Removable partial or complete dentures exposed to beverages and mouthwashes: evaluation of microhardness and roughness

• Autor(a) principal: Feitosa,Fernanda Alves
• Data de Publicação: 2015
• Outros Autores: Reggiani,Mateus Guimarães Lage, Araújo,Rodrigo Máximo de
• Tipo de documento: Artigo
• Idioma: eng
• Título da fonte: Revista de Odontologia da UNESP
• Texto Completo: http://old.scielo.br/scielo.php?script=sci_arttext&pid=S1807-25772015000400189
• topic: Dental prosthesis; denture bases; acrylic resin; mouthwashes

AbstractPurposeTo evaluate microhardness and roughness of denture base polymethylmethacrylate resinn exposed to acid beverages and mouthwashes.Material and methodRectangular samples (n=80) were prepared from poly (methyl methacrylate) (PMMA). They were divided into 8 groups and had the initial microhardness and Knoop roughness measured. Samples of each group were immersed for 10 min into a test solution (coffee, lemon juice, chlorhexidine gluconate, red wine, cola-based soft drink, vinegar or antiseptic with and without alcohol) and after stored in artificial saliva for 23 h and 50 min, completing a period of 24 h. This procedure was performed for 14 consecutive days and after this period the microhardness and surface roughness measurements were made again. Data were statistically analyzed using ANOVA non parametric, Kruskal-Walis and the Dunn´s test for microhardness and the t-Student and ANOVA for roughness.ResultFor microhardness there were found statistically significant differences among the chlorhexidine gluconate solution, antiseptic without alcohol and cola-based soft drink. For roughness was observed that the mean values between the initial period and after immersion in the test products differed statistically in all groups, without difference among groups.ConclusionThe microhardness of poly(methyl methacrylate) was affected by continue exposition to chlorhexidine gluconate, antiseptic without alcohol and cola-based soft drink. The roughness of poly(methyl methacrylate) is negatively influenced by the exposure to all tested products. It may be concluded that both, microhardness and roughness, were affected by the treatments.