Estudo das alterações das propriedades mecânicas em aço A-516 grau 70 soldado e submetido a tratamento térmico de alívio de tensões

• Autor(a) principal: Baltar, Edgard Henrique Soares [UNESP]
• Data de Publicação: 2014
• Tipo de documento: Trabalho de conclusão de curso
• Idioma: por
• Título da fonte: Repositório Institucional da UNESP
• Texto Completo: http://hdl.handle.net/11449/124259; http://www.athena.biblioteca.unesp.br/exlibris/bd/capelo/2015-05-05/000822489.pdf
• topic: Vasos de pressão; Tensões termicas; Aço - Tratamento termico; Solda e soldagem; Pressure vessels

Pressure vessels are equipments that require a great care because of their high cost and human life risk in case of fail, and its fabrication methods are different for each manufacturer. Normally, pressure vessels and its parts are fabricated by welding, which may change local properties of metals. The head of a pressure vessel is a very important structural component and it is fabricated by welding and mechanical conformation. Because its excellent mechanical properties, de steel A-516 Grade 70 is often used in manufacturing of large pressure vessels that are subjected to high pressure and temperature, but was verified that its mechanical resistance is decreased when submitted to a tension relief heat treatment. By experience it was defined that before mechanical conformation of the head of a large pressure vessel, the steel should be submitted to a stress relief heat treatment in order to facilitate the mechanical conformation, but there is no quantitative analysis to prove this method and study its possible risks. In the present work the steel A-516 Grade 70 demonstrated a decrease of its mechanical resistance when submitted to a stress relief heat treatment, but keeping above the minimum limit defined in the literature. By other side its ductility was substantially increased, being possible to deduce that the stress relief heat treatment before mechanical conformation is a viable e recommended technique, but with reservations. With the data acquired during the fabrication e preparation of the specimen and the result of the tests, it was possible to elaborate a welding procedure that provides the same results obtained in this present work