Influence of the hybrid layer thickness and resin tag length on microtensile bond strength.

• Autor(a) principal: Rahal, Vanessa
• Data de Publicação: 2011
• Outros Autores: Briso, André Luiz Fraga [UNESP], Santos, Paulo Henrique dos [UNESP], Sundefeld, Maria Lúcia Marçal Mazza [UNESP], Sundfeld, Renato Herman [UNESP]
• Tipo de documento: Artigo
• Idioma: eng
• Título da fonte: Repositório Institucional da UNESP
• Texto Completo: http://www.actaodontologicalat.com/archivo/v24n1/fulltext/articulo2.pdf; http://hdl.handle.net/11449/72963
• topic: Adper single bond 2; resin cement; tooth cement; dental bonding; materials testing; surface property; tensile strength; Dental Bonding; Dental Cements; Materials Testing; Resin Cements; Surface Properties; Tensile Strength

The purpose of this study was to evaluate the correlation between the hybrid layer thickness/resin tag length and the microtensile bond strength of conventional two-step adhesive system, when applied to healthy dentinal tissue. After performing the restorative adhesive procedures and tooth extractions, ten specimens were sectioned in the mesiodistal direction. One section was used for microscopic analysis of the resin tag lengths and the hybrid layer thickness, while the other was used for the microtensile bond strength test (0.5 mm/min). The fractured surface was classified according to the fracture pattern, under a stereoscopic microscope at 40x magnification. Data obtained were submitted to analysis using one-way ANOVA and Pearson's Correlation test (alpha=0.05). The means corresponding to the hybrid layer thickness, resin tag lengths and the microtensile test were 2.68 microm, 6.43 microm and 16.23 MPa, respectively. There was no correlation between the means of the values obtained for the microtensile test, and those presented by the hybrid layer (r2=0.40, p>0.05) and resin tags (r2=0.21, p>0.05). The microtensile bond strength of the conventional two-step adhesive system Adper Single Bond 2 did not depend on the thickness of the hybrid layer and length of resin tags.