Estudo tribológico da liga de alumínio SAE 305 com tratamentos superficiais : anodização e revestimento carbono tipo diamante

Detalhes bibliográficos
Autor(a) principal: Pires, Michel Sullivan Teixeira
Data de Publicação: 2018
Tipo de documento: Tese
Idioma: por
Título da fonte: Repositório Institucional da UnB
Texto Completo: http://repositorio.unb.br/handle/10482/34525
Resumo: Tese (doutorado)—Universidade de Brasília, Faculdade de Tecnologia, Departamento de Engenharia Mecânica, 2018.
id UNB_d7435e077b6a1f67857335ca1f0f4f55
oai_identifier_str oai:repositorio.unb.br:10482/34525
network_acronym_str UNB
network_name_str Repositório Institucional da UnB
repository_id_str
spelling Estudo tribológico da liga de alumínio SAE 305 com tratamentos superficiais : anodização e revestimento carbono tipo diamanteCabos condutoresLigas de alumínioAnodizaçãoResistência de materiaisDesgaste microabrasivoTese (doutorado)—Universidade de Brasília, Faculdade de Tecnologia, Departamento de Engenharia Mecânica, 2018.Ligas de alumínio são amplamente empregadas em diversas aplicações industriais, como por exemplo em sistemas de transmissão de energia elétrica. Nesse sistema, e mais especificamente na montagem grampo de suspensão/cabo condutor, as falhas podem ocorrer nas camadas internas do cabo ou na região de interface deste com a superfície do grampo de sustentação. Este trabalho explora este segundo tipo de falha. O presente trabalho apresenta estudos sobre o comportamento de um recobrimento de Diamond-Like Carbon (DLC) e de um tratamento por anodização quando aplicados a liga de alumínio SAE 305 (material empregado na confecção de grampos de sustentação dos cabos condutores). Estes tratamentos superficiais foram selecionados com base na sua ótima relação custo/benefício e boa resistência mecânica. Para analisar a resistência mecânica dos revestimentos, foram realizados os ensaios: de rugosidade, de dureza, de desgaste microabrasivos, de desgaste por fricção, e em uma bancada de ensaios de cabos condutores de energia em escala real. Os variados tipos de ensaios de desgaste tem por objetivo avaliar a eficácia contra o desgaste dos tratamentos superficiais sob diferentes condições tribológicas e de carregamentos, e analisar a dinâmica das partículas abrasivas nos tribossistemas. Nos ensaios microabrasivos do tipo “esfera livre”, um total de nove amostras, sendo três de cada grupo de material, foram testadas. Comparativamente ao alumínio sem revestimento, o DLC aumentou a resistência ao desgaste do substrato, enquanto que a anodização reduziu a resistência. Análises microestruturais permitiram concluir que a degradação superficial decorrente do processo de anodização e os mecanismos de desgaste foram os fatores principais pelo comportamento das amostras anodizadas. Os ensaios de desgaste por fricção foram realizados com um tribômetro convencional, na configuração esfera-sobre-plano, e do tipo deslizamento recíproco. Para todos os ensaios foi adotada uma carga normal de contato de 10 N, faixa de deslocamento de 4 mm, frequência de oscilação linear de 8 Hz, e dois tempos de duração de ensaio (30 minutos e 60 minutos). Os resultados obtidos mostram que as amostras anodizadas tiveram suave aumento na resistência ao desgaste em relação às amostras sem revestimento, enquanto que as amostras de DLC apresentaram significativo aumento na resistência. Os comportamentos das amostras foram discutidos com base em análise microestrutural e dos mecanismos de desgaste. Os ensaios com cabos condutores foram conduzidos com o intuito de avaliar o impacto da anodização e do DLC na vida útil desses elementos. Para tal, foram realizados 16 ensaios adotando-se a montagem grampos de suspensão revestidos/cabo condutor TERN. Três valores de deslocamento vertical (Yb) do condutor foram adotados: 0,84; 0,93 e 1,02 mm. Para todos os ensaios foi adotado um parâmetro H/w igual a 2144 m. Os resultados obtidos mostraram que ambos os tratamentos superficiais adotados não proporcionaram, de forma conclusiva, um aumento na vida útil do condutor. Análises morfológicas e de EDX das superfícies dos grampos tratados mostraram a formação de tribocamada de óxido de alumínio na interface de contato cabo-grampo. Os resultados reportados no presente trabalho demonstraram que o DLC contribuiu de forma significativa para o aumento da resistência ao desgaste dos espécimes nos ensaios microabrasivos e de desgaste por fricção. A expectativa para o aumento da vida útil do condutor utilizado em conjunto com grampos revestidos com DLC não foi observada de forma consistente. Dessa forma, trabalhos futuros são necessários para uma melhor investigação da contribuição do DLC para essa aplicação.Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES).Aluminum alloys are widely used in many industrial applications, such as in electric power transmission systems. In this application, and more specifically in an overhead conductor/clamping assembly, failures may occur in the inner layer of the conductor, or in the conductor/clamping interface. This work investigates the second type of failure. This work presents studies on the behavior of a Diamond-Like Carbon (DLC) coating and an anodization process when applied to aluminum alloy SAE 305 (material of the suspension clamp). These surfaces were selected based on their excellent cost/benefit ratio and good mechanical resistance. In order to evaluate the mechanical strength of the surfaces, the following tests were performed: roughness, hardness, micro-abrasive wear and friction wear. Moreover, experimental tests have been conducted on a real scale testing system. The wear tests aim to evaluate the wear resistance of the surface treatments under different tribological and loading conditions, besides analyzing the dynamics of the abrasive particles in the tribosystems. Micro-abrasive wear tests, using a free-ball system device, were carried-out on three specimens of each surface condition. Compared to the uncoated specimen, the DLC improved the wear resistance of the substrate, while anodization reduced the wear resistance. Microstructural analysis led to surface degradation due to the anodization process and wear mechanisms as the main factors of the anodized specimen behavior. Reciprocating sliding wear tests using a sphere-on-flat configuration were performed in a conventional tribometer. For all tribometer tests the following parameters were adopted: a normal load of 10 N; a stroke of 4 mm; a frequency of 8 Hz and two time durations (30 minutes and 60 minutes). In comparison to the untreated aluminum alloy, the DLC coating showed a significantly improved in wear resistance, whereas the anodization process showed a small improvement. The wear behavior of the specimens are discussed in terms of microstructural analysis and wear mechanisms. In addition, tests with overhead conductors were performed to evaluate the impact of anodization and DLC on the conductor lifetime. A total of 16 tests has been conducted on TERN conductor samples attached to coated suspension clamps. Tests were performed in three vertical displacements levels: 0.84, 0.93 and 1,02 mm. The H/w parameter was kept at 2144 m in all tests. The results showed that the investigated surface treatments did not provide a significant increase on the conductor lifetime. Morphological and EDX analysis of the clamping samples showed a tribolayer of aluminum oxide (Al2O3) in the interface of the contact conductor/clamp. The results reported in the present work showed that DLC improve the wear resistance of the specimens in the micro-abrasive and reciprocating sliding wear tests. The improve in conductor lifetime was not observed. Thus, future works are needed to better investigate the contribution of DLC for this application.Faculdade de Tecnologia (FT)Departamento de Engenharia Mecânica (FT ENM)Programa de Pós-Graduação em Ciências MecânicasDoca, Thiago de Carvalho RodriguesSteier, Volker FrancoPires, Michel Sullivan Teixeira2019-04-29T21:49:45Z2019-04-29T21:49:45Z2019-04-292018-10-30info:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/doctoralThesisapplication/pdfPIRES, Michel Sullivan Teixeira. Estudo tribológico da liga de alumínio SAE 305 com tratamentos superficiais: anodização e revestimento carbono tipo diamante. 2018. xvii, 130 f., il. Tese (Doutorado em Ciências Mecânicas)—Universidade de Brasília, Brasília, 2018.http://repositorio.unb.br/handle/10482/34525A concessão da licença deste item refere-se ao termo de autorização impresso assinado pelo autor com as seguintes condições: Na qualidade de titular dos direitos de autor da publicação, autorizo a Universidade de Brasília e o IBICT a disponibilizar por meio dos sites www.bce.unb.br, www.ibict.br, http://hercules.vtls.com/cgi-bin/ndltd/chameleon?lng=pt&skin=ndltd sem ressarcimento dos direitos autorais, de acordo com a Lei nº 9610/98, o texto integral da obra disponibilizada, conforme permissões assinaladas, para fins de leitura, impressão e/ou download, a título de divulgação da produção científica brasileira, a partir desta data.info:eu-repo/semantics/openAccessporreponame:Repositório Institucional da UnBinstname:Universidade de Brasília (UnB)instacron:UNB2024-02-08T21:43:33Zoai:repositorio.unb.br:10482/34525Repositório InstitucionalPUBhttps://repositorio.unb.br/oai/requestrepositorio@unb.bropendoar:2024-02-08T21:43:33Repositório Institucional da UnB - Universidade de Brasília (UnB)false
dc.title.none.fl_str_mv Estudo tribológico da liga de alumínio SAE 305 com tratamentos superficiais : anodização e revestimento carbono tipo diamante
title Estudo tribológico da liga de alumínio SAE 305 com tratamentos superficiais : anodização e revestimento carbono tipo diamante
spellingShingle Estudo tribológico da liga de alumínio SAE 305 com tratamentos superficiais : anodização e revestimento carbono tipo diamante
Pires, Michel Sullivan Teixeira
Cabos condutores
Ligas de alumínio
Anodização
Resistência de materiais
Desgaste microabrasivo
title_short Estudo tribológico da liga de alumínio SAE 305 com tratamentos superficiais : anodização e revestimento carbono tipo diamante
title_full Estudo tribológico da liga de alumínio SAE 305 com tratamentos superficiais : anodização e revestimento carbono tipo diamante
title_fullStr Estudo tribológico da liga de alumínio SAE 305 com tratamentos superficiais : anodização e revestimento carbono tipo diamante
title_full_unstemmed Estudo tribológico da liga de alumínio SAE 305 com tratamentos superficiais : anodização e revestimento carbono tipo diamante
title_sort Estudo tribológico da liga de alumínio SAE 305 com tratamentos superficiais : anodização e revestimento carbono tipo diamante
author Pires, Michel Sullivan Teixeira
author_facet Pires, Michel Sullivan Teixeira
author_role author
dc.contributor.none.fl_str_mv Doca, Thiago de Carvalho Rodrigues
Steier, Volker Franco
dc.contributor.author.fl_str_mv Pires, Michel Sullivan Teixeira
dc.subject.por.fl_str_mv Cabos condutores
Ligas de alumínio
Anodização
Resistência de materiais
Desgaste microabrasivo
topic Cabos condutores
Ligas de alumínio
Anodização
Resistência de materiais
Desgaste microabrasivo
description Tese (doutorado)—Universidade de Brasília, Faculdade de Tecnologia, Departamento de Engenharia Mecânica, 2018.
publishDate 2018
dc.date.none.fl_str_mv 2018-10-30
2019-04-29T21:49:45Z
2019-04-29T21:49:45Z
2019-04-29
dc.type.status.fl_str_mv info:eu-repo/semantics/publishedVersion
dc.type.driver.fl_str_mv info:eu-repo/semantics/doctoralThesis
format doctoralThesis
status_str publishedVersion
dc.identifier.uri.fl_str_mv PIRES, Michel Sullivan Teixeira. Estudo tribológico da liga de alumínio SAE 305 com tratamentos superficiais: anodização e revestimento carbono tipo diamante. 2018. xvii, 130 f., il. Tese (Doutorado em Ciências Mecânicas)—Universidade de Brasília, Brasília, 2018.
http://repositorio.unb.br/handle/10482/34525
identifier_str_mv PIRES, Michel Sullivan Teixeira. Estudo tribológico da liga de alumínio SAE 305 com tratamentos superficiais: anodização e revestimento carbono tipo diamante. 2018. xvii, 130 f., il. Tese (Doutorado em Ciências Mecânicas)—Universidade de Brasília, Brasília, 2018.
url http://repositorio.unb.br/handle/10482/34525
dc.language.iso.fl_str_mv por
language por
dc.rights.driver.fl_str_mv info:eu-repo/semantics/openAccess
eu_rights_str_mv openAccess
dc.format.none.fl_str_mv application/pdf
dc.source.none.fl_str_mv reponame:Repositório Institucional da UnB
instname:Universidade de Brasília (UnB)
instacron:UNB
instname_str Universidade de Brasília (UnB)
instacron_str UNB
institution UNB
reponame_str Repositório Institucional da UnB
collection Repositório Institucional da UnB
repository.name.fl_str_mv Repositório Institucional da UnB - Universidade de Brasília (UnB)
repository.mail.fl_str_mv repositorio@unb.br
_version_ 1814508356990140416

Registros relacionados