MECHANICAL BEHAVIOR OF CARBON FIBER/EPDXY FILAMENT WOUND LAMINATES EXPOSED TO HYGROTHERMAL CONDITIONING

• Autor(a) principal: Almeida Jr, Jose Humberto S.
• Data de Publicação: 2015
• Outros Autores: Souza, Samia D. B. [UNESP], Botelho, Edson C. [UNESP], Amico, Sandro C., Thomsen, O. T., Berggreen, C., Sorensen, B. F.
• Tipo de documento: Artigo de conferência
• Idioma: eng
• Título da fonte: Repositório Institucional da UNESP
• Texto Completo: http://hdl.handle.net/11449/218612
• topic: Advanced composites; environmental effect; filament winding; mechanical performance

This work aims to evaluate the effect of hygrothermal conditioning on the tensile, in-plane shear and viscoelastic properties of carbon fiber/epoxy laminates (fiber volume fraction approximate to 70%). The flat unidirectional laminates were manufactured by filament winding process using a KUKA robot and the composites were cured under hot compression molding. The laminates were later exposed to hygrothermal conditioning. All composite samples were tested before and after environmental conditioning in a hygrothermal chamber. Elastic and strength tensile properties reduced for aged specimens, e.g. [O](4) sample presented a reduction of 18% in tensile strength and 8% in elastic modulus. Shear strength and modulus followed the same trend, and shear modulus reduced in about 38%. Tensile and shear post-test specimens presented accepted failure modes, since for instance, shear specimens failed at the gage section with delaminations.