Comportamento de fadiga de uma cerâmica de uma cerâmica à base de silicato comportamento de fadiga de uma cerâmica à base de silicato de lítio e zircônia -
Autor(a) principal: | |
---|---|
Data de Publicação: | 2017 |
Tipo de documento: | Dissertação |
Idioma: | por |
Título da fonte: | Biblioteca de teses e dissertações da Universidade de Passo Fundo (BDTD UPF) |
Texto Completo: | http://tede.upf.br/jspui/handle/tede/1384 |
Resumo: | To evaluate the fatigue behavior of zirconia-reinforced lithium silicate ceramic (ZLS - VITA Suprinity, Vita Zahnfabrik), using the boundary and staircase methods. Methods: One hundred and twenty five ZLS ceramic bars with the dimensions of 18 mm x 4 mm x 1.2 mm were produced. Thirty specimens were tested for three-point bending using a universal testing machine in 37oC distilled water. Flexural strength data were analysed using Weibull statistics. Ninety five bars were subjected to cyclic fatigue using boundary and staircase methods. Fatigue tests were performed on a pneumatic cycling machine with a frequency of 2 Hz in 37oC distilled water. Two lifetimes were evaluated in each method, 10³ and 104cycles. Vickers hardness (HV) was evaluated using a microdurometer with a load of 4.9 N for 20 s.Fractographic analysis and EDS analysis of the specimens were also performed. Results: ZLS obtained a mean flexural strength of 178 MPa, Weibull modulus of 4 and HV of 680 MPa. After 103 cycles, for both methods, there was a degradation of 78% of the initial flexural strength. There was no significant degradation when the cycling time increased from 103 to 104cycles. For both the staircase and boundary methods, the stress for a failure probability of 50% (50%) after 10 cycles was 39 |
id |
UPF-1_5132502841de19b0b012f089f465805a |
---|---|
oai_identifier_str |
oai:tede.upf.br:tede/1384 |
network_acronym_str |
UPF-1 |
network_name_str |
Biblioteca de teses e dissertações da Universidade de Passo Fundo (BDTD UPF) |
repository_id_str |
|
spelling |
Borba, Márcia99782944068http://lattes.cnpq.br/523007456624738801996293042http://lattes.cnpq.br/7925834726491908Ottoni, Rodrigo2018-06-04T17:29:21Z2017-03-17OTTONI, Rodrigo. Comportamento de fadiga de uma cerâmica à base de silicato de lítio e zircônia - método Boundary vs. Staircase. 2017. 155 f. Dissertação (Mestrado em Odontologia) - Universidade de Passo Fundo, Passo Fundo, RS, 2017.http://tede.upf.br/jspui/handle/tede/1384To evaluate the fatigue behavior of zirconia-reinforced lithium silicate ceramic (ZLS - VITA Suprinity, Vita Zahnfabrik), using the boundary and staircase methods. Methods: One hundred and twenty five ZLS ceramic bars with the dimensions of 18 mm x 4 mm x 1.2 mm were produced. Thirty specimens were tested for three-point bending using a universal testing machine in 37oC distilled water. Flexural strength data were analysed using Weibull statistics. Ninety five bars were subjected to cyclic fatigue using boundary and staircase methods. Fatigue tests were performed on a pneumatic cycling machine with a frequency of 2 Hz in 37oC distilled water. Two lifetimes were evaluated in each method, 10³ and 104cycles. Vickers hardness (HV) was evaluated using a microdurometer with a load of 4.9 N for 20 s.Fractographic analysis and EDS analysis of the specimens were also performed. Results: ZLS obtained a mean flexural strength of 178 MPa, Weibull modulus of 4 and HV of 680 MPa. After 103 cycles, for both methods, there was a degradation of 78% of the initial flexural strength. There was no significant degradation when the cycling time increased from 103 to 104cycles. For both the staircase and boundary methods, the stress for a failure probability of 50% (50%) after 10 cycles was 39Avaliar o comportamento de fadiga de uma cerâmica à base de silicato de lítio e zircônia (ZLS - VITA Suprinity, Vita Zahnfabrik), utilizando os métodos boundary e staircase. Métodos: Foram confeccionadas cento e vinte e cinco barras de cerâmica ZLS com as dimensões de 18 mm x 4 mm x 1,2 mm. Trinta corpos-de-prova foram testados em flexão em três pontos utilizando uma máquina de ensaio universal, em água destilada a 37oC. Os dados de flexão foram analisados com estatística de Weibull. Noventa e cinco barras foram submetidas aos ensaios de fadiga cíclica pelos métodos boundary e staircase. Os ensaios de fadiga foram realizados em uma máquina de ciclagem pneumática, com uma frequência de 2 Hz, em água destilada a 37oC. Dois tempos de vida foram avaliados em cada método, 10³ e 104 ciclos. A dureza Vickers (HV) foi avaliada em um microdurômetro com uma carga de 4,9 N por 20 s. Foi realizada análise fractográfica e análise de EDS dos corpos-de-prova. Resultados: A ZLS obteve resistência flexural média de 178 MPa, módulo de Weibull de 4 e HV de 680 MPa. Após 103 ciclos, para ambos os métodos, houve uma degradação de 78% da resistência à flexão inicial. Não houve uma degradação significativa quando o tempo de ciclagem aumentou de 103 para 104 ciclos. Tanto para o método staircase como para o boundary, a resistência para uma probabilidade de falha de 50% (50%) após 103 ciclos foi de 39 MPa. Após 104 ciclos 50% foi de 34 MPa no método boundary e 37 MPa no método staircase. A origem das falhas foi localizada na superfície de tração dos corpos-de-prova. O EDS revelou a presença de 11,8% de zircônio na ZLS. Conclusão: A ZLS apresentou significativa degradação das propriedades mecânicas em fadiga. Houve uma boa concordância entre os dois métodos de fadiga investigados.Submitted by Aline Rezende (alinerezende@upf.br) on 2018-06-04T17:29:21Z No. of bitstreams: 1 2017RodrigoOttoni.pdf: 2201873 bytes, checksum: 7d08606f10198ef4fdb31c7587a23ac9 (MD5)Made available in DSpace on 2018-06-04T17:29:21Z (GMT). No. of bitstreams: 1 2017RodrigoOttoni.pdf: 2201873 bytes, checksum: 7d08606f10198ef4fdb31c7587a23ac9 (MD5) Previous issue date: 2017-03-17application/pdfporUniversidade de Passo FundoPrograma de Pós-Graduação em OdontologiaUPFBrasilFaculdade de Odontologia – FOOdontologiaCerâmica odontológicaSistemas CAD/CAMCIENCIAS DA SAUDE::ODONTOLOGIAComportamento de fadiga de uma cerâmica de uma cerâmica à base de silicato comportamento de fadiga de uma cerâmica à base de silicato de lítio e zircônia -Fatigue behavior of a ceramic of a ceramic-based silicate fatigue behavior of a ceramic based on lithium silicate and zirconia -info:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/masterThesis-80965548187336651645005006008090167142064557236-2070498469879244349info:eu-repo/semantics/openAccessreponame:Biblioteca de teses e dissertações da Universidade de Passo Fundo (BDTD UPF)instname:Universidade de Passo Fundo (UPF)instacron:UPFLICENSElicense.txtlicense.txttext/plain; charset=utf-81940http://tede.upf.br:8080/jspui/bitstream/tede/1384/1/license.txte0faded76e3df80302a4a0fb3f2bb5f3MD51ORIGINAL2017RodrigoOttoni.pdf2017RodrigoOttoni.pdfapplication/pdf2201873http://tede.upf.br:8080/jspui/bitstream/tede/1384/2/2017RodrigoOttoni.pdf7d08606f10198ef4fdb31c7587a23ac9MD52tede/13842020-02-19 16:52:47.132oai:tede.upf.br: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Biblioteca Digital de Teses e DissertaçõesPUBhttp://tede.upf.br/oai/requestbiblio@upf.br || bio@upf.br || cas@upf.br || car@upf.br || lve@upf.br || sar@upf.br || sol@upf.br || upfmundi@upf.br || jucelei@upf.bropendoar:2020-02-19T19:52:47Biblioteca de teses e dissertações da Universidade de Passo Fundo (BDTD UPF) - Universidade de Passo Fundo (UPF)false |
dc.title.por.fl_str_mv |
Comportamento de fadiga de uma cerâmica de uma cerâmica à base de silicato comportamento de fadiga de uma cerâmica à base de silicato de lítio e zircônia - |
dc.title.alternative.eng.fl_str_mv |
Fatigue behavior of a ceramic of a ceramic-based silicate fatigue behavior of a ceramic based on lithium silicate and zirconia - |
title |
Comportamento de fadiga de uma cerâmica de uma cerâmica à base de silicato comportamento de fadiga de uma cerâmica à base de silicato de lítio e zircônia - |
spellingShingle |
Comportamento de fadiga de uma cerâmica de uma cerâmica à base de silicato comportamento de fadiga de uma cerâmica à base de silicato de lítio e zircônia - Ottoni, Rodrigo Odontologia Cerâmica odontológica Sistemas CAD/CAM CIENCIAS DA SAUDE::ODONTOLOGIA |
title_short |
Comportamento de fadiga de uma cerâmica de uma cerâmica à base de silicato comportamento de fadiga de uma cerâmica à base de silicato de lítio e zircônia - |
title_full |
Comportamento de fadiga de uma cerâmica de uma cerâmica à base de silicato comportamento de fadiga de uma cerâmica à base de silicato de lítio e zircônia - |
title_fullStr |
Comportamento de fadiga de uma cerâmica de uma cerâmica à base de silicato comportamento de fadiga de uma cerâmica à base de silicato de lítio e zircônia - |
title_full_unstemmed |
Comportamento de fadiga de uma cerâmica de uma cerâmica à base de silicato comportamento de fadiga de uma cerâmica à base de silicato de lítio e zircônia - |
title_sort |
Comportamento de fadiga de uma cerâmica de uma cerâmica à base de silicato comportamento de fadiga de uma cerâmica à base de silicato de lítio e zircônia - |
author |
Ottoni, Rodrigo |
author_facet |
Ottoni, Rodrigo |
author_role |
author |
dc.contributor.advisor1.fl_str_mv |
Borba, Márcia |
dc.contributor.advisor1ID.fl_str_mv |
99782944068 |
dc.contributor.advisor1Lattes.fl_str_mv |
http://lattes.cnpq.br/5230074566247388 |
dc.contributor.authorID.fl_str_mv |
01996293042 |
dc.contributor.authorLattes.fl_str_mv |
http://lattes.cnpq.br/7925834726491908 |
dc.contributor.author.fl_str_mv |
Ottoni, Rodrigo |
contributor_str_mv |
Borba, Márcia |
dc.subject.por.fl_str_mv |
Odontologia Cerâmica odontológica Sistemas CAD/CAM |
topic |
Odontologia Cerâmica odontológica Sistemas CAD/CAM CIENCIAS DA SAUDE::ODONTOLOGIA |
dc.subject.cnpq.fl_str_mv |
CIENCIAS DA SAUDE::ODONTOLOGIA |
description |
To evaluate the fatigue behavior of zirconia-reinforced lithium silicate ceramic (ZLS - VITA Suprinity, Vita Zahnfabrik), using the boundary and staircase methods. Methods: One hundred and twenty five ZLS ceramic bars with the dimensions of 18 mm x 4 mm x 1.2 mm were produced. Thirty specimens were tested for three-point bending using a universal testing machine in 37oC distilled water. Flexural strength data were analysed using Weibull statistics. Ninety five bars were subjected to cyclic fatigue using boundary and staircase methods. Fatigue tests were performed on a pneumatic cycling machine with a frequency of 2 Hz in 37oC distilled water. Two lifetimes were evaluated in each method, 10³ and 104cycles. Vickers hardness (HV) was evaluated using a microdurometer with a load of 4.9 N for 20 s.Fractographic analysis and EDS analysis of the specimens were also performed. Results: ZLS obtained a mean flexural strength of 178 MPa, Weibull modulus of 4 and HV of 680 MPa. After 103 cycles, for both methods, there was a degradation of 78% of the initial flexural strength. There was no significant degradation when the cycling time increased from 103 to 104cycles. For both the staircase and boundary methods, the stress for a failure probability of 50% (50%) after 10 cycles was 39 |
publishDate |
2017 |
dc.date.issued.fl_str_mv |
2017-03-17 |
dc.date.accessioned.fl_str_mv |
2018-06-04T17:29:21Z |
dc.type.status.fl_str_mv |
info:eu-repo/semantics/publishedVersion |
dc.type.driver.fl_str_mv |
info:eu-repo/semantics/masterThesis |
format |
masterThesis |
status_str |
publishedVersion |
dc.identifier.citation.fl_str_mv |
OTTONI, Rodrigo. Comportamento de fadiga de uma cerâmica à base de silicato de lítio e zircônia - método Boundary vs. Staircase. 2017. 155 f. Dissertação (Mestrado em Odontologia) - Universidade de Passo Fundo, Passo Fundo, RS, 2017. |
dc.identifier.uri.fl_str_mv |
http://tede.upf.br/jspui/handle/tede/1384 |
identifier_str_mv |
OTTONI, Rodrigo. Comportamento de fadiga de uma cerâmica à base de silicato de lítio e zircônia - método Boundary vs. Staircase. 2017. 155 f. Dissertação (Mestrado em Odontologia) - Universidade de Passo Fundo, Passo Fundo, RS, 2017. |
url |
http://tede.upf.br/jspui/handle/tede/1384 |
dc.language.iso.fl_str_mv |
por |
language |
por |
dc.relation.program.fl_str_mv |
-8096554818733665164 |
dc.relation.confidence.fl_str_mv |
500 500 600 |
dc.relation.department.fl_str_mv |
8090167142064557236 |
dc.relation.cnpq.fl_str_mv |
-2070498469879244349 |
dc.rights.driver.fl_str_mv |
info:eu-repo/semantics/openAccess |
eu_rights_str_mv |
openAccess |
dc.format.none.fl_str_mv |
application/pdf |
dc.publisher.none.fl_str_mv |
Universidade de Passo Fundo |
dc.publisher.program.fl_str_mv |
Programa de Pós-Graduação em Odontologia |
dc.publisher.initials.fl_str_mv |
UPF |
dc.publisher.country.fl_str_mv |
Brasil |
dc.publisher.department.fl_str_mv |
Faculdade de Odontologia – FO |
publisher.none.fl_str_mv |
Universidade de Passo Fundo |
dc.source.none.fl_str_mv |
reponame:Biblioteca de teses e dissertações da Universidade de Passo Fundo (BDTD UPF) instname:Universidade de Passo Fundo (UPF) instacron:UPF |
instname_str |
Universidade de Passo Fundo (UPF) |
instacron_str |
UPF |
institution |
UPF |
reponame_str |
Biblioteca de teses e dissertações da Universidade de Passo Fundo (BDTD UPF) |
collection |
Biblioteca de teses e dissertações da Universidade de Passo Fundo (BDTD UPF) |
bitstream.url.fl_str_mv |
http://tede.upf.br:8080/jspui/bitstream/tede/1384/1/license.txt http://tede.upf.br:8080/jspui/bitstream/tede/1384/2/2017RodrigoOttoni.pdf |
bitstream.checksum.fl_str_mv |
e0faded76e3df80302a4a0fb3f2bb5f3 7d08606f10198ef4fdb31c7587a23ac9 |
bitstream.checksumAlgorithm.fl_str_mv |
MD5 MD5 |
repository.name.fl_str_mv |
Biblioteca de teses e dissertações da Universidade de Passo Fundo (BDTD UPF) - Universidade de Passo Fundo (UPF) |
repository.mail.fl_str_mv |
biblio@upf.br || bio@upf.br || cas@upf.br || car@upf.br || lve@upf.br || sar@upf.br || sol@upf.br || upfmundi@upf.br || jucelei@upf.br |
_version_ |
1809092290399961088 |