Comportamento mecânico sob fadiga de zircônia policristalina: efeito do desgaste por brocas para usinagem em CAD/CAM e tratamentos de superfície
Autor(a) principal: | |
---|---|
Data de Publicação: | 2022 |
Tipo de documento: | Tese |
Idioma: | por |
Título da fonte: | Repositório Institucional Manancial UFSM |
Texto Completo: | http://repositorio.ufsm.br/handle/1/26351 |
Resumo: | Three studies compose the present study. The first one evaluated the effect of different intaglio surface treatments on fatigue behavior (biaxial flexural fatigue strength) and surface characteristics (topography and roughness) of a 5 mol% partially stabilized zirconia ceramic (5YSZ). For that, ceramic discs (ISO 6872-2015) were allocated considering: Ctrl: no-treatment; GLZ: low-fusing porcelain glaze; SNF: SiO2 nanofilm deposition (5nm); AlOx: air-abrasion with aluminum oxide; SiC: air-abrasion with silica-coated AlOx; 7%Si: air-abrasion with 7% silica-coated AlOx. The biaxial flexural fatigue strength tests were performed (piston-on-three-balls assembly), besides topographic, surface roughness, fractographic and phase analysis. According to the results, low-fusing porcelain glaze enhances the fatigue performance of 5YSZ, while the deposition of silica nanofilms does not affect its mechanical properties. Among air-abrasions, the AlOx decreased the fatigue behavior of ceramic. The second study evaluated the distinct conditioning effect of the intaglio surface of bonded 5 mol% stabilized zirconia simplified restorations on the mechanical fatigue behavior of the set, prior to and after aging. Ceramic discs (Ø= 10mm; thick= 1mm) were allocated considering “surface treatments” (Ctrl: no-treatment; PM: primer; GLZ: glaze; SNF: SiO2 nanofilm deposition (5 nm); AlOx: air-abrasion with AlOx; SiC: air-abrasion with silica-coated AlOx; 7%Si: air-abrasion with 7% silica-coated AlOx; and “aging” (baseline: 24h (37°C); aged: 90 days (37°C) + 12,000 thermal cycles). The discs were treated, luted with resin cement onto the dentin analogue, subjected to aging or not, and subsequently tested under a step-stress fatigue test. Fractography, topography, surface roughness, contact angle, and atomic force microscopy were performed. In conclusion, conditioning the intaglio surface of zirconia is mandatory for fatigue behavior stability after aging of the set, while non-treatment induces unstable results. The third study evaluated the effect of in-lab simulation of CAD/CAM grinding and intaglio surface treatments on the surface characteristics (topography and roughness) and fatigue behavior of adhesively luted 4 mol% yttria-stabilized zirconia (4YSZ) simplified restorations. Ceramic discs (Ø= 10mm; thick= 1mm) were allocated considering “In-lab simulation of CAD/CAM grinding” (ground; polished) and “surface treatments” (Ctrl: no treatment; AlOx: air abrasion with AlOx; GLZ: glaze), and posteriorly luted with resin cement onto a dentin analogue material and tested under a step-stress fatigue test. Complementary analysis was performed to verify the ability of GLZ infiltration in surface defects to increase the flexural strength (FS) of 4YSZ. For that, specimens in bars were confeccioned considering the groups N-ID: non-indented; ID: indented; ID-GLZ: indented + GLZ, and tested in the FS test. In conclusion, in-lab simulation of CAD/CAM grinding promoted deleterious fatigue behavior of 4YSZ and GLZ induced a better performance compared to air abrasion. In addition, GLZ increased the flexural strength of the bars after indentation. Furthermore, there is an inverse relationship between roughness and fatigue failure load of 4YSZ, the higher the surface roughness, the lower the fatigue behavior of the set. |
id |
UFSM-20_9f5a3ceb3cfcb1d9ef7c98891f1d4e5e |
---|---|
oai_identifier_str |
oai:repositorio.ufsm.br:1/26351 |
network_acronym_str |
UFSM-20 |
network_name_str |
Repositório Institucional Manancial UFSM |
repository_id_str |
3913 |
spelling |
2022-10-05T12:47:57Z2022-10-05T12:47:57Z2022-09-16http://repositorio.ufsm.br/handle/1/26351Three studies compose the present study. The first one evaluated the effect of different intaglio surface treatments on fatigue behavior (biaxial flexural fatigue strength) and surface characteristics (topography and roughness) of a 5 mol% partially stabilized zirconia ceramic (5YSZ). For that, ceramic discs (ISO 6872-2015) were allocated considering: Ctrl: no-treatment; GLZ: low-fusing porcelain glaze; SNF: SiO2 nanofilm deposition (5nm); AlOx: air-abrasion with aluminum oxide; SiC: air-abrasion with silica-coated AlOx; 7%Si: air-abrasion with 7% silica-coated AlOx. The biaxial flexural fatigue strength tests were performed (piston-on-three-balls assembly), besides topographic, surface roughness, fractographic and phase analysis. According to the results, low-fusing porcelain glaze enhances the fatigue performance of 5YSZ, while the deposition of silica nanofilms does not affect its mechanical properties. Among air-abrasions, the AlOx decreased the fatigue behavior of ceramic. The second study evaluated the distinct conditioning effect of the intaglio surface of bonded 5 mol% stabilized zirconia simplified restorations on the mechanical fatigue behavior of the set, prior to and after aging. Ceramic discs (Ø= 10mm; thick= 1mm) were allocated considering “surface treatments” (Ctrl: no-treatment; PM: primer; GLZ: glaze; SNF: SiO2 nanofilm deposition (5 nm); AlOx: air-abrasion with AlOx; SiC: air-abrasion with silica-coated AlOx; 7%Si: air-abrasion with 7% silica-coated AlOx; and “aging” (baseline: 24h (37°C); aged: 90 days (37°C) + 12,000 thermal cycles). The discs were treated, luted with resin cement onto the dentin analogue, subjected to aging or not, and subsequently tested under a step-stress fatigue test. Fractography, topography, surface roughness, contact angle, and atomic force microscopy were performed. In conclusion, conditioning the intaglio surface of zirconia is mandatory for fatigue behavior stability after aging of the set, while non-treatment induces unstable results. The third study evaluated the effect of in-lab simulation of CAD/CAM grinding and intaglio surface treatments on the surface characteristics (topography and roughness) and fatigue behavior of adhesively luted 4 mol% yttria-stabilized zirconia (4YSZ) simplified restorations. Ceramic discs (Ø= 10mm; thick= 1mm) were allocated considering “In-lab simulation of CAD/CAM grinding” (ground; polished) and “surface treatments” (Ctrl: no treatment; AlOx: air abrasion with AlOx; GLZ: glaze), and posteriorly luted with resin cement onto a dentin analogue material and tested under a step-stress fatigue test. Complementary analysis was performed to verify the ability of GLZ infiltration in surface defects to increase the flexural strength (FS) of 4YSZ. For that, specimens in bars were confeccioned considering the groups N-ID: non-indented; ID: indented; ID-GLZ: indented + GLZ, and tested in the FS test. In conclusion, in-lab simulation of CAD/CAM grinding promoted deleterious fatigue behavior of 4YSZ and GLZ induced a better performance compared to air abrasion. In addition, GLZ increased the flexural strength of the bars after indentation. Furthermore, there is an inverse relationship between roughness and fatigue failure load of 4YSZ, the higher the surface roughness, the lower the fatigue behavior of the set.Três estudos compõe o presente trabalho. O primeiro avaliou o efeito de diferentes tratamentos de superfície interna no desempenho em fadiga (flexão biaxial) e características superficiais (topografia e rugosidade) de uma cerâmica de zircônia parcialmente estabilizada com 5 mol% de ítria (5YSZ). Para tal, discos cerâmicos (ISO 6872-2015) foram alocados considerando: Ctrl: sem tratamento; GLZ: glaze de baixa fusão; SNF: deposição de nanofilmes de sílica (5nm); AlOx: jateamento com óxido de alumínio; SiC: jateamento com AlOx revestido por sílica; 7%Si: jateamento com AlOx revestido por 7% de sílica. O teste de fadiga à flexão biaxial foi realizado (configuração piston-on-three-balls), assim como análises de topografia, conteúdo cristalino, rugosidade e fractografia. De acordo com o resultado, o GLZ melhora a performance em fadiga da 5YSZ, enquanto a deposição de filmes de sílica não afeta as propriedades mecânicas da mesma. Entre os jateamentos, AlOx diminui o comportamento em fadiga da cerâmica. O segundo avaliou o efeito de diferentes tratamentos na superfície interna de restaurações simplificadas de uma zircônia estabilizada com 5 mol% de óxido de ítrio no comportamento em fadiga mecânica antes e após envelhecimento. Discos cerâmicos (Ø= 10mm; espessura= 1mm) foram alocados considerando: “tratamentos de superfície” (Ctrl: sem tratamento; PM: primer; GLZ: glaze; SNF: deposição de nanofilmes de sílica (5nm); AlOx: jateamento com AlOx; SiC: jateamento com AlOx revestido por sílica; 7%Si: jateamento com AlOx revestido por 7% de sílica) e “envelhecimento” (baseline: 24h (37°C); envelhecido: 90 dias (37°C) + 12,000 ciclos térmicos). Os discos foram tratados, cimentados com cimento resinoso em análogo de dentina, submetidos ou não ao envelhecimento e subsequentemente ao teste de fadiga step-stress. Análises de fractografia, topografia, rugosidade, ângulo de contato e microscopia de força atômica foram realizadas. Como conclusão, tratamentos de superfície interna da zircônia são obrigatórios para estabilidade do comportamento à fadiga após o envelhecimento do conjunto restaurador, enquanto o não tratamento induz resultados instáveis. O terceiro avaliou o efeito da simulação em laboratório do desgaste do CAD/CAM e tratamentos de superfície interna nas características superficiais (topografia e rugosidade) e comportamento em fadiga de uma zircônia parcialmente estabilizada com 4 mol% de óxido de ítrio (4YSZ) cimentada adesivamente a um análogo de dentina. Discos cerâmicos (Ø= 10mm; espessura= 1mm) foram alocados considerando: “simulação em laboratório do desgaste do CAD/CAM” (desgastado; polido) e “tratamentos de superfície” (Ctrl: sem tratamento; AlOx: jateamento com AlOx; GLZ: glaze), e posteriormente cimentados com cimento resinoso em análogo de dentina e submetidos ao teste de fadiga step-stress. Foi realizada análise complementar para verificar a capacidade de infiltração do GLZ em defeitos superficiais no aumento da resistência flexural (RF) da 4YSZ. Para isso, espécimes em barras foram confeccionados considerando os grupos N-ID: sem indentação; ID: indentação; ID-GLZ: indentação+GLZ, e testados no ensaio de RF. Análises de rugosidade, topografia e fractografia foram realizadas. Como conclusão, a simulação em laboratório do desgaste do CAD/CAM promoveu um efeito prejudicial no comportamento em fadiga da 4YSZ e o GLZ induziu melhor performance em comparação ao jateamento. Além disso, o GLZ aumentou a resistência flexural das barras após indentação. Ademais, existe uma relação inversa entre rugosidade e carga para falha em fadiga da 4YSZ, quanto maior a rugosidade pior o comportamento mecânico do conjunto.Coordenação de Aperfeiçoamento de Pessoal de Nível Superior - CAPESporUniversidade Federal de Santa MariaCentro de Ciências da SaúdePrograma de Pós-Graduação em Ciências OdontológicasUFSMBrasilOdontologiaAttribution-NonCommercial-NoDerivatives 4.0 Internationalhttp://creativecommons.org/licenses/by-nc-nd/4.0/info:eu-repo/semantics/openAccessDesenho e fabricação auxiliados por computadorFadigaResistência flexuralTratamentos de superfícieZircônia translúcidaComputer-aided design and manufacturingFatigueFlexural strengthSurface treatmentsTranslucent zirconiaCNPQ::CIENCIAS DA SAUDE::ODONTOLOGIAComportamento mecânico sob fadiga de zircônia policristalina: efeito do desgaste por brocas para usinagem em CAD/CAM e tratamentos de superfícieMechanical behavior under fatigue of polycrystalline zirconia: effect of grinding bur for CAD/CAM machining and surface treatmentsinfo:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/doctoralThesisValandro, Luiz Felipehttp://lattes.cnpq.br/0535309012233484Kleverlaan, Cornelis JohannesDal Piva, Amanda Maria de OliveiraRodrigues, Camila da SilvaProchnow, CatinaFraga, Sarahttp://lattes.cnpq.br/1967607431706056Rodrigues, Ana Carolina Cadore400200000000600600600600600600600600381d00c6-91f3-43f9-b2ff-a634b10ed95d46a83279-262c-4543-beec-ae0672e635c2377e4329-fff3-4ed1-9dd8-6bbee03c1abc93111229-d2f4-468c-ab10-b3cd892a4db6221e07a8-8f3c-4b1e-85a6-16743d13eeaba818909d-55e6-44b9-95d9-013ede6bf9ed1e4d4697-7928-473e-8348-7487df13e59breponame:Repositório Institucional Manancial UFSMinstname:Universidade Federal de Santa Maria (UFSM)instacron:UFSMLICENSElicense.txtlicense.txttext/plain; charset=utf-81956http://repositorio.ufsm.br/bitstream/1/26351/3/license.txt2f0571ecee68693bd5cd3f17c1e075dfMD53CC-LICENSElicense_rdflicense_rdfapplication/rdf+xml; charset=utf-8805http://repositorio.ufsm.br/bitstream/1/26351/2/license_rdf4460e5956bc1d1639be9ae6146a50347MD52ORIGINALTES_PPGCO_2022_RODRIGUES_ANA.pdfTES_PPGCO_2022_RODRIGUES_ANA.pdfTeseapplication/pdf5086817http://repositorio.ufsm.br/bitstream/1/26351/1/TES_PPGCO_2022_RODRIGUES_ANA.pdfa81d3b3eeae6d10c930c3f4f4e74f36aMD511/263512022-10-05 09:47:57.532oai:repositorio.ufsm.br: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ório Institucionalhttp://repositorio.ufsm.br/PUBhttp://repositorio.ufsm.br/oai/requestouvidoria@ufsm.bropendoar:39132022-10-05T12:47:57Repositório Institucional Manancial UFSM - Universidade Federal de Santa Maria (UFSM)false |
dc.title.por.fl_str_mv |
Comportamento mecânico sob fadiga de zircônia policristalina: efeito do desgaste por brocas para usinagem em CAD/CAM e tratamentos de superfície |
dc.title.alternative.eng.fl_str_mv |
Mechanical behavior under fatigue of polycrystalline zirconia: effect of grinding bur for CAD/CAM machining and surface treatments |
title |
Comportamento mecânico sob fadiga de zircônia policristalina: efeito do desgaste por brocas para usinagem em CAD/CAM e tratamentos de superfície |
spellingShingle |
Comportamento mecânico sob fadiga de zircônia policristalina: efeito do desgaste por brocas para usinagem em CAD/CAM e tratamentos de superfície Rodrigues, Ana Carolina Cadore Desenho e fabricação auxiliados por computador Fadiga Resistência flexural Tratamentos de superfície Zircônia translúcida Computer-aided design and manufacturing Fatigue Flexural strength Surface treatments Translucent zirconia CNPQ::CIENCIAS DA SAUDE::ODONTOLOGIA |
title_short |
Comportamento mecânico sob fadiga de zircônia policristalina: efeito do desgaste por brocas para usinagem em CAD/CAM e tratamentos de superfície |
title_full |
Comportamento mecânico sob fadiga de zircônia policristalina: efeito do desgaste por brocas para usinagem em CAD/CAM e tratamentos de superfície |
title_fullStr |
Comportamento mecânico sob fadiga de zircônia policristalina: efeito do desgaste por brocas para usinagem em CAD/CAM e tratamentos de superfície |
title_full_unstemmed |
Comportamento mecânico sob fadiga de zircônia policristalina: efeito do desgaste por brocas para usinagem em CAD/CAM e tratamentos de superfície |
title_sort |
Comportamento mecânico sob fadiga de zircônia policristalina: efeito do desgaste por brocas para usinagem em CAD/CAM e tratamentos de superfície |
author |
Rodrigues, Ana Carolina Cadore |
author_facet |
Rodrigues, Ana Carolina Cadore |
author_role |
author |
dc.contributor.advisor1.fl_str_mv |
Valandro, Luiz Felipe |
dc.contributor.advisor1Lattes.fl_str_mv |
http://lattes.cnpq.br/0535309012233484 |
dc.contributor.advisor-co1.fl_str_mv |
Kleverlaan, Cornelis Johannes |
dc.contributor.referee1.fl_str_mv |
Dal Piva, Amanda Maria de Oliveira |
dc.contributor.referee2.fl_str_mv |
Rodrigues, Camila da Silva |
dc.contributor.referee3.fl_str_mv |
Prochnow, Catina |
dc.contributor.referee4.fl_str_mv |
Fraga, Sara |
dc.contributor.authorLattes.fl_str_mv |
http://lattes.cnpq.br/1967607431706056 |
dc.contributor.author.fl_str_mv |
Rodrigues, Ana Carolina Cadore |
contributor_str_mv |
Valandro, Luiz Felipe Kleverlaan, Cornelis Johannes Dal Piva, Amanda Maria de Oliveira Rodrigues, Camila da Silva Prochnow, Catina Fraga, Sara |
dc.subject.por.fl_str_mv |
Desenho e fabricação auxiliados por computador Fadiga Resistência flexural Tratamentos de superfície Zircônia translúcida |
topic |
Desenho e fabricação auxiliados por computador Fadiga Resistência flexural Tratamentos de superfície Zircônia translúcida Computer-aided design and manufacturing Fatigue Flexural strength Surface treatments Translucent zirconia CNPQ::CIENCIAS DA SAUDE::ODONTOLOGIA |
dc.subject.eng.fl_str_mv |
Computer-aided design and manufacturing Fatigue Flexural strength Surface treatments Translucent zirconia |
dc.subject.cnpq.fl_str_mv |
CNPQ::CIENCIAS DA SAUDE::ODONTOLOGIA |
description |
Three studies compose the present study. The first one evaluated the effect of different intaglio surface treatments on fatigue behavior (biaxial flexural fatigue strength) and surface characteristics (topography and roughness) of a 5 mol% partially stabilized zirconia ceramic (5YSZ). For that, ceramic discs (ISO 6872-2015) were allocated considering: Ctrl: no-treatment; GLZ: low-fusing porcelain glaze; SNF: SiO2 nanofilm deposition (5nm); AlOx: air-abrasion with aluminum oxide; SiC: air-abrasion with silica-coated AlOx; 7%Si: air-abrasion with 7% silica-coated AlOx. The biaxial flexural fatigue strength tests were performed (piston-on-three-balls assembly), besides topographic, surface roughness, fractographic and phase analysis. According to the results, low-fusing porcelain glaze enhances the fatigue performance of 5YSZ, while the deposition of silica nanofilms does not affect its mechanical properties. Among air-abrasions, the AlOx decreased the fatigue behavior of ceramic. The second study evaluated the distinct conditioning effect of the intaglio surface of bonded 5 mol% stabilized zirconia simplified restorations on the mechanical fatigue behavior of the set, prior to and after aging. Ceramic discs (Ø= 10mm; thick= 1mm) were allocated considering “surface treatments” (Ctrl: no-treatment; PM: primer; GLZ: glaze; SNF: SiO2 nanofilm deposition (5 nm); AlOx: air-abrasion with AlOx; SiC: air-abrasion with silica-coated AlOx; 7%Si: air-abrasion with 7% silica-coated AlOx; and “aging” (baseline: 24h (37°C); aged: 90 days (37°C) + 12,000 thermal cycles). The discs were treated, luted with resin cement onto the dentin analogue, subjected to aging or not, and subsequently tested under a step-stress fatigue test. Fractography, topography, surface roughness, contact angle, and atomic force microscopy were performed. In conclusion, conditioning the intaglio surface of zirconia is mandatory for fatigue behavior stability after aging of the set, while non-treatment induces unstable results. The third study evaluated the effect of in-lab simulation of CAD/CAM grinding and intaglio surface treatments on the surface characteristics (topography and roughness) and fatigue behavior of adhesively luted 4 mol% yttria-stabilized zirconia (4YSZ) simplified restorations. Ceramic discs (Ø= 10mm; thick= 1mm) were allocated considering “In-lab simulation of CAD/CAM grinding” (ground; polished) and “surface treatments” (Ctrl: no treatment; AlOx: air abrasion with AlOx; GLZ: glaze), and posteriorly luted with resin cement onto a dentin analogue material and tested under a step-stress fatigue test. Complementary analysis was performed to verify the ability of GLZ infiltration in surface defects to increase the flexural strength (FS) of 4YSZ. For that, specimens in bars were confeccioned considering the groups N-ID: non-indented; ID: indented; ID-GLZ: indented + GLZ, and tested in the FS test. In conclusion, in-lab simulation of CAD/CAM grinding promoted deleterious fatigue behavior of 4YSZ and GLZ induced a better performance compared to air abrasion. In addition, GLZ increased the flexural strength of the bars after indentation. Furthermore, there is an inverse relationship between roughness and fatigue failure load of 4YSZ, the higher the surface roughness, the lower the fatigue behavior of the set. |
publishDate |
2022 |
dc.date.accessioned.fl_str_mv |
2022-10-05T12:47:57Z |
dc.date.available.fl_str_mv |
2022-10-05T12:47:57Z |
dc.date.issued.fl_str_mv |
2022-09-16 |
dc.type.status.fl_str_mv |
info:eu-repo/semantics/publishedVersion |
dc.type.driver.fl_str_mv |
info:eu-repo/semantics/doctoralThesis |
format |
doctoralThesis |
status_str |
publishedVersion |
dc.identifier.uri.fl_str_mv |
http://repositorio.ufsm.br/handle/1/26351 |
url |
http://repositorio.ufsm.br/handle/1/26351 |
dc.language.iso.fl_str_mv |
por |
language |
por |
dc.relation.cnpq.fl_str_mv |
400200000000 |
dc.relation.confidence.fl_str_mv |
600 600 600 600 600 600 600 600 |
dc.relation.authority.fl_str_mv |
381d00c6-91f3-43f9-b2ff-a634b10ed95d 46a83279-262c-4543-beec-ae0672e635c2 377e4329-fff3-4ed1-9dd8-6bbee03c1abc 93111229-d2f4-468c-ab10-b3cd892a4db6 221e07a8-8f3c-4b1e-85a6-16743d13eeab a818909d-55e6-44b9-95d9-013ede6bf9ed 1e4d4697-7928-473e-8348-7487df13e59b |
dc.rights.driver.fl_str_mv |
Attribution-NonCommercial-NoDerivatives 4.0 International http://creativecommons.org/licenses/by-nc-nd/4.0/ info:eu-repo/semantics/openAccess |
rights_invalid_str_mv |
Attribution-NonCommercial-NoDerivatives 4.0 International http://creativecommons.org/licenses/by-nc-nd/4.0/ |
eu_rights_str_mv |
openAccess |
dc.publisher.none.fl_str_mv |
Universidade Federal de Santa Maria Centro de Ciências da Saúde |
dc.publisher.program.fl_str_mv |
Programa de Pós-Graduação em Ciências Odontológicas |
dc.publisher.initials.fl_str_mv |
UFSM |
dc.publisher.country.fl_str_mv |
Brasil |
dc.publisher.department.fl_str_mv |
Odontologia |
publisher.none.fl_str_mv |
Universidade Federal de Santa Maria Centro de Ciências da Saúde |
dc.source.none.fl_str_mv |
reponame:Repositório Institucional Manancial UFSM instname:Universidade Federal de Santa Maria (UFSM) instacron:UFSM |
instname_str |
Universidade Federal de Santa Maria (UFSM) |
instacron_str |
UFSM |
institution |
UFSM |
reponame_str |
Repositório Institucional Manancial UFSM |
collection |
Repositório Institucional Manancial UFSM |
bitstream.url.fl_str_mv |
http://repositorio.ufsm.br/bitstream/1/26351/3/license.txt http://repositorio.ufsm.br/bitstream/1/26351/2/license_rdf http://repositorio.ufsm.br/bitstream/1/26351/1/TES_PPGCO_2022_RODRIGUES_ANA.pdf |
bitstream.checksum.fl_str_mv |
2f0571ecee68693bd5cd3f17c1e075df 4460e5956bc1d1639be9ae6146a50347 a81d3b3eeae6d10c930c3f4f4e74f36a |
bitstream.checksumAlgorithm.fl_str_mv |
MD5 MD5 MD5 |
repository.name.fl_str_mv |
Repositório Institucional Manancial UFSM - Universidade Federal de Santa Maria (UFSM) |
repository.mail.fl_str_mv |
ouvidoria@ufsm.br |
_version_ |
1808854729739993088 |