Estudo da influência do agente nucleante )ALTi5%B1%) na microestrutura de chapas AA8011 obtidas por lingotamento contínuo

• Autor(a) principal: Almada, Gabriel Carvalho [UNESP]
• Data de Publicação: 2015
• Tipo de documento: Trabalho de conclusão de curso
• Idioma: por
• Título da fonte: Repositório Institucional da UNESP
• Texto Completo: http://hdl.handle.net/11449/123078; http://www.athena.biblioteca.unesp.br/exlibris/bd/capelo/2015-05-04/000821235.pdf
• topic: Fundição continua; Ligas de aluminio; Microestrutura; Cristalografia; Chapas de aluminio; Aluminum alloys

The aluminum includes several properties with excellent relation between weight and mechanical resistance. With technological advances, increasingly demand the development of new alloys and other production processes in order to reduce the cost of production and insert these new alloys in broader applications. The process of continuous caster (TRC promoted the unite of the aluminum smelting process with the first stage of rolling, making it most economical through the merger these two phases besides transform the continuous casting process. The AA8xxx series is one of the most versatile aluminum alloys and the most often used in continuous caster process provided a great potential application in the market. In order to further, optimize the process it is necessary to increase awareness of the aluminum solidification phenomena associated with the addition of grain refiner, and control of some aluminum production parameters in the process (production rate, metal temperature, etc.). In this study, AA8011 alloy samples were taken in the raw state obtained by the continuous casting process. The samples were laminated to a thickness of 7mm during the process itself and analyzed at three points along its width by microstructural analysis throughout its thickness, the variation rate of addition of the grain refiner in order to assess the influence of this addition with crystallographic formation and some formation of intermetallic precipitates during the solidification. Through this work, it was possible to improve the knowledge related to the addition of refiner with the monitoring of these production processes