tamanho de partícula, MEV-EDX, potencial zeta e tamanho hidrodinâmico. Adicionalmente, a utilização de uma fase vítrea composta por óxido de boro foi utilizada com parâmetros fixados para avaliar como a camada óxida interagiria com a camada vítrea, sendo o silicato de potássio do tipo vidro líquido o gerador da camada vítrea estudada nesta pesquisa. A mesma, então, foi dividida em quatro etapas: na primeira, o pó de ferro utilizado teve suas propriedades magnéticas melhoradas através de um tratamento térmico prévio em forno resistivo e caracterizadas com microscopia óptica e medição de propriedades magnéticas. Este tratamento reduziu em 43% as perdas por histerese e aumentou em 17% a permeabilidade em relação ao pó de ferro comercial. Na segunda etapa, houve o revestimento com Nb2O5 variando tempo de mistura da solução com Nb2O5 e sua concentração molar. A amostra com menor concentração molar de Nb2O5 e menor tempo de mistura (10 mM ? 15 min) se destacou como mais promissora. Na terceira etapa, novos métodos de medição magnética e elétrica foram desenvolvidos e dispositivos de medição magnética e elétrica foram produzidos devido a problemas ocorridos no equipamento comercial, onde os resultados obtidos nestes dispositivos foram comparados e validados com êxito. Por fim, ocorreu a última etapa: o recobrimento com silicato de potássio, variando a concentração de sólidos da solução. O novo SMC de dupla camada produzido foi avaliado utilizando as ferramentas de medição desenvolvidas no laboratório com resultado de resistividade promissor para fração de silicato de potássio de 1,5% em massa.Abstract: Energy efficiency is one of the main focuses of global technological development and, therefore, magnetic materials gain prominence, as new developments in this area seek to optimize devices linked to the generation and conversion of electrical energy. Soft Magnetic Composites (SMCs) are a class of magnetic materials whose configuration aims to reduce losses due to the high electrical resistivity introduced by the insulating coating of ferromagnetic particles in a compact, allowing the conduction of magnetic flux in an isotropic manner in three dimensions and enabling the miniaturization of electric motors, innovative designs and more sophisticated applications. These advantages have been linked to the increase in the working frequency of these engines. However, this increase leads to greater energy loss due to the appearance of eddy currents in the magnetic core. One way to mitigate these effects is through the development of properties in SMCs that simultaneously bring high saturation magnetization and high electrical resistivity. Such properties are dependent on the characteristics of the ferromagnetic particle and the insulating coating. Therefore, with all this in mind, the objective of this work is to evaluate an SMC containing niobium oxide nanoparticles (Nb2O5) as the first layer and a glass phase as the second layer. These oxide nanoparticles were obtained through a stable suspension of Nb2O5 received from a partner company and characterized through analysis of particle size distribution, SEM-EDX, zeta potential and hydrodynamic size. Additionally, the use of a glass phase composed of boron oxide was used with fixed parameters to evaluate how the oxide layer would interact with the glass layer, with liquid glass-type potassium silicate being the generator of the glass layer studied in this research. It was then divided into four stages: in the first, the iron powder used had its magnetic properties improved through prior heat treatment in a resistive furnace and characterized with optical microscopy and measurement of magnetic properties. This treatment reduced hysteresis losses by 43% and increased permeability by 17% compared to commercial iron powder. In the second stage, there was coating with Nb2O5 varying the mixing time of the solution with Nb2O5 and its molar concentration. The sample with the lowest molar concentration of Nb2O5 and the shortest mixing time (10 mM ? 15 min) stood out as the most promising. In the third stage, new magnetic and electrical measurement methods were developed and magnetic and electrical measurement devices were produced due to problems occurring in commercial equipment, where the results obtained from these devices were successfully compared and validated. Finally, the last stage occurred: coating with potassium silicate, varying the concentration of solids in the solution. The newly produced double-layer SMC was evaluated using the measurement tools developed in the laboratory with promising resistivity results for a potassium silicate fraction of 1.5% by mass.Klein, Aloisio NelmoEvangelista, Leandro LimaUniversidade Federal de Santa CatarinaSilva, Bernardo Sena da2024-01-15T23:24:20Z2024-01-15T23:24:20Z2023info:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/masterThesis85 p.| il., gráfs., tabs.application/pdf385761https://repositorio.ufsc.br/handle/123456789/254014porreponame:Repositório Institucional da UFSCinstname:Universidade Federal de Santa Catarina (UFSC)instacron:UFSCinfo:eu-repo/semantics/openAccess2024-01-15T23:24:20Zoai:repositorio.ufsc.br:123456789/254014Repositório InstitucionalPUBhttp://150.162.242.35/oai/requestopendoar:23732024-01-15T23:24:20Repositório Institucional da UFSC - Universidade Federal de Santa Catarina (UFSC)false
dc.title.none.fl_str_mv Avaliação de compósito magnético mole baseado em partículas ferromagnéticas recobertas com pentóxido de nióbio nanoparticulado e fases vítreas
title Avaliação de compósito magnético mole baseado em partículas ferromagnéticas recobertas com pentóxido de nióbio nanoparticulado e fases vítreas
spellingShingle Avaliação de compósito magnético mole baseado em partículas ferromagnéticas recobertas com pentóxido de nióbio nanoparticulado e fases vítreas
Silva, Bernardo Sena da
Ciência dos materiais
Engenharia de materiais
Perdas magnéticas
Nanopartículas
Nióbio
Boro
Óxidos
title_short Avaliação de compósito magnético mole baseado em partículas ferromagnéticas recobertas com pentóxido de nióbio nanoparticulado e fases vítreas
title_full Avaliação de compósito magnético mole baseado em partículas ferromagnéticas recobertas com pentóxido de nióbio nanoparticulado e fases vítreas
title_fullStr Avaliação de compósito magnético mole baseado em partículas ferromagnéticas recobertas com pentóxido de nióbio nanoparticulado e fases vítreas
title_full_unstemmed Avaliação de compósito magnético mole baseado em partículas ferromagnéticas recobertas com pentóxido de nióbio nanoparticulado e fases vítreas
title_sort Avaliação de compósito magnético mole baseado em partículas ferromagnéticas recobertas com pentóxido de nióbio nanoparticulado e fases vítreas
author Silva, Bernardo Sena da
author_facet Silva, Bernardo Sena da
author_role author
dc.contributor.none.fl_str_mv Klein, Aloisio Nelmo
Evangelista, Leandro Lima
Universidade Federal de Santa Catarina
dc.contributor.author.fl_str_mv Silva, Bernardo Sena da
dc.subject.por.fl_str_mv Ciência dos materiais
Engenharia de materiais
Perdas magnéticas
Nanopartículas
Nióbio
Boro
Óxidos
topic Ciência dos materiais
Engenharia de materiais
Perdas magnéticas
Nanopartículas
Nióbio
Boro
Óxidos
description Dissertação (mestrado) - Universidade Federal de Santa Catarina, Centro Tecnológico, Programa de Pós-Graduação em Ciência e Engenharia de Materiais, Florianópolis, 2023.
publishDate 2023
dc.date.none.fl_str_mv 2023
2024-01-15T23:24:20Z
2024-01-15T23:24:20Z
dc.type.status.fl_str_mv info:eu-repo/semantics/publishedVersion
dc.type.driver.fl_str_mv info:eu-repo/semantics/masterThesis
format masterThesis
status_str publishedVersion
dc.identifier.uri.fl_str_mv 385761
https://repositorio.ufsc.br/handle/123456789/254014
identifier_str_mv 385761
url https://repositorio.ufsc.br/handle/123456789/254014
dc.language.iso.fl_str_mv por
language por
dc.rights.driver.fl_str_mv info:eu-repo/semantics/openAccess
eu_rights_str_mv openAccess
dc.format.none.fl_str_mv 85 p.| il., gráfs., tabs.
application/pdf
dc.source.none.fl_str_mv reponame:Repositório Institucional da UFSC
instname:Universidade Federal de Santa Catarina (UFSC)
instacron:UFSC
instname_str Universidade Federal de Santa Catarina (UFSC)
instacron_str UFSC
institution UFSC
reponame_str Repositório Institucional da UFSC
collection Repositório Institucional da UFSC
repository.name.fl_str_mv Repositório Institucional da UFSC - Universidade Federal de Santa Catarina (UFSC)
repository.mail.fl_str_mv
_version_ 1808652123653537792

Registros relacionados