Influence of plaster drying on the amount of residual monomer in heat-cured acrylic resins

• Autor(a) principal: De Arruda Paes-Junior, Tarcisio José [UNESP]
• Data de Publicação: 2013
• Outros Autores: De Carvalho, Rodrigo Furtado [UNESP], Cavalcanti, Sâmia Carolina Mota [UNESP], Saavedra, Guilherme de Siqueira Ferreira Anzaloni [UNESP], Borges, Alexandre Luiz Souto [UNESP]
• Tipo de documento: Artigo
• Idioma: eng
• Título da fonte: Repositório Institucional da UNESP
• Texto Completo: http://dx.doi.org/10.1590/S1677-32252013000200003; http://hdl.handle.net/11449/75015
• topic: Acrylic resins; Chromatography; Laboratory research; Polymers

Aim: To evaluate the influence of plaster condition, dry or not, on the amount of residual monomer in heat-cured acrylic resin. Methods: Thirty acrylic resin specimens (65×10×3 mm) were fabricated and randomly assigned to 5 groups (n=6). The evaluated resins were heat-cured acrylic resins by conventional or microwave polymerization techniques and the plaster was previously dried in microwave oven in two groups. Each specimen was individually immersed in a test tube containing methanol (7 days) for surface analysis. In the groups for which internal monomer was evaluated, the specimens were fragmented and the small fragments were weighed prior to immersion in methanol. The analysis was made by high performance liquid chromatography (HPLC). Data were analyzed by ANOVA and Tukey test (p<5%) Results: showed statistical differences among the groups. Conclusions: The previous plaster drying influenced the residual monomer amount showing a decrease of these levels.