Desenvolvimento de argamassas autonivelantes com ativação alcalina de precursores residuais

Detalhes bibliográficos
Autor(a) principal: Tambara Júnior, Luís Urbano Durlo
Data de Publicação: 2016
Tipo de documento: Dissertação
Idioma: por
Título da fonte: Repositório Institucional da UFSC
Texto Completo: https://repositorio.ufsc.br/xmlui/handle/123456789/169900
Resumo: Dissertação (mestrado) - Universidade Federal de Santa Catarina, Centro Tecnológico, Programa de Pós-Graduação em Engenharia Civil, Florianópolis, 2016.
id UFSC_ebfdf92a23703533c0c3a216d2fbd6af
oai_identifier_str oai:repositorio.ufsc.br:123456789/169900
network_acronym_str UFSC
network_name_str Repositório Institucional da UFSC
repository_id_str 2373
spelling Desenvolvimento de argamassas autonivelantes com ativação alcalina de precursores residuais Engenharia civilMinerais industriaisCinza pesadaCimento portlandArgamassaDissertação (mestrado) - Universidade Federal de Santa Catarina, Centro Tecnológico, Programa de Pós-Graduação em Engenharia Civil, Florianópolis, 2016.Utilizar novas classes de ligantes cimentícios se faz recorrente atualmente, sendo os cimentos ativados alcalinamente, com valorização de percursores residuais, um tema que necessita de maiores pesquisas e investigações. Estes cimentos são formados a partir da ativação de minerais aluminossilicatos amorfos em soluções alcalinas. Resíduos industriais como cinza pesada (CZP) são utilizados como minerais aluminossilicatos em ativações alcalinas, motivando uma valorização dos mesmos. Para solução ativadora são difundidos os hidróxidos de sódio, potássio e silicatos solúveis. Nesta pesquisa foi realizado estudo de ativações alcalinas hibridas, em razão da baixa reatividade apresentada para ativações apenas para CZP, foram realizadas misturas binárias com cimento Portland (CP) nas proporções de 2,5, 5, 10 e 30% de substituição de CZP moída por 540? e calcinada a 600°C por CP e ternárias, substituindo na porcentagem de 10% de CP por cinza de casca de arroz (CCA) em 25, 50 e 75%. A cura foi feita em estufa a 80°C por 24 horas. Buscou-se obter composições que pudessem ser aplicadas em argamassas autonivelantes para uso em sistemas de revestimento de pisos. Para tanto, foram analisados os comportamentos de espalhamento em estado fresco das argamassas para a obtenção de um material autonivelante (espalhamento > 250 mm). No estado endurecido para as misturas binárias foi observado maiores resistências à tração na flexão e à compressão para maiores presenças de CP, amostra contendo 30% de CP obteve resistência de 7,53 MPa à tração e 33,5 MPa à compressão, entretanto o acréscimo de cimento acarretou em maiores perdas de trabalhabilidade e espalhamento. Foram realizadas análises por meio das técnicas de DRX e MEV, observando formação de géis N-A-S-H e (N,C)-A-S-H. Nas ternárias observou-se decréscimo de resistência à tração e à compressão para maiores substituições de CCA. Para todas as amostras constatou-se durabilidade similares as de argamassas comuns, havendo melhores resultados para ensaios de ataques ácidos, devido menores quantidades de cálcio. Houve menores valores de retração linear e empenamento de placas, absorção capilar e porosidade aberta para as ativações alcalinas quando comparadas a cimento Portland comum, havendo incremento da porosidade com o acréscimo da substituição de CP. Por fim, constatou-se a viabilidade na produção de produto autonivelante nas composições de ativações alcalinas híbridas binárias de CZP e CP, sendo a melhor mistura a contendo 10% de CP.<br>Abstract : Using new classes of cementitious binders is frequently today, the alkali-activated cements with residual precursors valorization is a topic that needs further research and investigation. These cements are formed from aluminosilicate minerals amorphous activated in an alkaline solution. Industrial waste, as bottom ash (CZP) are used as aluminosilicate minerals in alkaline activation, encouraging their valorization. Sodium and potassium hydroxides and sodium silicate are used as activating solution. This research was conducted of hybrid alkaline activation, due low reactivity presented from bottom ash, binary mixtures were made of bottom ash and Portland cement in proportions of 2.5%, 5%, 10% and 30% substitution of bottom ash grounded 450? and calcined 600°C of Portland cement, for ternary mixtures CP was replaced by rice husk ash (CCA) in proportions of 25%, 50% and 75% of Portland cement to rice husk ash, to the reference of binary 10% OPC (Ordinary Portland Cement). Curing was at 80°C for 24 hours. Was attempted to obtain compositions that could be applied in self-leveling mortars for coating systems. To this end, the spreading behavior were analyzed in the fresh mortar to obtain a self-leveling material (spreading > 250 mm). In the hardened state for binary mixtures was observed in greater tensile and compressive strength for higher CP amount, mortars with 30% CP obtained tensile resistance of 7,53 MPa and to compressive strength 33.5 MPa, however, the cement increasing resulted workability and spreading losses. Techniques SEM and XRD analyses were performed to observing the formation of N-A-S-H and (N,C)-A-S-H gels. In ternaries mixtures were observed resistance decrease with higher substitutions of CCA. For all samples were founded similar durability, with better results for acid attack test when compared with normal mortars, due lower amount of calcium. There were lower values of linear shrinkage, curling, capillary absorption and open porosity for alkaline activations compared to ordinary Portland cement, with increasing porosity with higher replacement of CP. Finally, it was viable the production of self-leveling products in the composition of binary hybrid alkaline activation of CZP600 and CP. The best mixture was the binary containing 10% CP.Rocha, Janaíde CavalcanteUniversidade Federal de Santa CatarinaTambara Júnior, Luís Urbano Durlo2016-10-25T03:11:23Z2016-10-25T03:11:23Z2016info:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/masterThesis201 p.| il., grafs., tabs.application/pdf342549https://repositorio.ufsc.br/xmlui/handle/123456789/169900porreponame:Repositório Institucional da UFSCinstname:Universidade Federal de Santa Catarina (UFSC)instacron:UFSCinfo:eu-repo/semantics/openAccess2016-10-25T03:11:23Zoai:repositorio.ufsc.br:123456789/169900Repositório InstitucionalPUBhttp://150.162.242.35/oai/requestopendoar:23732016-10-25T03:11:23Repositório Institucional da UFSC - Universidade Federal de Santa Catarina (UFSC)false
dc.title.none.fl_str_mv Desenvolvimento de argamassas autonivelantes com ativação alcalina de precursores residuais
title Desenvolvimento de argamassas autonivelantes com ativação alcalina de precursores residuais
spellingShingle Desenvolvimento de argamassas autonivelantes com ativação alcalina de precursores residuais
Tambara Júnior, Luís Urbano Durlo
Engenharia civil
Minerais industriais
Cinza pesada
Cimento portland
Argamassa
title_short Desenvolvimento de argamassas autonivelantes com ativação alcalina de precursores residuais
title_full Desenvolvimento de argamassas autonivelantes com ativação alcalina de precursores residuais
title_fullStr Desenvolvimento de argamassas autonivelantes com ativação alcalina de precursores residuais
title_full_unstemmed Desenvolvimento de argamassas autonivelantes com ativação alcalina de precursores residuais
title_sort Desenvolvimento de argamassas autonivelantes com ativação alcalina de precursores residuais
author Tambara Júnior, Luís Urbano Durlo
author_facet Tambara Júnior, Luís Urbano Durlo
author_role author
dc.contributor.none.fl_str_mv Rocha, Janaíde Cavalcante
Universidade Federal de Santa Catarina
dc.contributor.author.fl_str_mv Tambara Júnior, Luís Urbano Durlo
dc.subject.por.fl_str_mv Engenharia civil
Minerais industriais
Cinza pesada
Cimento portland
Argamassa
topic Engenharia civil
Minerais industriais
Cinza pesada
Cimento portland
Argamassa
description Dissertação (mestrado) - Universidade Federal de Santa Catarina, Centro Tecnológico, Programa de Pós-Graduação em Engenharia Civil, Florianópolis, 2016.
publishDate 2016
dc.date.none.fl_str_mv 2016-10-25T03:11:23Z
2016-10-25T03:11:23Z
2016
dc.type.status.fl_str_mv info:eu-repo/semantics/publishedVersion
dc.type.driver.fl_str_mv info:eu-repo/semantics/masterThesis
format masterThesis
status_str publishedVersion
dc.identifier.uri.fl_str_mv 342549
https://repositorio.ufsc.br/xmlui/handle/123456789/169900
identifier_str_mv 342549
url https://repositorio.ufsc.br/xmlui/handle/123456789/169900
dc.language.iso.fl_str_mv por
language por
dc.rights.driver.fl_str_mv info:eu-repo/semantics/openAccess
eu_rights_str_mv openAccess
dc.format.none.fl_str_mv 201 p.| il., grafs., tabs.
application/pdf
dc.source.none.fl_str_mv reponame:Repositório Institucional da UFSC
instname:Universidade Federal de Santa Catarina (UFSC)
instacron:UFSC
instname_str Universidade Federal de Santa Catarina (UFSC)
instacron_str UFSC
institution UFSC
reponame_str Repositório Institucional da UFSC
collection Repositório Institucional da UFSC
repository.name.fl_str_mv Repositório Institucional da UFSC - Universidade Federal de Santa Catarina (UFSC)
repository.mail.fl_str_mv
_version_ 1808651927783735296

Registros relacionados