Estudo do comportamento em fadiga de um tubo de aço microligado, grau API 5L X70

• Autor(a) principal: Bobilho, Bruno Cesar Milano [UNESP]
• Data de Publicação: 2013
• Tipo de documento: Trabalho de conclusão de curso
• Idioma: por
• Título da fonte: Repositório Institucional da UNESP
• Texto Completo: http://hdl.handle.net/11449/124262; http://www.athena.biblioteca.unesp.br/exlibris/bd/capelo/2015-05-05/000805733.pdf
• topic: Aço - Fadiga; Petróleo; Gás; Steel Fatigue

This work focuses on a study on the fatigue behavior of a microalloyed steel API 5L X70, used in pipes lines to transport oil and gas. These types of steels have excellent mechanical resistance values and ductility and therefore increased their study driven by increased demand for oil and especially natural gas, which consequently raises the need to build new pipelines to transport these products. The oil extraction units, composed of the risers (pipelines connecting the oil well to the ship), are dimensioned to remain installed for periods of 20 to 30 years in the marine environment, a hostile environment for high pressure, corrosion, low temperatures and the stresses caused by the movement of water and tides. For analysis, the S-N (stress versus number of cycles) curves were obtained from data collected from bodies-of-proof cylindrical longitudinal, transverse and that one removed from the weld area of the pipe, tested in accordance with ASTM E466. Tensile tests were performed for characterizing the mechanical properties of the samples and welded joints, concluded that the values meet the specifications of the standard API 5L. To characterize microstructural material, also metallographic analysis was made of regions of the base metal and the HAZ. The results of fatigue tests demonstrated a higher life for the specimens removed from the longitudinal direction the pipe, followed by those in the transverse direction and, finally, the welded joint. The origins of the fatigue cracks were determined by scanning electron microscopy (SEM)