Avaliação da resistência interlaminar do compósito PEI/Fibras de carbono soldado pelo método de resistência elétrica

• Autor(a) principal: Reis, Jonas Frank [UNESP]
• Data de Publicação: 2016
• Outros Autores: Abrahao, Ana Beatriz Moreira, Costa, Michelle Leali [UNESP], Botelho, Edson Cocchieri [UNESP]
• Tipo de documento: Artigo
• Idioma: por
• Título da fonte: Repositório Institucional da UNESP
• Texto Completo: http://dx.doi.org/10.1590/0104-9224/SI2103.13; http://hdl.handle.net/11449/178368
• topic: Composites; Electrical resistance welding; Mechanical test; Thermal analyses

This study has as main objective to evaluate the effectiveness of the welding process by electrical resistance in composite poly (éterimida) matrix reinforced with continuous fibers of carbon, from the study of the thermal and mechanical properties of the welded joint. To evaluate the thermal properties of the welded material samples were subjected to analysis by thermogravimetry and by thermomechanical analysis. With the intention to study the resulting weld interface, studies were made from the shear tests ILSS and Iosipescu, as well as end-Notched Flexure (ENF). The results of the thermal analysis in laminated PEI / carbon fiber non-welded show that the beginning of degradation for these composites is 460 °C, and it is also evident that the glass transition temperature of welded samples is about 15% higher than the results from samples not welded. In the mechanical tests show that there was an increase of 32% and 20% respectively in interlaminar shear results for the ILSS and Iosipescu welded samples, when they are compared to samples not welded. The ENF test results show satisfactory values of interlaminar fracture toughness in the composite welded from the values found in literature.