Análise fractal de fraturas em regime linear elástico: modo I de carregamento

• Autor(a) principal: Marion, Alexandre de Oliveira [UNESP]
• Data de Publicação: 2011
• Tipo de documento: Trabalho de conclusão de curso
• Idioma: por
• Título da fonte: Repositório Institucional da UNESP
• Texto Completo: http://hdl.handle.net/11449/119833
• topic: Processamento de imagens - Tecnicas digitais; Resinas fenolicas; Polimeros - Fratura; Fractais; Fractal; Phenolic resin

For the development of this graduate work of fractal fracture behavior, it is necessary to establish references for fractal analysis on fracture surfaces, evaluating, from tests of fracture tenacity on modes I, II and combined I / II, the behavior of fractures in fragile materials, on linear elastic regime. Fractures in the linear elastic regime are described by your fractal behavior by several researchers, especially Mecholsky JJ. The motivation of that present proposal stems from work done by the group and accepted for publication in the journal Materials Science and Engineering A (Horovistiz et al, 2010), where the model of Mecholsky could not be proven for fractures into grooved specimens for tests of diametric compression of titania on mode I. The general objective of this proposal is to quantify the distinguish surface regions formed by different mechanisms of fracture propagation in linear elastic regime in polymeric specimens (phenolic resin), relating tenacity, thickness of the specimens and fractal dimension. The analyzed fractures were obtained from SCB tests in mode I loading, and the acquisition of images taken using an optical reflection microscope and the surface topographies obtained by the extension focus method of reconstruction, calculating the values of fractal dimension with the use of maps of elevations. The fractal dimension was classified as monofractal dimension (Df), when the fracture is described by a single value, or texture size (Dt), which is a macroscopic analysis of the fracture, combined with the structural dimension (Ds), which is a microscopic analysis. The results showed that there is no clear relationship between tenacity, thickness and fractal values for the material investigated. On the other hand it is clear that the fractal values change with the evolution of cracks during the fracture process ... (Complete abstract click electronic access below)