Análise estrutural de aerogéis via espalhamento de luz a baixo ângulo

• Autor(a) principal: Lima, Bruna Patrocinio [UNESP]
• Data de Publicação: 2015
• Tipo de documento: Trabalho de conclusão de curso
• Idioma: por
• Título da fonte: Repositório Institucional da UNESP
• Texto Completo: http://hdl.handle.net/11449/131803; http://www.athena.biblioteca.unesp.br/exlibris/bd/capelo/2015-10-22/000852630.pdf
• topic: Física aplicada; Processo sol-gel; Adsorção; Gases - Absorção e adsorção; Nitrogenio; Fractais

The sol-gel process is a method for obtaining vitreous or vitro-ceramic materials which, are prepared a sol and by drying the liquid phase. This technique has been used extensively for the preparation of glassy gels, films, fibers and particles from the hydrolysis and polycondensation reactions of metal alkoxides. The usual methods for drying are: evaporation drying (xerogels), freeze drying (criogéis) and via supercritical CO2 extraction (aerogels). In the present work, we studied the preparation of silica gels by the sol-gel process from the hydrolysis of alkoxides tetraethylorthosilicate (TEOS) and 3-glycidoxypropyltrimethoxysilane (GPTS). The hydrolysis was promoted from GPTS and TEOS in proportion (4: 1) under acidic conditions. The hydrolysis reaction was promoted inside a Becker at room temperature. After hydrolyses the prepared sol had pH 2, and kept under mechanical agitation for a period of 1 hour. In order to accelerate the polycondensation reaction, the pH was corrected to a value near 5 by slowly adding NH4OH. Then the sols were leaked in sealed polycarbonate containers and maintained for 20 days at 40°C for gelation. Silica aerogels were prepared via supercritical CO2 extraction of the wet gel at temperature and pressure higher than 31°C and 74 atm, in an autoclave specially developed for the process. The structural characteristics were studied in the dry gel (aerogel). Aerogels were then characterized by nitrogen adsorption and small angle light scattering. The nitrogen adsorption data were analyzed for the determination of the BET specific surface (SBET), the total pore volume Vp, the pore mean size (lP=4Vp/SBET), the particle mean size (lS) and the pore size distribution (PSD). And the data from small angle light scattering were analyzed to determine the correlation function (γ'), the area per unit volume (S/V), average pore size (l ) and the average particle size...