Translucidez e valor: análise do comportamento das propriedades ópticas em resinas compostas estéticas
Autor(a) principal: | |
---|---|
Data de Publicação: | 2015 |
Tipo de documento: | Dissertação |
Idioma: | por |
Título da fonte: | Manancial - Repositório Digital da UFSM |
Texto Completo: | http://repositorio.ufsm.br/handle/1/6165 |
Resumo: | This study aimed to evaluate the translucency and value with different combinations of enamel , dentin and body of each composite regarding a standard thickness (1,5mm). Three different resin composites commercially available with a standard shade (A1), IPS Empress Direct, Charisma Diamond and Filtek Z350 XT were evaluated. A stainless steel matrix was used to prepare ninety disc-shaped specimens with 11mm diameter and 1,5mm thickness. The specimens were randomly allocated in 18 groups (n=5) according to different combinations of enamel , dentin and body presented in each resin composite evaluated. After light curing, specimens were stored in deionized water at 37º C for 24h. Three consecutive readings were performed according to the CIE L*a*b* color scale relative to the standard illuminant D65 on reflection spectrophotometer (SP60 - EX-Rite). The optical properties of translucency and value were measured by the parameters translucency (TP) and lightness in white background (L*w) and black background (L*b), respectively. The mean TP, L*w and L*b were analyzed by ANOVA (General Linear Models) and Tukey s post hoc tests (α =0.05). Scatter plots together with Spearman´s correlation coefficient were used to assess the relationship between TP and L*w and TP and L*b values. The groups had statistical significant different values (p=0.000). The resin composite Empress Direct when only a layer of enamel were employed presented the highest TP value, whereas the resin composite Filtek Z350 XT with a single layer of dentin presented the lowest TP value. A negative and strong correlation between TP and L*b and a positive and weak correlation between TP and L*w were observed. Optical properties as translucency and value rely on the material used. In general, there was statistical difference between the groups for TP and L* |
id |
UFSM-20_ada4f709b30b2e30c42310aaa539f6fd |
---|---|
oai_identifier_str |
oai:repositorio.ufsm.br:1/6165 |
network_acronym_str |
UFSM-20 |
network_name_str |
Manancial - Repositório Digital da UFSM |
repository_id_str |
3913 |
spelling |
2016-02-232016-02-232015-06-11SANTOS, Iuri Silveira dos. TRANSLUCENCY AND VALUE: OPTICAL PROPERTIES BEHAVIOR IN AESTHETIC RESIN COMPOSITES. 2015. 51 f. Dissertação (Mestrado em Odontologia) - Universidade Federal de Santa Maria, Santa Maria, 2015.http://repositorio.ufsm.br/handle/1/6165This study aimed to evaluate the translucency and value with different combinations of enamel , dentin and body of each composite regarding a standard thickness (1,5mm). Three different resin composites commercially available with a standard shade (A1), IPS Empress Direct, Charisma Diamond and Filtek Z350 XT were evaluated. A stainless steel matrix was used to prepare ninety disc-shaped specimens with 11mm diameter and 1,5mm thickness. The specimens were randomly allocated in 18 groups (n=5) according to different combinations of enamel , dentin and body presented in each resin composite evaluated. After light curing, specimens were stored in deionized water at 37º C for 24h. Three consecutive readings were performed according to the CIE L*a*b* color scale relative to the standard illuminant D65 on reflection spectrophotometer (SP60 - EX-Rite). The optical properties of translucency and value were measured by the parameters translucency (TP) and lightness in white background (L*w) and black background (L*b), respectively. The mean TP, L*w and L*b were analyzed by ANOVA (General Linear Models) and Tukey s post hoc tests (α =0.05). Scatter plots together with Spearman´s correlation coefficient were used to assess the relationship between TP and L*w and TP and L*b values. The groups had statistical significant different values (p=0.000). The resin composite Empress Direct when only a layer of enamel were employed presented the highest TP value, whereas the resin composite Filtek Z350 XT with a single layer of dentin presented the lowest TP value. A negative and strong correlation between TP and L*b and a positive and weak correlation between TP and L*w were observed. Optical properties as translucency and value rely on the material used. In general, there was statistical difference between the groups for TP and L*Este estudo tem como objetivo analisar o comportamento óptico de diferentes resinas compostas, em distintas combinações de esmalte, dentina e corpo de cada composto em relação à espessura padrão (1,5mm) na percepção da translucidez e valor. Foram analisadas três marcas comerciais de resina composta (IPS Empress Direct, Charisma Diamond, Filtek Z350 XT) na cor A1. Uma matriz metálica foi utilizada para confeccionar noventa espécimes (1,5mm de espessura e 11mm de diâmetro). Os espécimes foram randomizados e divididos em 18 grupos (n=5) conforme as possibilidades de combinações de esmalte, dentina e corpo. Após a fotopolimerização, os espécimes foram armazenados em água deionizada por 24h a 37°C. Três leituras consecutivas foram realizadas por um espectrofotômetro de reflexão (SP 60 EX-Rite) relativo ao iluminante padrão D65 de acordo com o sistema CIE L* a* b*. As propriedades ópticas, translucidez e valor, foram mensuradas pelo parâmetro de translucidez (TP) e pela variável L* sobre fundo preto e branco respectivamente. A média dos valores do TP, L*b e L*p foram analisadas por ANOVA (Modelo Linear Geral) e testes Tukey s post hoc (α=0,05). Gráficos de dispersão juntamente com o coeficiente de correlação de Spearman entre TP e L*p e TP e L*b foram calculados. Os grupos apresentaram diferença estatística (p = 0,000). A resina composta Empress Direct somente de esmalte apresentou o maior valor de TP, enquanto Filtek Z350 XT com uma única camada de dentina apresentou o menor valor de TP. Há uma forte correlação negativa entre TP e L*p e uma fraca correlação positiva entre TP e L*b. Propriedades ópticas de translucidez e valor são dependentes do material utilizado. De maneira geral, houve diferenças entre os grupos estudados quando analisados o TP e L*.application/pdfporUniversidade Federal de Santa MariaPrograma de Pós-Graduação em Ciências OdontológicasUFSMBROdontologiaMateriais dentáriosEstética dentalResinas compostasSistema CIE L*a*b*Dental materialsEsthetic dentalComposite resinsCIE L*a*b* systemCNPQ::CIENCIAS DA SAUDE::ODONTOLOGIATranslucidez e valor: análise do comportamento das propriedades ópticas em resinas compostas estéticasTranslucency and value: optical properties behavior in aesthetic resin compositesinfo:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/masterThesisPozzobon, Roselaine Terezinhahttp://buscatextual.cnpq.br/buscatextual/visualizacv.do?id=K4773209Z9Rocha, Rachel de Oliveirahttp://lattes.cnpq.br/0239294008628766Kaizer, Marina da Rosahttp://buscatextual.cnpq.br/buscatextual/visualizacv.do?id=K4764610Z2http://lattes.cnpq.br/8271713596204494Santos, Iuri Silveira dos400200000000400300300300300d8899efb-62e0-4a27-b994-198a09db6c00808c4d24-f135-44ac-93da-07d0ae42c349991eb734-f4d8-48d4-b231-3104d893e3dd9abfa676-e5ac-4b56-859b-b628ba260d01info:eu-repo/semantics/openAccessreponame:Manancial - Repositório Digital da UFSMinstname:Universidade Federal de Santa Maria (UFSM)instacron:UFSMORIGINALSANTOS, IURI SILVEIRA DOS.pdfapplication/pdf575968http://repositorio.ufsm.br/bitstream/1/6165/1/SANTOS%2c%20IURI%20SILVEIRA%20DOS.pdff0ce499de2a4eaedd4fe4a328f1c69f4MD51TEXTSANTOS, IURI SILVEIRA DOS.pdf.txtSANTOS, IURI SILVEIRA DOS.pdf.txtExtracted texttext/plain81840http://repositorio.ufsm.br/bitstream/1/6165/2/SANTOS%2c%20IURI%20SILVEIRA%20DOS.pdf.txt47f73ee4bf95c401dc9368f87fe18988MD52THUMBNAILSANTOS, IURI SILVEIRA DOS.pdf.jpgSANTOS, IURI SILVEIRA DOS.pdf.jpgIM Thumbnailimage/jpeg5021http://repositorio.ufsm.br/bitstream/1/6165/3/SANTOS%2c%20IURI%20SILVEIRA%20DOS.pdf.jpg118fa42bcd150ec7351a2d85e0a5f48fMD531/61652022-03-16 16:10:31.965oai:repositorio.ufsm.br:1/6165Repositório Institucionalhttp://repositorio.ufsm.br/PUBhttp://repositorio.ufsm.br/oai/requestopendoar:39132022-03-16T19:10:31Manancial - Repositório Digital da UFSM - Universidade Federal de Santa Maria (UFSM)false |
dc.title.por.fl_str_mv |
Translucidez e valor: análise do comportamento das propriedades ópticas em resinas compostas estéticas |
dc.title.alternative.eng.fl_str_mv |
Translucency and value: optical properties behavior in aesthetic resin composites |
title |
Translucidez e valor: análise do comportamento das propriedades ópticas em resinas compostas estéticas |
spellingShingle |
Translucidez e valor: análise do comportamento das propriedades ópticas em resinas compostas estéticas Santos, Iuri Silveira dos Materiais dentários Estética dental Resinas compostas Sistema CIE L*a*b* Dental materials Esthetic dental Composite resins CIE L*a*b* system CNPQ::CIENCIAS DA SAUDE::ODONTOLOGIA |
title_short |
Translucidez e valor: análise do comportamento das propriedades ópticas em resinas compostas estéticas |
title_full |
Translucidez e valor: análise do comportamento das propriedades ópticas em resinas compostas estéticas |
title_fullStr |
Translucidez e valor: análise do comportamento das propriedades ópticas em resinas compostas estéticas |
title_full_unstemmed |
Translucidez e valor: análise do comportamento das propriedades ópticas em resinas compostas estéticas |
title_sort |
Translucidez e valor: análise do comportamento das propriedades ópticas em resinas compostas estéticas |
author |
Santos, Iuri Silveira dos |
author_facet |
Santos, Iuri Silveira dos |
author_role |
author |
dc.contributor.advisor1.fl_str_mv |
Pozzobon, Roselaine Terezinha |
dc.contributor.advisor1Lattes.fl_str_mv |
http://buscatextual.cnpq.br/buscatextual/visualizacv.do?id=K4773209Z9 |
dc.contributor.referee1.fl_str_mv |
Rocha, Rachel de Oliveira |
dc.contributor.referee1Lattes.fl_str_mv |
http://lattes.cnpq.br/0239294008628766 |
dc.contributor.referee2.fl_str_mv |
Kaizer, Marina da Rosa |
dc.contributor.referee2Lattes.fl_str_mv |
http://buscatextual.cnpq.br/buscatextual/visualizacv.do?id=K4764610Z2 |
dc.contributor.authorLattes.fl_str_mv |
http://lattes.cnpq.br/8271713596204494 |
dc.contributor.author.fl_str_mv |
Santos, Iuri Silveira dos |
contributor_str_mv |
Pozzobon, Roselaine Terezinha Rocha, Rachel de Oliveira Kaizer, Marina da Rosa |
dc.subject.por.fl_str_mv |
Materiais dentários Estética dental Resinas compostas Sistema CIE L*a*b* |
topic |
Materiais dentários Estética dental Resinas compostas Sistema CIE L*a*b* Dental materials Esthetic dental Composite resins CIE L*a*b* system CNPQ::CIENCIAS DA SAUDE::ODONTOLOGIA |
dc.subject.eng.fl_str_mv |
Dental materials Esthetic dental Composite resins CIE L*a*b* system |
dc.subject.cnpq.fl_str_mv |
CNPQ::CIENCIAS DA SAUDE::ODONTOLOGIA |
description |
This study aimed to evaluate the translucency and value with different combinations of enamel , dentin and body of each composite regarding a standard thickness (1,5mm). Three different resin composites commercially available with a standard shade (A1), IPS Empress Direct, Charisma Diamond and Filtek Z350 XT were evaluated. A stainless steel matrix was used to prepare ninety disc-shaped specimens with 11mm diameter and 1,5mm thickness. The specimens were randomly allocated in 18 groups (n=5) according to different combinations of enamel , dentin and body presented in each resin composite evaluated. After light curing, specimens were stored in deionized water at 37º C for 24h. Three consecutive readings were performed according to the CIE L*a*b* color scale relative to the standard illuminant D65 on reflection spectrophotometer (SP60 - EX-Rite). The optical properties of translucency and value were measured by the parameters translucency (TP) and lightness in white background (L*w) and black background (L*b), respectively. The mean TP, L*w and L*b were analyzed by ANOVA (General Linear Models) and Tukey s post hoc tests (α =0.05). Scatter plots together with Spearman´s correlation coefficient were used to assess the relationship between TP and L*w and TP and L*b values. The groups had statistical significant different values (p=0.000). The resin composite Empress Direct when only a layer of enamel were employed presented the highest TP value, whereas the resin composite Filtek Z350 XT with a single layer of dentin presented the lowest TP value. A negative and strong correlation between TP and L*b and a positive and weak correlation between TP and L*w were observed. Optical properties as translucency and value rely on the material used. In general, there was statistical difference between the groups for TP and L* |
publishDate |
2015 |
dc.date.issued.fl_str_mv |
2015-06-11 |
dc.date.accessioned.fl_str_mv |
2016-02-23 |
dc.date.available.fl_str_mv |
2016-02-23 |
dc.type.status.fl_str_mv |
info:eu-repo/semantics/publishedVersion |
dc.type.driver.fl_str_mv |
info:eu-repo/semantics/masterThesis |
format |
masterThesis |
status_str |
publishedVersion |
dc.identifier.citation.fl_str_mv |
SANTOS, Iuri Silveira dos. TRANSLUCENCY AND VALUE: OPTICAL PROPERTIES BEHAVIOR IN AESTHETIC RESIN COMPOSITES. 2015. 51 f. Dissertação (Mestrado em Odontologia) - Universidade Federal de Santa Maria, Santa Maria, 2015. |
dc.identifier.uri.fl_str_mv |
http://repositorio.ufsm.br/handle/1/6165 |
identifier_str_mv |
SANTOS, Iuri Silveira dos. TRANSLUCENCY AND VALUE: OPTICAL PROPERTIES BEHAVIOR IN AESTHETIC RESIN COMPOSITES. 2015. 51 f. Dissertação (Mestrado em Odontologia) - Universidade Federal de Santa Maria, Santa Maria, 2015. |
url |
http://repositorio.ufsm.br/handle/1/6165 |
dc.language.iso.fl_str_mv |
por |
language |
por |
dc.relation.cnpq.fl_str_mv |
400200000000 |
dc.relation.confidence.fl_str_mv |
400 300 300 300 300 |
dc.relation.authority.fl_str_mv |
d8899efb-62e0-4a27-b994-198a09db6c00 808c4d24-f135-44ac-93da-07d0ae42c349 991eb734-f4d8-48d4-b231-3104d893e3dd 9abfa676-e5ac-4b56-859b-b628ba260d01 |
dc.rights.driver.fl_str_mv |
info:eu-repo/semantics/openAccess |
eu_rights_str_mv |
openAccess |
dc.format.none.fl_str_mv |
application/pdf |
dc.publisher.none.fl_str_mv |
Universidade Federal de Santa Maria |
dc.publisher.program.fl_str_mv |
Programa de Pós-Graduação em Ciências Odontológicas |
dc.publisher.initials.fl_str_mv |
UFSM |
dc.publisher.country.fl_str_mv |
BR |
dc.publisher.department.fl_str_mv |
Odontologia |
publisher.none.fl_str_mv |
Universidade Federal de Santa Maria |
dc.source.none.fl_str_mv |
reponame:Manancial - Repositório Digital da UFSM instname:Universidade Federal de Santa Maria (UFSM) instacron:UFSM |
instname_str |
Universidade Federal de Santa Maria (UFSM) |
instacron_str |
UFSM |
institution |
UFSM |
reponame_str |
Manancial - Repositório Digital da UFSM |
collection |
Manancial - Repositório Digital da UFSM |
bitstream.url.fl_str_mv |
http://repositorio.ufsm.br/bitstream/1/6165/1/SANTOS%2c%20IURI%20SILVEIRA%20DOS.pdf http://repositorio.ufsm.br/bitstream/1/6165/2/SANTOS%2c%20IURI%20SILVEIRA%20DOS.pdf.txt http://repositorio.ufsm.br/bitstream/1/6165/3/SANTOS%2c%20IURI%20SILVEIRA%20DOS.pdf.jpg |
bitstream.checksum.fl_str_mv |
f0ce499de2a4eaedd4fe4a328f1c69f4 47f73ee4bf95c401dc9368f87fe18988 118fa42bcd150ec7351a2d85e0a5f48f |
bitstream.checksumAlgorithm.fl_str_mv |
MD5 MD5 MD5 |
repository.name.fl_str_mv |
Manancial - Repositório Digital da UFSM - Universidade Federal de Santa Maria (UFSM) |
repository.mail.fl_str_mv |
|
_version_ |
1801223683280207872 |