Propriedades estruturais de géis de sílica preparados com adições de dodecil sulfato de sódio

• Autor(a) principal: Perissinotto, Amanda Pasquoto [UNESP]
• Data de Publicação: 2012
• Tipo de documento: Trabalho de conclusão de curso
• Idioma: por
• Título da fonte: Repositório Institucional da UNESP
• Texto Completo: http://hdl.handle.net/11449/120537
• topic: Física aplicada; Processo sol-gel; Adsorção; Nitrogenio; Silica gel; Sulfato de sodio

This work aims to study the structural characteristics of silica gels obtained from the acid hydrolysis of tetraethoxysilane (TEOS) in water solutions with different concentrations of sodium dodecyl sulfate (SDS). The structural characteristics were studied in stages ranging from the wet gel to the dry stages of the gels (aerogels and xerogels). Aerogels were obtained by ambient pressure drying (APD) after silylation process using trimethylchlorosilane (TMCS) as silylating agent. Xerogels were obtained by conventional evaporating the liquid phase from non silylated gels. The samples were characterized by nitrogen adsorption and small angle X-ray scattering (SAXS). The structure of the wet gels and of the aerogels prepared with the surfactant exhibited characteristics of mass-fractal structures with fractal dimension D in the range 2.1-2.2 for the wet gels and 2.3-2.4 for the aerogels. The characteristic size  of the fractal domain reduces while the size a0 of the primary silica particle composing the fractal structure increases with the drying of the gels, in a process in which share of the porosity is eliminated. Aerogels exhibited typical values for the specific surface of 900 m2g-1 and of 3.5 cm3.g-1 for the total pore volume. These values are correspondingly comparable to those of the aerogels prepared by supercritical drying, since the silylation process replaces hydrophilic –OH groups by hydrophobic –Si-R3 ones, inhibiting the porosity elimination on drying. The silica particle size also increases lightly with the silylation because the attachment of the –Si-R3 groups on the silica surface. The pore size distribution curves of the aerogels are similar for all samples exhibiting a maximum in around 40 nm, independent the concentration of surfactant. This suggests that the characteristic size of 40 nm is due to the association of surfactant micelles... (Complete abstract click electronic access below)