Thermocycling effect on microhardness of laboratory composite resins

• Autor(a) principal: Pereira, Sarina Maciel Braga [UNESP]
• Data de Publicação: 2007
• Outros Autores: Castilho, Anderson Almeida [UNESP], Salazar-Marocho, Susana María [UNESP], Oliveira, Karla Mychellyne Costa [UNESP], Váquez, Vanessa Zulema Ccahuana [UNESP], Bottino, Marco Antonio [UNESP]
• Tipo de documento: Artigo
• Idioma: eng
• Título da fonte: Repositório Institucional da UNESP
• Texto Completo: http://www.bibliotecadigital.unicamp.br/document/?code=24151&print=y; http://hdl.handle.net/11449/69774
• topic: Composite resins; Microhardness; Thermocycling

Tha aim of this study was to evaluate the thermocycling effect on microhardness of laboratory composite resins, 30 disks were fabricated, 5mm of diameter and 2mm of width, using 3 laboratory resins: G1 (n=10) - RESILAB MASTER (Wilcos-Brasil), G2 (n=10) - Vita VMLC (VITA Zahnfabrik-Germany), and G3 (n=10) - Vita Zeta (VITA Zahnfabrik-Germany). Vickers microhardness (HV) of all specimens was evaluated using a microhardness tester FM-700 (Future Tech- 50 g/10s). The specimens were measured before and after the thermocycling (3,000 times and 12,000 times - 5°/55°C±1). The microhardness values before cycling were (mean±SD): G1: 55.50±4.6; G2: 35.54±2.5; G3: 27.97±1.6; after 3,000 thermocycles: G1: 55.54±3.9; G2: 29.92±2.73; G3:21.01±1.4 and after 12,000 cycles G1: 54.27±3.2; G2: 30.91±1.6; G3: 23.81±0.9. Variance analysis (ANOVA) and Tukey's test was accomplished (p<0.05), the highest microhardness values were observed in G1: G2 and G3 showed reduction of microhardness values. It was concluded that, after thermocycling, the tested laboratory composites resins are susceptible to the decrease of surface microhardness.