Propriedades mecânicas e resistência da união de resinas compostas com matriz de silorano ou com nanopartículas

Detalhes bibliográficos
Autor(a) principal: Bosquiroli, Virginia, 1970-
Data de Publicação: 2011
Tipo de documento: Tese
Idioma: por
Título da fonte: Biblioteca Digital de Teses e Dissertações da Universidade Estadual de Campinas (UNICAMP)
Texto Completo: https://hdl.handle.net/20.500.12733/1616144
Resumo: Orientador: Mário Alexandre Coelho Sinhoreti
id UNICAMP-30_c6eb13f7edd3afaca9652bc561af84ea
oai_identifier_str oai::812177
network_acronym_str UNICAMP-30
network_name_str Biblioteca Digital de Teses e Dissertações da Universidade Estadual de Campinas (UNICAMP)
repository_id_str
spelling Propriedades mecânicas e resistência da união de resinas compostas com matriz de silorano ou com nanopartículasMechanical properties and bond strength of composite resins with silorane matrix or nanofillersPartículas inorgânicasRestauraçãoPolímerosInorganic particlesRestorationPolymersOrientador: Mário Alexandre Coelho SinhoretiTese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de PiracicabaResumo: O objetivo neste estudo foi analisar as propriedades mecânicas (microdureza, resistência coesiva, rugosidade e perda de massa por abrasão) e a resistência da união entre dente/restauração de diferentes resinas compostas. Para os testes de resistência da união e micro-dureza, trinta incisivos bovinos foram usados para três grupos experimentais (n=10). Cavidades tronco-cônicas (2,0 mm de altura x 2,0 mm de diâmetro maior x 1,5 mm de diâmetro menor) foram preparadas e restauradas com os seguintes sistemas adesivos e resinas compostas (Single Bond 2 e Z100; Single Bond 2 e Filtek Z350 e; P90 System Adhesive e Filtek P90 - 3M/ESPE), de acordo com as recomendações do fabricante. A fonte de luz LED Freelight 2 (3M/ESPE) foi usada para a fotoativação dos compósitos, durante 40 s. Após serem armazenados em estufa emergidos em água destilada a 37oC durante 24 h os corpos de prova receberam polimento e mensurações de microdureza (KHN) foram feitas no topo e na base ( HMV-2, Shimadzu, Tokyo). Em seguida, foram realizados nestes corpos de prova o teste de resistência de união push-out em uma máquina de ensaio universal (Instron modelo 4411, MA, USA). Os valores de resistência de união foram submetidos à análise de variância ANOVA 1-critério e os de KHN a análise de variância ANOVA 2-critérios, seguidos do teste de Tukey a 5%. A Filtek P90 mostrou o maior valor de resistência de união e menor em dureza Knoop diferindo estatisticamente das demais resinas compostas. A Filtek Z350 obteve valor de resistência de união e dureza Knoop intermediário entre as resinas compostas avaliadas. A Z100 obteve o menor valor de resistência de união e o maior valor de dureza Knoop diferindo estatisticamente das demais resinas compostas e diferindo entre valor de topo e base no próprio compósito. Para confeccionar as amostras para o teste de resistência coesiva (RC) foi preparado um molde de silicone com formato de ampulheta com 11 mm de comprimento, 2 mm de largura, 1 mm de espessura e 1 mm na região de constrição. Para mensuração de rugosidade de superfície (Ra) e perda de massa (PM), antes e após a escovação, foi preparado moldes de silicone com 5 mm de diâmetro e 2 mm de espessura. Todas as amostras foram polidas com lixas de SiC 2000 e estocadas em estufa emergidas em água destilada a 37 oC por 24 h. Para Ra e PM, após o ciclo de escovação, os corpos de prova foram armazenados em estufa emergidos em água destilada a 37 oC por 24 antes da mensuração final sendo limpos em ultrassom por 15 min e removida a umidade superficial com papel absorvente. A RC foi realizada em máquina de ensaio universal (Instron modelo 4411, MA, USA). Os dados obtidos de cada teste foram submetidas a análise de variância ANOVA 1- critério e teste de Tukey a 5%. A Filtek Z350 e Z100 obtiveram os maiores valores de RC superiores a Filtek P90 e não diferindo estatisticamente entre sí. A Filtek Z350 teve o menor aumento de Ra e a Filtek P90 obteve os maiores valores de PM diferindo estatisticamente das demais resinas compostas. Pode-se concluir que tanto a matriz orgânica como a partícula de carga podem influenciar nas propriedades mecânicas e na resistência de união de restaurações de resina compostaAbstract: The aim of this study was to analyze the mechanical properties (micro-hardness, cohesive strength, surface roughness and loss mass through abrasion) and the bond strength between tooth/restoration of different composite resins. For bond strength and micro-hardness analyzes, thirty bovine incisors were used for three experimental groups (n=10). Trunk- conical cavities (2,0 x 2,0 x 1,5 mm) were prepared and restored with the following adhesive systems and resin compounds (Single Bond 2 and Z100; Single Bond 2 and Filtek Z350 and; P90 System Adhesive and Filtek P90 - 3M/ESPE), following manufacture's recommendations. A LED Freelight 2 (3M/ESPE) was used for the photo-activation of the composites for 40 s. After being emerged in distilled water and stored in an incubator at 37o C for 24 hours, the specimens were polished and micro-hardness measurements (KHN) were taken at the top and base ( HMV-2, Shimadzu, Tokyo). After that, the push-out resistance test was performed with a universal testing machine (Instron modelo 4411, MA, USA). Bond strength values were submitted to a variance analysis ANOVA 1-way, and KHN to the variance analysis ANOVA 2-way followed by the Tukey's test at 5% level of significance. Filtek P90 showed the highest bond strength value and the lowest Knoop hardness values differing statistically from the others composite resins. Filtek Z350 obtained bond strength values and KHN values intermediate among the other resin composites. Z100 showed the lowest bond strength values and highest Knoop hardness value statically different from the others composite resins and differing from top and bottom values in itself. To prepare the specimens for the cohesive strength test (CS), an hourglass silicone mold was made measuring 11 mm in length by 2 mm wide, and 1 mm thick by 1mm wide in the narrowed region. To measure surface rugosity (Ra) and mass loss (ML) before and after brushing, silicone molds were prepared measuring 5 mm in diameter by 2 mm thick. All samples were polished with SiC 2000 sandpaper and emerged in distilled water and stored in an incubator at 37o C for 24 hours. For Ra and ML, after the brushing cycle, the specimens were emerged in distilled water and stored in an incubator at 37o C for 24 hours before the final measurements being cleaned in ultrasonic immersion for 15 minutes and having the surface moisture removed with absorbent paper. CS was performed in a universal testing machine (Instron modelo 4411, MA, USA). The obtained data were submitted to the ANOVA 1-way analysis and the Turkey test at 5% level significance. Filtek Z350 and Z100 obtained higher CS values than Filtek P90 without statistically difference among each other. Filtek Z350 showed the lowest increase of Ra and Filtek P90 the highest ML values differing statistically from the others composite resins. It can be concluded that both the organic matrix and the type of particle filler can influence in the mechanical properties and bond strength of resin composite restorationsDoutoradoMateriais DentáriosDoutor em Materiais Dentários[s.n.]Sinhoreti, Mário Alexandre Coelho, 1969-Konno, Alysson Noriyuky KajishimaBrandt, William CunhaConsani, Rafael Leonardo XediekPascon, Fernanda MioriUniversidade Estadual de Campinas (UNICAMP). Faculdade de Odontologia de Piracicaba (FOP)Programa de Pós-Graduação em Materiais DentáriosUNIVERSIDADE ESTADUAL DE CAMPINASBosquiroli, Virginia, 1970-2011info:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/doctoralThesisapplication/pdf38 f. : il.https://hdl.handle.net/20.500.12733/1616144BOSQUIROLI, Virginia. Propriedades mecânicas e resistência da união de resinas compostas com matriz de silorano ou com nanopartículas. 2011. 38 f. Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba , Piracicaba, SP. Disponível em: https://hdl.handle.net/20.500.12733/1616144. Acesso em: 3 set. 2024.https://repositorio.unicamp.br/acervo/detalhe/812177porreponame:Biblioteca Digital de Teses e Dissertações da Universidade Estadual de Campinas (UNICAMP)instname:Universidade Estadual de Campinas (UNICAMP)instacron:UNICAMPinfo:eu-repo/semantics/openAccess2017-02-18T06:22:52Zoai::812177Biblioteca Digital de Teses e DissertaçõesPUBhttp://repositorio.unicamp.br/oai/tese/oai.aspsbubd@unicamp.bropendoar:2017-02-18T06:22:52Biblioteca Digital de Teses e Dissertações da Universidade Estadual de Campinas (UNICAMP) - Universidade Estadual de Campinas (UNICAMP)false
dc.title.none.fl_str_mv Propriedades mecânicas e resistência da união de resinas compostas com matriz de silorano ou com nanopartículas
Mechanical properties and bond strength of composite resins with silorane matrix or nanofillers
title Propriedades mecânicas e resistência da união de resinas compostas com matriz de silorano ou com nanopartículas
spellingShingle Propriedades mecânicas e resistência da união de resinas compostas com matriz de silorano ou com nanopartículas
Bosquiroli, Virginia, 1970-
Partículas inorgânicas
Restauração
Polímeros
Inorganic particles
Restoration
Polymers
title_short Propriedades mecânicas e resistência da união de resinas compostas com matriz de silorano ou com nanopartículas
title_full Propriedades mecânicas e resistência da união de resinas compostas com matriz de silorano ou com nanopartículas
title_fullStr Propriedades mecânicas e resistência da união de resinas compostas com matriz de silorano ou com nanopartículas
title_full_unstemmed Propriedades mecânicas e resistência da união de resinas compostas com matriz de silorano ou com nanopartículas
title_sort Propriedades mecânicas e resistência da união de resinas compostas com matriz de silorano ou com nanopartículas
author Bosquiroli, Virginia, 1970-
author_facet Bosquiroli, Virginia, 1970-
author_role author
dc.contributor.none.fl_str_mv Sinhoreti, Mário Alexandre Coelho, 1969-
Konno, Alysson Noriyuky Kajishima
Brandt, William Cunha
Consani, Rafael Leonardo Xediek
Pascon, Fernanda Miori
Universidade Estadual de Campinas (UNICAMP). Faculdade de Odontologia de Piracicaba (FOP)
Programa de Pós-Graduação em Materiais Dentários
UNIVERSIDADE ESTADUAL DE CAMPINAS
dc.contributor.author.fl_str_mv Bosquiroli, Virginia, 1970-
dc.subject.por.fl_str_mv Partículas inorgânicas
Restauração
Polímeros
Inorganic particles
Restoration
Polymers
topic Partículas inorgânicas
Restauração
Polímeros
Inorganic particles
Restoration
Polymers
description Orientador: Mário Alexandre Coelho Sinhoreti
publishDate 2011
dc.date.none.fl_str_mv 2011
dc.type.status.fl_str_mv info:eu-repo/semantics/publishedVersion
dc.type.driver.fl_str_mv info:eu-repo/semantics/doctoralThesis
format doctoralThesis
status_str publishedVersion
dc.identifier.uri.fl_str_mv https://hdl.handle.net/20.500.12733/1616144
BOSQUIROLI, Virginia. Propriedades mecânicas e resistência da união de resinas compostas com matriz de silorano ou com nanopartículas. 2011. 38 f. Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba , Piracicaba, SP. Disponível em: https://hdl.handle.net/20.500.12733/1616144. Acesso em: 3 set. 2024.
url https://hdl.handle.net/20.500.12733/1616144
identifier_str_mv BOSQUIROLI, Virginia. Propriedades mecânicas e resistência da união de resinas compostas com matriz de silorano ou com nanopartículas. 2011. 38 f. Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba , Piracicaba, SP. Disponível em: https://hdl.handle.net/20.500.12733/1616144. Acesso em: 3 set. 2024.
dc.language.iso.fl_str_mv por
language por
dc.relation.none.fl_str_mv https://repositorio.unicamp.br/acervo/detalhe/812177
dc.rights.driver.fl_str_mv info:eu-repo/semantics/openAccess
eu_rights_str_mv openAccess
dc.format.none.fl_str_mv application/pdf
38 f. : il.
dc.publisher.none.fl_str_mv [s.n.]
publisher.none.fl_str_mv [s.n.]
dc.source.none.fl_str_mv reponame:Biblioteca Digital de Teses e Dissertações da Universidade Estadual de Campinas (UNICAMP)
instname:Universidade Estadual de Campinas (UNICAMP)
instacron:UNICAMP
instname_str Universidade Estadual de Campinas (UNICAMP)
instacron_str UNICAMP
institution UNICAMP
reponame_str Biblioteca Digital de Teses e Dissertações da Universidade Estadual de Campinas (UNICAMP)
collection Biblioteca Digital de Teses e Dissertações da Universidade Estadual de Campinas (UNICAMP)
repository.name.fl_str_mv Biblioteca Digital de Teses e Dissertações da Universidade Estadual de Campinas (UNICAMP) - Universidade Estadual de Campinas (UNICAMP)
repository.mail.fl_str_mv sbubd@unicamp.br
_version_ 1809189061569544192

Registros relacionados