Estudo da qualidade da fundição do titanio comercialmente puro e da união soldada a laser em estruturas de Ti cp e em liga de Ti-6AI-4V

Detalhes bibliográficos
Autor(a) principal: Nuñez-Pantoja, Juliana Maria Costa, 1984-
Data de Publicação: 2009
Tipo de documento: Dissertação
Idioma: por
Título da fonte: Biblioteca Digital de Teses e Dissertações da Universidade Estadual de Campinas (UNICAMP)
Texto Completo: https://hdl.handle.net/20.500.12733/1609136
Resumo: Orientador: Marcelo Ferraz Mesquita
id UNICAMP-30_5c216071b3cf0cc1ffbe6c925d6d0b2b
oai_identifier_str oai::440198
network_acronym_str UNICAMP-30
network_name_str Biblioteca Digital de Teses e Dissertações da Universidade Estadual de Campinas (UNICAMP)
repository_id_str
spelling Estudo da qualidade da fundição do titanio comercialmente puro e da união soldada a laser em estruturas de Ti cp e em liga de Ti-6AI-4VAnalysis of titanium casting's situation and of laser-weld joint's quality made in Ti cp and Ti-6AI-4V structuresSoldagem em odontologiaDentes - RadiografiaPróteses e implantesFadigaDental solderingDental radiographyProstheses and implantsFatigueOrientador: Marcelo Ferraz MesquitaDissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de PiracicabaResumo: O objetivo desse estudo foi: 1) Examinar por meio de radiografias, a incidência de porosidade interna em estruturas fundidas em titânio comercialmente puro, com diferentes diâmetros de secção transversal; 2) Analisar essa incidência em uniões soldadas a laser, com diferentes distâncias de soldagens, em espécimes de Ti cp e Ti-6Al-4V, variando o diâmetro da secção transversal; 3) Avaliar a resistência à fadiga dessas uniões e correlacionar esses achados com os resultados das analises radiográficas das uniões. Para a primeira análise, 60 halteres (n=20) com diâmetro de 1,5; 2,0 e 3,5 mm de secção transversal foram fundidos em Ti cp, por meio da técnica da cera perdida utilizando-se o sistema Rematitan. Os halteres receberam acabamento e polimento e foram submetidos à análise radiográfica (90 KV, 15 mA, 0,6 segundos e 10 a 13 mm de distância) com filme periapical. As radiografias foram analisadas visualmente quanto à presença de porosidade interna em toda a extensão dos halteres, e apenas na porção do diâmetro central. Os resultados foram submetidos ao teste Qui-quadrado (5%). Foi possível visualizar essas porosidades na maioria (91,7%) dos espécimes fundidos, especialmente nos de diâmetros mais delgados. Para a análise radiográfica das uniões soldadas a laser em espécimes de Ti-6Al-4V, 60 halteres com as mesmas dimensões foram usinados em liga de Ti-6Al-4V. Os halteres foram seccionados e soldados utilizando duas distâncias de soldagem (0,0 e 0,6 mm). O cruzamento das variáveis (distância e diâmetro) gerou seis grupos (n=10). A soldagem a laser foi realizada utilizando-se 360V/8ms (1,5 e 2,0 mm) e 380V/9ms (3,5 mm), com foco e freqüência regulados em zero. As uniões receberam acabamento e polimento e foram submetidas à idêntica análise radiográfica, verificando-se a presença de porosidades internas nas uniões. Os resultados, analisados pelo teste Qui-quadrado (5%), permitiram afirmar que é possível visualizar porosidade nas uniões analisadas. Para halteres de 1,5 mm, a incidência foi maior quando a distância entre as partes soldadas era 0,6 mm; ao contrário, para espécimes de 3,5 mm, essa incidência nessa distância foi menor. Para as análises radiográficas das uniões no Ti cp, 60 halteres fundidos e isentos de porosidade interna na região do diâmetro central, com as mesmas dimensões, foram seccionados, soldados e analisados da mesma maneira que para os espécimes de Ti-6Al-4V, sendo possível visualizar poros nas uniões. Em espécimes delgados (1,5 e 2,0 mm), a incidência de porosidade é maior quando a abertura da junta é maior. Entretanto, para espécimes de 3,5 mm a incidência é alta para ambas as distâncias de soldagem, sem diferença estatística. Para o estudo de resistência à fadiga das uniões em Ti-6Al-4V, os mesmos espécimes soldados que foram utilizados no segundo estudo, associados a espécimes intactos formaram 9 grupos (n=10). Esses espécimes foram submetidos a ensaios de ciclagem mecânica e o número de ciclos resistidos até a fratura foi registrado. A superfície de fratura foi examinada por meio de microscópio eletrônico de varredura (MEV). Os testes de Kruskal-Wallis e Dunn (5%) indicaram que o número de ciclos necessários para a fratura foi menor para todos os espécimes com distância de 0,6 mm, e para os espécimes de 3,5 mm distância 0,0 mm. O coeficiente de Spearman (5%) indicou correlação negativa entre número de ciclos e presença de porosidade nas radiografias. Finalmente, para a análise de resistência à fadiga das uniões no Ti cp, os mesmos halteres soldados do terceiro estudo associados a halteres intactos foram submetidos a similares ensaios mecânicos que os realizados no quarto estudo. Os números de ciclos necessários para a fratura foram registrados e a superfície fraturada, examinada igualmente, podendo-se tecer conclusões similares. Assim, concluiu-se que a qualidade das uniões é melhor quando espécimes mais delgados são soldados com justaposição das partes; e que a análise radiográfica é eficiente para se checar a presença de porosidades internas em espécimes fundidos e em uniões soldadas a laser.Abstract: soldados e analisados da mesma maneira que para os espécimes de Ti-6Al-4V, sendo possível visualizar poros nas uniões. Em espécimes delgados (1,5 e 2,0 mm), a incidência de porosidade é maior quando a abertura da junta é maior. Entretanto, para espécimes de 3,5 mm a incidência é alta para ambas as distâncias de soldagem, sem diferença estatística. Para o estudo de resistência à fadiga das uniões em Ti-6Al-4V, os mesmos espécimes soldados que foram utilizados no segundo estudo, associados a espécimes intactos formaram 9 grupos (n=10). Esses espécimes foram submetidos a ensaios de ciclagem mecânica e o número de ciclos resistidos até a fratura foi registrado. A superfície de fratura foi examinada por meio de microscópio eletrônico de varredura (MEV). Os testes de Kruskal-Wallis e Dunn (5%) indicaram que o número de ciclos necessários para a fratura foi menor para todos os espécimes com distância de 0,6 mm, e para os espécimes de 3,5 mm distância 0,0 mm. O coeficiente de Spearman (5%) indicou correlação negativa entre número de ciclos e presença de porosidade nas radiografias. Finalmente, para a análise de resistência à fadiga das uniões no Ti cp, os mesmos halteres soldados do terceiro estudo associados a halteres intactos foram submetidos a similares ensaios mecânicos que os realizados no quarto estudo. Os números de ciclos necessários para a fratura foram registrados e a superfície fraturada, examinada igualmente, podendo-se tecer conclusões similares. Assim, concluiu-se que a qualidade das uniões é melhor quando espécimes mais delgados são soldados com justaposição das partes; e que a análise radiográfica é eficiente para se checar a presença de porosidades internas em espécimes fundidos e em uniões soldadas a laser. specimens (1.5 and 2.0 mm), the porosity incidence is higher when the joint distance is larger. However, in 3.5 mm specimens, the incidence is high for both joint openings, without statistical difference. To Ti-6Al-4V joints fatigue strength study, the same laser-welded specimens analyzed in second study associated with the intact specimens made a total of 9 groups (n=10). These specimens were submitted to mechanical cyclic tests, and the number of cycles until failure was recorded. The fracture surface was examined with a scanning electron microscope (SEM). Kruskal-Wallis and Dunn test (5%) indicated that the number of cycles required for fracture was lower for all the diameters with joint openings of 0.6 mm, and for 3.5 mm diameter for the 0.0 mm joint openings. The Spearman correlation coefficient (5%) indicated a negative correlation between number of cycles and presence of porosity in radiographies. To CP Ti joints fatigue strength test, the last study, the same laser-welded specimens analyzed in third study associated with the intact specimens were submitted to similar mechanical cyclic test than fourth study. The number of cycles until failure was either recorded and the fracture surface was examined the same way. Conclusions can be weaved similar the anterior study. Within the limitations of these studies, it could be concluded that joints quality is better when thin specimens are welded with no distance among welding parts; and that radiography analyzes are efficient to check internal porosity in casted specimens and in laser-welded joints.MestradoPrótese DentalMestre em Clínica Odontológica[s.n.]Mesquita, Marcelo Ferraz, 1967-Vaz, Luiz GeraldoHenriques, Guilherme Elias PessanhaUniversidade Estadual de Campinas (UNICAMP). Faculdade de Odontologia de Piracicaba (FOP)Programa de Pós-Graduação em Clínica OdontológicaUNIVERSIDADE ESTADUAL DE CAMPINASNuñez-Pantoja, Juliana Maria Costa, 1984-2009info:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/masterThesisapplication/pdf116 p. : il.https://hdl.handle.net/20.500.12733/1609136NUÑEZ-PANTOJA, Juliana Maria Costa. Estudo da qualidade da fundição do titanio comercialmente puro e da união soldada a laser em estruturas de Ti cp e em liga de Ti-6AI-4V. 2009. 116 p. Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba, Piracicaba, SP. Disponível em: https://hdl.handle.net/20.500.12733/1609136. Acesso em: 2 set. 2024.https://repositorio.unicamp.br/acervo/detalhe/440198porreponame:Biblioteca Digital de Teses e Dissertações da Universidade Estadual de Campinas (UNICAMP)instname:Universidade Estadual de Campinas (UNICAMP)instacron:UNICAMPinfo:eu-repo/semantics/openAccess2017-02-18T05:29:10Zoai::440198Biblioteca Digital de Teses e DissertaçõesPUBhttp://repositorio.unicamp.br/oai/tese/oai.aspsbubd@unicamp.bropendoar:2017-02-18T05:29:10Biblioteca Digital de Teses e Dissertações da Universidade Estadual de Campinas (UNICAMP) - Universidade Estadual de Campinas (UNICAMP)false
dc.title.none.fl_str_mv Estudo da qualidade da fundição do titanio comercialmente puro e da união soldada a laser em estruturas de Ti cp e em liga de Ti-6AI-4V
Analysis of titanium casting's situation and of laser-weld joint's quality made in Ti cp and Ti-6AI-4V structures
title Estudo da qualidade da fundição do titanio comercialmente puro e da união soldada a laser em estruturas de Ti cp e em liga de Ti-6AI-4V
spellingShingle Estudo da qualidade da fundição do titanio comercialmente puro e da união soldada a laser em estruturas de Ti cp e em liga de Ti-6AI-4V
Nuñez-Pantoja, Juliana Maria Costa, 1984-
Soldagem em odontologia
Dentes - Radiografia
Próteses e implantes
Fadiga
Dental soldering
Dental radiography
Prostheses and implants
Fatigue
title_short Estudo da qualidade da fundição do titanio comercialmente puro e da união soldada a laser em estruturas de Ti cp e em liga de Ti-6AI-4V
title_full Estudo da qualidade da fundição do titanio comercialmente puro e da união soldada a laser em estruturas de Ti cp e em liga de Ti-6AI-4V
title_fullStr Estudo da qualidade da fundição do titanio comercialmente puro e da união soldada a laser em estruturas de Ti cp e em liga de Ti-6AI-4V
title_full_unstemmed Estudo da qualidade da fundição do titanio comercialmente puro e da união soldada a laser em estruturas de Ti cp e em liga de Ti-6AI-4V
title_sort Estudo da qualidade da fundição do titanio comercialmente puro e da união soldada a laser em estruturas de Ti cp e em liga de Ti-6AI-4V
author Nuñez-Pantoja, Juliana Maria Costa, 1984-
author_facet Nuñez-Pantoja, Juliana Maria Costa, 1984-
author_role author
dc.contributor.none.fl_str_mv Mesquita, Marcelo Ferraz, 1967-
Vaz, Luiz Geraldo
Henriques, Guilherme Elias Pessanha
Universidade Estadual de Campinas (UNICAMP). Faculdade de Odontologia de Piracicaba (FOP)
Programa de Pós-Graduação em Clínica Odontológica
UNIVERSIDADE ESTADUAL DE CAMPINAS
dc.contributor.author.fl_str_mv Nuñez-Pantoja, Juliana Maria Costa, 1984-
dc.subject.por.fl_str_mv Soldagem em odontologia
Dentes - Radiografia
Próteses e implantes
Fadiga
Dental soldering
Dental radiography
Prostheses and implants
Fatigue
topic Soldagem em odontologia
Dentes - Radiografia
Próteses e implantes
Fadiga
Dental soldering
Dental radiography
Prostheses and implants
Fatigue
description Orientador: Marcelo Ferraz Mesquita
publishDate 2009
dc.date.none.fl_str_mv 2009
dc.type.status.fl_str_mv info:eu-repo/semantics/publishedVersion
dc.type.driver.fl_str_mv info:eu-repo/semantics/masterThesis
format masterThesis
status_str publishedVersion
dc.identifier.uri.fl_str_mv https://hdl.handle.net/20.500.12733/1609136
NUÑEZ-PANTOJA, Juliana Maria Costa. Estudo da qualidade da fundição do titanio comercialmente puro e da união soldada a laser em estruturas de Ti cp e em liga de Ti-6AI-4V. 2009. 116 p. Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba, Piracicaba, SP. Disponível em: https://hdl.handle.net/20.500.12733/1609136. Acesso em: 2 set. 2024.
url https://hdl.handle.net/20.500.12733/1609136
identifier_str_mv NUÑEZ-PANTOJA, Juliana Maria Costa. Estudo da qualidade da fundição do titanio comercialmente puro e da união soldada a laser em estruturas de Ti cp e em liga de Ti-6AI-4V. 2009. 116 p. Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba, Piracicaba, SP. Disponível em: https://hdl.handle.net/20.500.12733/1609136. Acesso em: 2 set. 2024.
dc.language.iso.fl_str_mv por
language por
dc.relation.none.fl_str_mv https://repositorio.unicamp.br/acervo/detalhe/440198
dc.rights.driver.fl_str_mv info:eu-repo/semantics/openAccess
eu_rights_str_mv openAccess
dc.format.none.fl_str_mv application/pdf
116 p. : il.
dc.publisher.none.fl_str_mv [s.n.]
publisher.none.fl_str_mv [s.n.]
dc.source.none.fl_str_mv reponame:Biblioteca Digital de Teses e Dissertações da Universidade Estadual de Campinas (UNICAMP)
instname:Universidade Estadual de Campinas (UNICAMP)
instacron:UNICAMP
instname_str Universidade Estadual de Campinas (UNICAMP)
instacron_str UNICAMP
institution UNICAMP
reponame_str Biblioteca Digital de Teses e Dissertações da Universidade Estadual de Campinas (UNICAMP)
collection Biblioteca Digital de Teses e Dissertações da Universidade Estadual de Campinas (UNICAMP)
repository.name.fl_str_mv Biblioteca Digital de Teses e Dissertações da Universidade Estadual de Campinas (UNICAMP) - Universidade Estadual de Campinas (UNICAMP)
repository.mail.fl_str_mv sbubd@unicamp.br
_version_ 1809189004028936192

Registros relacionados