Solidificação unidirecional de ligas Zn-Mg : evolução microestrutural, propriedades mecânicas e resistência à corrosão

Detalhes bibliográficos
Autor(a) principal: Brito, Talita Almeida Vida de, 1985-
Data de Publicação: 2017
Tipo de documento: Tese
Idioma: por
Título da fonte: Biblioteca Digital de Teses e Dissertações da Universidade Estadual de Campinas (UNICAMP)
Texto Completo: https://hdl.handle.net/20.500.12733/1632563
Resumo: Orientador: Amauri Garcia
id UNICAMP-30_d4cdeedbf58a157972fdd3980d2c0cd3
oai_identifier_str oai::989810
network_acronym_str UNICAMP-30
network_name_str Biblioteca Digital de Teses e Dissertações da Universidade Estadual de Campinas (UNICAMP)
repository_id_str
spelling Solidificação unidirecional de ligas Zn-Mg : evolução microestrutural, propriedades mecânicas e resistência à corrosãoUnidirectional solidification of Zn-Mg alloys : microstructural evolution, mechanical properties and corrosion resistanceLigas de zinco - Propriedades mecânicasSolidificaçãoMicroestruturaCorrosãoZinc alloys - Mechanical propertiesSolidificationMicrostrutureMechanical resistanceCorrosionOrientador: Amauri GarciaTese (doutorado) - Universidade Estadual de Campinas, Faculdade de Engenharia MecânicaResumo: A adição de Mg para melhorar a estabilidade à corrosão de recobrimentos de Zn, é uma prática comum na produção de componentes de uso na construção civil e na indústria automotiva. O Zn é um metal biocompatível, biodegradável e bioabsorvível e essencial na nutrição humana. Apresenta ainda baixo ponto de fusão (420°C), boa resistência à corrosão e baixa reatividade no estado líquido. O Mg é um metal atóxico, biodegradável e biocompatível, no entanto, suas ligas apresentam elevada taxa de corrosão em meios fisiológicos. Sabe-se que o Zn é mais nobre que o Mg, e que a adição de Mg em ligas de Zn pode afetar positivamente tanto o comportamento mecânico quanto a resistência à corrosão. Em geral os comportamentos mecânico e eletroquímico das ligas Zn-Mg são influenciados diretamente por características microestruturais. Estudos experimentais enfatizando fatores relacionados à parâmetros da microestrutura, bem como sua correlação com propriedades mecânicas e químicas são escassos na literatura. No presente trabalho, foram realizados experimentos de solidificação unidirecional com ligas hipoeutéticas e hipereutéticas Zn-Mg ao longo de uma extensa faixa de taxas de resfriamento para a análise da evolução da microestrutura. Ligas Zn-Mg hipoeutéticas diluídas (0,3 e 0,5%Mg) apresentaram uma zona colunar curta seguida de zona equiaxial até o topo dos lingotes, enquanto as demais ligas examinadas apresentaram macroestrutura equiaxial ao longo de todo o comprimento dos lingotes. Mostra-se que a microestrutura é formada por uma matriz rica em Zn de diferentes morfologias e por misturas eutéticas competitivas (Zn-Zn11Mg2 e Zn-Zn2Mg). Para as ligas com 0,3 e 0,5%Mg, a matriz rica em Zn é caracterizada por células tipo placa de altas taxas de resfriamento (>9.5ºC/s e 24ºC/s, respectivamente), seguida de uma transição morfológica granular/dendrítica para taxas de resfriamento mais baixas. Em contrapartida, os lingotes das ligas hipoeutéticas (1,2 e 2,2%Mg) apresentaram uma matriz rica em Zn formada somente por grãos dendríticos equiaxiais, enquanto as ligas hipereutéticas (3,15 e 5,15%Mg), por grãos eutéticos equiaxiais de micromorfologia lamelar. Resultados de fluorescência de raios X mostraram a ocorrência de macrossegregação de Mg ao longo do comprimento de todos os lingotes unidirecionais, induzida por diferenças de densidade. São propostas leis experimentais de crescimento relacionando os espaçamentos entre células tipo placa, dendrítico primário e secundário e eutético com parâmetros térmicos de solidificação, ou seja, taxa de resfriamento e velocidade de solidificação. A combinação de macrossegregação de Mg e a evolução das escalas microestruturais em todos os lingotes unidirecionais das ligas Zn-Mg analisadas, conduziu a microdurezas Vickers essencialmente constantes ao longo dos comprimentos dos lingotes, entretanto, com o aumento no teor de Mg de 0,3 a 5,15 % a microdureza aumentou de 58 HV0,5 a 130 HV0,5. Ensaios de tração foram realizados apenas para as ligas Zn-0,3%, 1,2% e 3,15%Mg, sendo que a liga Zn-3,15%Mg, com morfologia microestrutural eutética, apresentou maiores valores de alongamento específico, limite de escoamento e limite de resistência à tração. A fim de se obter uma comparação direta com as propriedades mecânicas de tração, os ensaios de corrosão também foram realizados nas ligas Zn-Mg de mesmas composições, em uma solução de 0,06M de NaCl. Para a liga Zn-0,3%Mg, a amostra de micromorfologia celular tipo placa, da zona colunar, apresentou maior resistência à corrosão. As ligas Zn-1,2%Mg e Zn-3,15%Mg, de morfologia totalmente equiaxial, mostraram melhores resistências à corrosão associadas a amostras mais afastadas da base refrigerada, ou seja, de microestruturas mais grosseiras. Palavras-chave: Ligas Zn-Mg; Solidificação Transitória; Microestrutura; Propriedades Mecânicas; Resistência à CorrosãoAbstract: The addition of Mg to improve corrosion stability of Zn coatings is a technologically common practice for corrosion protection of products of use in the civil and automotive industries. These alloys show also potential application in biomedical implants. Zn is a biocompatible, biodegradable and bioabsorbable metal essential in human nutrition. It also has a low melting point (420 °C), good corrosion resistance and low reactivity in the liquid state. Mg is a non-toxic, biodegradable and biocompatible metal; however, its alloys have a high corrosion rate in physiological media. It is known that Zn is nobler than Mg, and that the addition of Mg to Zn alloys can positively affect both mechanical behavior and corrosion resistance. In general the mechanical and electrochemical behavior of Zn-Mg alloys is directly influenced by microstructural characteristics. Experimental studies emphasizing factors related to microstructure parameters as well as their correlation with mechanical and chemical properties are scarce in the literature. In the present work, transient directional solidification experiments have been carried out with Zn-Mg hypoeutectic and hypereutectic alloys under an extensive range of cooling rates with a view to analyzing the evolution of microstructure. Dilute hypoeutectic alloys Zn-Mg (0.3 and 0.5wt%Mg) alloys are shown to have a short columnar zone followed by an equiaxed zone up the top of the castings, while the other alloys examined are characterized by equiaxed macrostructures along the entire length of the castings. It is shown that the microstructure is formed by a Zn-rich matrix of different morphologies and competitive eutectic mixtures (Zn-Zn11Mg2 and Zn-Zn2Mg). For 0.3 and 0.5wt%Mg alloys, the Zn-rich matrix is shown to be characterized by high cooling rates plate-like cells (cooling rates > 9.5ºC/s and 24ºC/s, respectively), followed by a granular-dendritic morphological transition for lower cooling rates. In contrast, the hypoeutectic alloys castings (1.2 and 2.2wt%Mg) are shown to have the Zn-rich matrix formed only by dendritic equiaxed grains, while the hypereutectic alloys (3.15 and 5.15wt%Mg), by equiaxed eutectic grains of lamellar micromorphology. Results from X-ray fluorescence showed the occurrence of Mg macrosegregation along the length of all directionally solidified castings, induced by differences in density. Experimental growth laws are proposed relating the plate-like cellular interphase, the primary and secondary dendritic arm and the eutectic interphase spacings to solidification thermal parameters, i.e. cooling rate, and growth rate. The combination of Mg macrosegregation and the evolution of microstructural length scales in all the Zn-Mg alloys castings examined, has led to essentially constant Vickers microhardness along the length of the castings, however, with the increase in the alloys Mg content from 0.3 to 5.15wt%, the microhardness increased from 58 HV0.5 to 130 HV0.5. Tensile tests were carried for Zn-0.3, 1.2 and 3.15wt%Mg alloys and the Zn-3.15wt%Mg alloy, with eutectic microstructure, is shown to have higher elongation, yield strength and ultimate tensile strength. In order to obtain a direct comparison with tensile test results, the corrosion tests were also carried out in alloys of same compositions in a 0.06M NaCl solution. The Zn-0.3wt%Mg alloy showed better corrosion behavior associated with the sample of cellular plate-like micromorphology from the columnar region. The Zn-1.2 and 3.15 wt% Mg alloys, having equiaxed morphology, were shown to have better corrosion resistances associated with samples of coarser microstructures. Keywords: Zn-Mg alloys; Transient Solidification; Microstructure; Mechanical Properties; Corrosion ResistanceDoutoradoMateriais e Processos de FabricaçãoDoutor em Engenharia MecânicaCNPQ155863/2013-4[s.n.]Garcia, Amauri, 1949-Cheung, NoéIerardi, Maria Clara FilippiniSouza, Eduardo Netto deSandor, Leonardo TabordaUniversidade Estadual de Campinas (UNICAMP). Faculdade de Engenharia MecânicaPrograma de Pós-Graduação em Engenharia MecânicaUNIVERSIDADE ESTADUAL DE CAMPINASBrito, Talita Almeida Vida de, 1985-20172017-07-20T00:00:00Zinfo:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/doctoralThesisapplication/pdf1 recurso online (204 p.) : il., digital, arquivo PDF.https://hdl.handle.net/20.500.12733/1632563BRITO, Talita Almeida Vida de. Solidificação unidirecional de ligas Zn-Mg: evolução microestrutural, propriedades mecânicas e resistência à corrosão. 2017. 1 recurso online (204 p.) Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Engenharia Mecânica, Campinas, SP. Disponível em: https://hdl.handle.net/20.500.12733/1632563. Acesso em: 3 set. 2024.https://repositorio.unicamp.br/acervo/detalhe/989810Requisitos do sistema: Software para leitura de arquivo em PDFporreponame:Biblioteca Digital de Teses e Dissertações da Universidade Estadual de Campinas (UNICAMP)instname:Universidade Estadual de Campinas (UNICAMP)instacron:UNICAMPinfo:eu-repo/semantics/openAccess2020-03-19T10:10:17Zoai::989810Biblioteca Digital de Teses e DissertaçõesPUBhttp://repositorio.unicamp.br/oai/tese/oai.aspsbubd@unicamp.bropendoar:2020-03-19T10:10:17Biblioteca Digital de Teses e Dissertações da Universidade Estadual de Campinas (UNICAMP) - Universidade Estadual de Campinas (UNICAMP)false
dc.title.none.fl_str_mv Solidificação unidirecional de ligas Zn-Mg : evolução microestrutural, propriedades mecânicas e resistência à corrosão
Unidirectional solidification of Zn-Mg alloys : microstructural evolution, mechanical properties and corrosion resistance
title Solidificação unidirecional de ligas Zn-Mg : evolução microestrutural, propriedades mecânicas e resistência à corrosão
spellingShingle Solidificação unidirecional de ligas Zn-Mg : evolução microestrutural, propriedades mecânicas e resistência à corrosão
Brito, Talita Almeida Vida de, 1985-
Ligas de zinco - Propriedades mecânicas
Solidificação
Microestrutura
Corrosão
Zinc alloys - Mechanical properties
Solidification
Microstruture
Mechanical resistance
Corrosion
title_short Solidificação unidirecional de ligas Zn-Mg : evolução microestrutural, propriedades mecânicas e resistência à corrosão
title_full Solidificação unidirecional de ligas Zn-Mg : evolução microestrutural, propriedades mecânicas e resistência à corrosão
title_fullStr Solidificação unidirecional de ligas Zn-Mg : evolução microestrutural, propriedades mecânicas e resistência à corrosão
title_full_unstemmed Solidificação unidirecional de ligas Zn-Mg : evolução microestrutural, propriedades mecânicas e resistência à corrosão
title_sort Solidificação unidirecional de ligas Zn-Mg : evolução microestrutural, propriedades mecânicas e resistência à corrosão
author Brito, Talita Almeida Vida de, 1985-
author_facet Brito, Talita Almeida Vida de, 1985-
author_role author
dc.contributor.none.fl_str_mv Garcia, Amauri, 1949-
Cheung, Noé
Ierardi, Maria Clara Filippini
Souza, Eduardo Netto de
Sandor, Leonardo Taborda
Universidade Estadual de Campinas (UNICAMP). Faculdade de Engenharia Mecânica
Programa de Pós-Graduação em Engenharia Mecânica
UNIVERSIDADE ESTADUAL DE CAMPINAS
dc.contributor.author.fl_str_mv Brito, Talita Almeida Vida de, 1985-
dc.subject.por.fl_str_mv Ligas de zinco - Propriedades mecânicas
Solidificação
Microestrutura
Corrosão
Zinc alloys - Mechanical properties
Solidification
Microstruture
Mechanical resistance
Corrosion
topic Ligas de zinco - Propriedades mecânicas
Solidificação
Microestrutura
Corrosão
Zinc alloys - Mechanical properties
Solidification
Microstruture
Mechanical resistance
Corrosion
description Orientador: Amauri Garcia
publishDate 2017
dc.date.none.fl_str_mv 2017
2017-07-20T00:00:00Z
dc.type.status.fl_str_mv info:eu-repo/semantics/publishedVersion
dc.type.driver.fl_str_mv info:eu-repo/semantics/doctoralThesis
format doctoralThesis
status_str publishedVersion
dc.identifier.uri.fl_str_mv https://hdl.handle.net/20.500.12733/1632563
BRITO, Talita Almeida Vida de. Solidificação unidirecional de ligas Zn-Mg: evolução microestrutural, propriedades mecânicas e resistência à corrosão. 2017. 1 recurso online (204 p.) Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Engenharia Mecânica, Campinas, SP. Disponível em: https://hdl.handle.net/20.500.12733/1632563. Acesso em: 3 set. 2024.
url https://hdl.handle.net/20.500.12733/1632563
identifier_str_mv BRITO, Talita Almeida Vida de. Solidificação unidirecional de ligas Zn-Mg: evolução microestrutural, propriedades mecânicas e resistência à corrosão. 2017. 1 recurso online (204 p.) Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Engenharia Mecânica, Campinas, SP. Disponível em: https://hdl.handle.net/20.500.12733/1632563. Acesso em: 3 set. 2024.
dc.language.iso.fl_str_mv por
language por
dc.relation.none.fl_str_mv https://repositorio.unicamp.br/acervo/detalhe/989810
Requisitos do sistema: Software para leitura de arquivo em PDF
dc.rights.driver.fl_str_mv info:eu-repo/semantics/openAccess
eu_rights_str_mv openAccess
dc.format.none.fl_str_mv application/pdf
1 recurso online (204 p.) : il., digital, arquivo PDF.
dc.publisher.none.fl_str_mv [s.n.]
publisher.none.fl_str_mv [s.n.]
dc.source.none.fl_str_mv reponame:Biblioteca Digital de Teses e Dissertações da Universidade Estadual de Campinas (UNICAMP)
instname:Universidade Estadual de Campinas (UNICAMP)
instacron:UNICAMP
instname_str Universidade Estadual de Campinas (UNICAMP)
instacron_str UNICAMP
institution UNICAMP
reponame_str Biblioteca Digital de Teses e Dissertações da Universidade Estadual de Campinas (UNICAMP)
collection Biblioteca Digital de Teses e Dissertações da Universidade Estadual de Campinas (UNICAMP)
repository.name.fl_str_mv Biblioteca Digital de Teses e Dissertações da Universidade Estadual de Campinas (UNICAMP) - Universidade Estadual de Campinas (UNICAMP)
repository.mail.fl_str_mv sbubd@unicamp.br
_version_ 1809189117214326784

Registros relacionados