Fractografia quantitativa: correlação entre dimensão fractal e tenacidade à fratura em compósitos fibra de carbono/epóxi

• Autor(a) principal: Augusto, Juliana [UNESP]
• Data de Publicação: 2012
• Tipo de documento: Trabalho de conclusão de curso
• Idioma: por
• Título da fonte: Repositório Institucional da UNESP
• Texto Completo: http://hdl.handle.net/11449/118138
• topic: Fractografia; Compositos polimericos

The fracture surfaces express the sequence of events of energy release due to crack propagation by linking the relief of the fracture to the loading stresses. This study aims to evaluate the heterogeneity of the critical zone for the advancement of the crack along its entire length in a thermoset composite carbon fiber and epoxy matrix, fractured in DCB testing (Double Cantilever Beam) and ENF (End-Notched Flexure). Investigations were made from image stacks obtained by optical reflection of extended depth from focus reconstruction. The program NIH Image J was used to obtain elevation map and fully focused images of the fracture surface, whose topographies were quantitatively analyzed. The monofractal behavior for DCB samples was assessed as being heterogeneous along the crack front and along the crack for all the conditionings. For the samples fractured in ENF test, there was a strong positive correlation to the natural condition, considering the fibers at 0° for the monofractal dimension and structural dimension (Df and Ds). For fibers at 90° to crack propagation, there was a moderate positive correlation for the textural dimension of natural condition. However, for the samples under ultraviolet condition and those subjected to thermal cycles, there was no correlation between the fractal dimension and fracture toughness in mode II