Desgaste tridimensional e mecanismos de desgaste em ferramentas de PcBN e cerâmica no torneamento do aço AISI 52100

Detalhes bibliográficos
Autor(a) principal: Dorneles, Caroline Francisco
Data de Publicação: 2020
Tipo de documento: Dissertação
Idioma: por
Título da fonte: Repositório Institucional da UFSC
Texto Completo: https://repositorio.ufsc.br/handle/123456789/215707
Resumo: Dissertação (mestrado) - Universidade Federal de Santa Catarina, Centro Tecnológico, Programa de Pós-Graduação em Engenharia Mecânica, Florianópolis, 2019.
id UFSC_e68c1c63f610437e6a6e3ea74de45bde
oai_identifier_str oai:repositorio.ufsc.br:123456789/215707
network_acronym_str UFSC
network_name_str Repositório Institucional da UFSC
repository_id_str 2373
spelling Universidade Federal de Santa CatarinaDorneles, Caroline FranciscoSchroeter, Rolf BertrandBoing, Denis2020-10-21T21:19:38Z2020-10-21T21:19:38Z2019.368688https://repositorio.ufsc.br/handle/123456789/215707Dissertação (mestrado) - Universidade Federal de Santa Catarina, Centro Tecnológico, Programa de Pós-Graduação em Engenharia Mecânica, Florianópolis, 2019.O torneamento de materiais endurecidos, empregado na fabricação de componentes como eixos e rolamentos, é tipicamente realizado com ferramentas de PCBN e de cerâmica, devido às propriedades adequadas para suportar as condições tribológicas impostas pelo processo de usinagem. A melhora na tecnologia de torneamento de materiais endurecidos, principalmente no que se refere ao tempo de vida e avaliação de desgaste das ferramentas, ainda requer melhor entendimento dos fenômenos mecânicos e físicos do processo. Os métodos para previsão de vida e desempenho de ferramentas de usinagem geralmente são baseados em parâmetros bidimensionais, não fornecendo informações abrangentes acerca da superfície desgastada. Os métodos de medição tridimensionais têm permitido a obtenção de informações mais completas, permitindo análises mais completas sobre os mecanismos de desgaste atuantes nas ferramentas de corte. Neste contexto, o presente trabalho visa melhor compreender o desgaste das ferramentas de PcBN sem revestimento, de PcBN com revestimento e de cerâmica aplicadas no torneamento do aço AISI 52100 com 60 HRC de dureza, utilizando a taxa de desgaste com base nos parâmetros tridimensionais e a influência da velocidade de corte no desgaste e nas componentes da força de usinagem. Analisando as componentes da força de usinagem, os maiores valores da força passiva foram obtidos com a ferramenta de cerâmica, independentemente da velocidade de corte testadas. As forças de corte e passiva não apresentaram diferença significativa com o aumento da velocidade de corte. Verificou-se que para a maior velocidade de corte ensaiada (vc = 234 m/min) o desgaste de flanco (VBB) foi cerca de 1,6 vezes maior em comparação com o VBB para vc = 120 m/min para a ferramenta de PcBN não revestida e 1,3 vezes maior para as ferramentas de cerâmica e PcBN revestida. Para a velocidade de corte de 120 m/min, a ferramenta de PcBN não revestida apresentou desgaste WMD cerca de 28% maior que a ferramenta de PcBN revestida, comparando com a ferramenta de cerâmica esse parâmetro é aproximadamente 16% maior. O incremento da velocidade de corte de 120 m/min para 234 m/min acarretou em um acréscimo no volume de material removido de aproximadamente 325 % para a ferramenta de PcBN, 260% para a ferramenta de PcBN revestida e 85% para a ferramenta de cerâmica. Verificou-se também que a diferença no valor da taxa de desgaste entre as ferramentas de PcBN e de cerâmica torna-se cada vez maior com o aumento da velocidade de corte, passando de 43% para vc = 187,5 m/min para 87% a 234 m/min, apresentando a ferramenta de cerâmica melhor desempenho do que as outras ferramentas testadas.Abstract: The turning of hardened steels, used in the manufacture of components such as shafts and bearings, is performed with PcBN and ceramic tools for it supports by the tribological conditions imposed by the machining process. The improvement in the technology of turning of hardened steels, mainly with respect to the lifetime and evaluation of tool wear, still requires a better understanding of the mechanical and physical processes of the process. The methods for life prediction and performance of machining tools are generally based on two-dimensional parameters, not providing sufficient information about the worn surface. The three-dimensional measurement methods have allowed a greater number of information, allowing the most complete on the cutting tools to act on the cutting tools. In this context, the present work aims to better understand the wear of PCBN uncoated, PCBN coated and ceramic tools applied in the turning of AISI 52100 steel with 60 HRC hardness, using the wear rate based on threedimensional parameters and the influence of cutting speed on wear and machining force components. By analyzing the components of the machining force, the highest passive force values were obtained with the ceramic tool, regardless of the shear rate tested. The shearing and passive forces did not present significant difference with the increase of the cutting speed. It was found that for the highest cutting speed (vc = 234 m/min) the flank wear (VBB) was about 1.6 times higher compared to VBB for vc = 120 m/min for the tool PcBN uncoated and 1.3 times higher for ceramic and PcBN coated tools. For the cutting speed of 120 m/min, the uncoated PcBN tool presented WMD wear about 28% higher than the coated PcBN tool, compared to the ceramic tool this parameter is approximately 16% higher. The increase of the cutting speed from 120 m/min to 234 m/min resulted in an increase in the volume of removed material of approximately 325% for the PcBN tool, 260% for the coated PcBN tool and 85% for the tool. ceramics. It was also verified that the difference in the value of the wear rate between PcBN and ceramic tools increases with increasing cutting speed, from 43% for vc = 187.5 m/min to 87 % at 234 m/min, with the ceramic tool presenting better performance than the other tools tested.102 p.| il.porEngenharia mecânicaTorneamentoDesgaste mecânicoDesgaste tridimensional e mecanismos de desgaste em ferramentas de PcBN e cerâmica no torneamento do aço AISI 52100info:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/masterThesisreponame:Repositório Institucional da UFSCinstname:Universidade Federal de Santa Catarina (UFSC)instacron:UFSCinfo:eu-repo/semantics/openAccessORIGINALPEMC2007-D.pdfPEMC2007-D.pdfapplication/pdf6942864https://repositorio.ufsc.br/bitstream/123456789/215707/-1/PEMC2007-D.pdf11abe034f51b415be76d8d33d6c05f6dMD5-1123456789/2157072020-10-21 18:19:38.891oai:repositorio.ufsc.br:123456789/215707Repositório de PublicaçõesPUBhttp://150.162.242.35/oai/requestopendoar:23732020-10-21T21:19:38Repositório Institucional da UFSC - Universidade Federal de Santa Catarina (UFSC)false
dc.title.none.fl_str_mv Desgaste tridimensional e mecanismos de desgaste em ferramentas de PcBN e cerâmica no torneamento do aço AISI 52100
title Desgaste tridimensional e mecanismos de desgaste em ferramentas de PcBN e cerâmica no torneamento do aço AISI 52100
spellingShingle Desgaste tridimensional e mecanismos de desgaste em ferramentas de PcBN e cerâmica no torneamento do aço AISI 52100
Dorneles, Caroline Francisco
Engenharia mecânica
Torneamento
Desgaste mecânico
title_short Desgaste tridimensional e mecanismos de desgaste em ferramentas de PcBN e cerâmica no torneamento do aço AISI 52100
title_full Desgaste tridimensional e mecanismos de desgaste em ferramentas de PcBN e cerâmica no torneamento do aço AISI 52100
title_fullStr Desgaste tridimensional e mecanismos de desgaste em ferramentas de PcBN e cerâmica no torneamento do aço AISI 52100
title_full_unstemmed Desgaste tridimensional e mecanismos de desgaste em ferramentas de PcBN e cerâmica no torneamento do aço AISI 52100
title_sort Desgaste tridimensional e mecanismos de desgaste em ferramentas de PcBN e cerâmica no torneamento do aço AISI 52100
author Dorneles, Caroline Francisco
author_facet Dorneles, Caroline Francisco
author_role author
dc.contributor.none.fl_str_mv Universidade Federal de Santa Catarina
dc.contributor.author.fl_str_mv Dorneles, Caroline Francisco
dc.contributor.advisor1.fl_str_mv Schroeter, Rolf Bertrand
dc.contributor.advisor-co1.fl_str_mv Boing, Denis
contributor_str_mv Schroeter, Rolf Bertrand
Boing, Denis
dc.subject.classification.none.fl_str_mv Engenharia mecânica
Torneamento
Desgaste mecânico
topic Engenharia mecânica
Torneamento
Desgaste mecânico
description Dissertação (mestrado) - Universidade Federal de Santa Catarina, Centro Tecnológico, Programa de Pós-Graduação em Engenharia Mecânica, Florianópolis, 2019.
publishDate 2020
dc.date.issued.fl_str_mv 2019.
dc.date.accessioned.fl_str_mv 2020-10-21T21:19:38Z
dc.date.available.fl_str_mv 2020-10-21T21:19:38Z
dc.type.status.fl_str_mv info:eu-repo/semantics/publishedVersion
dc.type.driver.fl_str_mv info:eu-repo/semantics/masterThesis
format masterThesis
status_str publishedVersion
dc.identifier.uri.fl_str_mv https://repositorio.ufsc.br/handle/123456789/215707
dc.identifier.other.none.fl_str_mv 368688
identifier_str_mv 368688
url https://repositorio.ufsc.br/handle/123456789/215707
dc.language.iso.fl_str_mv por
language por
dc.rights.driver.fl_str_mv info:eu-repo/semantics/openAccess
eu_rights_str_mv openAccess
dc.format.none.fl_str_mv 102 p.| il.
dc.source.none.fl_str_mv reponame:Repositório Institucional da UFSC
instname:Universidade Federal de Santa Catarina (UFSC)
instacron:UFSC
instname_str Universidade Federal de Santa Catarina (UFSC)
instacron_str UFSC
institution UFSC
reponame_str Repositório Institucional da UFSC
collection Repositório Institucional da UFSC
bitstream.url.fl_str_mv https://repositorio.ufsc.br/bitstream/123456789/215707/-1/PEMC2007-D.pdf
bitstream.checksum.fl_str_mv 11abe034f51b415be76d8d33d6c05f6d
bitstream.checksumAlgorithm.fl_str_mv MD5
repository.name.fl_str_mv Repositório Institucional da UFSC - Universidade Federal de Santa Catarina (UFSC)
repository.mail.fl_str_mv
_version_ 1766805014640066560

Registros relacionados