Grafeno e seus derivados: estudo das propriedades de superfície e processos de transferência para substratos poliméricos
Autor(a) principal: | |
---|---|
Data de Publicação: | 2017 |
Tipo de documento: | Dissertação |
Idioma: | por |
Título da fonte: | Biblioteca Digital de Teses e Dissertações do Mackenzie |
Texto Completo: | http://dspace.mackenzie.br/handle/10899/26495 |
Resumo: | This dissertation describes a study of surface properties of graphene obtained by chemical vapor deposition (CVD) to evaluate its hydrophobicity and wetting transparency of this material deposited onto several hard substrates, for instance silicon wafer, glass, etc. To this end, contact angle measurements and the calculation of polar and dispersive components were performed to these samples, submitted or not to a thermal treatment at inert atmosphere. Moreover, a study of the influence of factors that rule transfers processes grounded in Direct Dry Transfer (DDT) of two-dimensional materials (CVD graphene and graphene oxide - GO) onto polymeric surfaces of two or three dimensions was executed, such as surface properties and chemical structure to each materials (two-dimensional and polymers) and rheological properties of polymers. The results indicated graphene is hydrophobic and partially wetting transparent due to influences of the nature of substrates in which it is deposited. However, the thermal treatment at inert atmosphere altered significantly the surface properties of this material, indicating that, for graphene, such properties are strongly influenced by molecules adsorbed onto surface, achieving results very close to those presented in the literature. Talking about transfer processes of 2D materials onto polymers surfaces, the evaluation of surface properties demonstrated to be efficient in predicting the quality and quantity of CVD graphene transferred using DDT. However, factors such as rheological properties and chemical structure must be evaluated concomitantly. Lastly, the efficacy of a technique developed to cover polymer surfaces of three-dimensional substrates with graphene oxide using injection molding processing was presented. |
id |
UPM_452f2a88c045c390daa5687d2d219f76 |
---|---|
oai_identifier_str |
oai:dspace.mackenzie.br:10899/26495 |
network_acronym_str |
UPM |
network_name_str |
Biblioteca Digital de Teses e Dissertações do Mackenzie |
repository_id_str |
10277 |
spelling |
http://lattes.cnpq.br/8109533360196619Fechine, Guilhermino José Macêdohttp://lattes.cnpq.br/4908088101369050Costa, Mariana Caldeira Ferraz da2018-05-04T12:44:02Z2020-12-07T15:07:12Z2020-12-07T15:07:12Z2017-12-13COSTA, Mariana Caldeira Ferraz da. Grafeno e seus derivados: estudo das propriedades de superfície e processos de transferência para substratos poliméricos. 2017. 125 f. Dissertação( Engenharia de Materiais) - Universidade Presbiteriana Mackenzie, São Paulo.http://dspace.mackenzie.br/handle/10899/26495This dissertation describes a study of surface properties of graphene obtained by chemical vapor deposition (CVD) to evaluate its hydrophobicity and wetting transparency of this material deposited onto several hard substrates, for instance silicon wafer, glass, etc. To this end, contact angle measurements and the calculation of polar and dispersive components were performed to these samples, submitted or not to a thermal treatment at inert atmosphere. Moreover, a study of the influence of factors that rule transfers processes grounded in Direct Dry Transfer (DDT) of two-dimensional materials (CVD graphene and graphene oxide - GO) onto polymeric surfaces of two or three dimensions was executed, such as surface properties and chemical structure to each materials (two-dimensional and polymers) and rheological properties of polymers. The results indicated graphene is hydrophobic and partially wetting transparent due to influences of the nature of substrates in which it is deposited. However, the thermal treatment at inert atmosphere altered significantly the surface properties of this material, indicating that, for graphene, such properties are strongly influenced by molecules adsorbed onto surface, achieving results very close to those presented in the literature. Talking about transfer processes of 2D materials onto polymers surfaces, the evaluation of surface properties demonstrated to be efficient in predicting the quality and quantity of CVD graphene transferred using DDT. However, factors such as rheological properties and chemical structure must be evaluated concomitantly. Lastly, the efficacy of a technique developed to cover polymer surfaces of three-dimensional substrates with graphene oxide using injection molding processing was presented.Esta dissertação relata um estudo das propriedades de superfície do grafeno obtido via deposição química na fase vapor (CVD) para avaliação da sua hidrofobicidade e transparência da molhabilidade, quando esse material se encontra depositado em diferentes substratos rígidos, tais como wafer de silício, vidro, entre outros. Para isso, medidas de ângulo de contato e cálculos das componentes polares e dispersivas foram realizados em amostras submetidas ou não a tratamento térmico em atmosfera inerte. Além disso, foi executado um estudo sobre a influência dos fatores que regem processos de transferência fundamentados na técnica Direct Dry Transfer (DDT), envolvendo materiais bidimensionais (grafeno CVD e óxido de grafeno – GO) para superfícies poliméricas, sejam elas de duas ou três dimensões, tais como as propriedades de superfície e estrutura química de ambos os materiais (bidimensionais e polímeros) e as propriedades reológicas dos polímeros. Os resultados indicaram que o grafeno é hidrofóbico e parcialmente transparente ao molhamento devido a influências da natureza do substrato no qual se encontra depositado. O tratamento térmico em atmosfera inerte altera significativamente as propriedades de superfície desse material, indicando que, para o grafeno, tais propriedades são fortemente influenciadas por moléculas adsorvidas na superfície, obtendo resultados muito próximos daqueles previstos teoricamente. Com relação aos processos de transferência de materiais 2D para polímeros, a avaliação das propriedades de superfície dos materiais se demonstrou eficiente na previsão da qualidade e quantidade do grafeno CVD transferido usando a técnica DDT. Contudo, fatores como propriedades reológicas e estrutura química devem ser avaliados concomitantemente. Por último, foi demonstrada a eficiência de uma técnica desenvolvida para recobrimento de superfícies poliméricas de substratos tridimensionais com óxido de grafeno utilizando processamento de moldagem por injeção.Coordenação de Aperfeiçoamento de Pessoal de Nível SuperiorFundo Mackenzie de Pesquisaapplication/pdfporUniversidade Presbiteriana Mackenziehttp://creativecommons.org/licenses/by-nc-nd/4.0/info:eu-repo/semantics/openAccessprocessos de transferênciapolímerografeno e seus derivadospropriedades de superfíciepropriedades reológicasestrutura químicaCNPQ::ENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICAGrafeno e seus derivados: estudo das propriedades de superfície e processos de transferência para substratos poliméricosinfo:eu-repo/semantics/publishedVersioninfo:eu-repo/semantics/masterThesishttp://tede.mackenzie.br/jspui/retrieve/16580/Mariana%20Caldeira%20Ferraz%20da%20Costa.pdf.jpgprocess transfer;polymergraphene and its derivativessurface propertiesrheological propertieschemical structurereponame:Biblioteca Digital de Teses e Dissertações do Mackenzieinstname:Universidade Presbiteriana Mackenzie (MACKENZIE)instacron:MACKENZIEMatos, Christiano José Santiago dehttp://lattes.cnpq.br/6843256597783676Petri, Denise Freitas Siqueirahttp://lattes.cnpq.br/3916542418374036BrasilEscola de Engenharia Mackenzie (EE)UPMEngenharia de MateriaisORIGINALMariana Caldeira Ferraz da Costa.pdfMariana Caldeira Ferraz da Costa.pdfapplication/pdf4262798https://dspace.mackenzie.br/bitstream/10899/26495/1/Mariana%20Caldeira%20Ferraz%20da%20Costa.pdf0e767c221fb06554cb0b9abd237eec91MD51TEXTMariana Caldeira Ferraz da Costa.pdf.txtMariana Caldeira Ferraz da Costa.pdf.txtExtracted texttext/plain236989https://dspace.mackenzie.br/bitstream/10899/26495/2/Mariana%20Caldeira%20Ferraz%20da%20Costa.pdf.txt55c39257c95279babcefa68a71a845ccMD52THUMBNAILMariana Caldeira Ferraz da Costa.pdf.jpgMariana Caldeira Ferraz da Costa.pdf.jpgGenerated Thumbnailimage/jpeg1171https://dspace.mackenzie.br/bitstream/10899/26495/3/Mariana%20Caldeira%20Ferraz%20da%20Costa.pdf.jpgad1ec2edd58914c10975075d35b4b445MD5310899/264952022-03-14 20:54:06.516oai:dspace.mackenzie.br:10899/26495Biblioteca Digital de Teses e Dissertaçõeshttp://tede.mackenzie.br/jspui/PRIhttp://tede.mackenzie.br/oai/requestdspace@mackenzie.br||dspace@mackenzie.bropendoar:102772022-03-14T23:54:06Biblioteca Digital de Teses e Dissertações do Mackenzie - Universidade Presbiteriana Mackenzie (MACKENZIE)false |
dc.title.por.fl_str_mv |
Grafeno e seus derivados: estudo das propriedades de superfície e processos de transferência para substratos poliméricos |
title |
Grafeno e seus derivados: estudo das propriedades de superfície e processos de transferência para substratos poliméricos |
spellingShingle |
Grafeno e seus derivados: estudo das propriedades de superfície e processos de transferência para substratos poliméricos Costa, Mariana Caldeira Ferraz da processos de transferência polímero grafeno e seus derivados propriedades de superfície propriedades reológicas estrutura química CNPQ::ENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICA |
title_short |
Grafeno e seus derivados: estudo das propriedades de superfície e processos de transferência para substratos poliméricos |
title_full |
Grafeno e seus derivados: estudo das propriedades de superfície e processos de transferência para substratos poliméricos |
title_fullStr |
Grafeno e seus derivados: estudo das propriedades de superfície e processos de transferência para substratos poliméricos |
title_full_unstemmed |
Grafeno e seus derivados: estudo das propriedades de superfície e processos de transferência para substratos poliméricos |
title_sort |
Grafeno e seus derivados: estudo das propriedades de superfície e processos de transferência para substratos poliméricos |
author |
Costa, Mariana Caldeira Ferraz da |
author_facet |
Costa, Mariana Caldeira Ferraz da |
author_role |
author |
dc.contributor.advisor1Lattes.fl_str_mv |
http://lattes.cnpq.br/8109533360196619 |
dc.contributor.advisor1.fl_str_mv |
Fechine, Guilhermino José Macêdo |
dc.contributor.authorLattes.fl_str_mv |
http://lattes.cnpq.br/4908088101369050 |
dc.contributor.author.fl_str_mv |
Costa, Mariana Caldeira Ferraz da |
contributor_str_mv |
Fechine, Guilhermino José Macêdo |
dc.subject.por.fl_str_mv |
processos de transferência polímero grafeno e seus derivados propriedades de superfície propriedades reológicas estrutura química |
topic |
processos de transferência polímero grafeno e seus derivados propriedades de superfície propriedades reológicas estrutura química CNPQ::ENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICA |
dc.subject.cnpq.fl_str_mv |
CNPQ::ENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICA |
description |
This dissertation describes a study of surface properties of graphene obtained by chemical vapor deposition (CVD) to evaluate its hydrophobicity and wetting transparency of this material deposited onto several hard substrates, for instance silicon wafer, glass, etc. To this end, contact angle measurements and the calculation of polar and dispersive components were performed to these samples, submitted or not to a thermal treatment at inert atmosphere. Moreover, a study of the influence of factors that rule transfers processes grounded in Direct Dry Transfer (DDT) of two-dimensional materials (CVD graphene and graphene oxide - GO) onto polymeric surfaces of two or three dimensions was executed, such as surface properties and chemical structure to each materials (two-dimensional and polymers) and rheological properties of polymers. The results indicated graphene is hydrophobic and partially wetting transparent due to influences of the nature of substrates in which it is deposited. However, the thermal treatment at inert atmosphere altered significantly the surface properties of this material, indicating that, for graphene, such properties are strongly influenced by molecules adsorbed onto surface, achieving results very close to those presented in the literature. Talking about transfer processes of 2D materials onto polymers surfaces, the evaluation of surface properties demonstrated to be efficient in predicting the quality and quantity of CVD graphene transferred using DDT. However, factors such as rheological properties and chemical structure must be evaluated concomitantly. Lastly, the efficacy of a technique developed to cover polymer surfaces of three-dimensional substrates with graphene oxide using injection molding processing was presented. |
publishDate |
2017 |
dc.date.issued.fl_str_mv |
2017-12-13 |
dc.date.accessioned.fl_str_mv |
2018-05-04T12:44:02Z 2020-12-07T15:07:12Z |
dc.date.available.fl_str_mv |
2020-12-07T15:07:12Z |
dc.type.status.fl_str_mv |
info:eu-repo/semantics/publishedVersion |
dc.type.driver.fl_str_mv |
info:eu-repo/semantics/masterThesis |
format |
masterThesis |
status_str |
publishedVersion |
dc.identifier.citation.fl_str_mv |
COSTA, Mariana Caldeira Ferraz da. Grafeno e seus derivados: estudo das propriedades de superfície e processos de transferência para substratos poliméricos. 2017. 125 f. Dissertação( Engenharia de Materiais) - Universidade Presbiteriana Mackenzie, São Paulo. |
dc.identifier.uri.fl_str_mv |
http://dspace.mackenzie.br/handle/10899/26495 |
identifier_str_mv |
COSTA, Mariana Caldeira Ferraz da. Grafeno e seus derivados: estudo das propriedades de superfície e processos de transferência para substratos poliméricos. 2017. 125 f. Dissertação( Engenharia de Materiais) - Universidade Presbiteriana Mackenzie, São Paulo. |
url |
http://dspace.mackenzie.br/handle/10899/26495 |
dc.language.iso.fl_str_mv |
por |
language |
por |
dc.rights.driver.fl_str_mv |
http://creativecommons.org/licenses/by-nc-nd/4.0/ info:eu-repo/semantics/openAccess |
rights_invalid_str_mv |
http://creativecommons.org/licenses/by-nc-nd/4.0/ |
eu_rights_str_mv |
openAccess |
dc.format.none.fl_str_mv |
application/pdf |
dc.publisher.none.fl_str_mv |
Universidade Presbiteriana Mackenzie |
publisher.none.fl_str_mv |
Universidade Presbiteriana Mackenzie |
dc.source.none.fl_str_mv |
reponame:Biblioteca Digital de Teses e Dissertações do Mackenzie instname:Universidade Presbiteriana Mackenzie (MACKENZIE) instacron:MACKENZIE |
instname_str |
Universidade Presbiteriana Mackenzie (MACKENZIE) |
instacron_str |
MACKENZIE |
institution |
MACKENZIE |
reponame_str |
Biblioteca Digital de Teses e Dissertações do Mackenzie |
collection |
Biblioteca Digital de Teses e Dissertações do Mackenzie |
bitstream.url.fl_str_mv |
https://dspace.mackenzie.br/bitstream/10899/26495/1/Mariana%20Caldeira%20Ferraz%20da%20Costa.pdf https://dspace.mackenzie.br/bitstream/10899/26495/2/Mariana%20Caldeira%20Ferraz%20da%20Costa.pdf.txt https://dspace.mackenzie.br/bitstream/10899/26495/3/Mariana%20Caldeira%20Ferraz%20da%20Costa.pdf.jpg |
bitstream.checksum.fl_str_mv |
0e767c221fb06554cb0b9abd237eec91 55c39257c95279babcefa68a71a845cc ad1ec2edd58914c10975075d35b4b445 |
bitstream.checksumAlgorithm.fl_str_mv |
MD5 MD5 MD5 |
repository.name.fl_str_mv |
Biblioteca Digital de Teses e Dissertações do Mackenzie - Universidade Presbiteriana Mackenzie (MACKENZIE) |
repository.mail.fl_str_mv |
dspace@mackenzie.br||dspace@mackenzie.br |
_version_ |
1757177212289679360 |