Fatigue Performance of AISI 4340 Steel Ni-Cr-B-Si-Fe HVOF Thermal Spray Coated
Main Author: | |
---|---|
Publication Date: | 2015 |
Other Authors: | , |
Format: | Conference object |
Language: | eng |
Source: | Repositório Institucional da UNESP |
Download full: | http://dx.doi.org/10.1016/j.proeng.2015.08.111 http://hdl.handle.net/11449/168117 |
Summary: | Coatings are deposited on high strength materials to improve the surface degradation resistance of several elements. As a consequence, the fatigue strength of coated materials is significantly influenced by internal residual stresses. Despite the fact that hard chromium electroplated is used to guarantee combinations of adhesion, hardness, corrosion and wear resistance, the method decreases the fatigue resistance of aeronautical components due to the high tensile residual stresses and microcracks density contained in the coating. In order to avoid this problem thermally sprayed HVOF coatings and shot peening process are widely used to improve surface properties of several alloys. The aim of the present study is to analyze the influence of Ni-Cr-B-Si-Fe coating applied by HVOF process on the axial fatigue strength of AISI 4340 steel. The shot peening effect on the fatigue results of coated AISI 4340 steel was also evaluated. The fractured fatigue specimens were investigated using a scanning electron microscope in order to obtain information about the crack initiation points. |
id |
UNSP_7d79b4a591037b71b71f0bb943115ca6 |
---|---|
oai_identifier_str |
oai:repositorio.unesp.br:11449/168117 |
network_acronym_str |
UNSP |
network_name_str |
Repositório Institucional da UNESP |
repository_id_str |
2946 |
spelling |
Fatigue Performance of AISI 4340 Steel Ni-Cr-B-Si-Fe HVOF Thermal Spray CoatedAISI 4340 steelfatigueresidual stressesshot peeningThermal spray coatingCoatings are deposited on high strength materials to improve the surface degradation resistance of several elements. As a consequence, the fatigue strength of coated materials is significantly influenced by internal residual stresses. Despite the fact that hard chromium electroplated is used to guarantee combinations of adhesion, hardness, corrosion and wear resistance, the method decreases the fatigue resistance of aeronautical components due to the high tensile residual stresses and microcracks density contained in the coating. In order to avoid this problem thermally sprayed HVOF coatings and shot peening process are widely used to improve surface properties of several alloys. The aim of the present study is to analyze the influence of Ni-Cr-B-Si-Fe coating applied by HVOF process on the axial fatigue strength of AISI 4340 steel. The shot peening effect on the fatigue results of coated AISI 4340 steel was also evaluated. The fractured fatigue specimens were investigated using a scanning electron microscope in order to obtain information about the crack initiation points.Materials and Technology Department, Fatigue and Aeronautic Materials Research Group, Av. Ariberto Pereira da Cunha, 333Faculdade de Engenharia de Guaratinguetá, UNESP-Universidade Estadual PaulistaFaculdade de Engenharia de Guaratinguetá, UNESP-Universidade Estadual PaulistaMaterials and Technology Department, Fatigue and Aeronautic Materials Research GroupUniversidade Estadual Paulista (Unesp)Vieira, L. F SVoorwald, H. J C [UNESP]Cioffi, M. O H [UNESP]2018-12-11T16:39:49Z2018-12-11T16:39:49Z2015-01-01info:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/conferenceObject606-612http://dx.doi.org/10.1016/j.proeng.2015.08.111Procedia Engineering, v. 114, p. 606-612.1877-7058http://hdl.handle.net/11449/16811710.1016/j.proeng.2015.08.1112-s2.0-84946056859Scopusreponame:Repositório Institucional da UNESPinstname:Universidade Estadual Paulista (UNESP)instacron:UNESPengProcedia Engineering0,282info:eu-repo/semantics/openAccess2021-10-23T21:44:18Zoai:repositorio.unesp.br:11449/168117Repositório InstitucionalPUBhttp://repositorio.unesp.br/oai/requestopendoar:29462021-10-23T21:44:18Repositório Institucional da UNESP - Universidade Estadual Paulista (UNESP)false |
dc.title.none.fl_str_mv |
Fatigue Performance of AISI 4340 Steel Ni-Cr-B-Si-Fe HVOF Thermal Spray Coated |
title |
Fatigue Performance of AISI 4340 Steel Ni-Cr-B-Si-Fe HVOF Thermal Spray Coated |
spellingShingle |
Fatigue Performance of AISI 4340 Steel Ni-Cr-B-Si-Fe HVOF Thermal Spray Coated Vieira, L. F S AISI 4340 steel fatigue residual stresses shot peening Thermal spray coating |
title_short |
Fatigue Performance of AISI 4340 Steel Ni-Cr-B-Si-Fe HVOF Thermal Spray Coated |
title_full |
Fatigue Performance of AISI 4340 Steel Ni-Cr-B-Si-Fe HVOF Thermal Spray Coated |
title_fullStr |
Fatigue Performance of AISI 4340 Steel Ni-Cr-B-Si-Fe HVOF Thermal Spray Coated |
title_full_unstemmed |
Fatigue Performance of AISI 4340 Steel Ni-Cr-B-Si-Fe HVOF Thermal Spray Coated |
title_sort |
Fatigue Performance of AISI 4340 Steel Ni-Cr-B-Si-Fe HVOF Thermal Spray Coated |
author |
Vieira, L. F S |
author_facet |
Vieira, L. F S Voorwald, H. J C [UNESP] Cioffi, M. O H [UNESP] |
author_role |
author |
author2 |
Voorwald, H. J C [UNESP] Cioffi, M. O H [UNESP] |
author2_role |
author author |
dc.contributor.none.fl_str_mv |
Materials and Technology Department, Fatigue and Aeronautic Materials Research Group Universidade Estadual Paulista (Unesp) |
dc.contributor.author.fl_str_mv |
Vieira, L. F S Voorwald, H. J C [UNESP] Cioffi, M. O H [UNESP] |
dc.subject.por.fl_str_mv |
AISI 4340 steel fatigue residual stresses shot peening Thermal spray coating |
topic |
AISI 4340 steel fatigue residual stresses shot peening Thermal spray coating |
description |
Coatings are deposited on high strength materials to improve the surface degradation resistance of several elements. As a consequence, the fatigue strength of coated materials is significantly influenced by internal residual stresses. Despite the fact that hard chromium electroplated is used to guarantee combinations of adhesion, hardness, corrosion and wear resistance, the method decreases the fatigue resistance of aeronautical components due to the high tensile residual stresses and microcracks density contained in the coating. In order to avoid this problem thermally sprayed HVOF coatings and shot peening process are widely used to improve surface properties of several alloys. The aim of the present study is to analyze the influence of Ni-Cr-B-Si-Fe coating applied by HVOF process on the axial fatigue strength of AISI 4340 steel. The shot peening effect on the fatigue results of coated AISI 4340 steel was also evaluated. The fractured fatigue specimens were investigated using a scanning electron microscope in order to obtain information about the crack initiation points. |
publishDate |
2015 |
dc.date.none.fl_str_mv |
2015-01-01 2018-12-11T16:39:49Z 2018-12-11T16:39:49Z |
dc.type.status.fl_str_mv |
info:eu-repo/semantics/publishedVersion |
dc.type.driver.fl_str_mv |
info:eu-repo/semantics/conferenceObject |
format |
conferenceObject |
status_str |
publishedVersion |
dc.identifier.uri.fl_str_mv |
http://dx.doi.org/10.1016/j.proeng.2015.08.111 Procedia Engineering, v. 114, p. 606-612. 1877-7058 http://hdl.handle.net/11449/168117 10.1016/j.proeng.2015.08.111 2-s2.0-84946056859 |
url |
http://dx.doi.org/10.1016/j.proeng.2015.08.111 http://hdl.handle.net/11449/168117 |
identifier_str_mv |
Procedia Engineering, v. 114, p. 606-612. 1877-7058 10.1016/j.proeng.2015.08.111 2-s2.0-84946056859 |
dc.language.iso.fl_str_mv |
eng |
language |
eng |
dc.relation.none.fl_str_mv |
Procedia Engineering 0,282 |
dc.rights.driver.fl_str_mv |
info:eu-repo/semantics/openAccess |
eu_rights_str_mv |
openAccess |
dc.format.none.fl_str_mv |
606-612 |
dc.source.none.fl_str_mv |
Scopus reponame:Repositório Institucional da UNESP instname:Universidade Estadual Paulista (UNESP) instacron:UNESP |
instname_str |
Universidade Estadual Paulista (UNESP) |
instacron_str |
UNESP |
institution |
UNESP |
reponame_str |
Repositório Institucional da UNESP |
collection |
Repositório Institucional da UNESP |
repository.name.fl_str_mv |
Repositório Institucional da UNESP - Universidade Estadual Paulista (UNESP) |
repository.mail.fl_str_mv |
|
_version_ |
1799965550811545600 |