Eletro-oxidação de metanol e etanol sobre PtAu/C em meio alcalino

• Autor(a) principal: Abreu, Thiago Holanda de [UNESP]
• Data de Publicação: 2012
• Tipo de documento: Trabalho de conclusão de curso
• Idioma: por
• Título da fonte: Repositório Institucional da UNESP
• Texto Completo: http://hdl.handle.net/11449/132462; http://www.athena.biblioteca.unesp.br/exlibris/bd/capelo/2015-12-22/000716678.pdf
• topic: Físico-química; Eletrocatálise; Células à combustível

The development of electrocatalysts for the oxidation of methanol and ethanol is very important, because these alcohols may be used in the anode fuel cells which convert chemical energy directly into electrical energy with high efficiency, cleanly and with low noise. Thus, this study reports to the synthesis of nanocatalysts of PtAu supported on carbon by microemulsion method. The physical characterization of these catalysts is performed through the techniques of X-ray diffraction and transmission electron microscopy. The catalytic activity of the prepared materials was studied using conventional electrochemical techniques and also the technique of spectro-electrochemical in situ FTIR, which allows identification of intermediates and products of the reactions. From the x-ray diffraction, it was observed that the thermal treatment applied to catalysts favored incorporation of Au into the crystal lattice of Pt,that is, increased the formation of PtAu alloy. Micrographs indicated particle size about 3 nm to materials not heat treated and 9 nm to materials subjected to thermal treatment (heating at 150 ° C for 1h and 30 min in argon atmosphere). Current density oxidation of methanol on PtAu / C were superior to pure platinum. Spectroscopic results indicated the presence of formate in solution in 50:50 and the composition showed bands for CO2, indicating complete oxidation, in lower potential. During ethanol oxidation on the catalyst PtAu, the main product formed was acetate, product of incomplete oxidation. The good performance for methanol oxidation can be attributed to large amounts of oxygen species adsorbed on the catalyst surface, or an electronic effect.