Avaliação clinica e laboratorial da colagem de braquetes metalicos com compositos ortodonticos

Detalhes bibliográficos
Autor(a) principal: Romano, Fabio Lourenço
Data de Publicação: 2009
Tipo de documento: Tese
Idioma: por
Título da fonte: Biblioteca Digital de Teses e Dissertações da Universidade Estadual de Campinas (UNICAMP)
Texto Completo: https://hdl.handle.net/20.500.12733/1609765
Resumo: Orientadores: Maria Beatriz Borges de Araujo Magnani, Lourenço Correr Sobrinho
id UNICAMP-30_96aabe73b84af75c0d6ed7c9734187cd
oai_identifier_str oai::448096
network_acronym_str UNICAMP-30
network_name_str Biblioteca Digital de Teses e Dissertações da Universidade Estadual de Campinas (UNICAMP)
repository_id_str
spelling Avaliação clinica e laboratorial da colagem de braquetes metalicos com compositos ortodonticosClinical and laboratory evaluation of metallic brackets bonded with orthodontic compositesResinas compostasResistência ao cisalhamentoBraquetes ortodônticosOrtodontiaComposite resinsShear strenghtOrthodontic BracketsOrthodonticsOrientadores: Maria Beatriz Borges de Araujo Magnani, Lourenço Correr SobrinhoTese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de PiracicabaResumo: O objetivo neste estudo foi avaliar clinicamente e em laboratório, a taxa de descolagem e a resistência ao cisalhamento de bráquetes metálicos colados com compósitos ortodônticos. O experimento clínico consistiu de 20 pacientes (10,5-15,1 anos de idade), que procuraram tratamento ortodôntico corretivo. Nestes pacientes foram colados bráquetes de 2° pré-molar a 2° pré-molar no arco superior e inferior com os sistemas adesivos: Concise Ortodôntico, Transbond XT convencional, Transbond XT sem agente de união e Transbond XT em esmalte preparado com ácido-primer Transbond Plus Self Etching Primer (TPSEP). Todos os sistemas foram utilizados em todos os pacientes, em rodízio pelos quadrantes, sendo que, a mesma sequência de colagem se repetiu em cada cinco pacientes. Arcos iniciais foram inseridos uma semana após a colagem dos bráquetes. Os pacientes foram avaliados durante seis meses para quantificar o número de bráquetes descolados. Ao final do período de observação ocorreram 8 descolagens com Concise Ortodôntico, 2 com Transbond XT convencional, 9 com Transbond XT sem agente de união e 1 com TPSEP + Transbond XT. Pelo Método de Kaplan-Meier foram encontradas diferenças estatísticas significantes na taxa de descolagem entre os materiais (P=0,0198) e o teste Logrank identificou estas diferenças. O Transbond XT convencional e TPSEP + Transbond XT foram estatisticamente superiores (apresentaram menos descolagens) em relação ao Concise Ortodôntico e Transbond XT sem agente de união (P<0,05). Entre os materiais Transbond XT convencional e TPSEP + Transbond XT não foram encontradas diferenças estatísticas significantes, assim como, entre Concise Ortodôntico e Transbond XT sem agente de união (P>0,05). O experimento laboratorial teve como objetivo avaliar a resistência ao cisalhamento de bráquetes metálicos colados com o novo compósito ortodôntico Transbond Plus Color Change (TPCC, 3M Unitek) em diferentes preparações de esmalte e analisar após a descolagem o Índice de Remanescente de Adesivo (IRA). Foram utilizados 72 pré-molares humanos divididos em seis grupos (n=12). No Grupo 1 (controle) foi utilizado o compósito Transbond XT convencionalmente. Nos demais grupos (2 a 6) utilizou-se o TPCC nas seguintes condições de esmalte: ácido fosfórico e XT primer; ácido-primer TPSEP; somente ácido fosfórico; ácido fosfórico, XT primer e saliva; TPSEP e saliva, respectivamente. Após a colagem dos bráquetes e fotoativação, os corpos de prova foram armazenados em água destilada em estufa a 37°C por 24 horas. Em seguida, os bráquetes foram carregados em máquina Instron à velocidade de 0,5 mm/min. e o IRA avaliado em lupa estereoscópica. Osvalores médios de resistência ao cisalhamento (MPa) foram: Grupo 1- 24,6; Grupo 2-18,7; Grupo 3-17,5; Grupo 4-19,7; Grupo 5-17,5 e Grupo 6-14,8. Os dados foram submetidos à ANOVA e ao teste de Tukey (5%). O Grupo 1 apresentou maior média e diferiu estatisticamente dos grupos 3, 5 e 6 (P<0,05) e sem diferença estatística significante em relação aos grupos 2 e 4 (P>0,05). Entre os grupos 2, 3, 4, 5 e 6 não foram encontradas diferenças estatísticas significantes (P>0,05). A colagem de bráquetes com TPCC apresentou valores comparáveis ao Transbond XT convencional e o tipo de preparo de superfície não influenciou esta adesãoAbstract: The aim of this study was to assess clinically and laboratory the bracket failure rate and shear bond strength of metallic brackets bonded with orthodontic composites. The in vivo study consisted of 20 patients aged between 10.5 to 15.1 years old who had sought corrective orthodontic treatment. Brackets were bonded of the second premolar - second premolar to their upper and lower arches using the adhesive systems: Orthodontic Concise, conventional Transbond XT, Transbond XT without primer, and Transbond XT applied to enamel etched with Transbond Plus Self-etching Primer (TPSEP). All the adhesive systems were used in all patients on a quadrant-rotation basis by repeating the same bonding sequence in every 5 patients. Initial archwires were inserted a week after the brackets bonding. The patients were evaluated during six months in order to quantify the number of brackets failure regarding each adhesive system. At the end of the observation period, 8 brackets failure rates were observed for Orthodontic Concise, 2 for conventional Transbond XT, 9 for Transbond XT without primer, and 1 with Transbond XT + TPSEP. By using the Kaplan-Meier methods, statistically significant differences were found between the materials (p=.0198), and the Logrank test identified these differences. It was observed that conventional Transbond XT and Transbond XT + TPSEP were statistically superior (fewer debonded brackets) compared to Orthodontic Concise and Transbond XT without primer (P<.05). However, no statistically significant differences were found between conventional Transbond XT and TPSEP + Transbond XT as well as between Orthodontic Concise and Transbond XT without primer (P>.05). The in vitro study aimed at assessing the shear bond strength of metallic brackets bonded to different enamel surfaces using the Transbond Plus Color Change composite (TPCC, 3M Unitek) as well as to analyse the Adhesive Remnant Index (ARI). Seventy-two human premolars were used for study, with all samples being divided into six groups (n =12). In Group 1 (control), Transbond XT composite was conventionally used. In other groups (2-6), TPCC was used under the following enamel conditions: phosphoric acid and XT primer; TPSEP; phosphoric acid only; phosphoric acid, XT primer and saliva; and TPSEP and saliva, respectively. After bracket bonding and photo-activation, the samples were stored in distilled water for 24 hours at 37°C in a stove. Next, the brackets were debonded by using an Instron machine at crosshead speed of 0.5 mm/min, and the ARI were evaluated by using a stereoscopic magnifying glass. The mean shear strength values (MPa) were the following: Group 1, 24.6; Group 2, 18.7; Group 3, 17.5; Group 4, 19.7; Group 5, 17.5; and Group 6, 14.8. Data were submitted to both ANOVA and Tukey's test (5%). Group 1 was found to be statistically superior to Groups 3, 5, and 6 (P<.05), with no statistically significant difference compared to Groups 2 and 4 (P>.05). No statistically significant differences were found between Groups 2, 3, 4, 5 and 6 (P>.05). The bracket bonding using TPCC composite showed values comparable to the conventional Transbond XT, and the type of enamel preparation had no influenceDoutoradoOrtodontiaDoutor em Radiologia Odontológica[s.n.]Magnani, Maria Beatriz Borges de Araújo, 1956-Correr Sobrinho, Lourenço, 1960-Ruellas, Antonio Carlos de OliveiraFerreira, Jose Tarcisio LimaConsani, SimonidesUniversidade Estadual de Campinas (UNICAMP). Faculdade de Odontologia de Piracicaba (FOP)Programa de Pós-Graduação em Radiologia OdontológicaUNIVERSIDADE ESTADUAL DE CAMPINASRomano, Fabio Lourenço2009info:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/doctoralThesisapplication/pdf64 f. : il.https://hdl.handle.net/20.500.12733/1609765ROMANO, Fabio Lourenço. Avaliação clinica e laboratorial da colagem de braquetes metalicos com compositos ortodonticos. 2009. 64 f. Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba, Campinas, SP. Disponível em: https://hdl.handle.net/20.500.12733/1609765. Acesso em: 3 set. 2024.https://repositorio.unicamp.br/acervo/detalhe/448096porreponame:Biblioteca Digital de Teses e Dissertações da Universidade Estadual de Campinas (UNICAMP)instname:Universidade Estadual de Campinas (UNICAMP)instacron:UNICAMPinfo:eu-repo/semantics/openAccess2017-02-18T05:34:52Zoai::448096Biblioteca Digital de Teses e DissertaçõesPUBhttp://repositorio.unicamp.br/oai/tese/oai.aspsbubd@unicamp.bropendoar:2017-02-18T05:34:52Biblioteca Digital de Teses e Dissertações da Universidade Estadual de Campinas (UNICAMP) - Universidade Estadual de Campinas (UNICAMP)false
dc.title.none.fl_str_mv Avaliação clinica e laboratorial da colagem de braquetes metalicos com compositos ortodonticos
Clinical and laboratory evaluation of metallic brackets bonded with orthodontic composites
title Avaliação clinica e laboratorial da colagem de braquetes metalicos com compositos ortodonticos
spellingShingle Avaliação clinica e laboratorial da colagem de braquetes metalicos com compositos ortodonticos
Romano, Fabio Lourenço
Resinas compostas
Resistência ao cisalhamento
Braquetes ortodônticos
Ortodontia
Composite resins
Shear strenght
Orthodontic Brackets
Orthodontics
title_short Avaliação clinica e laboratorial da colagem de braquetes metalicos com compositos ortodonticos
title_full Avaliação clinica e laboratorial da colagem de braquetes metalicos com compositos ortodonticos
title_fullStr Avaliação clinica e laboratorial da colagem de braquetes metalicos com compositos ortodonticos
title_full_unstemmed Avaliação clinica e laboratorial da colagem de braquetes metalicos com compositos ortodonticos
title_sort Avaliação clinica e laboratorial da colagem de braquetes metalicos com compositos ortodonticos
author Romano, Fabio Lourenço
author_facet Romano, Fabio Lourenço
author_role author
dc.contributor.none.fl_str_mv Magnani, Maria Beatriz Borges de Araújo, 1956-
Correr Sobrinho, Lourenço, 1960-
Ruellas, Antonio Carlos de Oliveira
Ferreira, Jose Tarcisio Lima
Consani, Simonides
Universidade Estadual de Campinas (UNICAMP). Faculdade de Odontologia de Piracicaba (FOP)
Programa de Pós-Graduação em Radiologia Odontológica
UNIVERSIDADE ESTADUAL DE CAMPINAS
dc.contributor.author.fl_str_mv Romano, Fabio Lourenço
dc.subject.por.fl_str_mv Resinas compostas
Resistência ao cisalhamento
Braquetes ortodônticos
Ortodontia
Composite resins
Shear strenght
Orthodontic Brackets
Orthodontics
topic Resinas compostas
Resistência ao cisalhamento
Braquetes ortodônticos
Ortodontia
Composite resins
Shear strenght
Orthodontic Brackets
Orthodontics
description Orientadores: Maria Beatriz Borges de Araujo Magnani, Lourenço Correr Sobrinho
publishDate 2009
dc.date.none.fl_str_mv 2009
dc.type.status.fl_str_mv info:eu-repo/semantics/publishedVersion
dc.type.driver.fl_str_mv info:eu-repo/semantics/doctoralThesis
format doctoralThesis
status_str publishedVersion
dc.identifier.uri.fl_str_mv https://hdl.handle.net/20.500.12733/1609765
ROMANO, Fabio Lourenço. Avaliação clinica e laboratorial da colagem de braquetes metalicos com compositos ortodonticos. 2009. 64 f. Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba, Campinas, SP. Disponível em: https://hdl.handle.net/20.500.12733/1609765. Acesso em: 3 set. 2024.
url https://hdl.handle.net/20.500.12733/1609765
identifier_str_mv ROMANO, Fabio Lourenço. Avaliação clinica e laboratorial da colagem de braquetes metalicos com compositos ortodonticos. 2009. 64 f. Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba, Campinas, SP. Disponível em: https://hdl.handle.net/20.500.12733/1609765. Acesso em: 3 set. 2024.
dc.language.iso.fl_str_mv por
language por
dc.relation.none.fl_str_mv https://repositorio.unicamp.br/acervo/detalhe/448096
dc.rights.driver.fl_str_mv info:eu-repo/semantics/openAccess
eu_rights_str_mv openAccess
dc.format.none.fl_str_mv application/pdf
64 f. : il.
dc.publisher.none.fl_str_mv [s.n.]
publisher.none.fl_str_mv [s.n.]
dc.source.none.fl_str_mv reponame:Biblioteca Digital de Teses e Dissertações da Universidade Estadual de Campinas (UNICAMP)
instname:Universidade Estadual de Campinas (UNICAMP)
instacron:UNICAMP
instname_str Universidade Estadual de Campinas (UNICAMP)
instacron_str UNICAMP
institution UNICAMP
reponame_str Biblioteca Digital de Teses e Dissertações da Universidade Estadual de Campinas (UNICAMP)
collection Biblioteca Digital de Teses e Dissertações da Universidade Estadual de Campinas (UNICAMP)
repository.name.fl_str_mv Biblioteca Digital de Teses e Dissertações da Universidade Estadual de Campinas (UNICAMP) - Universidade Estadual de Campinas (UNICAMP)
repository.mail.fl_str_mv sbubd@unicamp.br
_version_ 1809189010161008640

Registros relacionados