Influência do envelhecimento no grau de adaptação marginal de coroas protéticas confeccionadas em zircônia

Detalhes bibliográficos
Autor(a) principal: Luna, Maria Del Pinal
Data de Publicação: 2017
Tipo de documento: Tese
Idioma: por
Título da fonte: Repositório Institucional da UFSC
Texto Completo: https://repositorio.ufsc.br/xmlui/handle/123456789/176064
Resumo: Tese (doutorado) - Universidade Federal de Santa Catarina, Centro de Ciências da Saúde, Programa de Pós-Graduação em Odontologia, Florianópolis, 2017.
id UFSC_f4d80a482b66e903e205499941398419
oai_identifier_str oai:repositorio.ufsc.br:123456789/176064
network_acronym_str UFSC
network_name_str Repositório Institucional da UFSC
repository_id_str 2373
spelling Influência do envelhecimento no grau de adaptação marginal de coroas protéticas confeccionadas em zircônia OdontologiaOxido de zirconioEnvelhecimentoAdaptação Marginal DentáriaCimentação (Odontologia)Tese (doutorado) - Universidade Federal de Santa Catarina, Centro de Ciências da Saúde, Programa de Pós-Graduação em Odontologia, Florianópolis, 2017.Apesar do uso da zircônia em diversas aplicações técnicas e biomédicas, após 20 anos de pesquisa, a possibilidade de este material envelhecer em função, fenômeno conhecido como degradação em baixas temperaturas (DBT), continua sendo um assunto em controvérsia. O objetivo deste estudo "in vitro" foi analisar a influência do envelhecimento no grau de adaptação de coroas bilaminares feitas em Y-TZP (Z-CAD HD, Metoxit AG, Suíça) e recobertas com cerâmica (E-max, Ivoclar Vivadent, Liechtenstein) e coroas monolíticas (Z-CAD HTL, Metoxit AG, Suíça), assim como a influência do agente de cimentação (Rely X U200, 3M Espe, EUA) no grau de adaptação marginal dessas peças cerâmicas. Quarenta e oito corpos de prova foram usinados em aço inoxidável simulando um primeiro pré-molar inferior que receberia uma coroa protética. Os corpos de prova foram divididos aleatoriamente em quatro grupos com 12 espécimes cada e, após, foram confeccionadas as seguintes coroas: (1) coroas bilaminares (infraestrutura em zircônia e cerâmica de cobertura) cimentadas; (2) coroas bilaminares (infraestrutura em zircônia e cerâmica de cobertura) não cimentadas; (3) coroas monolíticas em zircônia não cimentadas; (4) coroas monolíticas em zircônia cimentadas. Em relação ao envelhecimento, todos os grupos foram submetidos a dois tempos diferentes: T1: nenhum tratamento de envelhecimento e armazenamento em ambiente seco e temperatura ambiente. T2: tratamento de envelhecimento artificial em autoclave, sob uma atmosfera úmida a 131°C e pressão de 1,7 bares durante 5 horas. A adaptação marginal foi avaliada pela medida da discrepância marginal absoluta das coroas realizadas, utilizando um microscópio eletrônico de varredura. A difração de raios X foi utilizada para calcular a fração de fase monoclínica e monitorizar a DBT. Tanto as coroas bilaminares como as monolíticas apresentaram discrepâncias marginais verticais semelhantes, entretanto, não foram observadas diferenças significativas na adaptação marginal entre os grupos testados (p= 0,41). Também não foram observadas diferenças na discrepância marginal quanto à presença ou não de agente de cimentação e quando o envelhecimento artificial foi empregado (p= 0,17). A intensidade do pico da fase monoclínica a tetragonal aumentou de 1,2 a 3% para as coroas bilaminares e de 0,8 a 1,6% para as coroas monolíticas. As coroas monolíticas e bilaminares de zircônia confeccionadas mediante tecnologia CAD/CAM apresentaram gaps marginais que estavam dentro de uma faixa aceitável de discrepância marginal. A cimentação não demonstrou ter uma influência significativa no ajuste marginal. A adaptação marginal não foi influenciada pelo envelhecimento, e este não levou a uma transformação significativa da fase tetragonal para a fase monoclínica. Estudos "in vitro" demonstraram que a tecnologia CAD / CAM pode produzir estruturas de zircônia com um ajuste marginal clinicamente aceitável. Com base na ausência de estudos científicos longitudinais, não parece claro a relação entre o ajuste marginal e a consequente degradação do envelhecimento.<br>Abstract : Despite the use of Yttria Tetragonal Zirconia Polycrystal (3Y-TZP) in several technical and biomedical applications, after over 20 years of research, the possibility that this material can aged in function, a phenomenon known as low temperature degradation (LTD), remains a subject under discussion. The aim of this "in vitro" research was to analyze the influence of aging on the degree of adaptation of Y-TZP based crowns, either monolithic (Z-CAD HTL, Metoxit AG, Tayngen, Switzerland) or ceramic coating (Z-CAD HD, Metoxit AG, Tayngen, Switzerland; E-max, Ivoclar Vivadent) as well as the influence of cementation (Rely X U200, 3M Espe) on the fit of the restorations. Forty-eight standardized dies will be prepared from stainless steel, to receive a ceramic crown. The specimens were randomly divided into 4 groups of 12 specimens each: (1) bilayer crown (zirconium structure with ceramic coating) cemented; (2) bilayer crown (zirconium structure with ceramic coating) without cement; (3) monolithic zirconia crown without cement; (4) cemented monolithic zirconia crown. All groups will be treated as a function of aging, in 2 different times: T1: No aging treatment and stored in a dry place at room temperature; T2: Treatment of artificial aging (hydrothermally), in autoclave, under a humid atmosphere at 131 °C and pressure of 1,7 bar for 5 hours. Marginal adaptation will be evaluated by measuring the absolute marginal discrepancy of the ceramic crowns on the specimens, using a scanning electron microscope. The monoclinic-to-tetragonal (m/t) peak intensity ratio measured by x-ray diffraction was used to calculate the monoclinic phase fraction and monitor LTD. Both zirconia groups showed similar vertical marginal discrepancies, however, no significant differences (p= 0.41) in marginal adaptation were observed among the experimental groups. Moreover, no differences were observed in either group in marginal discrepancies between cementation process neither artificial aging (p= 0.17). The relative XRD peak intensity of the monoclinic to tetragonal phase increased for 1,2 to 3% for bilayer crowns and from 0,8 to 1,6% for monolithic crowns. Monolithic and bilayer CAD /CAM zirconia crowns showed marginal gaps that were within an acceptable range of marginal discrepancy. Cementation was not found to have a statistically significant influence on the marginal fit. Marginal adaptation was not influenced by aging, and this did not lead a significant transformation from tetragonal to monoclinic phase. ?In vitro? studieshave demonstrated that CAD/CAM technology can produce zirconia structures with a clinically acceptable marginal fit. Based on the lack of rigorous scientific longitudinal studies, it seems not clear the relationship between the marginal fit and the resulting degradation of aging.Volpato, Cláudia Ângela MazieroUniversidade Federal de Santa CatarinaLuna, Maria Del Pinal2017-05-31T14:18:23Z2017-05-31T14:18:23Z2017info:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/doctoralThesis96 p.| il., gráfs., tabs.application/pdf345802https://repositorio.ufsc.br/xmlui/handle/123456789/176064porreponame:Repositório Institucional da UFSCinstname:Universidade Federal de Santa Catarina (UFSC)instacron:UFSCinfo:eu-repo/semantics/openAccess2017-05-31T14:18:23Zoai:repositorio.ufsc.br:123456789/176064Repositório InstitucionalPUBhttp://150.162.242.35/oai/requestopendoar:23732017-05-31T14:18:23Repositório Institucional da UFSC - Universidade Federal de Santa Catarina (UFSC)false
dc.title.none.fl_str_mv Influência do envelhecimento no grau de adaptação marginal de coroas protéticas confeccionadas em zircônia
title Influência do envelhecimento no grau de adaptação marginal de coroas protéticas confeccionadas em zircônia
spellingShingle Influência do envelhecimento no grau de adaptação marginal de coroas protéticas confeccionadas em zircônia
Luna, Maria Del Pinal
Odontologia
Oxido de zirconio
Envelhecimento
Adaptação Marginal Dentária
Cimentação (Odontologia)
title_short Influência do envelhecimento no grau de adaptação marginal de coroas protéticas confeccionadas em zircônia
title_full Influência do envelhecimento no grau de adaptação marginal de coroas protéticas confeccionadas em zircônia
title_fullStr Influência do envelhecimento no grau de adaptação marginal de coroas protéticas confeccionadas em zircônia
title_full_unstemmed Influência do envelhecimento no grau de adaptação marginal de coroas protéticas confeccionadas em zircônia
title_sort Influência do envelhecimento no grau de adaptação marginal de coroas protéticas confeccionadas em zircônia
author Luna, Maria Del Pinal
author_facet Luna, Maria Del Pinal
author_role author
dc.contributor.none.fl_str_mv Volpato, Cláudia Ângela Maziero
Universidade Federal de Santa Catarina
dc.contributor.author.fl_str_mv Luna, Maria Del Pinal
dc.subject.por.fl_str_mv Odontologia
Oxido de zirconio
Envelhecimento
Adaptação Marginal Dentária
Cimentação (Odontologia)
topic Odontologia
Oxido de zirconio
Envelhecimento
Adaptação Marginal Dentária
Cimentação (Odontologia)
description Tese (doutorado) - Universidade Federal de Santa Catarina, Centro de Ciências da Saúde, Programa de Pós-Graduação em Odontologia, Florianópolis, 2017.
publishDate 2017
dc.date.none.fl_str_mv 2017-05-31T14:18:23Z
2017-05-31T14:18:23Z
2017
dc.type.status.fl_str_mv info:eu-repo/semantics/publishedVersion
dc.type.driver.fl_str_mv info:eu-repo/semantics/doctoralThesis
format doctoralThesis
status_str publishedVersion
dc.identifier.uri.fl_str_mv 345802
https://repositorio.ufsc.br/xmlui/handle/123456789/176064
identifier_str_mv 345802
url https://repositorio.ufsc.br/xmlui/handle/123456789/176064
dc.language.iso.fl_str_mv por
language por
dc.rights.driver.fl_str_mv info:eu-repo/semantics/openAccess
eu_rights_str_mv openAccess
dc.format.none.fl_str_mv 96 p.| il., gráfs., tabs.
application/pdf
dc.source.none.fl_str_mv reponame:Repositório Institucional da UFSC
instname:Universidade Federal de Santa Catarina (UFSC)
instacron:UFSC
instname_str Universidade Federal de Santa Catarina (UFSC)
instacron_str UFSC
institution UFSC
reponame_str Repositório Institucional da UFSC
collection Repositório Institucional da UFSC
repository.name.fl_str_mv Repositório Institucional da UFSC - Universidade Federal de Santa Catarina (UFSC)
repository.mail.fl_str_mv
_version_ 1808652140442288128

Registros relacionados