Influência do método de fabricação no comportamento de fratura de coroas totalmente cerâmicas
Autor(a) principal: | |
---|---|
Data de Publicação: | 2014 |
Tipo de documento: | Dissertação |
Idioma: | por |
Título da fonte: | Biblioteca de teses e dissertações da Universidade de Passo Fundo (BDTD UPF) |
Texto Completo: | http://tede.upf.br/jspui/handle/tede/1639 |
Resumo: | In-Ceram Zirconia is an alumina-based zirconia-reinforced glassinfiltrated ceramic produced using two different techniques, slip-cast and CAD-CAM. Ceramics microstructure and fabrication methods are related to restorations mechanical performance. Thus, the objective of this study was to evaluate the influence of In-Ceram Zirconia’s fabrication method on the failure behavior of all-ceramic crowns. A glass fiber-reinforced composite die simulating a prosthetic preparation was used to produce the crowns. Two groups of crowns with In-Ceram Zirconia infrastructure (IE) were evaluated (n=30): IZC – IE produced with CAD/CAM technology and IZS – IE produced using slip-cast technique. IE were veneered with porcelain (Vita VM7) and cemented over the die with resin cement. Crowns were tested until failure using a universal testing machine with a compressive load being applied parallel to the crown long axis, with 1 mm/min cross -head speed, in 37º distilled water. Fractographic analysis was performed using a stereomicroscope. Data were statistically analyzed with student t test (α=0.05) and Weibull analysis. There was no significant differences between the experimental groups for the fracture load (p=0.481). Weibull modulus and characteristic strength were also similar among groups. For both groups, the failure mode was catastrophic failure involving IE and porcelain. It was concluded that both fabrication methods resulted in all-ceramic crowns with similar failure behavior and reliability. |
id |
UPF-1_72b4f1ce2176fdbbcbf31971c17ac221 |
---|---|
oai_identifier_str |
oai:tede.upf.br:tede/1639 |
network_acronym_str |
UPF-1 |
network_name_str |
Biblioteca de teses e dissertações da Universidade de Passo Fundo (BDTD UPF) |
repository_id_str |
|
spelling |
Borba, Márcia99782944068http://lattes.cnpq.br/523007456624738800716845067http://lattes.cnpq.br/3032802477732657Piccoli, Ana Carolina Antunes2019-03-20T19:18:22Z2014-04-30PICCOLI, Ana Carolina Antunes. Influência do método de fabricação no comportamento de fratura de coroas totalmente cerâmicas. 2014. 88 f. Dissertação (Mestrado em Odontologia) - Universidade de Passo Fundo, Passo Fundo, RS, 2014.http://tede.upf.br/jspui/handle/tede/1639In-Ceram Zirconia is an alumina-based zirconia-reinforced glassinfiltrated ceramic produced using two different techniques, slip-cast and CAD-CAM. Ceramics microstructure and fabrication methods are related to restorations mechanical performance. Thus, the objective of this study was to evaluate the influence of In-Ceram Zirconia’s fabrication method on the failure behavior of all-ceramic crowns. A glass fiber-reinforced composite die simulating a prosthetic preparation was used to produce the crowns. Two groups of crowns with In-Ceram Zirconia infrastructure (IE) were evaluated (n=30): IZC – IE produced with CAD/CAM technology and IZS – IE produced using slip-cast technique. IE were veneered with porcelain (Vita VM7) and cemented over the die with resin cement. Crowns were tested until failure using a universal testing machine with a compressive load being applied parallel to the crown long axis, with 1 mm/min cross -head speed, in 37º distilled water. Fractographic analysis was performed using a stereomicroscope. Data were statistically analyzed with student t test (α=0.05) and Weibull analysis. There was no significant differences between the experimental groups for the fracture load (p=0.481). Weibull modulus and characteristic strength were also similar among groups. For both groups, the failure mode was catastrophic failure involving IE and porcelain. It was concluded that both fabrication methods resulted in all-ceramic crowns with similar failure behavior and reliability.A In-Ceram Zircônia é uma cerâmica à base de alumina, reforçada com zircônia e infiltrada com vidro, que pode ser fabricada com duas técnicas diferentes, slip-cast (barbotina) e CAD-CAM. A microestrutura e os métodos de fabricação das restaurações cerâmicas estão diretamente relacionados com seu desempenho mecânico. Por isso, o objetivo deste estudo foi avaliar a influência da técnica de fabricação da In-Ceram Zircônia no comportamento de fratura de coroas totalmente cerâmicas. As coroas foram confeccionadas a partir de um modelo de resina epóxica reforçada por fibra de vidro (G10) simulando um preparo protético. Foram avaliados dois grupos de coroas com infraestrutura (IE) de In- Ceram Zircônia (Vita) (n=30): IZC ¿ IE fabricada com a técnica CAD/CAM e IZS ¿ IE fabricada com a técnica slip-cast. As IE foram recobertas com porcelana (Vita VM7) e cimentadas sobre o preparo com cimento resinoso. As coroas foram testadas até a fratura em uma máquina de ensaios com uma carga compressiva aplicada paralela ao longo eixo da coroa, com velocidade de 1 mm/min, em água destilada a 37°C. Foi realizada análise fractografica utilizando estereomicroscópio. Os dados foram analisados com teste t de student (¿=0,05) e análise estatística de Weibull. Não foi encontrada diferença estatística entre os grupos experimentais para carga de fratura (p=0,481). Os valores de módulo de Weibull e resistência caracterísitca também foram semelhantes entre os grupos. Para ambos os grupos o tipo de falha predominante foi catastrófica, envolvendo a porcelana e a IE. Concluiuse que ambos os métodos de fabricação resultaram em coroas com comportamento de fratura e confiabilidade semelhantes.Submitted by Aline Rezende (alinerezende@upf.br) on 2019-03-20T19:18:22Z No. of bitstreams: 1 Ana Piccoli 2019.pdf: 2771990 bytes, checksum: c144e151558cee21aed98efbb20f06a6 (MD5)Made available in DSpace on 2019-03-20T19:18:22Z (GMT). No. of bitstreams: 1 Ana Piccoli 2019.pdf: 2771990 bytes, checksum: c144e151558cee21aed98efbb20f06a6 (MD5) Previous issue date: 2014-04-30application/pdfporUniversidade de Passo FundoPrograma de Pós-Graduação em OdontologiaUPFBrasilFaculdade de Odontologia – FOCerâmica odontológicaMateriais dentáriosRestauração (Odontologia)Prótese dentáriaCIENCIAS DA SAUDE::ODONTOLOGIAInfluência do método de fabricação no comportamento de fratura de coroas totalmente cerâmicasInfluence of the manufacturing method on the fracture behavior of all-ceramic crownsinfo:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/masterThesis-80965548187336651645005006008090167142064557236-2070498469879244349info:eu-repo/semantics/openAccessreponame:Biblioteca de teses e dissertações da Universidade de Passo Fundo (BDTD UPF)instname:Universidade de Passo Fundo (UPF)instacron:UPFLICENSElicense.txtlicense.txttext/plain; charset=utf-81940http://tede.upf.br:8080/jspui/bitstream/tede/1639/1/license.txte0faded76e3df80302a4a0fb3f2bb5f3MD51ORIGINALAna Piccoli 2019.pdfAna Piccoli 2019.pdfapplication/pdf2771990http://tede.upf.br:8080/jspui/bitstream/tede/1639/2/Ana+Piccoli+2019.pdfc144e151558cee21aed98efbb20f06a6MD52tede/16392020-02-19 16:53:55.857oai:tede.upf.br: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Biblioteca Digital de Teses e DissertaçõesPUBhttp://tede.upf.br/oai/requestbiblio@upf.br || bio@upf.br || cas@upf.br || car@upf.br || lve@upf.br || sar@upf.br || sol@upf.br || upfmundi@upf.br || jucelei@upf.bropendoar:2020-02-19T19:53:55Biblioteca de teses e dissertações da Universidade de Passo Fundo (BDTD UPF) - Universidade de Passo Fundo (UPF)false |
dc.title.por.fl_str_mv |
Influência do método de fabricação no comportamento de fratura de coroas totalmente cerâmicas |
dc.title.alternative.eng.fl_str_mv |
Influence of the manufacturing method on the fracture behavior of all-ceramic crowns |
title |
Influência do método de fabricação no comportamento de fratura de coroas totalmente cerâmicas |
spellingShingle |
Influência do método de fabricação no comportamento de fratura de coroas totalmente cerâmicas Piccoli, Ana Carolina Antunes Cerâmica odontológica Materiais dentários Restauração (Odontologia) Prótese dentária CIENCIAS DA SAUDE::ODONTOLOGIA |
title_short |
Influência do método de fabricação no comportamento de fratura de coroas totalmente cerâmicas |
title_full |
Influência do método de fabricação no comportamento de fratura de coroas totalmente cerâmicas |
title_fullStr |
Influência do método de fabricação no comportamento de fratura de coroas totalmente cerâmicas |
title_full_unstemmed |
Influência do método de fabricação no comportamento de fratura de coroas totalmente cerâmicas |
title_sort |
Influência do método de fabricação no comportamento de fratura de coroas totalmente cerâmicas |
author |
Piccoli, Ana Carolina Antunes |
author_facet |
Piccoli, Ana Carolina Antunes |
author_role |
author |
dc.contributor.advisor1.fl_str_mv |
Borba, Márcia |
dc.contributor.advisor1ID.fl_str_mv |
99782944068 |
dc.contributor.advisor1Lattes.fl_str_mv |
http://lattes.cnpq.br/5230074566247388 |
dc.contributor.authorID.fl_str_mv |
00716845067 |
dc.contributor.authorLattes.fl_str_mv |
http://lattes.cnpq.br/3032802477732657 |
dc.contributor.author.fl_str_mv |
Piccoli, Ana Carolina Antunes |
contributor_str_mv |
Borba, Márcia |
dc.subject.por.fl_str_mv |
Cerâmica odontológica Materiais dentários Restauração (Odontologia) Prótese dentária |
topic |
Cerâmica odontológica Materiais dentários Restauração (Odontologia) Prótese dentária CIENCIAS DA SAUDE::ODONTOLOGIA |
dc.subject.cnpq.fl_str_mv |
CIENCIAS DA SAUDE::ODONTOLOGIA |
description |
In-Ceram Zirconia is an alumina-based zirconia-reinforced glassinfiltrated ceramic produced using two different techniques, slip-cast and CAD-CAM. Ceramics microstructure and fabrication methods are related to restorations mechanical performance. Thus, the objective of this study was to evaluate the influence of In-Ceram Zirconia’s fabrication method on the failure behavior of all-ceramic crowns. A glass fiber-reinforced composite die simulating a prosthetic preparation was used to produce the crowns. Two groups of crowns with In-Ceram Zirconia infrastructure (IE) were evaluated (n=30): IZC – IE produced with CAD/CAM technology and IZS – IE produced using slip-cast technique. IE were veneered with porcelain (Vita VM7) and cemented over the die with resin cement. Crowns were tested until failure using a universal testing machine with a compressive load being applied parallel to the crown long axis, with 1 mm/min cross -head speed, in 37º distilled water. Fractographic analysis was performed using a stereomicroscope. Data were statistically analyzed with student t test (α=0.05) and Weibull analysis. There was no significant differences between the experimental groups for the fracture load (p=0.481). Weibull modulus and characteristic strength were also similar among groups. For both groups, the failure mode was catastrophic failure involving IE and porcelain. It was concluded that both fabrication methods resulted in all-ceramic crowns with similar failure behavior and reliability. |
publishDate |
2014 |
dc.date.issued.fl_str_mv |
2014-04-30 |
dc.date.accessioned.fl_str_mv |
2019-03-20T19:18:22Z |
dc.type.status.fl_str_mv |
info:eu-repo/semantics/publishedVersion |
dc.type.driver.fl_str_mv |
info:eu-repo/semantics/masterThesis |
format |
masterThesis |
status_str |
publishedVersion |
dc.identifier.citation.fl_str_mv |
PICCOLI, Ana Carolina Antunes. Influência do método de fabricação no comportamento de fratura de coroas totalmente cerâmicas. 2014. 88 f. Dissertação (Mestrado em Odontologia) - Universidade de Passo Fundo, Passo Fundo, RS, 2014. |
dc.identifier.uri.fl_str_mv |
http://tede.upf.br/jspui/handle/tede/1639 |
identifier_str_mv |
PICCOLI, Ana Carolina Antunes. Influência do método de fabricação no comportamento de fratura de coroas totalmente cerâmicas. 2014. 88 f. Dissertação (Mestrado em Odontologia) - Universidade de Passo Fundo, Passo Fundo, RS, 2014. |
url |
http://tede.upf.br/jspui/handle/tede/1639 |
dc.language.iso.fl_str_mv |
por |
language |
por |
dc.relation.program.fl_str_mv |
-8096554818733665164 |
dc.relation.confidence.fl_str_mv |
500 500 600 |
dc.relation.department.fl_str_mv |
8090167142064557236 |
dc.relation.cnpq.fl_str_mv |
-2070498469879244349 |
dc.rights.driver.fl_str_mv |
info:eu-repo/semantics/openAccess |
eu_rights_str_mv |
openAccess |
dc.format.none.fl_str_mv |
application/pdf |
dc.publisher.none.fl_str_mv |
Universidade de Passo Fundo |
dc.publisher.program.fl_str_mv |
Programa de Pós-Graduação em Odontologia |
dc.publisher.initials.fl_str_mv |
UPF |
dc.publisher.country.fl_str_mv |
Brasil |
dc.publisher.department.fl_str_mv |
Faculdade de Odontologia – FO |
publisher.none.fl_str_mv |
Universidade de Passo Fundo |
dc.source.none.fl_str_mv |
reponame:Biblioteca de teses e dissertações da Universidade de Passo Fundo (BDTD UPF) instname:Universidade de Passo Fundo (UPF) instacron:UPF |
instname_str |
Universidade de Passo Fundo (UPF) |
instacron_str |
UPF |
institution |
UPF |
reponame_str |
Biblioteca de teses e dissertações da Universidade de Passo Fundo (BDTD UPF) |
collection |
Biblioteca de teses e dissertações da Universidade de Passo Fundo (BDTD UPF) |
bitstream.url.fl_str_mv |
http://tede.upf.br:8080/jspui/bitstream/tede/1639/1/license.txt http://tede.upf.br:8080/jspui/bitstream/tede/1639/2/Ana+Piccoli+2019.pdf |
bitstream.checksum.fl_str_mv |
e0faded76e3df80302a4a0fb3f2bb5f3 c144e151558cee21aed98efbb20f06a6 |
bitstream.checksumAlgorithm.fl_str_mv |
MD5 MD5 |
repository.name.fl_str_mv |
Biblioteca de teses e dissertações da Universidade de Passo Fundo (BDTD UPF) - Universidade de Passo Fundo (UPF) |
repository.mail.fl_str_mv |
biblio@upf.br || bio@upf.br || cas@upf.br || car@upf.br || lve@upf.br || sar@upf.br || sol@upf.br || upfmundi@upf.br || jucelei@upf.br |
_version_ |
1801045443532029952 |