Efeito da concentração de ácido fluorídrico na carga para falha em fadiga de uma cerâmica feldspática cimentada
Autor(a) principal: | |
---|---|
Data de Publicação: | 2018 |
Tipo de documento: | Tese |
Idioma: | por |
Título da fonte: | Biblioteca Digital de Teses e Dissertações do UFSM |
Texto Completo: | http://repositorio.ufsm.br/handle/1/14295 |
Resumo: | The present thesis is composed by two scientific articles that evaluated the influence of different hydrofluoric acid concentrations on the fatigue failure loads of feldspathic ceramic crowns and discs adhesively cemented to a dentin analogue material (epoxy resin). Therefore, eighty crowns with simplified geometry and eighty feldspathic ceramic discs (Vita Mark II, Vita Zahnfabrik) were randomly allocated, and the intaglio surface of each crown/disc was treated with one of the four surface conditioning methods (n=20): nonetched / control (CTRL), or etched for 60 s with different hydrofluoric acid concentrations: 1% (HF1), 5% (HF5), or 10% (HF10). The treated ceramic surface received the application of a silane coupling agent. The cementation surface of simplified complete crown preparations and discs (both in epoxy resin) were etched with 10% hydrofluoric acid for 60 s and received a primer coating specific to the cementation system. After the surface treatments, the ceramic crowns and discs were adhesively cemented to the respective prosthetic preparations and epoxy resin discs, which were subjected to cyclic loads in water by a staircase approach (500,000 cycles, 20 Hz). Fatigue failure load data were analyzed by 1-way ANOVA and Tukey’s tests (α= .05). For the ceramic crowns, mean failure loads of groups CTRL (245.0 ± 15.1 N), HF1 (242.5 ± 24.7 N) and HF10 (255.7 ± 53.8 N) were statistically similar (P>.05), while the mean load of the HF5 group (216.7 ± 22.5 N) was significantly lower. In the condition of cemented discs, mean failure load of the HF5 group (255.0 ± 23.0 N) was also significantly lower; HF1 group (301.7 ± 71.0 N) presented intermediate values, and the highest values were achieved in CTRL (351.7 ± 13.4 N) and HF10 (341.7 ± 20.6 N) groups. Etching with 5% hydrofluoric acid had a deleterious effect on the fatigue failure loads of adhesively cemented feldspathic ceramic crowns and discs, while etching with 10% hydrofluoric acid had no negative influence in both tested conditions (crowns and discs). |
id |
UFSM_3f327f5eaff24e2a72be409b9b5cb6f4 |
---|---|
oai_identifier_str |
oai:repositorio.ufsm.br:1/14295 |
network_acronym_str |
UFSM |
network_name_str |
Biblioteca Digital de Teses e Dissertações do UFSM |
repository_id_str |
|
spelling |
2018-09-13T14:57:20Z2018-09-13T14:57:20Z2018-03-16http://repositorio.ufsm.br/handle/1/14295The present thesis is composed by two scientific articles that evaluated the influence of different hydrofluoric acid concentrations on the fatigue failure loads of feldspathic ceramic crowns and discs adhesively cemented to a dentin analogue material (epoxy resin). Therefore, eighty crowns with simplified geometry and eighty feldspathic ceramic discs (Vita Mark II, Vita Zahnfabrik) were randomly allocated, and the intaglio surface of each crown/disc was treated with one of the four surface conditioning methods (n=20): nonetched / control (CTRL), or etched for 60 s with different hydrofluoric acid concentrations: 1% (HF1), 5% (HF5), or 10% (HF10). The treated ceramic surface received the application of a silane coupling agent. The cementation surface of simplified complete crown preparations and discs (both in epoxy resin) were etched with 10% hydrofluoric acid for 60 s and received a primer coating specific to the cementation system. After the surface treatments, the ceramic crowns and discs were adhesively cemented to the respective prosthetic preparations and epoxy resin discs, which were subjected to cyclic loads in water by a staircase approach (500,000 cycles, 20 Hz). Fatigue failure load data were analyzed by 1-way ANOVA and Tukey’s tests (α= .05). For the ceramic crowns, mean failure loads of groups CTRL (245.0 ± 15.1 N), HF1 (242.5 ± 24.7 N) and HF10 (255.7 ± 53.8 N) were statistically similar (P>.05), while the mean load of the HF5 group (216.7 ± 22.5 N) was significantly lower. In the condition of cemented discs, mean failure load of the HF5 group (255.0 ± 23.0 N) was also significantly lower; HF1 group (301.7 ± 71.0 N) presented intermediate values, and the highest values were achieved in CTRL (351.7 ± 13.4 N) and HF10 (341.7 ± 20.6 N) groups. Etching with 5% hydrofluoric acid had a deleterious effect on the fatigue failure loads of adhesively cemented feldspathic ceramic crowns and discs, while etching with 10% hydrofluoric acid had no negative influence in both tested conditions (crowns and discs).A presente tese é composta por dois artigos científicos que avaliaram a influência de diferentes concentrações de ácido fluorídrico na carga para falha em fadiga de coroas e discos de cerâmica feldspática cimentados à um material análogo a dentina (resina epóxi). Para tanto, oitenta coroas com geometria simplificada e oitenta discos de cerâmica feldspática (Vita Mark II, Vita Zahnfabrik) foram divididos aleatoriamente, e a superfície interna de cada coroa/disco foi tratada de acordo com um dos quatro métodos de condicionamento de superfície (n=20): sem condicionamento/controle (CTRL), ou condicionamento por 60 s com diferentes concentrações de ácido fluorídrico: 1% (HF1), 5% (HF5) ou 10% (HF10). A superfície cerâmica tratada recebeu a aplicação de um agente de união silano. A superfície de cimentação dos preparos para coroas totais simplificadas e dos discos (ambos em resina epóxi) foram condicionados com ácido fluorídrico 10% por 60 s seguido da aplicação de uma camada de adesivo específico do sistema de cimentação. Após os tratamentos de superfície, as coroas e discos cerâmicos foram cimentados adesivamente aos respectivos preparos protéticos e discos de resina epóxi, os quais foram submetidos a cargas cíclicas em água pelo método da escada (500.000 ciclos, 20 Hz). Os dados de carga para falha em fadiga foram analisados pela análise de variância (ANOVA-1 fator) e testes de Tukey (α=0,05). Para as coroas cerâmicas, as cargas médias para falha em fadiga dos grupos CTRL (245,0 ± 15,1 N), HF1 (242,5 ± 24,7 N) e HF10 (255,7 ± 53,8 N) foram estatisticamente semelhantes (P>0,05), enquanto que a carga média do grupo HF5 (216,7 ± 22,5 N) foi significativamente inferior. Na condição de discos cimentados, a carga de falha média do grupo HF5 (255,0 ± 23,0 N) também foi significativamente inferior; o grupo HF1 (301,7 ± 71,0 N) apresentou valores intermediários e os valores mais altos foram alcançados nos grupos CTRL (351,7 ± 13,4 N) e HF10 (341,7 ± 20,6 N). O condicionamento com ácido fluorídrico 5% teve um efeito deletério nos valores de carga para falha em fadiga de coroas e discos de cerâmica feldspática cimentados adesivamente, visto que o condicionamento com ácido fluorídrico 10% não teve influência negativa em ambas as condições testadas (coroas e discos).Coordenação de Aperfeiçoamento de Pessoal de Nível Superior - CAPESporUniversidade Federal de Santa MariaCentro de Ciências da SaúdePrograma de Pós-Graduação em Ciências OdontológicasUFSMBrasilOdontologiaAttribution-NonCommercial-NoDerivatives 4.0 Internationalhttp://creativecommons.org/licenses/by-nc-nd/4.0/info:eu-repo/semantics/openAccessÁcido fluorídricoCarregamento cíclicoCerâmica feldspáticaFadigaTratamento de superfícieCyclic loadingFatigueFeldspathic ceramicHydrofluoric acidSurface treatmentCNPQ::CIENCIAS DA SAUDE::ODONTOLOGIAEfeito da concentração de ácido fluorídrico na carga para falha em fadiga de uma cerâmica feldspática cimentadaEffect of hydrofluoric acid concentration on the fatigue failure load of a cemented feldspathic ceramicinfo:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/doctoralThesisValandro, Luiz Felipehttp://lattes.cnpq.br/0535309012233484Rippe, Marília Pivettahttp://lattes.cnpq.br/3336921465345785Bergoli, César Dalmolinhttp://lattes.cnpq.br/4313918234580023Aurélio, Iana Lamadridhttp://lattes.cnpq.br/9679295945027664Fraga, Sarahttp://lattes.cnpq.br/8179821009699942http://lattes.cnpq.br/6047481428080936Venturini, Andressa Borin400200000000600381d00c6-91f3-43f9-b2ff-a634b10ed95d98353ab5-051b-4b91-96a3-af686a38b9f5b94db58c-9556-4c38-a539-a64d09d0fc559b70de8d-eb7b-43f5-97fa-12237e0e3a0ceb79352b-76f7-4bf5-b259-0737ae90c5331e4d4697-7928-473e-8348-7487df13e59breponame:Biblioteca Digital de Teses e Dissertações do UFSMinstname:Universidade Federal de Santa Maria (UFSM)instacron:UFSMORIGINALTES_PPGCO_2018_VENTURINI_ANDRESSA.pdfTES_PPGCO_2018_VENTURINI_ANDRESSA.pdfTese de Doutoradoapplication/pdf4358494http://repositorio.ufsm.br/bitstream/1/14295/1/TES_PPGCO_2018_VENTURINI_ANDRESSA.pdf0c2f209e86bb7757e31bdbdd4ce72ac5MD51CC-LICENSElicense_rdflicense_rdfapplication/rdf+xml; charset=utf-8804http://repositorio.ufsm.br/bitstream/1/14295/2/license_rdfc1efe8e24d7281448e873be30ea326ffMD52LICENSElicense.txtlicense.txttext/plain; charset=utf-81956http://repositorio.ufsm.br/bitstream/1/14295/3/license.txt2f0571ecee68693bd5cd3f17c1e075dfMD53TEXTTES_PPGCO_2018_VENTURINI_ANDRESSA.pdf.txtTES_PPGCO_2018_VENTURINI_ANDRESSA.pdf.txtExtracted texttext/plain177293http://repositorio.ufsm.br/bitstream/1/14295/4/TES_PPGCO_2018_VENTURINI_ANDRESSA.pdf.txt42cdb568a418909b89ca26bb8032af17MD54THUMBNAILTES_PPGCO_2018_VENTURINI_ANDRESSA.pdf.jpgTES_PPGCO_2018_VENTURINI_ANDRESSA.pdf.jpgIM Thumbnailimage/jpeg4472http://repositorio.ufsm.br/bitstream/1/14295/5/TES_PPGCO_2018_VENTURINI_ANDRESSA.pdf.jpgd7375331e6e1bab587e54ed873d099d4MD551/142952018-09-13 11:57:21.143oai:repositorio.ufsm.br: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 Digital de Teses e Dissertaçõeshttps://repositorio.ufsm.br/ONGhttps://repositorio.ufsm.br/oai/requestatendimento.sib@ufsm.br||tedebc@gmail.comopendoar:2018-09-13T14:57:21Biblioteca Digital de Teses e Dissertações do UFSM - Universidade Federal de Santa Maria (UFSM)false |
dc.title.por.fl_str_mv |
Efeito da concentração de ácido fluorídrico na carga para falha em fadiga de uma cerâmica feldspática cimentada |
dc.title.alternative.eng.fl_str_mv |
Effect of hydrofluoric acid concentration on the fatigue failure load of a cemented feldspathic ceramic |
title |
Efeito da concentração de ácido fluorídrico na carga para falha em fadiga de uma cerâmica feldspática cimentada |
spellingShingle |
Efeito da concentração de ácido fluorídrico na carga para falha em fadiga de uma cerâmica feldspática cimentada Venturini, Andressa Borin Ácido fluorídrico Carregamento cíclico Cerâmica feldspática Fadiga Tratamento de superfície Cyclic loading Fatigue Feldspathic ceramic Hydrofluoric acid Surface treatment CNPQ::CIENCIAS DA SAUDE::ODONTOLOGIA |
title_short |
Efeito da concentração de ácido fluorídrico na carga para falha em fadiga de uma cerâmica feldspática cimentada |
title_full |
Efeito da concentração de ácido fluorídrico na carga para falha em fadiga de uma cerâmica feldspática cimentada |
title_fullStr |
Efeito da concentração de ácido fluorídrico na carga para falha em fadiga de uma cerâmica feldspática cimentada |
title_full_unstemmed |
Efeito da concentração de ácido fluorídrico na carga para falha em fadiga de uma cerâmica feldspática cimentada |
title_sort |
Efeito da concentração de ácido fluorídrico na carga para falha em fadiga de uma cerâmica feldspática cimentada |
author |
Venturini, Andressa Borin |
author_facet |
Venturini, Andressa Borin |
author_role |
author |
dc.contributor.advisor1.fl_str_mv |
Valandro, Luiz Felipe |
dc.contributor.advisor1Lattes.fl_str_mv |
http://lattes.cnpq.br/0535309012233484 |
dc.contributor.referee1.fl_str_mv |
Rippe, Marília Pivetta |
dc.contributor.referee1Lattes.fl_str_mv |
http://lattes.cnpq.br/3336921465345785 |
dc.contributor.referee2.fl_str_mv |
Bergoli, César Dalmolin |
dc.contributor.referee2Lattes.fl_str_mv |
http://lattes.cnpq.br/4313918234580023 |
dc.contributor.referee3.fl_str_mv |
Aurélio, Iana Lamadrid |
dc.contributor.referee3Lattes.fl_str_mv |
http://lattes.cnpq.br/9679295945027664 |
dc.contributor.referee4.fl_str_mv |
Fraga, Sara |
dc.contributor.referee4Lattes.fl_str_mv |
http://lattes.cnpq.br/8179821009699942 |
dc.contributor.authorLattes.fl_str_mv |
http://lattes.cnpq.br/6047481428080936 |
dc.contributor.author.fl_str_mv |
Venturini, Andressa Borin |
contributor_str_mv |
Valandro, Luiz Felipe Rippe, Marília Pivetta Bergoli, César Dalmolin Aurélio, Iana Lamadrid Fraga, Sara |
dc.subject.por.fl_str_mv |
Ácido fluorídrico Carregamento cíclico Cerâmica feldspática Fadiga Tratamento de superfície |
topic |
Ácido fluorídrico Carregamento cíclico Cerâmica feldspática Fadiga Tratamento de superfície Cyclic loading Fatigue Feldspathic ceramic Hydrofluoric acid Surface treatment CNPQ::CIENCIAS DA SAUDE::ODONTOLOGIA |
dc.subject.eng.fl_str_mv |
Cyclic loading Fatigue Feldspathic ceramic Hydrofluoric acid Surface treatment |
dc.subject.cnpq.fl_str_mv |
CNPQ::CIENCIAS DA SAUDE::ODONTOLOGIA |
description |
The present thesis is composed by two scientific articles that evaluated the influence of different hydrofluoric acid concentrations on the fatigue failure loads of feldspathic ceramic crowns and discs adhesively cemented to a dentin analogue material (epoxy resin). Therefore, eighty crowns with simplified geometry and eighty feldspathic ceramic discs (Vita Mark II, Vita Zahnfabrik) were randomly allocated, and the intaglio surface of each crown/disc was treated with one of the four surface conditioning methods (n=20): nonetched / control (CTRL), or etched for 60 s with different hydrofluoric acid concentrations: 1% (HF1), 5% (HF5), or 10% (HF10). The treated ceramic surface received the application of a silane coupling agent. The cementation surface of simplified complete crown preparations and discs (both in epoxy resin) were etched with 10% hydrofluoric acid for 60 s and received a primer coating specific to the cementation system. After the surface treatments, the ceramic crowns and discs were adhesively cemented to the respective prosthetic preparations and epoxy resin discs, which were subjected to cyclic loads in water by a staircase approach (500,000 cycles, 20 Hz). Fatigue failure load data were analyzed by 1-way ANOVA and Tukey’s tests (α= .05). For the ceramic crowns, mean failure loads of groups CTRL (245.0 ± 15.1 N), HF1 (242.5 ± 24.7 N) and HF10 (255.7 ± 53.8 N) were statistically similar (P>.05), while the mean load of the HF5 group (216.7 ± 22.5 N) was significantly lower. In the condition of cemented discs, mean failure load of the HF5 group (255.0 ± 23.0 N) was also significantly lower; HF1 group (301.7 ± 71.0 N) presented intermediate values, and the highest values were achieved in CTRL (351.7 ± 13.4 N) and HF10 (341.7 ± 20.6 N) groups. Etching with 5% hydrofluoric acid had a deleterious effect on the fatigue failure loads of adhesively cemented feldspathic ceramic crowns and discs, while etching with 10% hydrofluoric acid had no negative influence in both tested conditions (crowns and discs). |
publishDate |
2018 |
dc.date.accessioned.fl_str_mv |
2018-09-13T14:57:20Z |
dc.date.available.fl_str_mv |
2018-09-13T14:57:20Z |
dc.date.issued.fl_str_mv |
2018-03-16 |
dc.type.status.fl_str_mv |
info:eu-repo/semantics/publishedVersion |
dc.type.driver.fl_str_mv |
info:eu-repo/semantics/doctoralThesis |
format |
doctoralThesis |
status_str |
publishedVersion |
dc.identifier.uri.fl_str_mv |
http://repositorio.ufsm.br/handle/1/14295 |
url |
http://repositorio.ufsm.br/handle/1/14295 |
dc.language.iso.fl_str_mv |
por |
language |
por |
dc.relation.cnpq.fl_str_mv |
400200000000 |
dc.relation.confidence.fl_str_mv |
600 |
dc.relation.authority.fl_str_mv |
381d00c6-91f3-43f9-b2ff-a634b10ed95d 98353ab5-051b-4b91-96a3-af686a38b9f5 b94db58c-9556-4c38-a539-a64d09d0fc55 9b70de8d-eb7b-43f5-97fa-12237e0e3a0c eb79352b-76f7-4bf5-b259-0737ae90c533 1e4d4697-7928-473e-8348-7487df13e59b |
dc.rights.driver.fl_str_mv |
Attribution-NonCommercial-NoDerivatives 4.0 International http://creativecommons.org/licenses/by-nc-nd/4.0/ info:eu-repo/semantics/openAccess |
rights_invalid_str_mv |
Attribution-NonCommercial-NoDerivatives 4.0 International http://creativecommons.org/licenses/by-nc-nd/4.0/ |
eu_rights_str_mv |
openAccess |
dc.publisher.none.fl_str_mv |
Universidade Federal de Santa Maria Centro de Ciências da Saúde |
dc.publisher.program.fl_str_mv |
Programa de Pós-Graduação em Ciências Odontológicas |
dc.publisher.initials.fl_str_mv |
UFSM |
dc.publisher.country.fl_str_mv |
Brasil |
dc.publisher.department.fl_str_mv |
Odontologia |
publisher.none.fl_str_mv |
Universidade Federal de Santa Maria Centro de Ciências da Saúde |
dc.source.none.fl_str_mv |
reponame:Biblioteca Digital de Teses e Dissertações do UFSM instname:Universidade Federal de Santa Maria (UFSM) instacron:UFSM |
instname_str |
Universidade Federal de Santa Maria (UFSM) |
instacron_str |
UFSM |
institution |
UFSM |
reponame_str |
Biblioteca Digital de Teses e Dissertações do UFSM |
collection |
Biblioteca Digital de Teses e Dissertações do UFSM |
bitstream.url.fl_str_mv |
http://repositorio.ufsm.br/bitstream/1/14295/1/TES_PPGCO_2018_VENTURINI_ANDRESSA.pdf http://repositorio.ufsm.br/bitstream/1/14295/2/license_rdf http://repositorio.ufsm.br/bitstream/1/14295/3/license.txt http://repositorio.ufsm.br/bitstream/1/14295/4/TES_PPGCO_2018_VENTURINI_ANDRESSA.pdf.txt http://repositorio.ufsm.br/bitstream/1/14295/5/TES_PPGCO_2018_VENTURINI_ANDRESSA.pdf.jpg |
bitstream.checksum.fl_str_mv |
0c2f209e86bb7757e31bdbdd4ce72ac5 c1efe8e24d7281448e873be30ea326ff 2f0571ecee68693bd5cd3f17c1e075df 42cdb568a418909b89ca26bb8032af17 d7375331e6e1bab587e54ed873d099d4 |
bitstream.checksumAlgorithm.fl_str_mv |
MD5 MD5 MD5 MD5 MD5 |
repository.name.fl_str_mv |
Biblioteca Digital de Teses e Dissertações do UFSM - Universidade Federal de Santa Maria (UFSM) |
repository.mail.fl_str_mv |
atendimento.sib@ufsm.br||tedebc@gmail.com |
_version_ |
1801485348530814976 |