Análise das resistências de embutimento e de compressão para madeiras de pinus e eucalipto

• Autor(a) principal: Almeida, Diego Henrique de [UNESP]
• Data de Publicação: 2011
• Tipo de documento: Trabalho de conclusão de curso
• Idioma: por
• Título da fonte: Repositório Institucional da UNESP
• Texto Completo: http://hdl.handle.net/11449/117985
• topic: Madeira; Madeira - Estruturas; Ligações parafusadas; Eucalipto; Pinus taeda; Wood

The connections in the wood structures are the places with high concentrations of stresses and therefore are more fragile than the rest of the structure. The connections between pieces of wood can be made by metal pins (nails or screws). The compression and embedment strength has significant influence on the calculation of the connections. The main aim of this work was to evaluate the compression and embedment strength in the directions parallel, inclined at 45° and normal to the grain, using standard specimens according to ABNT NBR 7190/1997 standard. The compression and embedment strength were initially evaluated according to ABNT NBR 7190/1997, which admits the deformation of 2‰ as limit of embedment and the ratio between the ultimate strength and the area of application of load in the specimen for the compressive strength. Afterward, the embedment strength was evaluated by the EUROCEDE 5 /1995 European standard, which use the limit of 5 mm of the displacement for the embedment. Specimens of Pinus oocarpa, Cumaru and Pinus taeda were used in tests to calibration of equipment and specimens of Pinus taeda and Eucalipto citriodora were used to compare the results of strength. The results of strength were evaluated based on statistical analysis. The results of compressive strength for the Pinus taeda showed no significant differences in embedment strength in the directions parallel and normal to the grain. For the Eucalipto citriodora only in the direction parallel to grain the compression strength was not significant compared with the embedment strength. For both species, only the parallel compression strength and inclined at 45o to the grain, which were to the grain, which were admitted the strain of 2‰ were not significantly different compared with the compression strength determined according to ABNT NBR 7190/1997. The normal compression strength obtained according to ABNT NBR 7190/1997 and ultimate compression strength not ...