Avaliação da tenacidade à fratura em juntas soldadas circunferenciais de tubulações de processo

• Autor(a) principal: Gumieri, Thierry Henrique Machado [UNESP]
• Data de Publicação: 2012
• Tipo de documento: Trabalho de conclusão de curso
• Idioma: por
• Título da fonte: Repositório Institucional da UNESP
• Texto Completo: http://hdl.handle.net/11449/119384
• topic: Mecanica da fratura; Juntas soldadas

This work aims to analyze the toughness of a welded joint in the presence of a crack through the analysis of maximum tension the material can withstand the presence of this type of defect, since a discontinuity is likely to occur in this type of joint and its detection and its design is simple, using non-destructive testing techniques. The study will be conducted through the CTOD test - Crack-Tip Opening Displacement, with type specimens SE (B) - Single Edge Bend taken from a weld in the L-C position in relation to the length (longitudinal axis) of a test tube. The main idea is to simulate the welding conditions for the manufacture of industrial pipes, made in boiler shops (pipe-shop) within petrochemical plants. These pipes are often subject to operation with flammable and toxic subjected to high pressures and temperatures, where one can break the line can cause irreparable damage to the plant, the environment and the health of surrounding communities. With this study we evaluate whether the weld metal has the same properties as fracture toughness of the base material. This study shows the importance of using a qualified welding procedure for performing quality welds while maintaining the properties of the fracture toughness of the base metal. It was found from the results of tests using a welding procedure described for carrying out welding ensures mechanical properties very close to the base metal, which in terms of design is great, since one can ensure that the weld will the same characteristics of the base metal specified for the assembly of the pipe