Microfresamento de aço inoxidável duplex UNS S32205 com ferramentas de metal duro revestidas com nitreto de titânio
Autor(a) principal: | |
---|---|
Data de Publicação: | 2016 |
Tipo de documento: | Dissertação |
Idioma: | por |
Título da fonte: | Repositório Institucional da UFU |
Texto Completo: | https://repositorio.ufu.br/handle/123456789/15018 http://doi.org/10.14393/ufu.di.2016.201 |
Resumo: | The development of technology in many areas has increased the demand for production of components with small dimensions. In this scenario, the micro machining has emerged as an important tool because it is a process with great precision in producing micro-scaled components. This technique allows processing of composites, polymers, ceramics, and metallic alloys, including stainless steels. Stainless steels are popular due to their chemical characteristics like high resistance to corrosion and oxidation. The main goal of this work is the study of phenomena involved in micromilling a UNS S32205 duplex stainless steel, using TiN coated carbide tools. Accordingly, it was investigated tool wear type and mechanism, burr formation and machined surface quality. For this purpose, this work was carried out with a 4-axis CNC micromill machine tool using 0.381 mm diameter tools. Pre-tests were carried out in order to select the most appropriate cutting condition for further analysis. Tool wear, machined surface and burr were examined in a scanning electron microscope. The burr height and roughness were measured by a profilometer. The results show that the major forms of wear are nose and flank wear, with predominance of the adhesion wear mechanism. The wear land as a function of machined length showed similar behavior to macro machining operations with three well defined regions of different wear rates. Taylor s equation was obtained and the coefficients are similar to those obtained in conventional operations. It was observed that the top burr presented the most significant size. The results obtained for the surface roughness, Ra, varied in the range of 0.131 to 0.469 μm. |
id |
UFU_b65f51602a39e5f5d15d9156b487ae8e |
---|---|
oai_identifier_str |
oai:repositorio.ufu.br:123456789/15018 |
network_acronym_str |
UFU |
network_name_str |
Repositório Institucional da UFU |
repository_id_str |
|
spelling |
2016-06-22T18:41:10Z2016-06-072016-06-22T18:41:10Z2016-03-01SANTOS, Aline Gonçalves dos. Micromilling UNS S32205 duplex stainless steel using titanium nitride coated carbide tools. 2016. 107 f. Dissertação (Mestrado em Engenharias) - Universidade Federal de Uberlândia, Uberlândia, 2016. DOI http://doi.org/10.14393/ufu.di.2016.201https://repositorio.ufu.br/handle/123456789/15018http://doi.org/10.14393/ufu.di.2016.201The development of technology in many areas has increased the demand for production of components with small dimensions. In this scenario, the micro machining has emerged as an important tool because it is a process with great precision in producing micro-scaled components. This technique allows processing of composites, polymers, ceramics, and metallic alloys, including stainless steels. Stainless steels are popular due to their chemical characteristics like high resistance to corrosion and oxidation. The main goal of this work is the study of phenomena involved in micromilling a UNS S32205 duplex stainless steel, using TiN coated carbide tools. Accordingly, it was investigated tool wear type and mechanism, burr formation and machined surface quality. For this purpose, this work was carried out with a 4-axis CNC micromill machine tool using 0.381 mm diameter tools. Pre-tests were carried out in order to select the most appropriate cutting condition for further analysis. Tool wear, machined surface and burr were examined in a scanning electron microscope. The burr height and roughness were measured by a profilometer. The results show that the major forms of wear are nose and flank wear, with predominance of the adhesion wear mechanism. The wear land as a function of machined length showed similar behavior to macro machining operations with three well defined regions of different wear rates. Taylor s equation was obtained and the coefficients are similar to those obtained in conventional operations. It was observed that the top burr presented the most significant size. The results obtained for the surface roughness, Ra, varied in the range of 0.131 to 0.469 μm.O desenvolvimento da tecnologia em diversas áreas tem demandado cada vez mais a produção de componentes com pequenas dimensões. Neste cenário, a microusinagem tem se apresentado como uma importante ferramenta, pois se trata de um processo de usinagem com grande precisão, que envolve a fabricação de peças com dimensões de escala reduzida. Ela permite o processamento de diversas variedades de metais e ligas, compósitos, polímeros, cerâmicas e alguns aços inoxidáveis, sendo que estes últimos despertam grande interesse para a indústria devido à sua característica de grande resistência à corrosão e à oxidação. Diante desse contexto, os estudos do processo de microusinagem, bem como dos aços inoxidáveis se intensificaram, o que motivou a realização do presente trabalho, que tem como principal objetivo analisar fenômenos envolvidos no processo de microfresamento do aço inoxidável duplex UNS S32205, utilizando ferramentas de metal duro revestidas com nitreto de titânio. Nesse sentido, foram analisados o tipo e mecanismos de desgaste de ferramenta, a formação de rebarba e a qualidade da superfície gerada. Para tanto, foram realizados ensaios para fabricação de microcanais, utilizando uma microfresadora CNC de quatro eixos e microfresas de metal duro com diâmetro de 381 μm. Pré-testes foram realizados a fim de escolher a condição de corte mais adequada para análise aprofundada. As ferramentas, as superfícies geradas e as rebarbas foram examinadas no microscópio eletrônico de varredura. A altura da rebarba e a rugosidade foram medidas através de um perfilômetro. Os resultados mostram que as principais formas de desgaste apresentadas pelas microfresas foram desgaste de ponta e de flanco, sendo o mecanismo de desgaste predominante o de adesão. O gráfico obtido para o desgaste em função do comprimento usinado apresentou comportamento semelhante ao apresentado na macrousinagem, com três regiões de taxa de desgaste diferentes. A equação de Taylor foi determinada para o par ferramenta-peça analisado. Foi observado que a rebarba de topo foi aquela que apresentou tamanho mais expressivo. Os resultados obtidos para rugosidade variaram de 0,131 a 0,469 μm.Fundação de Amparo a Pesquisa do Estado de Minas GeraisMestre em Engenharia Mecânicaapplication/pdfporUniversidade Federal de UberlândiaPrograma de Pós-graduação em Engenharia MecânicaUFUBREngenhariasMicrousinagemAço inoxidável duplexDesgasteRebarbaQualidade superficialAço inoxidávelDesgaste mecânicoUsinagemMicromachiningDuplex stainless steelWearBurrSurface qualityCNPQ::ENGENHARIAS::ENGENHARIA MECANICAMicrofresamento de aço inoxidável duplex UNS S32205 com ferramentas de metal duro revestidas com nitreto de titânioMicromilling UNS S32205 duplex stainless steel using titanium nitride coated carbide toolsinfo:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/masterThesisJackson, Mark Jameshttp://buscatextual.cnpq.br/buscatextual/visualizacv.do?id=K8548996J9Silva, Marcio Bacci dahttp://buscatextual.cnpq.br/buscatextual/visualizacv.do?id=K4785913J0Silva, Rosemar Batista dahttp://buscatextual.cnpq.br/buscatextual/visualizacv.do?id=K4706048P0Rodrigues, Alessandro Rogerhttp://buscatextual.cnpq.br/buscatextual/visualizacv.do?id=K4760771A2http://buscatextual.cnpq.br/buscatextual/visualizacv.do?id=K4381306U1Santos, Aline Gonçalves dos8175612051077b7f-2a0d-4bd9-a513-1043c8690d8binfo:eu-repo/semantics/openAccessreponame:Repositório Institucional da UFUinstname:Universidade Federal de Uberlândia (UFU)instacron:UFUTHUMBNAILMicrofresamentoAcoInoxidavel.pdf.jpgMicrofresamentoAcoInoxidavel.pdf.jpgGenerated Thumbnailimage/jpeg1309https://repositorio.ufu.br/bitstream/123456789/15018/3/MicrofresamentoAcoInoxidavel.pdf.jpg37462dd94b18846e6b4fb1e111a59917MD53ORIGINALMicrofresamentoAcoInoxidavel.pdfapplication/pdf6524152https://repositorio.ufu.br/bitstream/123456789/15018/1/MicrofresamentoAcoInoxidavel.pdfa6f1cc49155ec28e204e61d3e908d44eMD51TEXTMicrofresamentoAcoInoxidavel.pdf.txtMicrofresamentoAcoInoxidavel.pdf.txtExtracted texttext/plain177200https://repositorio.ufu.br/bitstream/123456789/15018/2/MicrofresamentoAcoInoxidavel.pdf.txt690f570c386d3dfd6234d047943ee639MD52123456789/150182021-10-19 16:40:28.188oai:repositorio.ufu.br:123456789/15018Repositório InstitucionalONGhttp://repositorio.ufu.br/oai/requestdiinf@dirbi.ufu.bropendoar:2021-10-19T19:40:28Repositório Institucional da UFU - Universidade Federal de Uberlândia (UFU)false |
dc.title.por.fl_str_mv |
Microfresamento de aço inoxidável duplex UNS S32205 com ferramentas de metal duro revestidas com nitreto de titânio |
dc.title.alternative.eng.fl_str_mv |
Micromilling UNS S32205 duplex stainless steel using titanium nitride coated carbide tools |
title |
Microfresamento de aço inoxidável duplex UNS S32205 com ferramentas de metal duro revestidas com nitreto de titânio |
spellingShingle |
Microfresamento de aço inoxidável duplex UNS S32205 com ferramentas de metal duro revestidas com nitreto de titânio Santos, Aline Gonçalves dos Microusinagem Aço inoxidável duplex Desgaste Rebarba Qualidade superficial Aço inoxidável Desgaste mecânico Usinagem Micromachining Duplex stainless steel Wear Burr Surface quality CNPQ::ENGENHARIAS::ENGENHARIA MECANICA |
title_short |
Microfresamento de aço inoxidável duplex UNS S32205 com ferramentas de metal duro revestidas com nitreto de titânio |
title_full |
Microfresamento de aço inoxidável duplex UNS S32205 com ferramentas de metal duro revestidas com nitreto de titânio |
title_fullStr |
Microfresamento de aço inoxidável duplex UNS S32205 com ferramentas de metal duro revestidas com nitreto de titânio |
title_full_unstemmed |
Microfresamento de aço inoxidável duplex UNS S32205 com ferramentas de metal duro revestidas com nitreto de titânio |
title_sort |
Microfresamento de aço inoxidável duplex UNS S32205 com ferramentas de metal duro revestidas com nitreto de titânio |
author |
Santos, Aline Gonçalves dos |
author_facet |
Santos, Aline Gonçalves dos |
author_role |
author |
dc.contributor.advisor-co1.fl_str_mv |
Jackson, Mark James |
dc.contributor.advisor-co1Lattes.fl_str_mv |
http://buscatextual.cnpq.br/buscatextual/visualizacv.do?id=K8548996J9 |
dc.contributor.advisor1.fl_str_mv |
Silva, Marcio Bacci da |
dc.contributor.advisor1Lattes.fl_str_mv |
http://buscatextual.cnpq.br/buscatextual/visualizacv.do?id=K4785913J0 |
dc.contributor.referee1.fl_str_mv |
Silva, Rosemar Batista da |
dc.contributor.referee1Lattes.fl_str_mv |
http://buscatextual.cnpq.br/buscatextual/visualizacv.do?id=K4706048P0 |
dc.contributor.referee2.fl_str_mv |
Rodrigues, Alessandro Roger |
dc.contributor.referee2Lattes.fl_str_mv |
http://buscatextual.cnpq.br/buscatextual/visualizacv.do?id=K4760771A2 |
dc.contributor.authorLattes.fl_str_mv |
http://buscatextual.cnpq.br/buscatextual/visualizacv.do?id=K4381306U1 |
dc.contributor.author.fl_str_mv |
Santos, Aline Gonçalves dos |
contributor_str_mv |
Jackson, Mark James Silva, Marcio Bacci da Silva, Rosemar Batista da Rodrigues, Alessandro Roger |
dc.subject.por.fl_str_mv |
Microusinagem Aço inoxidável duplex Desgaste Rebarba Qualidade superficial Aço inoxidável Desgaste mecânico Usinagem |
topic |
Microusinagem Aço inoxidável duplex Desgaste Rebarba Qualidade superficial Aço inoxidável Desgaste mecânico Usinagem Micromachining Duplex stainless steel Wear Burr Surface quality CNPQ::ENGENHARIAS::ENGENHARIA MECANICA |
dc.subject.eng.fl_str_mv |
Micromachining Duplex stainless steel Wear Burr Surface quality |
dc.subject.cnpq.fl_str_mv |
CNPQ::ENGENHARIAS::ENGENHARIA MECANICA |
description |
The development of technology in many areas has increased the demand for production of components with small dimensions. In this scenario, the micro machining has emerged as an important tool because it is a process with great precision in producing micro-scaled components. This technique allows processing of composites, polymers, ceramics, and metallic alloys, including stainless steels. Stainless steels are popular due to their chemical characteristics like high resistance to corrosion and oxidation. The main goal of this work is the study of phenomena involved in micromilling a UNS S32205 duplex stainless steel, using TiN coated carbide tools. Accordingly, it was investigated tool wear type and mechanism, burr formation and machined surface quality. For this purpose, this work was carried out with a 4-axis CNC micromill machine tool using 0.381 mm diameter tools. Pre-tests were carried out in order to select the most appropriate cutting condition for further analysis. Tool wear, machined surface and burr were examined in a scanning electron microscope. The burr height and roughness were measured by a profilometer. The results show that the major forms of wear are nose and flank wear, with predominance of the adhesion wear mechanism. The wear land as a function of machined length showed similar behavior to macro machining operations with three well defined regions of different wear rates. Taylor s equation was obtained and the coefficients are similar to those obtained in conventional operations. It was observed that the top burr presented the most significant size. The results obtained for the surface roughness, Ra, varied in the range of 0.131 to 0.469 μm. |
publishDate |
2016 |
dc.date.accessioned.fl_str_mv |
2016-06-22T18:41:10Z |
dc.date.available.fl_str_mv |
2016-06-07 2016-06-22T18:41:10Z |
dc.date.issued.fl_str_mv |
2016-03-01 |
dc.type.status.fl_str_mv |
info:eu-repo/semantics/publishedVersion |
dc.type.driver.fl_str_mv |
info:eu-repo/semantics/masterThesis |
format |
masterThesis |
status_str |
publishedVersion |
dc.identifier.citation.fl_str_mv |
SANTOS, Aline Gonçalves dos. Micromilling UNS S32205 duplex stainless steel using titanium nitride coated carbide tools. 2016. 107 f. Dissertação (Mestrado em Engenharias) - Universidade Federal de Uberlândia, Uberlândia, 2016. DOI http://doi.org/10.14393/ufu.di.2016.201 |
dc.identifier.uri.fl_str_mv |
https://repositorio.ufu.br/handle/123456789/15018 |
dc.identifier.doi.pt_BR.fl_str_mv |
http://doi.org/10.14393/ufu.di.2016.201 |
identifier_str_mv |
SANTOS, Aline Gonçalves dos. Micromilling UNS S32205 duplex stainless steel using titanium nitride coated carbide tools. 2016. 107 f. Dissertação (Mestrado em Engenharias) - Universidade Federal de Uberlândia, Uberlândia, 2016. DOI http://doi.org/10.14393/ufu.di.2016.201 |
url |
https://repositorio.ufu.br/handle/123456789/15018 http://doi.org/10.14393/ufu.di.2016.201 |
dc.language.iso.fl_str_mv |
por |
language |
por |
dc.rights.driver.fl_str_mv |
info:eu-repo/semantics/openAccess |
eu_rights_str_mv |
openAccess |
dc.format.none.fl_str_mv |
application/pdf |
dc.publisher.none.fl_str_mv |
Universidade Federal de Uberlândia |
dc.publisher.program.fl_str_mv |
Programa de Pós-graduação em Engenharia Mecânica |
dc.publisher.initials.fl_str_mv |
UFU |
dc.publisher.country.fl_str_mv |
BR |
dc.publisher.department.fl_str_mv |
Engenharias |
publisher.none.fl_str_mv |
Universidade Federal de Uberlândia |
dc.source.none.fl_str_mv |
reponame:Repositório Institucional da UFU instname:Universidade Federal de Uberlândia (UFU) instacron:UFU |
instname_str |
Universidade Federal de Uberlândia (UFU) |
instacron_str |
UFU |
institution |
UFU |
reponame_str |
Repositório Institucional da UFU |
collection |
Repositório Institucional da UFU |
bitstream.url.fl_str_mv |
https://repositorio.ufu.br/bitstream/123456789/15018/3/MicrofresamentoAcoInoxidavel.pdf.jpg https://repositorio.ufu.br/bitstream/123456789/15018/1/MicrofresamentoAcoInoxidavel.pdf https://repositorio.ufu.br/bitstream/123456789/15018/2/MicrofresamentoAcoInoxidavel.pdf.txt |
bitstream.checksum.fl_str_mv |
37462dd94b18846e6b4fb1e111a59917 a6f1cc49155ec28e204e61d3e908d44e 690f570c386d3dfd6234d047943ee639 |
bitstream.checksumAlgorithm.fl_str_mv |
MD5 MD5 MD5 |
repository.name.fl_str_mv |
Repositório Institucional da UFU - Universidade Federal de Uberlândia (UFU) |
repository.mail.fl_str_mv |
diinf@dirbi.ufu.br |
_version_ |
1802110445552664576 |