Caracterização físico-mecânica de elementos estruturais roliços perfilados de Amaru

• Autor(a) principal: Santos, Caio Victor Fernandes dos [UNESP]
• Data de Publicação: 2013
• Tipo de documento: Trabalho de conclusão de curso
• Idioma: por
• Título da fonte: Repositório Institucional da UNESP
• Texto Completo: http://hdl.handle.net/11449/120982
• topic: Madeira; Madeira - Propriedades mecânicas; Madeira - Testes; Elasticidade; Madeira - Estruturas; Eucalipto; Wood

The study of physical and mechanical properties of wood is essential for its structural use and it is of great importance to the construction industry. Thus, this study aimed to determine the physical and mechanical properties of the wood Amaru - a hybrid of Eucalyptus, developed by Plantar Projects and Forest Products Ltda. In order to determine the properties of Amaru, round samples were used, which were provided to the Laboratory of Wood and Wooden Structures of the School of Engineering of São Carlos, University of São Paulo - LaMEM / EESC / USP. For the characterization of the physical properties, the apparent specific gravity and moisture content of the samples were determined. To the mechanical characterization, the following properties were evaluated: strength and stiffness in compression, strength and stiffness in bending, shear and tension. The procedures of the tests performed in this study were done according to the recommendations of the Brazilian Wood Standard ABNT NBR 7190:1997. The specimen used were confectioned in actual dimensions, according to as those used in the construction system proposed by Plantar. The results obtained from the tests performed showed that the mechanical properties approached the values proposed by the Wood Standard NBR 7190. The visual grading was important to provide a primary idea about the failure modes to be obtained from the tests performed. The bending test showed the modulus of elasticity (MOE) and Modulus of Rupture (MOR), which resulted in 15822 MPa and 101,7 MPa, respectively. The compression test resulted in values Ec0,m and fc0, 15698 MPa and 50,7 MPa. The tensile strength (ft0) of this hybrid was calculated and its value obtained was 60,8 MPa. The shear strength (fv0) was 8,2 MPa. The results obtained from the tests are the basis for engineers and architects to design structures using wood species Amaru