Produção e caracterização de monolitos catalíticos para reação de reforma a vapor e oxidação parcial de etanol

Detalhes bibliográficos
Autor(a) principal: Palm, Maíra Oliveira
Data de Publicação: 2018
Tipo de documento: Dissertação
Idioma: por
Título da fonte: Repositório Institucional da UFSC
Texto Completo: https://repositorio.ufsc.br/handle/123456789/219890
Resumo: Dissertação (mestrado) - Universidade Federal de Santa Catarina, Campus Joinville, Programa de Pós-Graduação em Engenharia e Ciências Mecânicas, Joinville, 2018.
id UFSC_ee148a546276e2724e83d6bc485373a9
oai_identifier_str oai:repositorio.ufsc.br:123456789/219890
network_acronym_str UFSC
network_name_str Repositório Institucional da UFSC
repository_id_str 2373
spelling Produção e caracterização de monolitos catalíticos para reação de reforma a vapor e oxidação parcial de etanolEngenharia mecânicaCatalisadoresEtanolDissertação (mestrado) - Universidade Federal de Santa Catarina, Campus Joinville, Programa de Pós-Graduação em Engenharia e Ciências Mecânicas, Joinville, 2018.Hidrogênio (H2) é uma fonte de energia ambientalmente promissora, por ter água como efluente único em sua utilização. Porém, devido ao seu difícil manuseio, transporte e armazenamento, torna-se necessário o desenvolvimento de técnicas para produção deste combustível próxima ao seu uso. Para produção embarcada de H2 é necessário um reator catalítico que proporcione condições para a reação ocorrer em baixo tempo de residência, com inúmeros ciclos térmicos e de arranques e paradas. O objetivo desse trabalho é produzir e caracterizar monolitos catalíticos para as reações de reforma a vapor e oxidação parcial de etanol em reatores de baixo tempo de residência. Para isso, espumas cerâmicas comerciais de alumina (Al2O3) foram revestidas com partículas de alumina de 2 µm, formando um recobrimento em toda a superfície. Após o revestimento, foram impregnadas com níquel (Ni). Os monolitos produzidos foram caracterizados em microscópio eletrônico de varredura com emissão de campo (MEV-FEG), por espectroscopia de energia dispersiva (EDS) e por espectroscopia de fotoeléctrons excitados por raios-X (XPS). A atividade catalítica dos monolitos produzidos foi testada em reações de reforma a vapor (SR) e oxidação parcial de etanol (POX). Observou-se que as espumas com revestimento apresentaram menor teor do metal aderido sobre o suporte, porém, mais homogêneo. Foi observada a influência do teor mássico da pasta usada para recobrimento na espessura. Pastas com 3 imersões na pasta de 30 % em massa de Al2O3 apresentaram resultados semelhantes com espuma que foi imersa 1 vez na pasta de 40 %, o torna o processo de produção mais rápido. Por MEV observou-se que o processo de impregnação da fase ativa foi satisfatório. As partículas de Ni estavam aderidas em toda a superfície, apresentando boa dispersão em toda a camada de recobrimento. Com análises em XPS foi possível observar que as partículas de Ni impregnadas no monolito apresentavam espécies não-oxidadas, essenciais para atividades catalíticas, e que a impregnação de Ni alterou a superfície da espuma, tornando-a cataliticamente ativa. A temperatura de ignição do monolito de Ni/Al2O3 é de aproximadamente 392 ± 8 oC, para ambas as reações POX e SR. A camada de recobrimento apresentou influencia na atividade catalítica, tanto na conversão quanto na seletividade para ambas as reações. A maior conversão foi obtida nos testes de POX com recobrimento. A maior seletividade para H2 foi observada na reação de SR, quando utilizado monolito com recobrimento.Abstract : Hydrogen (H2) is an environmentally promising energy source, having only water as its effluent when used. However, it is difficult to handling, transport and storage, which makes it necessary to develop techniques for H2 on-board production. For on-board production of H2, a catalytic reactor is required, providing conditions for the reaction to occur in low residence times, with numerous thermal cycles, start-ups and shut-downs. The objective of this work is to produce and characterize catalytic monoliths used as low residence time reactors for steam reforming and partial oxidation reactions of ethanol. Thus, alumina Al2O3 commercial foams were coated with 2 µm alumina particles, producing a coating on the entire foam surface. After coating, the monoliths were impregnated with nickel (Ni). The monoliths produced were characterized by scanning electron microscope with field emission gun (SEM-FEG), energy dispersive spectroscopy (EDS) and X-ray photoelectron spectroscopy (XPS). The catalytic activity of monoliths was tested in the steam reforming and partial oxidation reaction of ethanol. It was observed that with washcoat the adhered mass content was lower, but more homogeneous. It was observed the influence of the content mass of the slurry used in washcoat. Foam with 3 immersions in the slurries with 30 % by weight of alumina showed similar results with foam that was immersed once in the slurry with 40 % by weight of alumina, making the production process faster. By SEM it was observed that the impregnation of the active phase was satisfactory. Ni particles were adhered to the entire surface, showing good dispersion throughout the coating layer. With XPS analysis it was possible to observe that the Ni particles impregnated in the monolith had non-oxidized species, providing an active catalytic surface on alumina foam. The ignition temperature of Ni/Al2O3 is around 392 ± 8 oC, for both SR and POX reactions. The coating layer influenced the catalytic activity in conversion and selectivity for both reactions. The highest conversion was obtained in the partial oxidation (POX) tests with washcoat. The highest selectivity for H2 was observed in the steam reforming (SR) when using monolith with washcoat.Catapan, Rafael de CamargoDuarte, Diego AlexandreUniversidade Federal de Santa CatarinaPalm, Maíra Oliveira2021-02-05T01:57:40Z2021-02-05T01:57:40Z2018info:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/masterThesis101 p.| il., gráfs., tabs.application/pdf356525https://repositorio.ufsc.br/handle/123456789/219890porreponame:Repositório Institucional da UFSCinstname:Universidade Federal de Santa Catarina (UFSC)instacron:UFSCinfo:eu-repo/semantics/openAccess2021-02-05T01:57:40Zoai:repositorio.ufsc.br:123456789/219890Repositório InstitucionalPUBhttp://150.162.242.35/oai/requestopendoar:23732021-02-05T01:57:40Repositório Institucional da UFSC - Universidade Federal de Santa Catarina (UFSC)false
dc.title.none.fl_str_mv Produção e caracterização de monolitos catalíticos para reação de reforma a vapor e oxidação parcial de etanol
title Produção e caracterização de monolitos catalíticos para reação de reforma a vapor e oxidação parcial de etanol
spellingShingle Produção e caracterização de monolitos catalíticos para reação de reforma a vapor e oxidação parcial de etanol
Palm, Maíra Oliveira
Engenharia mecânica
Catalisadores
Etanol
title_short Produção e caracterização de monolitos catalíticos para reação de reforma a vapor e oxidação parcial de etanol
title_full Produção e caracterização de monolitos catalíticos para reação de reforma a vapor e oxidação parcial de etanol
title_fullStr Produção e caracterização de monolitos catalíticos para reação de reforma a vapor e oxidação parcial de etanol
title_full_unstemmed Produção e caracterização de monolitos catalíticos para reação de reforma a vapor e oxidação parcial de etanol
title_sort Produção e caracterização de monolitos catalíticos para reação de reforma a vapor e oxidação parcial de etanol
author Palm, Maíra Oliveira
author_facet Palm, Maíra Oliveira
author_role author
dc.contributor.none.fl_str_mv Catapan, Rafael de Camargo
Duarte, Diego Alexandre
Universidade Federal de Santa Catarina
dc.contributor.author.fl_str_mv Palm, Maíra Oliveira
dc.subject.por.fl_str_mv Engenharia mecânica
Catalisadores
Etanol
topic Engenharia mecânica
Catalisadores
Etanol
description Dissertação (mestrado) - Universidade Federal de Santa Catarina, Campus Joinville, Programa de Pós-Graduação em Engenharia e Ciências Mecânicas, Joinville, 2018.
publishDate 2018
dc.date.none.fl_str_mv 2018
2021-02-05T01:57:40Z
2021-02-05T01:57:40Z
dc.type.status.fl_str_mv info:eu-repo/semantics/publishedVersion
dc.type.driver.fl_str_mv info:eu-repo/semantics/masterThesis
format masterThesis
status_str publishedVersion
dc.identifier.uri.fl_str_mv 356525
https://repositorio.ufsc.br/handle/123456789/219890
identifier_str_mv 356525
url https://repositorio.ufsc.br/handle/123456789/219890
dc.language.iso.fl_str_mv por
language por
dc.rights.driver.fl_str_mv info:eu-repo/semantics/openAccess
eu_rights_str_mv openAccess
dc.format.none.fl_str_mv 101 p.| il., gráfs., tabs.
application/pdf
dc.source.none.fl_str_mv reponame:Repositório Institucional da UFSC
instname:Universidade Federal de Santa Catarina (UFSC)
instacron:UFSC
instname_str Universidade Federal de Santa Catarina (UFSC)
instacron_str UFSC
institution UFSC
reponame_str Repositório Institucional da UFSC
collection Repositório Institucional da UFSC
repository.name.fl_str_mv Repositório Institucional da UFSC - Universidade Federal de Santa Catarina (UFSC)
repository.mail.fl_str_mv
_version_ 1808651937720041472