Surface roughness and hardness of yttria stabilized zirconia (Y-TZP) after 10 years of simulated brushing

• Autor(a) principal: Candido,Lucas Miguel
• Data de Publicação: 2014
• Outros Autores: Fais,Laiza Maria Grassi, Reis,José Mauricio dos Santos Nunes, Pinelli,Ligia Antunes Pereira
• Tipo de documento: Artigo
• Idioma: eng
• Título da fonte: Revista de Odontologia da UNESP
• Texto Completo: http://old.scielo.br/scielo.php?script=sci_arttext&pid=S1807-25772014000600379
• topic: Hardness; toothbrushing; ceramics

Introduction:The Y-TZP zirconia used for prosthetic infrastructure, in some clinical situations, can be exposed to the oral environment. In these situations, a polished surface without changes is extremely important.Objective:The aim of this study was to evaluate the mean roughness (Ra) and Vickers hardness of Y-TZP zirconia (Lava™) after simulating ten years of brushing.Material and method:Thirty-six Y-TZP bar-shaped specimens (20mm X 4mm X 1.2mm) were divided into three groups: storage in distilled water (DW, n=12, control); brushing with distilled water (BDW, n=12) and brushing with distilled water and fluoride toothpaste (BFT, n=12). Brushing was performed using a brushing machine with a soft-bristled toothbrush, simulating 10 years of brushing (878.400 cycles, 100gf). The mean roughness (Ra in μm) and Vickers hardness (VHN) of all specimens were measured twice: before and after the experimental treatment, in profilometer and microhardness tester (500gf, 30 seconds), respectively. Data were analyzed using the two-way ANOVA test (α = 0.05).Result:The interaction between groups was not significant for roughness (p = 0.701) nor for hardness (p = 0.928). The final averages for Ra (μm) were equal to: DW - 0.63; BDW - 0.64; and, BFT - 0.68. The final averages for Vickers hardness (VHN) were: DW - 1301.16; BDW - 1316.60; and, BFT - 1299.58.Conclusion:It was concluded that the brushing with distilled or fluoridated toothpaste was not able to change the roughness and hardness of Y-TZP zirconia used in this study.